# Influence of degree of deformation on welding pore reduction in high-carbon steels

Authors: Bernd-Arno Behrens, Hans Jürgen Maier, Gerhard Poll, Ludger Overmeyer, Hendrik Wester, Johanna Uhe, Thomas Hassel, Florian Pape, Marius Lammers, Jörg Hermsdorf, Stefan Kaierle, Laura Budde, Felix Saure, Maximilian Mildebrath, Timm Coors, Mohamad Yusuf Faqiri, Christoph Büdenbender

Published in: Production Engineering | Issue 2/2021

print
PRINT
insite
SEARCH

## Abstract

Locally adapted properties within a machine component offer opportunities to increase the performance of a component by using high strenght materials where they are needed. The economic production of such hybrid components on the other hand represents a major challenge. The new tailored forming process chain, which is developed within the collaborative research center (CRC 1153) represents a possible solution to produce hybrid components. This is made possible by the use of pre-joined hybrid semi-finished products made from two different steel alloys, which are subsequently formed. The semi-finished products can be manufactured for example by means of deposition welding. Due to a thermal mechanical treatment, an overall higher component strength of the joining zone can be achieved. The deposition welding processes can be used to generate a cladding on a base material. During the welding, one of the most difficult tasks is to reduce the amount and size of pores in the joining zone. These pores can reduce the strength in the joining zone of the welded parts. However, additional pores can occur in the intermediate zone between the substrate and the cladding. In the presented study, the influence of the forming process on the closing of pores in the cladding and in the intermediate zone was investigated. Therefore, cylindrical specimen were extracted in longitudinal direction of the welding track by wire-cut eroding. These welding tracks are manufactured by plasma-transferred arc welding of AISI 52100 on a base plate made of AISI 1015. Further, specimens were prepared transversely, so that the base material, the intermediate layer, and the welded material are axially arranged in the specimen. The prepared specimen were checked for pores by means of scanning acoustic microscopy. Subsequently, an uniaxial compression test was carried out with various degrees of deformation and the two specimen designs were examined again for pores. A microstructure analysis was carried out after each step. The investigations show that there is a need for a minimum degree of deformation to reduce pores in the welded material. However, this required plastic strain cannot be achieved in the welded material of the hybrid specimen, which is a result of the homogeneous temperature distribution in the specimen. The homogeneous temperature distribution leads to different flow properties in the specimen, which means that the main plastic deformation is taking place in the base material.
Disclaimer

## Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## 1 Introduction

In many industrial sectors, miniaturisation, lightweight design and optimised functional integration are increasing the demands on the components being used. They have to be manufactured at low cost and with high efficiency, while fulfilling various tribological and mechanical properties. In some cases, a resource-efficient manufacturing process is also desired. A simultaneous optimisation of all requirements is rarely possible when using monomaterial components. Therefore, the development and use of hybrid components is steadily gaining importance. One innovative hybrid manufacturing concept is the so called tailored forming process chain which is based on the use of a pre-joined hybrid semi-finished product in a following forming process [1]. This enables an economic and resource-saving production of parts with locally adapted properties. Material and energy can be saved by combining cost-effective materials, such as structural steel or lightweight materials, with high-strength materials. For the combination of different materials, novel joining techniques and forming processes are used. The tailored forming process can be used, for example, to manufacture shafts, gears or axial bearing washers in a hybrid design [2, 3]. The main work steps required to produce components using the tailored forming process are for example the deposition welding of the high strength functional layer on the base material. This provides a hybrid semi-finished product, which is thermo-mechanically improved by a subsequent forming step. In previous investigations it could be shown, that axial bearing washers, which were produced by manufacturing a martensitic chromium-silicon steel AISI HNV3 cladding onto the mild steel AISI 1015 by laser metal deposition by wire and subsequent forming, achieve almost 70% of the service life of conventional industrial bearings made of the rolling bearing steel AISI 52100. The endurance tests showed that the bearing failed due to pitting while the joining zone was intact [2]. This suggests that the service life of hybrid rolling bearings can be further increased through the use of higher-strength materials. An example of a cladding with AISI HNV3 is shown in Fig. 1. In the cladding manufactured by laser metal deposition with wire, pores could only be detected at the turnaround points. These pores have no influence on the strength of the later component, as they are removed during post-processing. To increase the service life of the hybrid components, the rolling bearing material AISI 52100 is to be welded onto the substrates and investigated. This material has a higher strength and hardness than the substrate material. While AISI HNV3 is one of the standard welding materials and has good welding properties, AISI 52100 is not considered as weldable due to its high carbon content. Initial investigations on the welding of AISI 52100 have shown that the material tends to form pores. Therefore, the aim of this paper is to investigate to what extent the degree of deformation of the subsequent forming process can influence the pores in terms of number, size, position and shape. With these findings, quality requirements for the weld seam can be defined and the process window for the cladding process can be enlarged if necessary. Based on these investigations, the basis for the development of a process chain for hybrid components with AISI 52100 claddings has been provided.

## 3 Material and methods

### 3.1 Plasma-powder-transferred arc welding

Plasma transferred arc (PTA) welding is a thermal process to obtain various surface properties on metallic components. During the process, a non-melting tungsten electrode creates a plasma arc in order to melt the surface of the workpiece. In the meantime, a powder system inserts the cladding material in the molten welding zone, which results in a substance-to-substance bond after solidification. The welding process is carried out on a six-axis KR 22 industrial robot (Kuka GmbH), where two additional axes are realized by a turn and tilt table (DKP 400, Kuka GmbH). The welding torch is a PTR450 (AUTOGEN-RITTER GmbH), which is supplied by the current source PSI 400 (Kjellberg Finsterwalde Schweißtechnik und Verschleischutzsysteme GmbH). The experimental setup for the welding process is shown in Fig. 2. The chemical compositions of the base and cladding material are shown in Table 1. The glains of the cladding material have a diamter of minimum 50 $$\upmu$$m to maximum 200 $$\upmu$$m which corresponds to the current industrial standard for PTA welding [15].
Table 1
Chemical composition in wt.% of cladding material AISI 52100 and base material AISI 1015
AISI
C
Mn
Si
P
S
Cr
52100
1.05
0.45
0.35
< 0.025
< 0.015
1.6
1015
0.17
1.40
< 0.03
< 0.03
Table 2
Welding parameters
Parameter
Value
Shielding gas flow (Argon)
7 l/min
Plasma gas flow (Argon)
1.5 l/min
Transport gas flow (Argon)
2 l/min
Welding speed
0.078 m/min
Length of the weld seam
0.42 m
Current
140–120 A
Powder material
AISI 52100
Deposition rate
0.48 kg/h
Powder mesh
63–200 $$\upmu$$m
Before the welding process starts, the components get sandblasted in order to clean the surface. To start the welding process, the components are fixed on the turn and tilt table, which is aligned in horizontal position. The welding is carried out at room temperature. During the welding process, three lanes are welded overlapping side by side, whereby the lanes form a closed weld seam. Therefore, the welding torch oscillates with an amplitude of 1 mm and frequency of 1.3 Hz at an angle of 90$$^\circ$$ to the welding direction. The whole welding process takes a total time of 5 min and 23 s, whereby the sample heats up to a maximum of 650 $$^\circ$$C. With rising temperatures, also the dilution between the cladding material and the substrate increases. To counteract the heating a dynamic adjustment of the welding parameters is required. At the beginning a current of 140 A is selected to generate a fast heating of the sample. In the further process the current is reduced by 10 A for each following weld seam in order to keep the dilution low and the properties for each seam as constant as possible. An overview of the welding parameters is given in Table 2.

### 3.2 Specimen preparation

In order to investigate the influence of plastic strain on the closing of pores, cylindrical samples of AISI 52100 were taken from the welding track in longitudinal direction by wire erosion and were subsequently compressed. The specimens had a diameter of 5 mm and a height of 8 mm. The pores in the material were detected before and after the forming investigations by means of scanning acoustic microscopy (SAM).
The area between the base material and the cladding has a high affinity for pore formation during the welding process [7]. In order to investigate the bonding zone, also cylindrical specimens were prepared transversely, so that base material, the intermediate layer and the welded material are axially arranged in the specimen. For the base plates, different heights were used (10 mm, 12 mm and 15 mm) to investigate whether the proportion of the base material has an influence on the overall forming process (Fig. 3)
The height of the welding track was kept constant to $$h_{cladding}$$ = 3 mm. This design of the specimens leads to three different kinds of the specimen with different resulting heights (13 mm, 15 mm and 18 mm). Also a diameter of 5 mm was chosen for the hybrid specimen.

### 3.3 Compression test of mono and hybrid cylindrical specimen

All cylindrical specimens were compressed in the forming simulator Gleeble 3800-GTC by DSI Inc. (cf. Fig. 4). The investigated plastic strains vary from $$\varphi =0.3$$, $$\varphi =0.5$$ and $$\varphi =0.7$$ to observe the influence of the forming process on the ability to close pores. The temperature for the compression tests was 1100 $$^\circ$$C. The test chamber was evacuated during the test to exclude the influence of oxidation. The tests were performed with a strain rate of $${{\dot{\varphi }}}$$ = 0.1 $$\mathrm{{s}}^{-1}$$. In Fig. 4 the orientation of the hybrid specimen is presented. In all tests the cladding is pressed into the base material as depicted in Fig. 4. Graphite was used as a lubricant between the surface of the sample and the forming tool, so that the influence of friction can be neglected. After the two specimen designs were formed, investigations were then carried out with SAM to investigate the influence of plastic deformation on the closing of pores, as previously demonstrated in [7].

### 3.4 Numerical model of the hybrid compression test

To examine the distribution of the plastic strain within the hybrid specimen, an axial symmetric numerical model of the performed compression test was built up with the commercial software Simufact Forming v16. The forming tools were modelled as thermally conductive bodies. The friction between the specimen and the forming tool was modelled with the combined friction model, consisting of the Tresca and Coulomb formulation. The parameters of friction were set at m $$= 0.1$$ and $$\mu$$ $$= 0.08$$, which corresponds to a low frictional behaviour like in the experimental test. An adhesive condition was set between the base material and the welding track material, which cannot be relieved during the forming process. A homogeneous temperature distribution of 1100 $$^\circ$$C was assigned to the hybrid samples. An elasto-plastic material model was used to set the material behaviour. The required material data for the base material (AISI 1015) and for the welding track material (AISI 52100) were taken from the Simufact Forming material database.

### 3.5 Scanning acoustic microscopy

Scanning acoustic microscopy (SAM) on a modified PVA TePla SAM 301 system is used for non-destructive testing after sample preparation for experimental investigations, see Fig. 5. For this purpose, an ultrasonic pulse is sent into the sample via a coupling medium, in this case distilled water. To improve corrosion protection, the samples are sprayed with penetrating oil. The interaction at interfaces between different materials, e.g. at defects or material transitions, can be evaluated by analysing the reflected acoustic waves in the run-time signal. An acoustic horizontal sectional image (C-scan) is calculated by scanning the samples line by line using an XY-scanner to which the ultrasound probe (transducer) is attached. Parameters for ultrasonic microscopy are shown in Table 3.
Table 3
Transducer properties for scanning acoustic microscopy
Frequency in MHz
Focal length in mm
Axial resolution in $$\upmu$$m
Detection limit in $$\upmu$$m
30
12.7
49.5
16.5
75
20
20
6.7
110
8
13.7
4.5

## 4 Results and discussion

### 4.1 Properties of the cladding material

Figure 6 shows SAM images for a typical sample after welding without forming. In level by level orthogonal views, welding defects like pores with a typical size of 20–100 $$\upmu$$m and above, can be seen at depths of − 0.3 to − 0.9 mm. The slightly pixelated areas indicate signal interference, e.g. due to the surface structure or to the travel speed of the scanner being set to high. Welding defects with a diameter above 20 $$\upmu$$m were found in 25 out of 40 samples of this set. For further investigations only specimens with pores were used. For samples declared as non-porous, however, it cannot be ruled out that no pores are present below this detection limit.
Figure 7 shows the microsections of the cylindrical samples at different degrees of deformation. All samples have been taken from the same weld seam. Therefore, the metallurgical properties are the same. Figure 7a shows the initial state of a sample ($$\varphi$$ = 0). An increased number of pores can be identified which appear in form of black dots. The pores are marked with red circles. Figure 7b shows the sample for the degree of deformation ($$\varphi$$ = 0.3). There are still pores visible, but less than in the previous Fig. 7a. With increasing degree of deformation, the porosity decreases significantly, as can be seen in Fig. 7c ($$\varphi$$ = 0.5), or disappear almost completely (Fig. 7d, $$\varphi$$ = 0.7). Due to the higher degree of deformation in the middle of the samples, significantly fewer pores are visible than in the edge areas. The direction of material flow can be seen particularly well in Fig. 7c and d. It can be assumed that above a degree of deformation of $$\varphi$$ = 0.5 the porosity is effectively reduced. The SAM images confirm this result. As the degree of deformation increases, the porosity also decreases, which can be seen by a reduction of the white areas.
Figure 8 shows the microstructure images of the respective samples from Fig. 7. Despite the different degrees of deformation, a similar martensitic microstructure prevails in all samples. This is due to the fast cooling of the samples. After forming, the samples cool down very quickly, which results in a martensitic microstructure.

### 4.2 Investigations of hybrid samples

The results for hybrid samples taken in transverse direction of the specimen are depicted in Fig. 9. As can be seen, for $$\varphi =0.3$$ larger pores up to 0.5 mm length are present. With increasing degree of deformation $$\varphi$$, the overall pore size is reduced. However, even samples with $$\varphi =0.7$$ are not free of defects. A variation of $$h_{base}$$ doesn’t seem to have an influence for constant $$\varphi$$. A total closing of the existing pores is not possible depending on the degree of forming and forming temperature. This is due to gas inclusions existing in the microstructure which cannot leak.
In Fig. 10, the hybrid specimens are depicted. The results show the situation after a global plastic strain of $$\varphi =0.3$$, $$\varphi =0.5$$ or $$\varphi =0.7$$ was achieved. Figure 10a show the specimen with a baseplate height of 15 mm, (b) with 12 mm and (c) with 10 mm.
The results of the numerical investigation of the forming process of the hybrid sample underline the results of the pore analysis results of the hybrid specimen. When considering the degree of deformation distribution of the different sample designs, the following is noticeable: in the intermediate area of the hybrid specimen, a local plastic strain about $$\varphi _{max}=0.56$$ was achieved for all three designs of the investigated specimen with a global plastic strain of $$\varphi _{global,max}=0.7$$. This indicates that the height of the base plate has no significant influence of the achieved plastic strain in the intermediate area. In the cladding itself a maximum of $$\varphi _{local,max} =0.5$$ was achieved independently of $$h_{base}$$. From the results of the forming tests of the mono specimens in which it was determined that pores were closed from a degree of deformation $$\varphi _{global} > 0.5$$, the necessary degree of deformation to close or reduce pores was not achieved in the cladding of the test series with hybrid specimen. This suggets that the pores could not be closed due to an insufficient degree of deformation. The main deformation always takes place in the base material (cf. Fig. 10). This can be explained by the much lower flow stress of the base material compared to the cladding material AISI 52100. Therefore an inhomogeneous heating of the hybrid sample is necessary, so that the flow stress levels are balanced and the cladding can be deformed to a degree of deformation of $$\varphi > 0.5$$ or higher.
Figure 11 shows the stress triaxiality for the three cases, which are identical to Fig. 10. The stress triaxiality represents the well known ratio of hydrostatic stress to von Mises equivalent stress. The results show that a uniaxial or hydrostatic compressive stress is present in both the base material and cladding material. Since the degree of deformation is the only variable parameter in the investigations considered, it seems feasible that a combination of compressive stresses and high degrees of deformation helps to reduce pores in claddings.

## 5 Summary and outlook

The present study shows the investigation of the influence of the plastic strain on the closing of pores in mono (AISI 52100) and in hybrid specimen (AISI 1015 and 52100). The hybrid specimen was designed so that the base and the cladding material contained in the specimen. Before and after the compression test the specimens were checked for pores by means of SAM. In the forming investigations, a global plastic strain of $$\varphi =0.3$$, $$\varphi =0.5$$ and $$\varphi =0.7$$ was chosen. The results of the forming of the mono specimens show that with an increasing plastic strain, the number of pores reduces significantly. From a global plastic strain of $$\varphi > 0.5$$, a reduction of pores can be observed. These results were observed by means of the SAM and a subsequent micro section of the specimens. By a plastic strain of $$\varphi = 0.7$$, the pores disappear nearly completely. A closing of pores in the cladding and in the intermediate zone of the hybrid specimen cannot be observed. The amount of pores is reduced but completely defect-free samples could not be provided by the uniaxial compression test. This is a result of the different material flows within the hybrid specimen, which was investigated by means of a numerical investigation. The results indicate that the maximum achieved plastic strain within the cladding was $$\varphi _{local,max} < 0.5$$, which is below the plastic strain required to close the pores seen in the forming tests of the mono specimen. Due to the homogeneous heating of the hybrid specimen the flow stress of the base material is much lower than the flow stress of the cladding. Therefore, the main deformation takes place in the base material and the required plastic strain to close pores cannot be achieved in the cladding and in the intermediate layer. To avoid the main deformation in the soft base material, an inhomogeneous temperature distribution within in the hybrid sample is necessary. This could be achieved by induction heating. A suitable temperature distribution can be designed by numerical simulation of the induction heating process. In further investigations, the required temperature gradient of the hybrid specimen needs to be calculated by means of the numerical investigation in order to achieve the required plastic strain in the cladding. The aim is to achieve a higher material flow in the cladding by increasing the temperature in this zone. The transfer of inhomogeneous temperature distributions can be realised in industrial processes by an inductive heating method. Here, the heating of the surface layers can be controlled in a targeted manner. The new investigation will be evaluated subsequently by the presented experimental test method. The results will be used within the tailored forming process chain to manufacture high performance components using hybrid semi-finished products. For example the manufacturing of an bearing washer can participate from the findings within this manuscript. Within the tailored forming process chain, the running surface is welded on a base material and formed, subsequently. The results presented indicate that sufficient forming and the presence of uniaxial pressure or hydrostatic stress can reduce welding defects such as pores in the running surface.

## Acknowledgements

The results presented in this paper were obtained within the Collaborative Research Centre 1153 Process chain to produce hybrid high-performance components by tailored forming in subproject A4, T1, C1 and C3. The authors would like to thank the German Research Foundation (DFG) for the financial support of this project-Grant number 252662854.

## Compliance with ethical standards

### Conflict of interest

The authors declare that they have no conflict of interest.

## Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
print
PRINT
Literature
1.
Behrens B-A, Overmeyer L, Barroi A, Frischkorn C, Hermsdorf J, Kaierle S, Stonis M, Huskic A (2013) Basic study on the process combination of deposition welding and subsequent hot bulk forming. Prod Eng 7(6):585591
2.
Pape F, Coors T, Barroi A, Hermsdorf J, Mildebrath M, Hassel T, Kaierle S, Matthias T, Chugreev A, Chugreeva A, Behrens B-A, Overmeyer L, Poll G (2018) Tribological study on tailored-formed axial bearing washers. Tribol Online 13(6):320–326 CrossRef
3.
Chugreeva A, Mildebrath M, Diefenbach J, Barroi A, Lammers M, Hermsdorf J, Hassel T, Overmeyer L, Behrens B-A (2018) Manufacturing of high-performance bi-metal bevel gears by combined deposition welding and forging. Metals 8(11):898 CrossRef
4.
Schneider M (1998) Laser cladding with powder, effect of some machining parameters on clad properties. Ph.D. Thesis at the University of Twente, Enschede, The Netherland
5.
Kaierle S, Barroi A, Noelke C, Hermsdorf J, Overmeyer L, Haferkamp H (2012) Review on laser deposition welding: from micro to macro. Phys Procedia 39:336–345 CrossRef
6.
Al-Sayed A, Hussein A-H, Nofa A, Hassab E-S, Elgazzar H, Sabour H (2017) Laser powder cladding of Ti-6Al-4V $$\alpha$$/ $$\beta$$ Alloy. Materials. https://​doi.​org/​10.​3390/​ma10101178 CrossRef
7.
Behrens B-A, Chugreev A, Matthias T, Poll G, Pape F, Coors T, Hassel T, Maier H-J, Mildebrath M (2019) Manufacturing and evaluation of multi-material axial-bearing washers by tailored forming. Metals 9:232 CrossRef
8.
Schneider W, Twrdek J (2019) Praxiswissen Schweißtechnik, 6th edn. Springer Vieweg, Wiesbaden, p 268
9.
Dilthey U (2005) Schweißtechnische Fertigungsverfahren 2Verhalten der Werkstoffe beim Schweißen. Springer, Berlin, p 130. ISBN 978-3540216742
10.
Matthes K, Schneider W (2016) Schweißtechnik Schweißen von metallischen Konstruktionswerkstoffen, 6th edn. Hanser Verlag, Munich, pp 33–34 CrossRef
11.
Yuan Y, Li Z (2017) Microstructure and tribology behaviors of in-situ WC/Fe carbide cladding fabricated by plasma transferred arc metallurgic reaction. Appl Surf Sci 423:1324 CrossRef
12.
Ferozhkhan M-M, Duraiselvam M, Ganesh Kumar K, Ravibharath R (2016) Plasma transfered arc welding of stellite 6 alloy on stainless steel for wear resistance. Procedia Technol 25:1305–1311 CrossRef
13.
Liu C, Peng H, Zhao Y, Yuan Y, Guo H-B, Xu H-B (2018) Microstructure, mechanical and corrosion properties of electron-beam-melted and plasma-transferred arc-welded WCp/NiBSi metal matrix composites. Rare Met 110:818
14.
Narayanan G, Gnanamoorthy R (2007) Rolling/sliding contact fatigue life prediction of sintered and hardened steels. Wear 262:70–78 CrossRef
15.
Dilthey U (2005) Schweißtechnische Fertigungsverfahren 1 - Schweiß- und Schneidtechnologien, 3rd edn. Springer, Berlin, p 208
Title
Influence of degree of deformation on welding pore reduction in high-carbon steels
Authors
Bernd-Arno Behrens
Hans Jürgen Maier
Gerhard Poll
Ludger Overmeyer
Hendrik Wester
Johanna Uhe
Thomas Hassel
Florian Pape
Marius Lammers
Jörg Hermsdorf
Stefan Kaierle
Laura Budde
Felix Saure
Maximilian Mildebrath
Timm Coors
Christoph Büdenbender
Publication date
16-02-2021
Publisher
Springer Berlin Heidelberg
Published in
Production Engineering / Issue 2/2021
Print ISSN: 0944-6524
Electronic ISSN: 1863-7353
DOI
https://doi.org/10.1007/s11740-020-01009-z

Go to the issue