Published in: Metallurgical and Materials Transactions A 7/2019

17-05-2019

Investigation into the Extrudability of a New Mg-Al-Zn-RE Alloy with Large Amounts of Alloying Elements

Authors: Sheng-Wen Bai, Gang Fang, Jie Zhou

Published in: Metallurgical and Materials Transactions A | Issue 7/2019

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

The present study was aimed at determining the extrudability of a newly developed Mg-Al-Zn-RE magnesium alloy with large amounts of alloying elements. The experimental and numerical investigation clearly showed that the extrudate temperature was a crucial factor in deciding if a critical temperature between 754 K and 768 K (481 °C and 495 °C) was reached during extrusion, above which hot shortness occurred. Under the extrusion conditions applied, dynamic recrystallization (DRX) occurred, leading to grain refinement from a mean grain size of 165 μm in the as-solid-solution-treated billet to 8.0 to 10.9 μm in the extruded rods. Second-phase particles, such as Mg17Al12 and Al11La3, were found to distribute on grain boundaries and aid in grain refinement. The mechanical properties of the extrudate were greatly influenced by the as-extruded microstructure and extrusion condition. As the initial billet temperature decreased, the ultimate tensile strength (UTS) and elongation of the alloy increased, while yield strength (YS) remained almost unchanged. At an initial billet temperature of 523 K (250 °C), a stem speed of 3.93 mm/s, and a reduction ratio of 29.8, the extruded magnesium alloy had a mean grain size of 8 μm. Its YS, UTS, and elongation reached 217 ± 3 MPa, 397 ± 7 MPa, and 20 ± 1.3 pct, respectively.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literature
1.
3.
4.
go back to reference S. Yao and Y.F. Li: Sci. Total Environ., 2015, vol. 44, pp. 89–96. S. Yao and Y.F. Li: Sci. Total Environ., 2015, vol. 44, pp. 89–96.
5.
go back to reference H. Pan, Y. Ren, H. Fu, H. Zhao, L. Wang, X. Meng, and G. Qin: J. Alloys Compds., 2016, vol. 663, pp. 321–31.CrossRef H. Pan, Y. Ren, H. Fu, H. Zhao, L. Wang, X. Meng, and G. Qin: J. Alloys Compds., 2016, vol. 663, pp. 321–31.CrossRef
6.
go back to reference D. Letzig, J. Swiostek, J. Bohlen, P. A. Beaven, and K.U. Kainer: Met. Sci. J., 2013, vol. 24, pp. 991–96. D. Letzig, J. Swiostek, J. Bohlen, P. A. Beaven, and K.U. Kainer: Met. Sci. J., 2013, vol. 24, pp. 991–96.
8.
go back to reference W.A. Monteiro, S.J. Buso, and L.V. da Silva: in New Features on Magnesium Alloys, W.A. Monteiro, ed., InTech, Rijeka, 2012, pp. 1–14. W.A. Monteiro, S.J. Buso, and L.V. da Silva: in New Features on Magnesium Alloys, W.A. Monteiro, ed., InTech, Rijeka, 2012, pp. 1–14.
9.
go back to reference S. You, Y. Huang, K.U. Kainer, and N. Hort: J. Magn. Alloys, 2017, vol. 5, pp. 239–53.CrossRef S. You, Y. Huang, K.U. Kainer, and N. Hort: J. Magn. Alloys, 2017, vol. 5, pp. 239–53.CrossRef
10.
go back to reference Z. Zeng, N. Stanford, C.H.J. Davies, J.F. Nie, and N. Birbilis: Int. Mater. Rev., 2018, vol. 2, pp. 1–36. Z. Zeng, N. Stanford, C.H.J. Davies, J.F. Nie, and N. Birbilis: Int. Mater. Rev., 2018, vol. 2, pp. 1–36.
11.
go back to reference C. Bettles and M. Barnett: Advances in Wrought Magnesium Alloys: Fundamentals of Processing, Properties and Applications, Woodhead Publishing, Philadelphia, PA, 2012, pp. 304–22.CrossRef C. Bettles and M. Barnett: Advances in Wrought Magnesium Alloys: Fundamentals of Processing, Properties and Applications, Woodhead Publishing, Philadelphia, PA, 2012, pp. 304–22.CrossRef
12.
go back to reference D.S. Yin, E.L. Zhang, and S.Y. Zeng: Trans. Nonferr. Met. Soc., 2008, vol. 18, pp. 763–68.CrossRef D.S. Yin, E.L. Zhang, and S.Y. Zeng: Trans. Nonferr. Met. Soc., 2008, vol. 18, pp. 763–68.CrossRef
13.
go back to reference W.N. Tang, S.S. Park, and B.S. You: Mater. Des., 2011, vol. 32, pp. 3537–43.CrossRef W.N. Tang, S.S. Park, and B.S. You: Mater. Des., 2011, vol. 32, pp. 3537–43.CrossRef
14.
go back to reference S.M. Masoudpanah and R. Mahmudi: Mater. Sci. Eng. A, 2009, vol. 526, pp. 22–30.CrossRef S.M. Masoudpanah and R. Mahmudi: Mater. Sci. Eng. A, 2009, vol. 526, pp. 22–30.CrossRef
15.
go back to reference B. Zhang, Y. Wang, L. Geng, and C. Lu: Mater. Sci. Eng. A, 2012, vol. 539, pp. 56–60.CrossRef B. Zhang, Y. Wang, L. Geng, and C. Lu: Mater. Sci. Eng. A, 2012, vol. 539, pp. 56–60.CrossRef
16.
go back to reference J. Bohlen, S. Yi, D. Letzig, and K.U. Kainer: Mater. Sci. Eng. A, 2010, vol. 527, pp. 7092–98.CrossRef J. Bohlen, S. Yi, D. Letzig, and K.U. Kainer: Mater. Sci. Eng. A, 2010, vol. 527, pp. 7092–98.CrossRef
17.
go back to reference D.K. Xu, W.N. Tang, L. Liu, Y.B. Xu, and E.H. Han: J. Alloys Compds., 2007, vol. 432, pp. 129–34.CrossRef D.K. Xu, W.N. Tang, L. Liu, Y.B. Xu, and E.H. Han: J. Alloys Compds., 2007, vol. 432, pp. 129–34.CrossRef
18.
go back to reference D.K. Xu, L. Liu, Y.B. Xu, and E.H. Han: J. Alloys Compds., 2006, vol. 426, pp. 155–61.CrossRef D.K. Xu, L. Liu, Y.B. Xu, and E.H. Han: J. Alloys Compds., 2006, vol. 426, pp. 155–61.CrossRef
19.
go back to reference N. Stanford and M.R. Barnett: Mater. Sci. Eng. A, 2008, vol. 496, pp. 399–408.CrossRef N. Stanford and M.R. Barnett: Mater. Sci. Eng. A, 2008, vol. 496, pp. 399–408.CrossRef
20.
go back to reference M. Yamasaki, K. Hashimoto, K. Hagihara, and Y. Kawamura: Acta Mater., 2011, vol. 59, pp. 3646–58.CrossRef M. Yamasaki, K. Hashimoto, K. Hagihara, and Y. Kawamura: Acta Mater., 2011, vol. 59, pp. 3646–58.CrossRef
21.
go back to reference X. Li, W. Qi, K. Zheng, and N. Zhou: J. Magn. Alloys, 2013, vol. 1, pp. 54–63.CrossRef X. Li, W. Qi, K. Zheng, and N. Zhou: J. Magn. Alloys, 2013, vol. 1, pp. 54–63.CrossRef
22.
go back to reference X. Zeng, Y. Zhang, C. Lu, W. Ding, Y. Wang, and Y. Zhu: J. Alloys Compds., 2005, vol. 395, pp. 213–19.CrossRef X. Zeng, Y. Zhang, C. Lu, W. Ding, Y. Wang, and Y. Zhu: J. Alloys Compds., 2005, vol. 395, pp. 213–19.CrossRef
23.
go back to reference N. Stanford, D. Atwell, and M.R. Barnett: Acta Mater., 2010, vol. 58, pp. 6773–83.CrossRef N. Stanford, D. Atwell, and M.R. Barnett: Acta Mater., 2010, vol. 58, pp. 6773–83.CrossRef
24.
go back to reference J.B. Zhang, L.B. Tong, C. Xu, Z.H. Jiang, L.R. Cheng, S. Kamado, and H.J. Zhang: Mater. Sci. Eng. A, 2017, vol. 708, pp. 11–20.CrossRef J.B. Zhang, L.B. Tong, C. Xu, Z.H. Jiang, L.R. Cheng, S. Kamado, and H.J. Zhang: Mater. Sci. Eng. A, 2017, vol. 708, pp. 11–20.CrossRef
25.
go back to reference T. Homma, N. Kunito, and S. Kamado: Scripta Mater., 2009, vol. 61, pp. 644–47.CrossRef T. Homma, N. Kunito, and S. Kamado: Scripta Mater., 2009, vol. 61, pp. 644–47.CrossRef
26.
go back to reference M. Yamasaki, T. Anan, S. Yoshimoto, and Y. Kawamura: Scripta Mater., 2005, vol. 53, pp. 799–803.CrossRef M. Yamasaki, T. Anan, S. Yoshimoto, and Y. Kawamura: Scripta Mater., 2005, vol. 53, pp. 799–803.CrossRef
27.
go back to reference Y. Chen, L. Hao, Y. Ruiyu, G. Liu, and T. Xia: Mater. Sci. Technol., 2014, vol. 30, pp. 495–500.CrossRef Y. Chen, L. Hao, Y. Ruiyu, G. Liu, and T. Xia: Mater. Sci. Technol., 2014, vol. 30, pp. 495–500.CrossRef
28.
go back to reference A.A. Luo, C. Zhang, and A.K. Sachdev: Scripta Mater., 2012, vol. 66, pp. 491–94.CrossRef A.A. Luo, C. Zhang, and A.K. Sachdev: Scripta Mater., 2012, vol. 66, pp. 491–94.CrossRef
29.
go back to reference T. Murai, S.I. Matsuoka, S. Miyamoto, and Y. Oki: J. Mater. Process. Technol., 2001, vol. 141, pp. 207–12.CrossRef T. Murai, S.I. Matsuoka, S. Miyamoto, and Y. Oki: J. Mater. Process. Technol., 2001, vol. 141, pp. 207–12.CrossRef
30.
go back to reference S. Ishihara, H. Shibata, K. Komano, T. Goshima, and Z.Y. Nan: Key Eng. Mater., 2007, vol. 353, pp. 291–94.CrossRef S. Ishihara, H. Shibata, K. Komano, T. Goshima, and Z.Y. Nan: Key Eng. Mater., 2007, vol. 353, pp. 291–94.CrossRef
31.
go back to reference B.P. Zhang, L. Geng, L.J. Huang, X.X Zhang, and C.C. Dong: Scripta Mater., 2010, vol. 63, pp. 1024–27.CrossRef B.P. Zhang, L. Geng, L.J. Huang, X.X Zhang, and C.C. Dong: Scripta Mater., 2010, vol. 63, pp. 1024–27.CrossRef
32.
go back to reference L.B. Tong, M.Y. Zheng, L.R. Cheng, D.P. Zhang, S. Kamado, J. Meng, and H.J. Zhang: Mater. Charact., 2015, vol. 104, pp. 66–72.CrossRef L.B. Tong, M.Y. Zheng, L.R. Cheng, D.P. Zhang, S. Kamado, J. Meng, and H.J. Zhang: Mater. Charact., 2015, vol. 104, pp. 66–72.CrossRef
33.
go back to reference S.H. Park, J.G. Jung, Y.M. Kim, and B.S. You: Mater. Lett., 2015, vol. 139, pp. 35–38.CrossRef S.H. Park, J.G. Jung, Y.M. Kim, and B.S. You: Mater. Lett., 2015, vol. 139, pp. 35–38.CrossRef
34.
go back to reference M. Shahzad and L. Wagner: Mater. Sci. Eng. A, 2009, vol. 506, pp. 141–47.CrossRef M. Shahzad and L. Wagner: Mater. Sci. Eng. A, 2009, vol. 506, pp. 141–47.CrossRef
35.
go back to reference Q. Chen, D. Shu, Z. Zhao, Z. Zhao, Y. Wang, and B. Yuan: Mater. Des., 2012, vol. 40, pp. 488–96.CrossRef Q. Chen, D. Shu, Z. Zhao, Z. Zhao, Y. Wang, and B. Yuan: Mater. Des., 2012, vol. 40, pp. 488–96.CrossRef
36.
go back to reference A. Singh, Y. Osawa, and H. Somekawa: Metall. Mater. Trans. A, 2014, vol. 45A, pp. 3232–40.CrossRef A. Singh, Y. Osawa, and H. Somekawa: Metall. Mater. Trans. A, 2014, vol. 45A, pp. 3232–40.CrossRef
37.
go back to reference S.H. Park, J.H. Bae, S.H. Kim, J. Yoon, and B.S. You: Metall. Mater. Trans. A, 2015, vol. 46A, pp. 5482–88.CrossRef S.H. Park, J.H. Bae, S.H. Kim, J. Yoon, and B.S. You: Metall. Mater. Trans. A, 2015, vol. 46A, pp. 5482–88.CrossRef
38.
go back to reference F. Bu, Q. Yang, K. Guan, X. Qiu, D. Zhang, and W. Sun: J. Alloys Compds., 2016, vol. 688, pp. 1241–50.CrossRef F. Bu, Q. Yang, K. Guan, X. Qiu, D. Zhang, and W. Sun: J. Alloys Compds., 2016, vol. 688, pp. 1241–50.CrossRef
39.
go back to reference X. Luo, S. Dang, and L. Kang: Adv. Mater. Sci. Eng., 2014, vol. 2014, pp. 1–7. X. Luo, S. Dang, and L. Kang: Adv. Mater. Sci. Eng., 2014, vol. 2014, pp. 1–7.
40.
go back to reference J. Mohammadi, M. Ghoreishi, and Y. Behnamian: Mater. Res., 2014, vol. 17, pp. 994–1002.CrossRef J. Mohammadi, M. Ghoreishi, and Y. Behnamian: Mater. Res., 2014, vol. 17, pp. 994–1002.CrossRef
41.
42.
go back to reference L. Li, H. Zhang, J. Zhou, J. Duszczyk, G. Li, and Z.H. Zhong: Mater. Des., 2008, vol. 29, pp. 1190–98.CrossRef L. Li, H. Zhang, J. Zhou, J. Duszczyk, G. Li, and Z.H. Zhong: Mater. Des., 2008, vol. 29, pp. 1190–98.CrossRef
43.
go back to reference G. Liu, J. Zhou, and J. Duszczyk: J. Mater. Process. Technol., 2008, vol. 200, pp. 185–98.CrossRef G. Liu, J. Zhou, and J. Duszczyk: J. Mater. Process. Technol., 2008, vol. 200, pp. 185–98.CrossRef
44.
go back to reference L. Li, J. Zhou, and J. Duszczyk: J. Mater. Process. Technol., 2006, vol. 172, pp. 372–80.CrossRef L. Li, J. Zhou, and J. Duszczyk: J. Mater. Process. Technol., 2006, vol. 172, pp. 372–80.CrossRef
45.
go back to reference J. Zhou, L. Li, and J. Duszczyk: J. Mater. Process. Technol., 2003, vol. 134, pp. 383–97.CrossRef J. Zhou, L. Li, and J. Duszczyk: J. Mater. Process. Technol., 2003, vol. 134, pp. 383–97.CrossRef
46.
go back to reference T. Sheppard: Extrusion of Aluminum Alloys, Kluwer Academic Publishers, Dordrecht, The Netherlands, 1999, pp. 227–52.CrossRef T. Sheppard: Extrusion of Aluminum Alloys, Kluwer Academic Publishers, Dordrecht, The Netherlands, 1999, pp. 227–52.CrossRef
47.
go back to reference M.P. Clade and T. Sheppard: Mater. Sci. Technol., 1993, vol. 9, pp. 313–18.CrossRef M.P. Clade and T. Sheppard: Mater. Sci. Technol., 1993, vol. 9, pp. 313–18.CrossRef
48.
go back to reference W. Wei, C. Xu, J. Zhang, and X. Niu: China Foundry, 2014, vol. 11, pp. 157–62. W. Wei, C. Xu, J. Zhang, and X. Niu: China Foundry, 2014, vol. 11, pp. 157–62.
49.
go back to reference Y.S. Yang, J.C. Wang, T. Wang, C.M. Liu, and Z.M. Zhang: Trans. Nonferr. Met. Soc., 2014, vol. 24, pp. 76–81.CrossRef Y.S. Yang, J.C. Wang, T. Wang, C.M. Liu, and Z.M. Zhang: Trans. Nonferr. Met. Soc., 2014, vol. 24, pp. 76–81.CrossRef
51.
go back to reference X.D. Wang, W.B. Du, K. Liu, Z.H. Wang, and S.B. Li: J. Alloys Compds., 2012, vol. 522, pp. 78–84.CrossRef X.D. Wang, W.B. Du, K. Liu, Z.H. Wang, and S.B. Li: J. Alloys Compds., 2012, vol. 522, pp. 78–84.CrossRef
52.
go back to reference J.C. Wurst and J.A. Nelson: J. Am. Ceram. Soc., 1972, vol. 55, pp. 109–09.CrossRef J.C. Wurst and J.A. Nelson: J. Am. Ceram. Soc., 1972, vol. 55, pp. 109–09.CrossRef
53.
go back to reference H. Ding, L. Liu, S. Kamado, D. Wang, and Y. Kojima: J. Alloys Compds., 2008, vol. 456, pp. 400–06.CrossRef H. Ding, L. Liu, S. Kamado, D. Wang, and Y. Kojima: J. Alloys Compds., 2008, vol. 456, pp. 400–06.CrossRef
54.
go back to reference S.M. Fatemi-Varzaneh, A. Zarei-Hanzaki, and H. Beladi: Mater. Sci. Eng. A, 2007, vol. 456, pp. 52–57.CrossRef S.M. Fatemi-Varzaneh, A. Zarei-Hanzaki, and H. Beladi: Mater. Sci. Eng. A, 2007, vol. 456, pp. 52–57.CrossRef
55.
go back to reference S.M. Fatemi-Varzaneh, A. Zarei-Hanzaki, and H. Beladi: Mater. Sci. Eng. A, 2007, vol. 456, pp. 52–57.CrossRef S.M. Fatemi-Varzaneh, A. Zarei-Hanzaki, and H. Beladi: Mater. Sci. Eng. A, 2007, vol. 456, pp. 52–57.CrossRef
56.
57.
go back to reference A.G. Beer and M.R. Barnett: Metall. Mater. Trans. A, 2007, vol. 38A, pp. 1856–67.CrossRef A.G. Beer and M.R. Barnett: Metall. Mater. Trans. A, 2007, vol. 38A, pp. 1856–67.CrossRef
58.
go back to reference L. Wang, G. Fang, and L. Qian: Mater. Sci. Eng. A, 2018, vol. 711, pp. 268–83.CrossRef L. Wang, G. Fang, and L. Qian: Mater. Sci. Eng. A, 2018, vol. 711, pp. 268–83.CrossRef
59.
go back to reference J.D. Robson, D.T. Henry, and B. Davis: Acta Mater., 2009, vol. 57, pp. 2739–47.CrossRef J.D. Robson, D.T. Henry, and B. Davis: Acta Mater., 2009, vol. 57, pp. 2739–47.CrossRef
60.
go back to reference K.K. Deng, X.J. Wang, Y.W. Wu, X.S. Hu, K. Wu, and W.M. Gan: Mater. Sci. Eng. A, 2012, vol. 543, pp. 158–63.CrossRef K.K. Deng, X.J. Wang, Y.W. Wu, X.S. Hu, K. Wu, and W.M. Gan: Mater. Sci. Eng. A, 2012, vol. 543, pp. 158–63.CrossRef
61.
go back to reference Q. Liao, X. Chen, Q. Lan, F. Ning, and Q. Le: Mater. Res. Express, 2018, vol. 5, pp. 1–10. Q. Liao, X. Chen, Q. Lan, F. Ning, and Q. Le: Mater. Res. Express, 2018, vol. 5, pp. 1–10.
62.
go back to reference D.C. Foley, M. Al-Maharbi, K.T. Hartwig, I. Karaman, L.J. Kecskes, and S.N. Mathaudhu: Scripta Mater., 2011, vol. 64, pp. 193–96.CrossRef D.C. Foley, M. Al-Maharbi, K.T. Hartwig, I. Karaman, L.J. Kecskes, and S.N. Mathaudhu: Scripta Mater., 2011, vol. 64, pp. 193–96.CrossRef
63.
go back to reference S.M. Razavi, D.C. Foley, I. Karaman, K.T. Hartwig, O. Duygulu, L.J. Kecskes, S.N. Mathaudhu, and V.H. Hammond: Scripta Mater., 2012, vol. 67, pp. 439–42.CrossRef S.M. Razavi, D.C. Foley, I. Karaman, K.T. Hartwig, O. Duygulu, L.J. Kecskes, S.N. Mathaudhu, and V.H. Hammond: Scripta Mater., 2012, vol. 67, pp. 439–42.CrossRef
64.
go back to reference K. Cai, Z. Gao, Q. Zhu, Y. Jin, Y. Chai, and D. Fang: Rare Metal Mater. Eng., 2015, vol. 44, pp. 1489–93. K. Cai, Z. Gao, Q. Zhu, Y. Jin, Y. Chai, and D. Fang: Rare Metal Mater. Eng., 2015, vol. 44, pp. 1489–93.
65.
go back to reference Q. Zhu, C. Fang, N. Li, L. Meng, Y. Wang, Y. Wu, and X. Zhang: Rare Metal Mater. Eng., 2013, vol. 42, pp. 771–75. Q. Zhu, C. Fang, N. Li, L. Meng, Y. Wang, Y. Wu, and X. Zhang: Rare Metal Mater. Eng., 2013, vol. 42, pp. 771–75.
66.
go back to reference C. Che, Z. Cai, X. Yang, L. Cheng, and Y. Du: Mater. Sci. Eng. A, 2017, vol. 705, pp. 282–90.CrossRef C. Che, Z. Cai, X. Yang, L. Cheng, and Y. Du: Mater. Sci. Eng. A, 2017, vol. 705, pp. 282–90.CrossRef
67.
go back to reference L. Fu, X.B. Wang, P.L. Gou, Q.C. Le, W. T. Jia, and Y. Tang: Adv. Eng. Mater., 2017, vol. 19, pp. 1700230.CrossRef L. Fu, X.B. Wang, P.L. Gou, Q.C. Le, W. T. Jia, and Y. Tang: Adv. Eng. Mater., 2017, vol. 19, pp. 1700230.CrossRef
68.
go back to reference A.A. Luo, W. Wu, R.K. Mishra, L. Jin, A.K. Sachdev, and W. Ding: Metall. Mater. Trans. A, 2010, vol. 41, pp. 2662–74.CrossRef A.A. Luo, W. Wu, R.K. Mishra, L. Jin, A.K. Sachdev, and W. Ding: Metall. Mater. Trans. A, 2010, vol. 41, pp. 2662–74.CrossRef
69.
go back to reference M. Easton, A. Beer, M. Barnett, C. Davies, G. Dunlop, Y. Durandet, S. Blacket, T. Hilditch, and P. Beggs: JOM, 2008, vol. 60, pp. 57–62.CrossRef M. Easton, A. Beer, M. Barnett, C. Davies, G. Dunlop, Y. Durandet, S. Blacket, T. Hilditch, and P. Beggs: JOM, 2008, vol. 60, pp. 57–62.CrossRef
70.
go back to reference H. Borkar, M. Hoseini, and M. Pekguleryuz: Mater. Sci. Eng. A, 2012, vol. 549, pp. 168–75.CrossRef H. Borkar, M. Hoseini, and M. Pekguleryuz: Mater. Sci. Eng. A, 2012, vol. 549, pp. 168–75.CrossRef
Metadata
Title
Investigation into the Extrudability of a New Mg-Al-Zn-RE Alloy with Large Amounts of Alloying Elements
Authors
Sheng-Wen Bai
Gang Fang
Jie Zhou
Publication date
17-05-2019
Publisher
Springer US
Published in
Metallurgical and Materials Transactions A / Issue 7/2019
Print ISSN: 1073-5623
Electronic ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-019-05242-9

Other articles of this Issue 7/2019

Metallurgical and Materials Transactions A 7/2019 Go to the issue

Premium Partners