Evaluation of the anticorrosive behavior of epoxy-Nb2O5 paint in high temperatures submitted to the environment with sulfuric acid

Authors: Maria Eduarda Dias Serenario, Bernardo Augusto Farah Santos, Luiz Roberto Martins de Miranda, Alysson Helton Santos Bueno

Published in: Journal of Coatings Technology and Research | Issue 5/2020

Login to get access
share
SHARE

Abstract

The aim of the present work is to evaluate the corrosion resistance of epoxy-Nb2O5 paint in acid atmosphere and high temperatures. For comparison, samples of SAE1020 carbon steel were coated with an epoxy-Nb2O5 paint and an epoxy commercial paint. The samples were partially immersed for 720 h and 1440 h in 40% (v/v) H2SO4 solution at temperatures of 25°C, 60°C, and 80°C. The degradation analysis, mechanical characterization, and electrochemical measurements of the samples were carried out after immersion period. The coatings were characterized by scanning electron microscopy. Electrochemical impedance spectroscopy was used to evaluate the electrochemical behavior. Results showed the epoxy-Nb2O5 paint was less blistering, cracked, flaked, and rusted than the commercial epoxy paint samples. However, it was important to note that the increase in temperature led to the degradation of epoxy-Nb2O5 paint. The addition of temperature was probably responsible for the degradation of epoxy resin over the immersion time.

To get access to this content you need the following product:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 15 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 15 Tage kostenlos.

Literature
1.
go back to reference Furtado, P, “Pintura anticorrosiva dos metais.” 378 (2009) Furtado, P, “Pintura anticorrosiva dos metais.” 378 (2009)
2.
go back to reference Serenário, MED, Abreu, FT, Souza, RC, Santos, BAF, Miranda, LRM, Bueno, AHS, “Estudo das propriedades da tinta epóxi-Nb 2O 5 aplicada na indústria química.” Revista Virtual de Química, 11 (1) 218–236 (2019) CrossRef Serenário, MED, Abreu, FT, Souza, RC, Santos, BAF, Miranda, LRM, Bueno, AHS, “Estudo das propriedades da tinta epóxi-Nb 2O 5 aplicada na indústria química.” Revista Virtual de Química, 11 (1) 218–236 (2019) CrossRef
3.
go back to reference Brostow, W, Dutta, M, Rusek, P, “Modified epoxy coatings on mild steel: tribology and surface energy.” European Polymer Journal, 46 (11) 2181–2189 (2010) CrossRef Brostow, W, Dutta, M, Rusek, P, “Modified epoxy coatings on mild steel: tribology and surface energy.” European Polymer Journal, 46 (11) 2181–2189 (2010) CrossRef
4.
go back to reference Longhi, M, Zini, LP, Pistor, V, Kunst, SR, Zattera, AJ, “Evaluation of the mechanic and electrochemical properties of an epoxy coating with addition of different polyhedral oligomeric silsesquioxanes (POSS) applied on substrate of low alloy steel.” Materials Research, 20 (5) 1388–1401 (2017) CrossRef Longhi, M, Zini, LP, Pistor, V, Kunst, SR, Zattera, AJ, “Evaluation of the mechanic and electrochemical properties of an epoxy coating with addition of different polyhedral oligomeric silsesquioxanes (POSS) applied on substrate of low alloy steel.” Materials Research, 20 (5) 1388–1401 (2017) CrossRef
5.
go back to reference Zhang, Y, Zhao, M, Zhang, J, Shao, Q, Li, J, Li, H, Lin, B, Yu, M, Chen, S, Guo, Z, “Excellent corrosion protection performance of epoxy composite coatings filled with silane functionalized silicon nitride.” Journal of Polymer Research, 25 130 (2018) CrossRef Zhang, Y, Zhao, M, Zhang, J, Shao, Q, Li, J, Li, H, Lin, B, Yu, M, Chen, S, Guo, Z, “Excellent corrosion protection performance of epoxy composite coatings filled with silane functionalized silicon nitride.” Journal of Polymer Research, 25 130 (2018) CrossRef
6.
go back to reference Mathieu, S, Knittel, S, Berthod, P, Mathieu, S, Vilasi, M, “On the oxidation mechanism of niobium-base in situ composites.” Corrosion Science, 60 181–192 (2012) CrossRef Mathieu, S, Knittel, S, Berthod, P, Mathieu, S, Vilasi, M, “On the oxidation mechanism of niobium-base in situ composites.” Corrosion Science, 60 181–192 (2012) CrossRef
7.
go back to reference Melo, RS, Brasil, SLDC, Carvalho, LJ, Reznik, LY, “Using electrochemical impedance spectroscopy sinusoidal potential amplitude to assess the efficiency of niobium oxide based organic coating in oil wells produced water.” International Journal of Electrochemical Science, 11 (12) 10511–10521 (2016) CrossRef Melo, RS, Brasil, SLDC, Carvalho, LJ, Reznik, LY, “Using electrochemical impedance spectroscopy sinusoidal potential amplitude to assess the efficiency of niobium oxide based organic coating in oil wells produced water.” International Journal of Electrochemical Science, 11 (12) 10511–10521 (2016) CrossRef
8.
go back to reference Miranda, LRM, Carvalho, LJ, Pereira, AC, “United States Patent - Niobium based paint and coating, its oxides and anticorrosive use (US 6.992.126 B2).” (2006) Miranda, LRM, Carvalho, LJ, Pereira, AC, “United States Patent - Niobium based paint and coating, its oxides and anticorrosive use (US 6.992.126 B2).” (2006)
9.
go back to reference Novoa, L, Cortes, LE, Gonzales, E, Jimenez, A, Cortes, LG, Ojeda, M, Barbosa, AL, “Evaluation of anticorrosive effect of niobium carbide coating applied on carbon steel.” Chemical Engineering Transactions, 57 1387–1392 (2017) Novoa, L, Cortes, LE, Gonzales, E, Jimenez, A, Cortes, LG, Ojeda, M, Barbosa, AL, “Evaluation of anticorrosive effect of niobium carbide coating applied on carbon steel.” Chemical Engineering Transactions, 57 1387–1392 (2017)
10.
go back to reference Pehlivan, E, Koc, K, Tepehan, FZ, Tepehan, GG, “Structural, optical and electrochromic properties of tantalum pentoxide-doped niobium pentoxide thin films.” Journal of Sol-Gel Science and Technology, 77 (1) 172–178 (2016) CrossRef Pehlivan, E, Koc, K, Tepehan, FZ, Tepehan, GG, “Structural, optical and electrochromic properties of tantalum pentoxide-doped niobium pentoxide thin films.” Journal of Sol-Gel Science and Technology, 77 (1) 172–178 (2016) CrossRef
11.
go back to reference Pourbaix, M, “Atlas of electrochemical equilibria in aqueous solutions.” Houston, Tex: National Association of Corrosion Engineers, 644 (1974) Pourbaix, M, “Atlas of electrochemical equilibria in aqueous solutions.” Houston, Tex: National Association of Corrosion Engineers, 644 (1974)
12.
go back to reference Bodstein, HEM, “Estudos de sistemas de pintura para altas temperaturas à base de resinas pigmentadas com Nb 2O 5.” Doctoral Thesis in Metallurgical and Materials Science and Engineering – Federal University of Rio de Janeiro, 137 (2006) Bodstein, HEM, “Estudos de sistemas de pintura para altas temperaturas à base de resinas pigmentadas com Nb 2O 5.” Doctoral Thesis in Metallurgical and Materials Science and EngineeringFederal University of Rio de Janeiro, 137 (2006)
13.
go back to reference Sahir, ZS, Sykes, JM, “Effect of temperature on the impedance response of coated metals.” Progress in Organic Coatings, 77 (12) 2039–2044 (2014) CrossRef Sahir, ZS, Sykes, JM, “Effect of temperature on the impedance response of coated metals.” Progress in Organic Coatings, 77 (12) 2039–2044 (2014) CrossRef
14.
go back to reference Sharer, Z, Sykes, JM, “Insights into protection mechanisms of organic coatings from thermal testing with EIS.” Progress in Organic Coatings, 74 (2) 405–409 (2012) CrossRef Sharer, Z, Sykes, JM, “Insights into protection mechanisms of organic coatings from thermal testing with EIS.” Progress in Organic Coatings, 74 (2) 405–409 (2012) CrossRef
15.
go back to reference Valentinelli, L, Vogelsang, J, Fedrizzi, L, “Evaluation of barrier coatings by cycling testing.” Progress in Organic Coatings, 45 (4) 405–413 (2002) CrossRef Valentinelli, L, Vogelsang, J, Fedrizzi, L, “Evaluation of barrier coatings by cycling testing.” Progress in Organic Coatings, 45 (4) 405–413 (2002) CrossRef
16.
go back to reference ISO INTERNATIONAL. “Preparation of steel substrates before application of paints and related products—Visual assessment of surface cleanliness.” ISO 8501-1 (2007) ISO INTERNATIONAL. “Preparation of steel substrates before application of paints and related products—Visual assessment of surface cleanliness.” ISO 8501-1 (2007)
17.
go back to reference ISO INTERNATIONAL. “Paints and varnishes: Evaluation of degradation of coatings—Designation of quantity and size of defects, and of intensity of uniform changes in appearance.” ISO 4628 (2016) ISO INTERNATIONAL. “Paints and varnishes: Evaluation of degradation of coatings—Designation of quantity and size of defects, and of intensity of uniform changes in appearance.” ISO 4628 (2016)
18.
go back to reference ASTM E384-17. “Standard Test Method for Microindentation Hardness of Materials.” (2017) ASTM E384-17. “Standard Test Method for Microindentation Hardness of Materials.” (2017)
19.
go back to reference ISO INTERNATIONAL. “Paints, varnishes and plastics: Pull-off test for adhesion.” ISO 4624 (2003) ISO INTERNATIONAL. “Paints, varnishes and plastics: Pull-off test for adhesion.” ISO 4624 (2003)
20.
go back to reference Malinowski, SA, “Pintura em ambientes imersos de usinas hidrelétricas utilizando tintas livres de alcatrão de hulha Pintura em ambientes imersos de usinas hidrelétricas utilizando tintas livres de alcatrão de hulha.” Master’s Dissertation in Technology Development— Federal University of Paraná, 123 (2013) Malinowski, SA, “Pintura em ambientes imersos de usinas hidrelétricas utilizando tintas livres de alcatrão de hulha Pintura em ambientes imersos de usinas hidrelétricas utilizando tintas livres de alcatrão de hulha.” Master’s Dissertation in Technology DevelopmentFederal University of Paraná, 123 (2013)
21.
go back to reference Silva, TC, “Efeitos da variação de temperatura em revestimentos compósitos anticorrosivos.” Master’s Dissertation in Metallurgical and Materials Science and Engineering— Federal University of Rio de Janeiro, 107 (2013) Silva, TC, “Efeitos da variação de temperatura em revestimentos compósitos anticorrosivos.” Master’s Dissertation in Metallurgical and Materials Science and EngineeringFederal University of Rio de Janeiro, 107 (2013)
22.
go back to reference Zhang, JT, Hu, JM, Zhang, JQ, Cao, CN, “Studies of water transport behavior and impedance models of epoxy-coated metals in NaCl solution by EIS.” Progress in Organic Coatings, 51 (2) 145–151 (2004) CrossRef Zhang, JT, Hu, JM, Zhang, JQ, Cao, CN, “Studies of water transport behavior and impedance models of epoxy-coated metals in NaCl solution by EIS.” Progress in Organic Coatings, 51 (2) 145–151 (2004) CrossRef
23.
go back to reference Ha, HM, Alfantazi, A, “On the role of water, temperature, and glass transition in the corrosion protection behavior of epoxy coatings for underground pipelines.” Journal of Coatings Technology and Research, 12 (6) 1095–1110 (2015) CrossRef Ha, HM, Alfantazi, A, “On the role of water, temperature, and glass transition in the corrosion protection behavior of epoxy coatings for underground pipelines.” Journal of Coatings Technology and Research, 12 (6) 1095–1110 (2015) CrossRef
24.
go back to reference Hare, CH, Protective Coatings: Fundamentals of Chemistry and Composition. Technology Pub, Co (1994) Hare, CH, Protective Coatings: Fundamentals of Chemistry and Composition. Technology Pub, Co (1994)
25.
go back to reference Zhou, J, Lucas, JP, “Hygrothermal effects of epoxy resin. Part I: the nature of water in epoxy.” Polymer, 40 (20) 5505–5512 (1999) CrossRef Zhou, J, Lucas, JP, “Hygrothermal effects of epoxy resin. Part I: the nature of water in epoxy.” Polymer, 40 (20) 5505–5512 (1999) CrossRef
26.
go back to reference Quelhas, KAS, “Estudo da corrosão do nióbio em meio metanólico.” Doctoral Thesis in Metallurgical and Materials Science and Engineering— Federal University of Rio de Janeiro, 105 (2007) Quelhas, KAS, “Estudo da corrosão do nióbio em meio metanólico.” Doctoral Thesis in Metallurgical and Materials Science and EngineeringFederal University of Rio de Janeiro, 105 (2007)
27.
go back to reference Pillis, MF, Oliveira, MCL, Antunes, RA, “Surface chemistry and the corrosion behavior of magnetron sputtered niobium oxide films in sulfuric acid solution.” Applied Surface Science, 462 (31) 344–352 (2018) CrossRef Pillis, MF, Oliveira, MCL, Antunes, RA, “Surface chemistry and the corrosion behavior of magnetron sputtered niobium oxide films in sulfuric acid solution.” Applied Surface Science, 462 (31) 344–352 (2018) CrossRef
28.
go back to reference Asselin, E, Ahmed, TM, Alfantazi, A, “Corrosion of niobium in sulphuric and hydrochloric acid solutions at 75 and 95°C.” Corrosion Science, 49 (2) 694–710 (2007) CrossRef Asselin, E, Ahmed, TM, Alfantazi, A, “Corrosion of niobium in sulphuric and hydrochloric acid solutions at 75 and 95°C.” Corrosion Science, 49 (2) 694–710 (2007) CrossRef
29.
go back to reference Boubakri, A, Haddar, N, Elleuch, K, Bienvenu, Y, “Influence of thermal aging on tensile and creep behavior of thermoplastic polyurethane.” Comptes Rendus Mecanique, 339 (10) 666–673 (2011) CrossRef Boubakri, A, Haddar, N, Elleuch, K, Bienvenu, Y, “Influence of thermal aging on tensile and creep behavior of thermoplastic polyurethane.” Comptes Rendus Mecanique, 339 (10) 666–673 (2011) CrossRef
30.
go back to reference Oliveira, RM, Oliveira, AC, Carreri, FC, Gomes, GF, Ueda, M, Silva, MMNF, Pichon, L, Tóth, A, “Detailed surface analyses and improved mechanical and tribological properties of niobium treated by high temperature nitrogen plasma based ion implantation.” Applied Surface Science, 283 382–388 (2013) CrossRef Oliveira, RM, Oliveira, AC, Carreri, FC, Gomes, GF, Ueda, M, Silva, MMNF, Pichon, L, Tóth, A, “Detailed surface analyses and improved mechanical and tribological properties of niobium treated by high temperature nitrogen plasma based ion implantation.” Applied Surface Science, 283 382–388 (2013) CrossRef
31.
go back to reference Vosgien Lacombre, C, Bouvet, G, Trinh, D, Mallarino, S, Touzain, S, “Effect of pigment and temperature onto swelling and water uptake during organic coating ageing.” Progress in Organic Coatings, 124 249–255 (2018) CrossRef Vosgien Lacombre, C, Bouvet, G, Trinh, D, Mallarino, S, Touzain, S, “Effect of pigment and temperature onto swelling and water uptake during organic coating ageing.” Progress in Organic Coatings, 124 249–255 (2018) CrossRef
32.
go back to reference Behzadnasab, M, Mirabedini, SM, Kabriri, K, Jamali, S, “Corrosion performance of epoxy coatings containing silane treated ZrO 2 nanoparticles on mild steel in 3.5% NaCl solution.” Corrosion Science, 53 (1) 89–98 (2011) CrossRef Behzadnasab, M, Mirabedini, SM, Kabriri, K, Jamali, S, “Corrosion performance of epoxy coatings containing silane treated ZrO 2 nanoparticles on mild steel in 3.5% NaCl solution.” Corrosion Science, 53 (1) 89–98 (2011) CrossRef
33.
go back to reference Hou, WP, Liu, Y, Ge, ZY, Zhao, WY, “Comparison study on anticorrosion performances of the epoxy coatings with two different nano-polyanilines for Q235 steel.” Materials and Corrosion, 64 (11) 960–968 (2013) CrossRef Hou, WP, Liu, Y, Ge, ZY, Zhao, WY, “Comparison study on anticorrosion performances of the epoxy coatings with two different nano-polyanilines for Q235 steel.” Materials and Corrosion, 64 (11) 960–968 (2013) CrossRef
34.
go back to reference Javidparvar, AA, Naderi, R, Ramezanzadeh, B, “Epoxy-polyamide nanocomposite coating with graphene oxide as cerium nanocontainer generating effective dual active/barrier corrosion protection.” Composites Part B: Engineering, 172 363–375 (2019) CrossRef Javidparvar, AA, Naderi, R, Ramezanzadeh, B, “Epoxy-polyamide nanocomposite coating with graphene oxide as cerium nanocontainer generating effective dual active/barrier corrosion protection.” Composites Part B: Engineering, 172 363–375 (2019) CrossRef
35.
go back to reference Bahlakeh, G, Ramezanzadeh, B, Saeb, MR, Terryn, H, Ghaffarie, M, “Corrosion protection properties and interfacial adhesion mechanism of an epoxy/polyamide coating applied on the steel surface decorated with cerium oxide nanofilm: Complementary experimental, molecular dynamics (MD) and first principle quantum mechanics.” Applied Surface Science, 419 650–669 (2017) CrossRef Bahlakeh, G, Ramezanzadeh, B, Saeb, MR, Terryn, H, Ghaffarie, M, “Corrosion protection properties and interfacial adhesion mechanism of an epoxy/polyamide coating applied on the steel surface decorated with cerium oxide nanofilm: Complementary experimental, molecular dynamics (MD) and first principle quantum mechanics.” Applied Surface Science, 419 650–669 (2017) CrossRef
36.
go back to reference Pan, TJ, Chen, Y, Zhang, B, Hu, J, Li, C, “Corrosion behavior of niobium coated 304 stainless steel in acid solution.” Applied Surface Science, 369 320–325 (2016) CrossRef Pan, TJ, Chen, Y, Zhang, B, Hu, J, Li, C, “Corrosion behavior of niobium coated 304 stainless steel in acid solution.” Applied Surface Science, 369 320–325 (2016) CrossRef
37.
go back to reference Macedo, MCSS, Margarit-Mattos, ICP, Fragata, FL, Jorcin, JB, Pébêre, N, Mattos, OT, “Contribution to a better understanding of different behaviour patterns observed with organic coatings evaluated by electrochemical impedance spectroscopy.” Corrosion Science, 51 (6) 1322–1327 (2009) CrossRef Macedo, MCSS, Margarit-Mattos, ICP, Fragata, FL, Jorcin, JB, Pébêre, N, Mattos, OT, “Contribution to a better understanding of different behaviour patterns observed with organic coatings evaluated by electrochemical impedance spectroscopy.” Corrosion Science, 51 (6) 1322–1327 (2009) CrossRef
38.
go back to reference Grundmeier, G, Schmidt, W, Stratmann, M, “Corrosion protection by organic coatings: Electrochemical mechanism and novel methods of investigation.” Electrochimica Acta, 45 (15–16) 2515–2533 (2000) CrossRef Grundmeier, G, Schmidt, W, Stratmann, M, “Corrosion protection by organic coatings: Electrochemical mechanism and novel methods of investigation.” Electrochimica Acta, 45 (15–16) 2515–2533 (2000) CrossRef
39.
go back to reference Rojas, PN, Rodil, SE, “Corrosion behaviour of amorphous niobium oxide coatings.” International Journal of Electrochemical Science, 7 1443–1458 (2012) Rojas, PN, Rodil, SE, “Corrosion behaviour of amorphous niobium oxide coatings.” International Journal of Electrochemical Science, 7 1443–1458 (2012)
40.
go back to reference Selvaraj, M, Sathianarayanan, S, Muthukrishnan, S, Venkatachari, G, “Corrosion protective performance studies of coating systems in soda ash chemical industry.” Progress in Organic Coatings, 66 (3) 206–212 (2009) CrossRef Selvaraj, M, Sathianarayanan, S, Muthukrishnan, S, Venkatachari, G, “Corrosion protective performance studies of coating systems in soda ash chemical industry.” Progress in Organic Coatings, 66 (3) 206–212 (2009) CrossRef
Metadata
Title
Evaluation of the anticorrosive behavior of epoxy-Nb2O5 paint in high temperatures submitted to the environment with sulfuric acid
Authors
Maria Eduarda Dias Serenario
Bernardo Augusto Farah Santos
Luiz Roberto Martins de Miranda
Alysson Helton Santos Bueno
Publication date
14-05-2020
Publisher
Springer US
Published in
Journal of Coatings Technology and Research / Issue 5/2020
Print ISSN: 1547-0091
Electronic ISSN: 1935-3804
DOI
https://doi.org/10.1007/s11998-020-00354-z

Other articles of this Issue 5/2020

Journal of Coatings Technology and Research 5/2020 Go to the issue

Premium Partners