In vitro evaluation of the biocompatibility and bioactivity of plasma electrolyte oxidized titania/calcium phosphate nanocoatings on Ti

Authors: S. Abbasi, M. R. Bilesan, F. Golestani-Fard

Published in: Journal of Materials Science | Issue 5/2019

Activate our intelligent search to find suitable subject content or patents.

search-config

AI-assisted search

Off

Abstract

In this study, monolayer and two-layer composite coatings of titania and calcium phosphate were fabricated via plasma electrolyte oxidation technique on titanium substrates. The calcium phosphate layers were produced by using an electrolyte containing calcium acetate and β-glycerophosphate. In order to study and compare their biocompatibility and bioactivity properties MTT, cell adhesion, and soaking in SBF solution tests were performed on both coatings. According to the XPS and AFM analysis results, two-layer coatings have a higher Ca/P proportion on their surface and rougher surface. Higher cell proliferation rate was observed on two-layer specimen’s surface. An appropriate cell adhesion was observed in both coatings. Higher amount of hydroxyapatite (HAp) nanocrystals were observed on coatings with two-layer in comparison with monolayer after being soaked in SBF solution for 28 days. Besides, the proportion of HAp to calcium triphosphate after soaking in SBF solution was higher in two-layer coating.

previous article Improved wear, mechanical, and biological behavior of UHMWPE-HAp-zirconia hybrid nanocomposites with a prospective application in total hip joint replacement

next article Characterization and antimicrobial activity of a 2-O-methyl-β-cyclodextrin inclusion complex containing hexahydro-β-acids

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

inform now

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

inform now

Yin X, Liang C, Ge F (2018) Electrodeposition of a YSZ–Yttria stabilized zirconia composite coating on a titanium bone implant. Int J Electrochem Sci 13:822–831CrossRef

Ren Bing, Wan Yi, Wang Guisen, Liu Zhanqiang, Huang Yong, Wang Hongwei (2018) Morphologically modified surface with hierarchical micro-/nano-structures for enhanced bioactivity of titanium implants. J Mater Sci 53(18):12679–12691CrossRef

Chirivella EG, Pérez-Feito R, Ribeiroc C, Ribeiro S, Correia DM, González-Martín ML, Manero JM, Lanceros-Méndez S, Ferrer GG, Gómez-Ribelles JL (2017) Chitosan patterning on titanium implants. Prog Org Coat 111:23–28CrossRef

Habraken W, Habibovic P, Epple M, Bohner M (2016) Calcium phosphates in biomedical applications: materials for the future? Mater Today 19:69–87CrossRef

Ye H, Liu XY, Hong H (2009) Cladding of titanium/hydroxyapatite composites onto Ti6Al4 V for load-bearing implant applications. Mater Sci Eng, C 29:2036–2044CrossRef

Parcharoen Y, Termsuksawad P, Sirivisoot S (2016) Improved bonding strength of hydroxyapatite on titanium dioxide nanotube arrays following alkaline pretreatment for orthopedic implants. J. Nanomater. 2016:1–13CrossRef

Mihailescu IN, Torricelli P, Bigi A, Mayer I, Iliescu M, Werckmann J, Socol G, Miroiu F, Cuisinier F, Elkaim R, Hildebrand G (2005) Calcium phosphate thin films synthesized by pulsed laser deposition: physico-chemical characterization and in vitro cell response. Appl Surf Sci 248:344–348CrossRef

Kwok CT, Wong PK, Cheng FT, Man HC (2009) Characterization and corrosion behavior of hydroxyapatite coatings on Ti6Al4 V fabricated by electrophoretic deposition. Appl Surf Sci 255:6736–6744CrossRef

Gross KA, Muller D, Lucas H, Haynes DR (2012) Osteoclast resorption of thermal spray hydoxyapatite coatings is influenced by surface topography. Acta Biomater 8:1948–1956CrossRef

10.

Auger MA, Savoini B, Muñoz A, Leguey T, Monge MA, Pareja R, Victoria J (2009) Mechanical characteristics of porous hydroxyapatite/oxide composites produced by post-sintering hot isostatic pressing. Ceram Int 35:2373–2380CrossRef

11.

Abrishamchian A, Hooshmand T, Mohammadi M, Najafi F (2013) Preparation and characterization of two-walled carbon nanotube/hydroxyapatite nanocomposite film dip coated on Ti–6Al–4 V by sol–gel method for biomedical applications: an in vitro study. Mater Sci Eng, C 33:2002–2010CrossRef

12.

Khalid M, Mujahid M, Nusair Khan A, Rawat RS (2013) Dip coating of nano hydroxyapatite on titanium alloy with plasma assisted γ-alumina buffer layer: a novel coating approach. J Mater Sci Technol 29:557–564CrossRef

13.

Yang YC, Yang CY (2013) Mechanical and histological evaluation of a plasma sprayed hydroxyapatite coating on a titanium bond coat. Ceram Int 39:6509–6516CrossRef

14.

Luo R, Liu Z, Yan F, Kong Y, Zhang Y (2013) The biocompatibility of hydroxyapatite film deposition on micro-arc oxidation Ti6Al4 V alloy. Appl Surf Sci 266:57–61CrossRef

15.

Khan RHU, Yerokhin A, Li X, Dong H, Matthews A (2010) Surface characterization of DC plasma electrolytic oxidation treated 6082 aluminium alloy: effect of current density and electrolyte concentration. Surf Coat Technol 205:1679–1688CrossRef

16.

Yao ZQ, Ivanisenko Yu, Diemant T, Caron A, Chuvilin A, Jiang JZ, Valiev RZ, Qi M, Fecht H-J (2010) Synthesis and properties of hydroxyapatite-containing porous Titania coating on ultrafine-grained titanium by micro-arc oxidation. Acta Biomater 6:2816–2825CrossRef

17.

Zhao X, Cai Q, Li D, He J, Luo Q, Li X, Sun W (2010) Preparation and characterization of bio-ceramic coatings on the surface of pure titanium by plasma electrolytic oxidation-alkali and heat treatment. J Ceram Process Res 11:575–580

18.

Golestani-Fard F, Bayati MR, Zargar HR, Abbasi S, Rezaei HR (2011) MAO-preparation of nanocrystalline hydroxyapatite–Titania composite films: formation stages and effect of the growth time. Mater Res Bull 46:2422–2426CrossRef

19.

Abbasi S, Golestani-Fard F, Rezaie HR, Mirhosseini SMM, Ziaee A (2012) MAO-derived hydroxyapatite–TiO₂ nanostructured bio-ceramic films on titanium. Mater Res Bull 47:3407–3412CrossRef

20.

Abbasi S, Golestani-Fard F, Mirhosseini SMM, Ziaee A, Mehrjoo M (2013) Effect of electrolyte concentration on microstructure and properties of micro arc oxidized hydroxyapatite/titania nanostructured composite. Mater Sci Eng, C 33:2555–2561CrossRef

21.

Abbasi S, Golestani-Fard F, Rezaie HR, Mirhosseini SMM (2012) MAO-derived hydroxyapatite/TiO₂ nanostructured two-layer coatings on titanium substrate. Appl Surf Sci 261:37–42CrossRef

22.

Gutowska I, Machoy Z, Machalin´ski B (2005) The role of bivalent metals in hydroxyapatite structures as revealed by molecular modeling with the HyperChem software. J Biomed Mater Res 75A:788–793CrossRef

23.

Ratner BD, Hoffman AS, Schoen FJ, lemons JE (eds) (2012) Biomaterials science: an introduction to materials in medicine, ISBN: 978-008-087-780-8

24.

Vandrovcová M, Bačáková l (2011) Adhesion, growth and differentiation of osteoblasts on surface modified materials developed for bone implants. Physiol Res 60:403–417

25.

Anil S, Anand PS, Alghamdi H, Jansen JA, Turkyilmaz I (Ed.) Dental implant surface enhancement and osseointegration, implant dentistry—a rapidly evolving practice, ISBN: 978-953-307-658-4 (2011)

26.

Yerokhin AL, Lyubimov VV, Ashitkof RV (1998) Phase formation in ceramic coatings during plasma electrolytic oxidation of aluminium alloys. Ceram Int 24:1–6CrossRef

27.

Hepler PK (2005) historical perspective essay, calcium: a central regulator of plant growth and development. Plant cell 17:2142–2155CrossRef

28.

Lee IS, Whang CN, Kim HE, Park JC, Song JH, Kim SR (2002) Various Ca/P ratios of thin calcium phosphate films. Mater Sci Eng, C 22:15–20CrossRef

29.

Chang HI, Wang Y, Eberli D (eds) (2011) cell responses to surface and architecture of tissue engineering scaffolds, regenerative medicine and tissue engineering—cells and biomaterials, ISBN: 978-953-307-663-8

30.

Kumar KA, Bhatt V, Balakrishnan M, Hashem M, Vellappally S, Aziz A, Al Kheraif A, Halawany HS, Abraham NB, Anil S (2015) Bioactivity and surface characteristics of titanium implants following various surface treatments: an in vitro study. J Oral Implantol 41:183–188CrossRef

31.

Tas AC, Bhaduri SB (2004) Rapid coating of Ti6Al4 V at room temperature with a calcium phosphate solution similar to 10 × simulated body fluid. J Mater Res 19:2742–2749CrossRef

32.

Ferraz MP, Monteiro FJ, Manuel CM (2004) Hydroxyapatite nanoparticles: a review of preparation methodologies. J Appl Biomater Biomech 2:74–80

Title: In vitro evaluation of the biocompatibility and bioactivity of plasma electrolyte oxidized titania/calcium phosphate nanocoatings on Ti
Authors: S. Abbasi
M. R. Bilesan
F. Golestani-Fard
Publication date: 26-11-2018
Publisher: Springer US
Published in: Journal of Materials Science / Issue 5/2019
Print ISSN: 0022-2461
Electronic ISSN: 1573-4803
DOI: https://doi.org/10.1007/s10853-018-3147-x

Springer Professional

Abstract

Please log in to get access to your license.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Other articles of this Issue 5/2019

Atomistic modeling of interfacial segregation and structural transitions in ternary alloys

3D microstructure of magnesium potassium phosphate ceramics from X-ray tomography: new insights into the reaction mechanisms

Transition from microcellular to nanocellular chain extended poly(lactic acid)/hydroxyl-functionalized graphene foams by supercritical CO2

Study of the microstructure and texture heterogeneities of Fe–48wt%Ni alloy severely deformed by equal channel angular pressing

Fabrication of superrepellent microstructured polypropylene/graphene surfaces with enhanced wear resistance

High-performance copper reinforced with dispersed nanoparticles

Premium Partners