Fluidity and strength behaviors of cemented foam backfill: effect of particle size distribution and foaming agent dosage

Authors: Shiyu Zhang, Lei Yang, Jingping Qiu, Chen Hou, Zhenbang Guo

Published in: Bulletin of Engineering Geology and the Environment | Issue 4/2021

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

The influence of aggregate gradation (11 gradations with volume moment mean diameter ranging from 192 to 398 μm) and hydrogen peroxide (HP) dosage (0%, 0.8%, 1.6%, 2.4%, and 3.2% by weight of cement) on the fluidity, strength, and microstructure of cemented foam backfill (CFB) was comprehensively evaluated in this study. The fluidity, expansion ratio, and water film thickness for fresh CFB and 28-day strength and microstructural properties for hardened CFB were compared as a function of aggregate gradation and HP dosage. The end results reveal that the fluidity of fresh CFB decreases with finer aggregate and higher HP dosage due to their effect on water film thickness, but the expansion ratio increases. The strength for hardened backfill without foaming agent increases with coarser aggregate, but that for cemented foam backfill decreases. Additionally, the mercury intrusion porosimetry (MIP) results denote that the variation of aggregate gradation and HP dosage mainly influences the volume of large pores (>1 μm) and consequently the overall porosity of CFB, resulting in the strength variation. The linear relationship between compressive strength and averaged fractal dimensions of cross-sections obtained from X-ray CT indicates that the number of extra-large pores (100~500 μm) determines the strength of CFB. The influence of HP on the hydration reaction of backfill and the potential application of CFB in mining practices are also discussed.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Literature
go back to reference Abdollahnejad Z, PachecoTorgal F, Félix T, Tahri W, Aguiar JB (2015) Mix design, properties and cost analysis of fly ash-based geopolymer foam. Constr Build Mater 80:18–30CrossRef Abdollahnejad Z, PachecoTorgal F, Félix T, Tahri W, Aguiar JB (2015) Mix design, properties and cost analysis of fly ash-based geopolymer foam. Constr Build Mater 80:18–30CrossRef
go back to reference Benzaazoua M, Fall M, Belem T (2004) A contribution to understanding the hardening process of cemented pastefill. Miner Eng 17:141–152CrossRef Benzaazoua M, Fall M, Belem T (2004) A contribution to understanding the hardening process of cemented pastefill. Miner Eng 17:141–152CrossRef
go back to reference Çakır Ö, Aköz F (2008) Effect of curing conditions on the mortars with and without GGBFS. Constr Build Mater 22:308–314CrossRef Çakır Ö, Aköz F (2008) Effect of curing conditions on the mortars with and without GGBFS. Constr Build Mater 22:308–314CrossRef
go back to reference Cao S, Song W, Yilmaz E (2018) Influence of structural factors on uniaxial compressive strength of cemented tailings backfill. Constr Build Mater 174:190–201CrossRef Cao S, Song W, Yilmaz E (2018) Influence of structural factors on uniaxial compressive strength of cemented tailings backfill. Constr Build Mater 174:190–201CrossRef
go back to reference Consoli NC, Nierwinski HP, da Silva AP, Sosnoski J (2017) Durability and strength of fiber-reinforced compacted gold tailings-cement blends. Geotext Geomembr 45:98–102CrossRef Consoli NC, Nierwinski HP, da Silva AP, Sosnoski J (2017) Durability and strength of fiber-reinforced compacted gold tailings-cement blends. Geotext Geomembr 45:98–102CrossRef
go back to reference Coppola B, Di Maio L, Courard L, Scarfato P, Incarnato L (2015) Lightweight cementitious mortar made with foamed plastic waste aggregates. Spec Publ 305:31.31–31.10 Coppola B, Di Maio L, Courard L, Scarfato P, Incarnato L (2015) Lightweight cementitious mortar made with foamed plastic waste aggregates. Spec Publ 305:31.31–31.10
go back to reference Costopoulos NG, Newhouse HK (1987) Building material manufacturing from fly ash. Google Patents Costopoulos NG, Newhouse HK (1987) Building material manufacturing from fly ash. Google Patents
go back to reference Deng X, Klein B, Hallbom D, de Wit B, Zhang J (2018) Influence of particle size on the basic and time-dependent rheological behaviors of cemented paste backfill. J Mater Eng Perform 27:3478–3487CrossRef Deng X, Klein B, Hallbom D, de Wit B, Zhang J (2018) Influence of particle size on the basic and time-dependent rheological behaviors of cemented paste backfill. J Mater Eng Perform 27:3478–3487CrossRef
go back to reference Deng X, Zhang J, Klein B, Zhou N, Dewit B (2017) Experimental characterization of the influence of solid components on the rheological and mechanical properties of cemented paste backfill. Int J Miner Process 168:116–125CrossRef Deng X, Zhang J, Klein B, Zhou N, Dewit B (2017) Experimental characterization of the influence of solid components on the rheological and mechanical properties of cemented paste backfill. Int J Miner Process 168:116–125CrossRef
go back to reference Fall M, Benzaazoua M (2005) Modeling the effect of sulphate on strength development of paste backfill and binder mixture optimization. Cem Concr Res 35:301–314CrossRef Fall M, Benzaazoua M (2005) Modeling the effect of sulphate on strength development of paste backfill and binder mixture optimization. Cem Concr Res 35:301–314CrossRef
go back to reference Fall M, Benzaazoua M, Ouellet S (2005) Experimental characterization of the influence of tailings fineness and density on the quality of cemented paste backfill. Miner Eng 18:41–44CrossRef Fall M, Benzaazoua M, Ouellet S (2005) Experimental characterization of the influence of tailings fineness and density on the quality of cemented paste backfill. Miner Eng 18:41–44CrossRef
go back to reference Fall M, Benzaazoua M, Saa E (2008) Mix proportioning of underground cemented tailings backfill. Tunn Undergr Space Technol 23:80–90CrossRef Fall M, Benzaazoua M, Saa E (2008) Mix proportioning of underground cemented tailings backfill. Tunn Undergr Space Technol 23:80–90CrossRef
go back to reference Fall M, Célestin J, Pokharel M, Touré M (2010) A contribution to understanding the effects of curing temperature on the mechanical properties of mine cemented tailings backfill. Eng Geol 114:397–413CrossRef Fall M, Célestin J, Pokharel M, Touré M (2010) A contribution to understanding the effects of curing temperature on the mechanical properties of mine cemented tailings backfill. Eng Geol 114:397–413CrossRef
go back to reference Fall M, Pokharel M (2010) Coupled effects of sulphate and temperature on the strength development of cemented tailings backfills: Portland cement-paste backfill. Cem Concr Compos 32:819–828CrossRef Fall M, Pokharel M (2010) Coupled effects of sulphate and temperature on the strength development of cemented tailings backfills: Portland cement-paste backfill. Cem Concr Compos 32:819–828CrossRef
go back to reference Fernandez A, Calvo JG, Alonso M (2018) Ordinary Portland cement composition for the optimization of the synergies of supplementary cementitious materials of ternary binders in hydration processes. Cem Concr Compos 89:238–250CrossRef Fernandez A, Calvo JG, Alonso M (2018) Ordinary Portland cement composition for the optimization of the synergies of supplementary cementitious materials of ternary binders in hydration processes. Cem Concr Compos 89:238–250CrossRef
go back to reference Fridjonsson E, Hasan A, Fourie A, Johns M (2013) Pore structure in a gold mine cemented paste backfill. Miner Eng 53:144–151CrossRef Fridjonsson E, Hasan A, Fourie A, Johns M (2013) Pore structure in a gold mine cemented paste backfill. Miner Eng 53:144–151CrossRef
go back to reference Hamidah M, Azmi I, Ruslan M, Kartini K, Fadhil N Optimisation of foamed concrete mix of different sand-cement ratio and curing conditions. In: Use of foamed concrete in construction: Proceedings of the International Conference held at the University of Dundee, Scotland, UK on 5 July 2005, 2005. Thomas Telford Publishing, pp 37–44 Hamidah M, Azmi I, Ruslan M, Kartini K, Fadhil N Optimisation of foamed concrete mix of different sand-cement ratio and curing conditions. In: Use of foamed concrete in construction: Proceedings of the International Conference held at the University of Dundee, Scotland, UK on 5 July 2005, 2005. Thomas Telford Publishing, pp 37–44
go back to reference Han J, Jia D, Yan P (2016) Understanding the shrinkage compensating ability of type K expansive agent in concrete. Constr Build Mater 116:36–44CrossRef Han J, Jia D, Yan P (2016) Understanding the shrinkage compensating ability of type K expansive agent in concrete. Constr Build Mater 116:36–44CrossRef
go back to reference Hefni M, Hassani F, Nokken M, Kermani M, Vatne D Investigation into the development of foam mine fill. In: Proceedings of the Eleventh International Symposium on Mining with Backfill, 2014. Australian Centre for Geomechanics, pp 49–59 Hefni M, Hassani F, Nokken M, Kermani M, Vatne D Investigation into the development of foam mine fill. In: Proceedings of the Eleventh International Symposium on Mining with Backfill, 2014. Australian Centre for Geomechanics, pp 49–59
go back to reference Hou C, Zhu W, Yan B, Guan K, Du J (2018) Influence of binder content on temperature and internal strain evolution of early age cemented tailings backfill. Constr Build Mater 189:585–593CrossRef Hou C, Zhu W, Yan B, Guan K, Du J (2018) Influence of binder content on temperature and internal strain evolution of early age cemented tailings backfill. Constr Build Mater 189:585–593CrossRef
go back to reference Huang Z, Zhang T, Wen Z (2015) Proportioning and characterization of Portland cement-based ultra-lightweight foam concretes. Constr Build Mater 79:390–396CrossRef Huang Z, Zhang T, Wen Z (2015) Proportioning and characterization of Portland cement-based ultra-lightweight foam concretes. Constr Build Mater 79:390–396CrossRef
go back to reference Jiang H, Fall M, Cui L (2016) Yield stress of cemented paste backfill in sub-zero environments: experimental results. Miner Eng 92:141–150CrossRef Jiang H, Fall M, Cui L (2016) Yield stress of cemented paste backfill in sub-zero environments: experimental results. Miner Eng 92:141–150CrossRef
go back to reference Jiang H, Fall M, Yilmaz E, Li Y, Yang L (2020) Effect of mineral admixtures on flow properties of fresh cemented paste backfill: assessment of time dependency and thixotropy. Powder Technol 372:258–266CrossRef Jiang H, Fall M, Yilmaz E, Li Y, Yang L (2020) Effect of mineral admixtures on flow properties of fresh cemented paste backfill: assessment of time dependency and thixotropy. Powder Technol 372:258–266CrossRef
go back to reference Jin S, Zhang J, Han S (2017) Fractal analysis of relation between strength and pore structure of hardened mortar. Constr Build Mater 135:1–7CrossRef Jin S, Zhang J, Han S (2017) Fractal analysis of relation between strength and pore structure of hardened mortar. Constr Build Mater 135:1–7CrossRef
go back to reference Kastiukas G, Zhou X, Wan KT, Castro Gomes J (2019) Lightweight alkali-activated material from mining and glass waste by chemical and physical foaming. J Mater Civ Eng 31 Kastiukas G, Zhou X, Wan KT, Castro Gomes J (2019) Lightweight alkali-activated material from mining and glass waste by chemical and physical foaming. J Mater Civ Eng 31
go back to reference Ke X, Hou H, Zhou M, Wang Y, Zhou X (2015) Effect of particle gradation on properties of fresh and hardened cemented paste backfill. Constr Build Mater 96:378–382CrossRef Ke X, Hou H, Zhou M, Wang Y, Zhou X (2015) Effect of particle gradation on properties of fresh and hardened cemented paste backfill. Constr Build Mater 96:378–382CrossRef
go back to reference Koohestani B, Belem T, Koubaa A, Bussiere B (2016) Experimental investigation into the compressive strength development of cemented paste backfill containing Nano-silica. Cem Concr Compos 72:180–189CrossRef Koohestani B, Belem T, Koubaa A, Bussiere B (2016) Experimental investigation into the compressive strength development of cemented paste backfill containing Nano-silica. Cem Concr Compos 72:180–189CrossRef
go back to reference Kumar R, Bhattacharjee B (2003) Study on some factors affecting the results in the use of MIP method in concrete research. Cem Concr Res 33:417–424CrossRef Kumar R, Bhattacharjee B (2003) Study on some factors affecting the results in the use of MIP method in concrete research. Cem Concr Res 33:417–424CrossRef
go back to reference Kwan A, McKinley M (2014) Effects of limestone fines on water film thickness, paste film thickness and performance of mortar. Powder Technol 261:33–41CrossRef Kwan A, McKinley M (2014) Effects of limestone fines on water film thickness, paste film thickness and performance of mortar. Powder Technol 261:33–41CrossRef
go back to reference Kwan A, Wong H (2008) Effects of packing density, excess water and solid surface area on flowability of cement paste. Adv Cem Res 20:1–11CrossRef Kwan A, Wong H (2008) Effects of packing density, excess water and solid surface area on flowability of cement paste. Adv Cem Res 20:1–11CrossRef
go back to reference Li W, Fall M (2018) Strength and self-desiccation of slag-cemented paste backfill at early ages: Link to initial sulphate concentration. Cem Concr Compos 89:160–168CrossRef Li W, Fall M (2018) Strength and self-desiccation of slag-cemented paste backfill at early ages: Link to initial sulphate concentration. Cem Concr Compos 89:160–168CrossRef
go back to reference Libre NA, Khoshnazar R, Shekarchi M (2010) Relationship between fluidity and stability of self-consolidating mortar incorporating chemical and mineral admixtures. Constr Build Mater 24:1262–1271CrossRef Libre NA, Khoshnazar R, Shekarchi M (2010) Relationship between fluidity and stability of self-consolidating mortar incorporating chemical and mineral admixtures. Constr Build Mater 24:1262–1271CrossRef
go back to reference Liu WB, Zhang X (2017) Study on volume stability of chemical foaming cement paste. KSCE J Civ Eng 21:2790–2797CrossRef Liu WB, Zhang X (2017) Study on volume stability of chemical foaming cement paste. KSCE J Civ Eng 21:2790–2797CrossRef
go back to reference Luo YF, Yu QJ, Wei JX, Hu J, Li FX Characteristics of pore structure of free-steaming foamed concrete and its influence on the compression strength. In: Applied Mechanics and Materials, 2013. Trans Tech Publ, pp 1130-1137 Luo YF, Yu QJ, Wei JX, Hu J, Li FX Characteristics of pore structure of free-steaming foamed concrete and its influence on the compression strength. In: Applied Mechanics and Materials, 2013. Trans Tech Publ, pp 1130-1137
go back to reference Ma SJ, Kang EG, Kim DM The study on development of light-weight foamed mortar for tunnel backfill. In: International Journal of Modern Physics: Conference Series, 2012. World Scientific, pp 449-454 Ma SJ, Kang EG, Kim DM The study on development of light-weight foamed mortar for tunnel backfill. In: International Journal of Modern Physics: Conference Series, 2012. World Scientific, pp 449-454
go back to reference Manikandan R, Ramamurthy K (2007) Influence of fineness of fly ash on the aggregate pelletization process. Cem Concr Compos 29:456–464CrossRef Manikandan R, Ramamurthy K (2007) Influence of fineness of fly ash on the aggregate pelletization process. Cem Concr Compos 29:456–464CrossRef
go back to reference Mehdipour I, Razzaghi MS, Amini K, Shekarchi M (2013) Effect of mineral admixtures on fluidity and stability of self-consolidating mortar subjected to prolonged mixing time. Constr Build Mater 40:1029–1037CrossRef Mehdipour I, Razzaghi MS, Amini K, Shekarchi M (2013) Effect of mineral admixtures on fluidity and stability of self-consolidating mortar subjected to prolonged mixing time. Constr Build Mater 40:1029–1037CrossRef
go back to reference Nambiar EK, Ramamurthy K (2007) Air-void characterisation of foam concrete. Cem Concr Res 37:221–230CrossRef Nambiar EK, Ramamurthy K (2007) Air-void characterisation of foam concrete. Cem Concr Res 37:221–230CrossRef
go back to reference Odler I, Rößler M (1985) Investigations on the relationship between porosity, structure and strength of hydrated Portland cement pastes. II. Effect of pore structure and of degree of hydration. Cem Concr Res 15:401–410CrossRef Odler I, Rößler M (1985) Investigations on the relationship between porosity, structure and strength of hydrated Portland cement pastes. II. Effect of pore structure and of degree of hydration. Cem Concr Res 15:401–410CrossRef
go back to reference Ouellet S, Bussiere B, Aubertin M, Benzaazoua M (2008) Characterization of cemented paste backfill pore structure using SEM and IA analysis. Bull Eng Geol Environ 67:139–152CrossRef Ouellet S, Bussiere B, Aubertin M, Benzaazoua M (2008) Characterization of cemented paste backfill pore structure using SEM and IA analysis. Bull Eng Geol Environ 67:139–152CrossRef
go back to reference Qiu JP, Guo Z, Yang L, Jiang H, Zhao Y (2020) Effects of packing density and water film thickness on the fluidity behaviour of cemented paste backfill. Powder Technol 359:27–35CrossRef Qiu JP, Guo Z, Yang L, Jiang H, Zhao Y (2020) Effects of packing density and water film thickness on the fluidity behaviour of cemented paste backfill. Powder Technol 359:27–35CrossRef
go back to reference Qiu JP, Yang L, Sun X, Xing J, Li S (2017) Strength characteristics and failure mechanism of cemented super-fine unclassified tailings backfill. Minerals 7:58CrossRef Qiu JP, Yang L, Sun X, Xing J, Li S (2017) Strength characteristics and failure mechanism of cemented super-fine unclassified tailings backfill. Minerals 7:58CrossRef
go back to reference Qiu JP, Yang L, Xing J, Sun XG (2018) Analytical solution for determining the required strength of mine backfill based on its damage constitutive model. Soil Mech Found Eng 54:371–376CrossRef Qiu JP, Yang L, Xing J, Sun XG (2018) Analytical solution for determining the required strength of mine backfill based on its damage constitutive model. Soil Mech Found Eng 54:371–376CrossRef
go back to reference Wang Y, Fall M, Wu A (2016) Initial temperature-dependence of strength development and self-desiccation in cemented paste backfill that contains sodium silicate. Cem Concr Compos 67:101–110CrossRef Wang Y, Fall M, Wu A (2016) Initial temperature-dependence of strength development and self-desiccation in cemented paste backfill that contains sodium silicate. Cem Concr Compos 67:101–110CrossRef
go back to reference Wong HH, Kwan AK (2008) Packing density of cementitious materials: part 1—measurement using a wet packing method. Mater Struct 41:689–701CrossRef Wong HH, Kwan AK (2008) Packing density of cementitious materials: part 1—measurement using a wet packing method. Mater Struct 41:689–701CrossRef
go back to reference Xu S, Suorineni FT, Li K, Li Y (2017) Evaluation of the strength and ultrasonic properties of foam-cemented paste backfill. Int J Min Reclam Environ 31:544–557CrossRef Xu S, Suorineni FT, Li K, Li Y (2017) Evaluation of the strength and ultrasonic properties of foam-cemented paste backfill. Int J Min Reclam Environ 31:544–557CrossRef
go back to reference Yang L, Qiu JP, Jiang H, Hu S, Li H, Li S (2017) Use of cemented super-fine unclassified tailings backfill for control of subsidence. Minerals 7:216CrossRef Yang L, Qiu JP, Jiang H, Hu S, Li H, Li S (2017) Use of cemented super-fine unclassified tailings backfill for control of subsidence. Minerals 7:216CrossRef
go back to reference Yang L, Xu W, Yilmaz E, Wang Q, Qiu JP (2020) A combined experimental and numerical study on the triaxial and dynamic compression behavior of cemented tailings backfill. Eng Struct 219:110957CrossRef Yang L, Xu W, Yilmaz E, Wang Q, Qiu JP (2020) A combined experimental and numerical study on the triaxial and dynamic compression behavior of cemented tailings backfill. Eng Struct 219:110957CrossRef
go back to reference Yang L, Yilmaz E, Li J, Liu H, Jiang H (2018) Effect of superplasticizer type and dosage on fluidity and strength behavior of cemented tailings backfill with different solid contents. Constr Build Mater 187:290–298CrossRef Yang L, Yilmaz E, Li J, Liu H, Jiang H (2018) Effect of superplasticizer type and dosage on fluidity and strength behavior of cemented tailings backfill with different solid contents. Constr Build Mater 187:290–298CrossRef
go back to reference Ye H, Gao X, Wang R, Wang H (2017) Relationship among particle characteristic, water film thickness and flowability of fresh paste containing different mineral admixtures. Constr Build Mater 153:193–201CrossRef Ye H, Gao X, Wang R, Wang H (2017) Relationship among particle characteristic, water film thickness and flowability of fresh paste containing different mineral admixtures. Constr Build Mater 153:193–201CrossRef
go back to reference Yi X, Ma G, Fourie A (2015) Compressive behaviour of fibre-reinforced cemented paste backfill. Geotext Geomembr 43:207–215CrossRef Yi X, Ma G, Fourie A (2015) Compressive behaviour of fibre-reinforced cemented paste backfill. Geotext Geomembr 43:207–215CrossRef
go back to reference Yilmaz E, Belem T, Bussière B, Benzaazoua M (2011) Relationships between microstructural properties and compressive strength of consolidated and unconsolidated cemented paste backfills. Cem Concr Compos 33:702–715CrossRef Yilmaz E, Belem T, Bussière B, Benzaazoua M (2011) Relationships between microstructural properties and compressive strength of consolidated and unconsolidated cemented paste backfills. Cem Concr Compos 33:702–715CrossRef
go back to reference Zhang S, Ren F, Guo Z, Qiu JP, Ding H (2020) Strength and deformation behavior of cemented foam backfill in sub-zero environment. J Mater Res Technol 9:9219–9231CrossRef Zhang S, Ren F, Guo Z, Qiu JP, Ding H (2020) Strength and deformation behavior of cemented foam backfill in sub-zero environment. J Mater Res Technol 9:9219–9231CrossRef
go back to reference Zhang S, Yang L, Ren F, Qiu JP, Ding H (2020) Rheological and mechanical properties of cemented foam backfill: effect of mineral admixture type and dosage. Cem Concr Compos 112:103689CrossRef Zhang S, Yang L, Ren F, Qiu JP, Ding H (2020) Rheological and mechanical properties of cemented foam backfill: effect of mineral admixture type and dosage. Cem Concr Compos 112:103689CrossRef
go back to reference Zhao H, Ma F, Zhang Y, Guo J (2013) Monitoring and mechanisms of ground deformation and ground fissures induced by cut-and-fill mining in the Jinchuan Mine 2, China. Environ Earth Sci 68:1903–1911CrossRef Zhao H, Ma F, Zhang Y, Guo J (2013) Monitoring and mechanisms of ground deformation and ground fissures induced by cut-and-fill mining in the Jinchuan Mine 2, China. Environ Earth Sci 68:1903–1911CrossRef
go back to reference Zhao JW, Wang XM, Peng K, Li S (2017) Utilization of foaming technology in cemented paste backfill of high-mud superfine unclassified tailings. Adv Mater Sci Eng 2017 Zhao JW, Wang XM, Peng K, Li S (2017) Utilization of foaming technology in cemented paste backfill of high-mud superfine unclassified tailings. Adv Mater Sci Eng 2017
Metadata
Title
Fluidity and strength behaviors of cemented foam backfill: effect of particle size distribution and foaming agent dosage
Authors
Shiyu Zhang
Lei Yang
Jingping Qiu
Chen Hou
Zhenbang Guo
Publication date
07-02-2021
Publisher
Springer Berlin Heidelberg
Published in
Bulletin of Engineering Geology and the Environment / Issue 4/2021
Print ISSN: 1435-9529
Electronic ISSN: 1435-9537
DOI
https://doi.org/10.1007/s10064-021-02117-5

Other articles of this Issue 4/2021

Bulletin of Engineering Geology and the Environment 4/2021 Go to the issue