Journal of Failure Analysis and Prevention
Published in: Journal of Failure Analysis and Prevention 5/2011

01-10-2011 | Case History---Peer-Reviewed

Hot Cracking in Inductively Bent Austenitic Stainless Steel Pipes

Authors: Andreas Neidel, Susanne Riesenbeck

Published in: Journal of Failure Analysis and Prevention | Issue 5/2011

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

Surface cracks found on austenitic stainless steel piping after inductive bending into manifolds were shown to be caused by liquation cracking due to over heating. The cracked manifolds were dicarded and a new vendor was selected.
previous article Accelerated Corrosion of a Boiler Chimney: Causes and Preventive Steps
next article Unexpected Thermal Fracture of a Ceramic Sensor

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

inform now

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

inform now
Literature
1.
Cross, C.E.: Private Communication. Federal Institute for Materials Research and Testing, Berlin, May 19, 2010
2.
Cottrell, A.H., Swann, P.R.: Technical lessons of Flixborough. A metallurgical examination of the eight-inch line. Chem. Eng. 308, 266–274 (1976)
3.
Hough, R.R., Rolls, R.: Creep fracture phenomena in iron embrittled by liquid copper. J. Mater. Sci. 6, 1493–1498 (1971)CrossRef
4.
Pohl, M.: Private Communication. Ruhr-Universität Bochum, Bochum, February 16, 2010
Metadata
Title
Hot Cracking in Inductively Bent Austenitic Stainless Steel Pipes
Authors
Andreas Neidel
Susanne Riesenbeck
Publication date
01-10-2011
Publisher
Springer US
Published in
Journal of Failure Analysis and Prevention / Issue 5/2011
Print ISSN: 1547-7029
Electronic ISSN: 1864-1245
DOI
https://doi.org/10.1007/s11668-011-9478-4

Other articles of this Issue 5/2011

Journal of Failure Analysis and Prevention 5/2011 Go to the issue

Editorial

Having a Good Day

Technical Article---Peer-Reviewed

Development of a Cornering Bench Fatigue Test for the Validation of a Lightweight Commercial Vehicle Front Hub

Technical Article---Peer-Reviewed

Failure Analysis of a Ruptured Trunkline

News

Product News

Case History—Peer-Reviewed

Fatigue Failure of Flanged Thermowell

Case History---Peer-Reviewed

Accelerated Corrosion of a Boiler Chimney: Causes and Preventive Steps

Premium Partners

    Image Credits