Failure Analysis of Type 1.4301 Stainless Steel in a Cooling Water System

Journal:
Journal of Failure Analysis and Prevention > Issue 3/2015
Authors:
Chao Guo, Ming Li, Quanfeng Shen, Biao Tian, Shan Gao

Abstract

Pitting of Type 1.4301 stainless steel pipe in a brackish cooling water system was studied. The results showed that pitting of the Type 1.4301 stainless steel occurred when the water temperature was more than 40 °C, and the introduction of Fe2+ or Fe3+ with concentrated chloride ions led to more severe corrosion in this cooling water system.

Please log in to get access to this content

To get access to this content you need the following product:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Literature
About this article

Other articles of this Issue 3/2015

Journal of Failure Analysis and Prevention 3/2015 Go to the issue

Calendar

Training

Premium Partners

    Image Credits