Formation of the Carbon-Enriched Zone and Its Evolution During the Long-Term Aging Process for 9% Cr-CrMoV Dissimilar Welded Joint

Authors : Kai Ding, Bingge Zhao, Yuanheng Zhang, Tao Wei, Guanzhi Wu, Yuanfang Wang, Yulai Gao

Published in: Characterization of Minerals, Metals, and Materials 2020

Publisher: Springer International Publishing

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

The appearance of carbon migration in the 9% Cr-CrMoV dissimilar welded joint was resulted from the sharp content transition of the strong carbide-forming element Cr between the weld (~2.3 wt%) and the base metal (~10.6 wt%). The width of the carbon-enriched zone (CEZ) under original state was about 46 μm, and the width of CEZ increased and then kept in 65 μm during the 10,000 h aging treatment. The microhardness test showed that the carbon-depleted zone (CDZ) exhibited low hardness value (~220 HV) compared with that (~340 HV) in CEZ. The significant difference in carbide content was the crucial factor in the sharp change of hardness adjacent to the fusion line. Thus, it is important to understand the evolution of the CEZ to experience a long-term aging to avoid its negative influence on the impact toughness and fatigue performance.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literature
1.
go back to reference Gupta SK, Pandey KN, Kumar R (2015) Comparison of ANN and regression modeling for predicting the responses of friction stir welded dissimilar AA5083-AA6063 aluminum alloys joint. Appl Mech Mater 813–814:415–419CrossRef Gupta SK, Pandey KN, Kumar R (2015) Comparison of ANN and regression modeling for predicting the responses of friction stir welded dissimilar AA5083-AA6063 aluminum alloys joint. Appl Mech Mater 813–814:415–419CrossRef
2.
go back to reference Shang YB, Shi HJ, Wang ZX, Zhang GD (2015) In-situ SEM study of short fatigue crack propagation behavior in a dissimilar metal welded joint of nuclear power plant. Mater Des 88:598–609CrossRef Shang YB, Shi HJ, Wang ZX, Zhang GD (2015) In-situ SEM study of short fatigue crack propagation behavior in a dissimilar metal welded joint of nuclear power plant. Mater Des 88:598–609CrossRef
3.
go back to reference Ding K, Wang P, Liu X, Li XH, Zhao BG, Gao YL (2018) Formation of lamellar carbides in alloy 617-HAZ and their role in the impact toughness of alloy 617/9%Cr dissimilar welded joint. J Mater Eng Perform 27(11):6027–6039CrossRef Ding K, Wang P, Liu X, Li XH, Zhao BG, Gao YL (2018) Formation of lamellar carbides in alloy 617-HAZ and their role in the impact toughness of alloy 617/9%Cr dissimilar welded joint. J Mater Eng Perform 27(11):6027–6039CrossRef
5.
go back to reference Dehaghi EM, Moshayedi H, Sattari-Far I, Arezoodar A (2017) Residual stresses due to cladding, buttering and dissimilar welding of the main feed water nozzle in a power plant reactor. Int J Press Vessels Pip 152:56–64CrossRef Dehaghi EM, Moshayedi H, Sattari-Far I, Arezoodar A (2017) Residual stresses due to cladding, buttering and dissimilar welding of the main feed water nozzle in a power plant reactor. Int J Press Vessels Pip 152:56–64CrossRef
6.
go back to reference Guo Q, Lu FG, Liu X, Yang RJ, Cui HC, Gao YL (2015) Correlation of microstructure and fracture toughness of advanced 9Cr/CrMoV dissimilarly welded joint. Mater Sci Eng A 638:240–250CrossRef Guo Q, Lu FG, Liu X, Yang RJ, Cui HC, Gao YL (2015) Correlation of microstructure and fracture toughness of advanced 9Cr/CrMoV dissimilarly welded joint. Mater Sci Eng A 638:240–250CrossRef
7.
go back to reference Rahmani M, Eghlimi A, Shamanian M (2014) Evaluation of microstructure and mechanical properties in dissimilar austenitic/super duplex stainless steel joint. J Mater Eng Perform 23(10):3746–3753CrossRef Rahmani M, Eghlimi A, Shamanian M (2014) Evaluation of microstructure and mechanical properties in dissimilar austenitic/super duplex stainless steel joint. J Mater Eng Perform 23(10):3746–3753CrossRef
8.
go back to reference Liu LM, Wang SX, Zhao LM (2008) Study on the dissimilar magnesium alloy and copper lap joint by TIG welding. Mater Sci Eng A 476(1–2):206–209CrossRef Liu LM, Wang SX, Zhao LM (2008) Study on the dissimilar magnesium alloy and copper lap joint by TIG welding. Mater Sci Eng A 476(1–2):206–209CrossRef
9.
go back to reference Ramachandran KK, Murugan N, Shashi Kumar S (2015) Effect of tool axis offset and geometry of tool pin profile on the characteristics of friction stir welded dissimilar joints of aluminum alloy AA5052 and HSLA steel. Mater Sci Eng A 639:219–233CrossRef Ramachandran KK, Murugan N, Shashi Kumar S (2015) Effect of tool axis offset and geometry of tool pin profile on the characteristics of friction stir welded dissimilar joints of aluminum alloy AA5052 and HSLA steel. Mater Sci Eng A 639:219–233CrossRef
10.
go back to reference Hosseini HS, Alishahi M, Shamanian M (2012) Zonular evaluation of inconel 617/310 SS dissimilar joint by shear punch test. Mater Lett 67(1):259–262CrossRef Hosseini HS, Alishahi M, Shamanian M (2012) Zonular evaluation of inconel 617/310 SS dissimilar joint by shear punch test. Mater Lett 67(1):259–262CrossRef
11.
go back to reference Bouché K, Barbier F, Coulet A (1998) Intermetallic compound layer growth between solid iron and molten aluminium. Mater Sci Eng A 249(1–2):167–175CrossRef Bouché K, Barbier F, Coulet A (1998) Intermetallic compound layer growth between solid iron and molten aluminium. Mater Sci Eng A 249(1–2):167–175CrossRef
12.
go back to reference Chen SH, Huang JH, Ma K, Zhang HQ, Zhao XK (2012) Influence of a Ni-foil interlayer on Fe/Al dissimilar joint by laser penetration welding. Mater Lett 79:296–299CrossRef Chen SH, Huang JH, Ma K, Zhang HQ, Zhao XK (2012) Influence of a Ni-foil interlayer on Fe/Al dissimilar joint by laser penetration welding. Mater Lett 79:296–299CrossRef
13.
go back to reference Wang YQ, Cui HC, Fan MJ, Chen YX, Lu FG (2019) Characterization on the gradient microstructure near the fusion interface of dissimilar metal between high Cr heat-resistant steel and Ni-based Alloy 617. Mater Charact 151:227–236CrossRef Wang YQ, Cui HC, Fan MJ, Chen YX, Lu FG (2019) Characterization on the gradient microstructure near the fusion interface of dissimilar metal between high Cr heat-resistant steel and Ni-based Alloy 617. Mater Charact 151:227–236CrossRef
14.
go back to reference Ding K, Ji HJ, Liu X, Wang P, Zhang QL, Li XH, Gao YL (2018) Prevention of carbon migration in 9% Cr/CrMoV dissimilar welded joint by adding tungsten inert gas overlaying layer. J Iron Steel Res Int 25:847–853CrossRef Ding K, Ji HJ, Liu X, Wang P, Zhang QL, Li XH, Gao YL (2018) Prevention of carbon migration in 9% Cr/CrMoV dissimilar welded joint by adding tungsten inert gas overlaying layer. J Iron Steel Res Int 25:847–853CrossRef
15.
go back to reference Wu QJ, Lu FG, Cui HC, Liu X, Wang P, Gao YL (2015) Soft zone formation by carbon migration and its effect on the high-cycle fatigue in 9% Cr-CrMoV dissimilar welded joint. Mater Lett 141:242–244CrossRef Wu QJ, Lu FG, Cui HC, Liu X, Wang P, Gao YL (2015) Soft zone formation by carbon migration and its effect on the high-cycle fatigue in 9% Cr-CrMoV dissimilar welded joint. Mater Lett 141:242–244CrossRef
16.
go back to reference Abe F (2008) Precipitate design for creep strengthening of 9% Cr tempered martensitic steel for ultra-supercritical power plants. Sci Technol Adv Mater 9(1):1–15CrossRef Abe F (2008) Precipitate design for creep strengthening of 9% Cr tempered martensitic steel for ultra-supercritical power plants. Sci Technol Adv Mater 9(1):1–15CrossRef
17.
go back to reference Wei YH, Qiao SF, Lu FG, Liu W (2016) Failure transition mechanism in creep rupture of modified casting 9Cr-1.5Mo-1Co welded joint. Mater Des 97:268–278CrossRef Wei YH, Qiao SF, Lu FG, Liu W (2016) Failure transition mechanism in creep rupture of modified casting 9Cr-1.5Mo-1Co welded joint. Mater Des 97:268–278CrossRef
18.
go back to reference Liu X, Cai ZP, Deng XL, Lu FG (2017) Investigation on the weakest zone in toughness of 9Cr/NiCrMoV dissimilar welded joint and its enhancement. J Mater Res 32(16):3117–3127CrossRef Liu X, Cai ZP, Deng XL, Lu FG (2017) Investigation on the weakest zone in toughness of 9Cr/NiCrMoV dissimilar welded joint and its enhancement. J Mater Res 32(16):3117–3127CrossRef
19.
go back to reference Rahman S, Priyadarshan G, Raja KS, Nesbitt C, Misra M (2008) Investigation of the secondary phases of alloy 617 by scanning kelvin probe force microscope. Mater Lett 62(15):2263–2266CrossRef Rahman S, Priyadarshan G, Raja KS, Nesbitt C, Misra M (2008) Investigation of the secondary phases of alloy 617 by scanning kelvin probe force microscope. Mater Lett 62(15):2263–2266CrossRef
20.
go back to reference Kang JH, Rivera-Díaz-Del-Castillo PEJ (2013) Carbide dissolution in bearing steels. Comput Mater Sci 67:364–372CrossRef Kang JH, Rivera-Díaz-Del-Castillo PEJ (2013) Carbide dissolution in bearing steels. Comput Mater Sci 67:364–372CrossRef
21.
go back to reference Sandberg N, Henriksson KOE, Wallenius J (2008) Carbon impurity dissolution and migration in bcc Fe-Cr: first-principles calculations. Phys Rev B 78(9):1–7CrossRef Sandberg N, Henriksson KOE, Wallenius J (2008) Carbon impurity dissolution and migration in bcc Fe-Cr: first-principles calculations. Phys Rev B 78(9):1–7CrossRef
22.
go back to reference Lin RQ, Cui HC, Lu FG, Huo X, Wang P (2016) Study on the microstructure and toughness of dissimilarly welded joints of advanced 9Cr/CrMoV. J Mater Res 31(22):3597–3609CrossRef Lin RQ, Cui HC, Lu FG, Huo X, Wang P (2016) Study on the microstructure and toughness of dissimilarly welded joints of advanced 9Cr/CrMoV. J Mater Res 31(22):3597–3609CrossRef
23.
go back to reference Wen T, Hu XF, Song YY, Yan DS, Rong LJ (2013) Carbides and mechanical properties in a Fe–Cr–Ni–Mo high-strength steel with different V contents. Mater Sci Eng A 588:201–207CrossRef Wen T, Hu XF, Song YY, Yan DS, Rong LJ (2013) Carbides and mechanical properties in a Fe–Cr–Ni–Mo high-strength steel with different V contents. Mater Sci Eng A 588:201–207CrossRef
24.
go back to reference Liu W, Liu X, Lu FG, Tang XH, Cui HC, Gao YL (2015) Creep behavior and microstructure evaluation of welded joint in dissimilar modified 9Cr-1Mo steels. Mater Sci Eng A 644:337–346CrossRef Liu W, Liu X, Lu FG, Tang XH, Cui HC, Gao YL (2015) Creep behavior and microstructure evaluation of welded joint in dissimilar modified 9Cr-1Mo steels. Mater Sci Eng A 644:337–346CrossRef
Metadata
Title
Formation of the Carbon-Enriched Zone and Its Evolution During the Long-Term Aging Process for 9% Cr-CrMoV Dissimilar Welded Joint
Authors
Kai Ding
Bingge Zhao
Yuanheng Zhang
Tao Wei
Guanzhi Wu
Yuanfang Wang
Yulai Gao
Copyright Year
2020
DOI
https://doi.org/10.1007/978-3-030-36628-5_27

Premium Partners