Influence of Yb doping on optical and upconversion photoluminescence properties of Yb-, Er-co-doped Y2O3 transparent ceramics prepared by SPS

Authors: Hiromi Kimura, Takumi Kato, Shin-ichi Yamamoto, Daisuke Nakauchi, Noriaki Kawaguchi, Takayuki Yanagida

Published in: Journal of Materials Science: Materials in Electronics | Issue 5/2021

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

x% Yb-, 0.5% Er-co-doped Y2O3 transparent ceramics (x = 0, 0.1, 0.5, 1.0, 5.0 and 10) were prepared by the spark plasma sintering, and then we evaluated the effect of Yb doping on optical and upconversion (UC) photoluminescence (PL) properties. Under an excitation at 380 nm, the sharp emission peaks appeared around 550 and 660 nm, and the quantum yield was approximately 2%. The PL decay curves monitoring around 550 nm were fitted by a single exponential decay function. The decay time constants were 0.03–0.11 ms, and the values were typical for the 4f → 4f transitions of Er3+. Regarding the UC PL properties, the sharp UC emission peaks around 550 and 660 nm were observed, and the UC emission intensity of 5.0% Yb-, 0.5% Er-co-doped Y2O3 transparent ceramic sample was the highest among the prepared samples. With increasing x, the chromaticity of UC emission color was tuned from green to red region. Regarding the UC PL decay curves, the rise time became slower as increasing x. This behavior is one of the evidence of energy transfer from Yb3+ to Er3+.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literature
2.
go back to reference K. Bando, K. Sakano, Y. Noguchi, Y. Shimizu, J. Light Vis. Environ. 22, 2 (1998)CrossRef K. Bando, K. Sakano, Y. Noguchi, Y. Shimizu, J. Light Vis. Environ. 22, 2 (1998)CrossRef
3.
go back to reference D. Chen, W. Xiang, X. Liang, J. Zhong, H. Yu, M. Ding, H. Lu, Z. Ji, J. Eur. Ceram. Soc. 35, 859 (2015)CrossRef D. Chen, W. Xiang, X. Liang, J. Zhong, H. Yu, M. Ding, H. Lu, Z. Ji, J. Eur. Ceram. Soc. 35, 859 (2015)CrossRef
4.
go back to reference K. Yoshimura, H. Fukunaga, M. Izumi, M. Masuda, T. Uemura, K. Takahashi, R.-J. Xie, N. Hirosaki, J. Soc. Inf. Disp. 24, 449 (2016)CrossRef K. Yoshimura, H. Fukunaga, M. Izumi, M. Masuda, T. Uemura, K. Takahashi, R.-J. Xie, N. Hirosaki, J. Soc. Inf. Disp. 24, 449 (2016)CrossRef
6.
go back to reference J. Lu, J. Lu, T. Murai, K. Takaichi, T. Uematsu, K. Ueda, H. Yagi, T. Yanagitani, A.A. Kaminskii, Jpn. J. Appl. Phys. 40, L1277 (2001)CrossRef J. Lu, J. Lu, T. Murai, K. Takaichi, T. Uematsu, K. Ueda, H. Yagi, T. Yanagitani, A.A. Kaminskii, Jpn. J. Appl. Phys. 40, L1277 (2001)CrossRef
7.
8.
go back to reference H. Kimura, T. Kato, D. Nakauchi, G. Okada, N. Kawaguchi, T. Yanagida, Nucl. Instruments Methods Phys. Res. A 954, 161226 (2020)CrossRef H. Kimura, T. Kato, D. Nakauchi, G. Okada, N. Kawaguchi, T. Yanagida, Nucl. Instruments Methods Phys. Res. A 954, 161226 (2020)CrossRef
9.
go back to reference L. Wang, M.S. Draz, W. Wang, G. Liao, Y. Xu, J. Biomed. Nanotechnol. 11, 325 (2015)CrossRef L. Wang, M.S. Draz, W. Wang, G. Liao, Y. Xu, J. Biomed. Nanotechnol. 11, 325 (2015)CrossRef
11.
go back to reference C. Duan, L. Liang, L. Li, R. Zhang, Z.P. Xu, J. Mater. Chem. B 6, 192 (2018)CrossRef C. Duan, L. Liang, L. Li, R. Zhang, Z.P. Xu, J. Mater. Chem. B 6, 192 (2018)CrossRef
12.
go back to reference B. Zhu, B. Qian, Y. Liu, C. Xu, C. Liu, Q. Chen, J. Zhou, X. Liu, J. Qiu, NPG Asia Mater. 9, e394 (2017)CrossRef B. Zhu, B. Qian, Y. Liu, C. Xu, C. Liu, Q. Chen, J. Zhou, X. Liu, J. Qiu, NPG Asia Mater. 9, e394 (2017)CrossRef
13.
go back to reference L. Gao, X. Shan, X. Xu, Y. Liu, B. Liu, S. Li, S. Wen, C. Ma, D. Jin, F. Wang, Nanoscale 12, 18595 (2020)CrossRef L. Gao, X. Shan, X. Xu, Y. Liu, B. Liu, S. Li, S. Wen, C. Ma, D. Jin, F. Wang, Nanoscale 12, 18595 (2020)CrossRef
14.
15.
go back to reference X. Chen, W. Xu, H. Song, C. Chen, H. Xia, Y. Zhu, D. Zhou, S. Cui, Q. Dai, J. Zhang, A.C.S. Appl, Mater. Interfaces 8, 9071 (2016)CrossRef X. Chen, W. Xu, H. Song, C. Chen, H. Xia, Y. Zhu, D. Zhou, S. Cui, Q. Dai, J. Zhang, A.C.S. Appl, Mater. Interfaces 8, 9071 (2016)CrossRef
16.
go back to reference Y. Zhang, L. Zhang, R. Deng, J. Tian, Y. Zong, D. Jin, X. Liu, J. Am. Chem. Soc. 136, 4893 (2014)CrossRef Y. Zhang, L. Zhang, R. Deng, J. Tian, Y. Zong, D. Jin, X. Liu, J. Am. Chem. Soc. 136, 4893 (2014)CrossRef
17.
go back to reference Q. Zhao, J. Zhao, M. Tao, C. Wang, X. Zeng, Y. Hu, S. Wang, M. Zeng, W. Zhou, H. Gu, Y. Li, J. Lumin. 214, 116580 (2019)CrossRef Q. Zhao, J. Zhao, M. Tao, C. Wang, X. Zeng, Y. Hu, S. Wang, M. Zeng, W. Zhou, H. Gu, Y. Li, J. Lumin. 214, 116580 (2019)CrossRef
18.
go back to reference E. Palo, L. Pihlgren, M. Tuomisto, T. Laihinen, I. Hyppänen, J. Kankare, M. Lastusaari, T. Soukka, H.C. Swart, J. Hölsä, Opt. Mater. 59, 49 (2016)CrossRef E. Palo, L. Pihlgren, M. Tuomisto, T. Laihinen, I. Hyppänen, J. Kankare, M. Lastusaari, T. Soukka, H.C. Swart, J. Hölsä, Opt. Mater. 59, 49 (2016)CrossRef
19.
go back to reference G.Y. Chen, H.C. Liu, G. Somesfalean, Y.Q. Sheng, H.J. Liang, Z.G. Zhang, Q. Sun, F.P. Wang, Appl. Phys. Lett. 92, 113114 (2008)CrossRef G.Y. Chen, H.C. Liu, G. Somesfalean, Y.Q. Sheng, H.J. Liang, Z.G. Zhang, Q. Sun, F.P. Wang, Appl. Phys. Lett. 92, 113114 (2008)CrossRef
20.
go back to reference S.-I. Yamamoto, K. Ohyama, T. Ban, T. Nonaka, Mater. Res. Express 6, 036202 (2018)CrossRef S.-I. Yamamoto, K. Ohyama, T. Ban, T. Nonaka, Mater. Res. Express 6, 036202 (2018)CrossRef
21.
22.
go back to reference L.A. Diaz-Torres, P. Salas, J. Oliva, E. Resendiz-L, C. Rodriguez-Gonzalez, O. Meza, Appl. Phys. A 123, 25 (2017)CrossRef L.A. Diaz-Torres, P. Salas, J. Oliva, E. Resendiz-L, C. Rodriguez-Gonzalez, O. Meza, Appl. Phys. A 123, 25 (2017)CrossRef
23.
go back to reference J. Zhang, Z. Hao, J. Li, X. Zhang, Y. Luo, G. Pan, Light Sci. Appl. 4, e239 (2015)CrossRef J. Zhang, Z. Hao, J. Li, X. Zhang, Y. Luo, G. Pan, Light Sci. Appl. 4, e239 (2015)CrossRef
24.
go back to reference T. Nonaka, T. Ban, S.-I. Yamamoto, Trans. Mater. Res. Soc. Jpn. 42, 139 (2017)CrossRef T. Nonaka, T. Ban, S.-I. Yamamoto, Trans. Mater. Res. Soc. Jpn. 42, 139 (2017)CrossRef
25.
go back to reference B.-C. Hwang, S. Jiang, T. Luo, J. Watson, G. Sorbello, N. Peyghambarian, J. Opt. Soc. Am. B 17, 833 (2000)CrossRef B.-C. Hwang, S. Jiang, T. Luo, J. Watson, G. Sorbello, N. Peyghambarian, J. Opt. Soc. Am. B 17, 833 (2000)CrossRef
28.
go back to reference G. Cabello-Guzmán, D. González, C. Caro-Díaz, L. Lillo-Arroyo, F. Valenzuela-Melgarejo, G. Cárdenas Triviño, G.E. Buono-Core, B. Chornik, Y. Huentupil, J. Lumin. 204, 401 (2018)CrossRef G. Cabello-Guzmán, D. González, C. Caro-Díaz, L. Lillo-Arroyo, F. Valenzuela-Melgarejo, G. Cárdenas Triviño, G.E. Buono-Core, B. Chornik, Y. Huentupil, J. Lumin. 204, 401 (2018)CrossRef
30.
go back to reference V. Singh, P. Haritha, V. Venkatramu, S.H. Kim, Spectrochim. Acta A 126, 306 (2014)CrossRef V. Singh, P. Haritha, V. Venkatramu, S.H. Kim, Spectrochim. Acta A 126, 306 (2014)CrossRef
32.
33.
go back to reference N. Wang, X. Zhang, H. Jiang, T. Dong, D. Yang, Mater. Chem. Phys. 135, 709 (2012)CrossRef N. Wang, X. Zhang, H. Jiang, T. Dong, D. Yang, Mater. Chem. Phys. 135, 709 (2012)CrossRef
34.
35.
go back to reference J. Wang, J. Ma, J. Zhang, P. Liu, D. Luo, D. Yin, D. Tang, L.B. Kong, Opt. Mater. 71, 117 (2017)CrossRef J. Wang, J. Ma, J. Zhang, P. Liu, D. Luo, D. Yin, D. Tang, L.B. Kong, Opt. Mater. 71, 117 (2017)CrossRef
36.
37.
go back to reference Q. Yi, S. Zhou, H. Teng, H. Lin, X. Hou, T. Jia, J. Eur. Ceram. Soc. 32, 381 (2012)CrossRef Q. Yi, S. Zhou, H. Teng, H. Lin, X. Hou, T. Jia, J. Eur. Ceram. Soc. 32, 381 (2012)CrossRef
38.
go back to reference K. Ning, J. Wang, J. Ma, Z. Dong, L.B. Kong, D. Tang, Mater. Today Commun. 24, 101185 (2020)CrossRef K. Ning, J. Wang, J. Ma, Z. Dong, L.B. Kong, D. Tang, Mater. Today Commun. 24, 101185 (2020)CrossRef
40.
41.
go back to reference H. Furuse, S. Nakasawa, H. Yoshida, K. Morita, T.S. Suzuki, B.-N. Kim, Y. Sakka, K. Hiraga, J. Am. Ceram. Soc. 101, 694 (2018)CrossRef H. Furuse, S. Nakasawa, H. Yoshida, K. Morita, T.S. Suzuki, B.-N. Kim, Y. Sakka, K. Hiraga, J. Am. Ceram. Soc. 101, 694 (2018)CrossRef
42.
go back to reference X. Hou, S. Zhou, W. Li, Y. Li, H. Lin, H. Teng, T. Jia, J. Am. Ceram. Soc. 93, 2779 (2010)CrossRef X. Hou, S. Zhou, W. Li, Y. Li, H. Lin, H. Teng, T. Jia, J. Am. Ceram. Soc. 93, 2779 (2010)CrossRef
43.
go back to reference T. Nonaka, T. Kanamori, K. Ohyama, S.I. Yamamoto, Jpn. J. Appl. Phys. 54, 03CA02 (2015)CrossRef T. Nonaka, T. Kanamori, K. Ohyama, S.I. Yamamoto, Jpn. J. Appl. Phys. 54, 03CA02 (2015)CrossRef
44.
go back to reference A. Camenzind, R. Strobel, S.E. Pratsinis, Chem. Phys. Lett. 415, 193 (2005)CrossRef A. Camenzind, R. Strobel, S.E. Pratsinis, Chem. Phys. Lett. 415, 193 (2005)CrossRef
45.
go back to reference W. Zhang, T. Lu, N. Wei, Y. Wang, B. Ma, F. Li, Z. Lu, J. Qi, J. Alloys Compd. 520, 36 (2012)CrossRef W. Zhang, T. Lu, N. Wei, Y. Wang, B. Ma, F. Li, Z. Lu, J. Qi, J. Alloys Compd. 520, 36 (2012)CrossRef
46.
47.
go back to reference X. Huang, X. Zhang, Z. Hu, Y. Feng, J. Wei, X. Liu, X. Li, H. Chen, L. Wu, H. Pan, J. Li, Opt. Mater. 92, 359 (2019)CrossRef X. Huang, X. Zhang, Z. Hu, Y. Feng, J. Wei, X. Liu, X. Li, H. Chen, L. Wu, H. Pan, J. Li, Opt. Mater. 92, 359 (2019)CrossRef
48.
go back to reference Z. Hu, X. Xu, J. Wang, P. Liu, D. Li, X. Wang, J. Zhang, J. Xu, D. Tang, J. Eur. Ceram. Soc. 38, 1981 (2018)CrossRef Z. Hu, X. Xu, J. Wang, P. Liu, D. Li, X. Wang, J. Zhang, J. Xu, D. Tang, J. Eur. Ceram. Soc. 38, 1981 (2018)CrossRef
49.
51.
go back to reference J. Zhang, L. An, M. Liu, S. Shimai, S. Wang, J. Eur. Ceram. Soc. 29, 305 (2009)CrossRef J. Zhang, L. An, M. Liu, S. Shimai, S. Wang, J. Eur. Ceram. Soc. 29, 305 (2009)CrossRef
52.
go back to reference A.N. Meza-Rocha, E.F. Huerta, U. Caldiño, E. Zaleta-Alejandre, S.H. Murrieta, J.M. Hernández, E. Camarillo, Z. Rivera-Álvarez, G.C. Righini, C. Falcony, J. Lumin. 154, 106 (2014)CrossRef A.N. Meza-Rocha, E.F. Huerta, U. Caldiño, E. Zaleta-Alejandre, S.H. Murrieta, J.M. Hernández, E. Camarillo, Z. Rivera-Álvarez, G.C. Righini, C. Falcony, J. Lumin. 154, 106 (2014)CrossRef
54.
go back to reference V.K. Tikhomirov, V.D. Rodríguez, J. Méndez-Ramos, J. Del-Castillo, D. Kirilenko, G. Van Tendeloo, V.V. Moshchalkov, Sol. Energy Mater. Sol. Cells 100, 209 (2012)CrossRef V.K. Tikhomirov, V.D. Rodríguez, J. Méndez-Ramos, J. Del-Castillo, D. Kirilenko, G. Van Tendeloo, V.V. Moshchalkov, Sol. Energy Mater. Sol. Cells 100, 209 (2012)CrossRef
55.
go back to reference Y. Tian, Y. Fu, M. Xing, X. Luo, J. Nanomater. 2015, 1 (2015) Y. Tian, Y. Fu, M. Xing, X. Luo, J. Nanomater. 2015, 1 (2015)
56.
58.
59.
go back to reference R. Martín-Rodríguez, S. Fischer, A. Ivaturi, B. Froehlich, K.W. Krämer, J.C. Goldschmidt, B.S. Richards, A. Meijerink, Chem. Mater. 25, 1912 (2013)CrossRef R. Martín-Rodríguez, S. Fischer, A. Ivaturi, B. Froehlich, K.W. Krämer, J.C. Goldschmidt, B.S. Richards, A. Meijerink, Chem. Mater. 25, 1912 (2013)CrossRef
Metadata
Title
Influence of Yb doping on optical and upconversion photoluminescence properties of Yb-, Er-co-doped Y2O3 transparent ceramics prepared by SPS
Authors
Hiromi Kimura
Takumi Kato
Shin-ichi Yamamoto
Daisuke Nakauchi
Noriaki Kawaguchi
Takayuki Yanagida
Publication date
04-02-2021
Publisher
Springer US
Published in
Journal of Materials Science: Materials in Electronics / Issue 5/2021
Print ISSN: 0957-4522
Electronic ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-021-05346-2

Other articles of this Issue 5/2021

Journal of Materials Science: Materials in Electronics 5/2021 Go to the issue