Metamagnetic DyAlO₃ nanoparticles with very low magnetic moment

Nanocrystalline dysprosium monoaluminate (DyAlO₃) has been synthesized by modified sol–gel method after sintering the precursor gel at 950 °C. The micro-structural features have been verified by X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy. The XRD pattern confirms the formation of single-phase DyAlO₃; the average size of the nanoparticles is 50 nm. X-Ray photoelectron spectroscopy has been used to study the chemical composition and bonding in the samples. The binding energies of core-level electrons in Dy, Al and O in DyAlO₃ nanopowder have been found slightly shifted compared to the respective values of the same elements. Both AC and DC magnetic susceptibilities have been measured in the temperature range 2–300 K. Unusually low effective magnetic moment of Dy³⁺, μ_eff = 0.38, has been derived from the inverse magnetic susceptibility–temperature plot between 4 and 252 K. The Nèel temperature, T_N = 3.920 K and exchange interaction constant J/k = −1.74 K, have been also determined.