Failure Analysis of Weld Cracking in a Thick-Walled 2.25Cr-1Mo Steel Pressure Vessel

Journal:
Journal of Materials Engineering and Performance > Issue 4/2014
Authors:
Xiaowei Lei, Jing Niu, Jianxun Zhang, Anqing Fu, Yaorong Feng

Abstract

A crack in thick-walled 2.25Cr-1Mo steel pressure vessel girth weld was found during manufacturing. To investigate the cause of failure, optical microscopy, scanning electron microscopy, energy dispersive spectrometer, transmission electron microscopy, and microhardness tester were used in this study. According to test results, the fracture is classified as reheat cracking with multiple origins. The cracking occurred during surfacing or final post-weld heat treatment process. Coarse-grains in the weld and bulk-carbides precipitated along grain boundaries induced by multiple heating are main causes of the fracture from material aspect, while high level of the hoop stress component and excess localized deformation in stress relief procedure are mechanical aspect causes of the cracking. The fracture surfaces present major intergranular feature with a small fraction of transgranular morphologies. Large numbers of M3C and M23C6 carbides particles were found on the fracture surface, these carbides mainly precipitated on prior austenite-grain boundaries, columnar-grain boundaries, and sub-grain boundaries. Additionally, several proposals were also offered to reduce weld cracking of 2.25Cr-1Mo steel pressure vessels.

Please log in to get access to this content

To get access to this content you need the following product:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe​​​​​​​




Testen Sie jetzt 30 Tage kostenlos.

Literature
About this article

Other articles of this Issue 4/2014

Journal of Materials Engineering and Performance 4/2014 Go to the issue

Premium Partner

    Image Credits