Physical properties and morphology of siloxane–polyacrylate dispersion and coating films

Authors: W. Pramualkijja, N. Jiratumnukul

Published in: Journal of Coatings Technology and Research | Issue 5/2020

Login to get access
share
SHARE

Abstract

The aim of this work was to study the morphology and physical properties of siloxane–polyacrylate (SPA) dispersion and coating films. The SPA dispersion was synthesized by seeded emulsion polymerization using two different types of silane coupling agents, i.e., vinyltriethoxysilane (VTES) and 3-(trimethoxysilyl) propyl methacrylate (MPTMS), at 1–9% by weight. The effect of the type and content of silane coupling agent used in the SPA dispersion synthesis on the resulting morphology and physical properties of the obtained SPA dispersion and coating films were studied. The results revealed that SPA dispersion synthesized using VTES exhibited a smaller particle size and a higher stability than those using MPTMS. Furthermore, the hydrophobic surfaces and water repellence of the coating films using VTES in the emulsion were higher than those using MPTMS, due to the smoother surface morphology.

To get access to this content you need the following product:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 15 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 15 Tage kostenlos.

Literature
1.
go back to reference Pedna, A, et al., “Obtaining SiO 2–Fluorinated PLA Bionanocomposites with Application as Reversible and Highly-Hydrophobic Coatings of Buildings.” Prog. Org. Coat., 90 91–100 (2016) Pedna, A, et al., “Obtaining SiO 2–Fluorinated PLA Bionanocomposites with Application as Reversible and Highly-Hydrophobic Coatings of Buildings.” Prog. Org. Coat., 90 91–100 (2016)
2.
go back to reference Jeyasubramanian, K, et al., “Fabrication of Water Repellent Cotton Fabric by Coating Nano Particle Impregnated Hydrophobic Additives and Its Characterization.” J. Ind. Eng. Chem., 37 180–189 (2016) CrossRef Jeyasubramanian, K, et al., “Fabrication of Water Repellent Cotton Fabric by Coating Nano Particle Impregnated Hydrophobic Additives and Its Characterization.” J. Ind. Eng. Chem., 37 180–189 (2016) CrossRef
3.
go back to reference Mahltig, B, “Smart Hydrophobic and Soil-Repellent Protective Composite Coatings for Textiles and Leather.” In Smart Composite Coatings and Membranes, pp. 261–292. Elsevier, Amsterdam (2016) Mahltig, B, “Smart Hydrophobic and Soil-Repellent Protective Composite Coatings for Textiles and Leather.” In Smart Composite Coatings and Membranes, pp. 261–292. Elsevier, Amsterdam (2016)
4.
go back to reference Park, H-S, et al., “Preparation and Characterization of Weather Resistant Silicone/Acrylic Resin Coatings.” J. Coat. Technol., 75 (936) 55–64 (2003) CrossRef Park, H-S, et al., “Preparation and Characterization of Weather Resistant Silicone/Acrylic Resin Coatings.” J. Coat. Technol., 75 (936) 55–64 (2003) CrossRef
5.
go back to reference Yu, M, Liu, F, Du, F, “Synthesis and Properties of a Green and Self-cleaning Hard Protective Coating.” Prog. Org. Coat., 94 34–40 (2016) CrossRef Yu, M, Liu, F, Du, F, “Synthesis and Properties of a Green and Self-cleaning Hard Protective Coating.” Prog. Org. Coat., 94 34–40 (2016) CrossRef
6.
go back to reference Christopher, KR, et al., “Synthesis and Characterization of Polystyrene-Acrylate/Polysiloxane (PSA/PSi) Core Shell Polymers and Evaluation of Their Properties for High Durable Exterior Coatings.” Prog. Org. Coat., 77 (6) 1063–1068 (2014) CrossRef Christopher, KR, et al., “Synthesis and Characterization of Polystyrene-Acrylate/Polysiloxane (PSA/PSi) Core Shell Polymers and Evaluation of Their Properties for High Durable Exterior Coatings.” Prog. Org. Coat., 77 (6) 1063–1068 (2014) CrossRef
7.
go back to reference Huang, Y, et al., “Preparation and Characterization of Silica/Fluorinated Acrylate Copolymers Hybrid Films and the Investigation of Their Icephobicity.” Thin Solid Films, 520 (17) 5644–5651 (2012) CrossRef Huang, Y, et al., “Preparation and Characterization of Silica/Fluorinated Acrylate Copolymers Hybrid Films and the Investigation of Their Icephobicity.” Thin Solid Films, 520 (17) 5644–5651 (2012) CrossRef
8.
go back to reference Cappelletti, G, and Fermo, P, “15—Hydrophobic and Superhydrophobic Coatings for Limestone and Marble Conservation” In: Montemor, MF (ed.) Smart Composite Coatings and Membranes, pp. 421–452. Woodhead Publishing, Sawston (2016) Cappelletti, G, and Fermo, P, “15—Hydrophobic and Superhydrophobic Coatings for Limestone and Marble Conservation” In: Montemor, MF (ed.) Smart Composite Coatings and Membranes, pp. 421–452. Woodhead Publishing, Sawston (2016)
9.
go back to reference Ammar, S, et al., “A Novel Coating Material That Uses Nano-sized SiO 2 Particles to Intensify Hydrophobicity and Corrosion Protection Properties.” Electrochim. Acta, 220 417–426 (2016) CrossRef Ammar, S, et al., “A Novel Coating Material That Uses Nano-sized SiO 2 Particles to Intensify Hydrophobicity and Corrosion Protection Properties.” Electrochim. Acta, 220 417–426 (2016) CrossRef
10.
go back to reference Kumar, AM, et al., “In-Situ Synthesis of Hydrophobic SiO 2-PMMA Composite for Surface Protective Coatings: Experimental and Quantum Chemical Analysis.” Polymer, 77 79–86 (2015) CrossRef Kumar, AM, et al., “In-Situ Synthesis of Hydrophobic SiO 2-PMMA Composite for Surface Protective Coatings: Experimental and Quantum Chemical Analysis.” Polymer, 77 79–86 (2015) CrossRef
11.
go back to reference Yuan, X, et al., “Effect of Siloxane-Modified Polyacrylate on Water Uptake and Anticorrosion Mechanism of Silicone–Epoxy Coatings.” J. Coat. Technol. Res, 13 (1) 123–132 (2016) CrossRef Yuan, X, et al., “Effect of Siloxane-Modified Polyacrylate on Water Uptake and Anticorrosion Mechanism of Silicone–Epoxy Coatings.” J. Coat. Technol. Res, 13 (1) 123–132 (2016) CrossRef
12.
go back to reference Bas, S, Soucek, MD, “Optimization and Comparison of Polysiloxane Acrylic Hybrid Latex Synthesis Methods.” J. Polym. Res., 19 (7) 9907 (2012) CrossRef Bas, S, Soucek, MD, “Optimization and Comparison of Polysiloxane Acrylic Hybrid Latex Synthesis Methods.” J. Polym. Res., 19 (7) 9907 (2012) CrossRef
13.
go back to reference Bas, S, Soucek, MD, “Comparison of Approaches to Prepare Polysiloxane-Functionalized Acrylic Latexes.” Silicon, 5 (2) 139–159 (2013) CrossRef Bas, S, Soucek, MD, “Comparison of Approaches to Prepare Polysiloxane-Functionalized Acrylic Latexes.” Silicon, 5 (2) 139–159 (2013) CrossRef
14.
go back to reference Zhang, YF, et al., “Synthesis of Ambient Temperature Self-crosslinking VTES-Based Core–Shell Polyacrylate Emulsion via Modified Micro-emulsion Polymerization Process.” Polym. Bull., 70 (5) 1631–1645 (2013) CrossRef Zhang, YF, et al., “Synthesis of Ambient Temperature Self-crosslinking VTES-Based Core–Shell Polyacrylate Emulsion via Modified Micro-emulsion Polymerization Process.” Polym. Bull., 70 (5) 1631–1645 (2013) CrossRef
15.
go back to reference Zhang, YF, et al., “Stable Acrylate/triethoxyvinylsilane (VTES) Core–Shell Emulsion with Low Surface Tension Made by Modified Micro-emulsion Polymerization: Effect of Different Mass Ratio of MMA/BA in the Core and Shell.” Colloids Surf. A Physicochem. Eng. Asp.,  436 549–556 (2013) CrossRef Zhang, YF, et al., “Stable Acrylate/triethoxyvinylsilane (VTES) Core–Shell Emulsion with Low Surface Tension Made by Modified Micro-emulsion Polymerization: Effect of Different Mass Ratio of MMA/BA in the Core and Shell.” Colloids Surf. A Physicochem. Eng. Asp.436 549–556 (2013) CrossRef
16.
go back to reference Zou, M, et al., “Preparation and Characterization of Core–Shell Polystyrene and Polymethylsilsesquioxane Structure Latex Particles by Seeded Polymerization.” Polym. Int., 55 (3) 305–311 (2006) CrossRef Zou, M, et al., “Preparation and Characterization of Core–Shell Polystyrene and Polymethylsilsesquioxane Structure Latex Particles by Seeded Polymerization.” Polym. Int., 55 (3) 305–311 (2006) CrossRef
17.
go back to reference Bourgeat-Lami, E, Tissot, I, Lefebvre, F, “Synthesis and Characterization of SiOH-Functionalized Polymer Latexes Using Methacryloxy Propyl Trimethoxysilane in Emulsion Polymerization.” Macromolecules, 35 (16) 6185–6191 (2002) CrossRef Bourgeat-Lami, E, Tissot, I, Lefebvre, F, “Synthesis and Characterization of SiOH-Functionalized Polymer Latexes Using Methacryloxy Propyl Trimethoxysilane in Emulsion Polymerization.” Macromolecules, 35 (16) 6185–6191 (2002) CrossRef
18.
go back to reference Huang, S, et al., “Alkoxysilane-Functionalized Acrylic Copolymer Latexes. I. Particle Size, Morphology, and Film-Forming Properties.” J. Appl. Polym. Sci., 94 (3) 954–960 (2004) CrossRef Huang, S, et al., “Alkoxysilane-Functionalized Acrylic Copolymer Latexes. I. Particle Size, Morphology, and Film-Forming Properties.” J. Appl. Polym. Sci., 94 (3) 954–960 (2004) CrossRef
19.
go back to reference Jiang, X, et al., “Styrene-Butyl Acrylate Copolymers Latexes Prepared with Different Functional Monomers and Their Application as Anti-icing Coatings.” J. Polym. Res., 21 (6) 473 (2014) CrossRef Jiang, X, et al., “Styrene-Butyl Acrylate Copolymers Latexes Prepared with Different Functional Monomers and Their Application as Anti-icing Coatings.” J. Polym. Res., 21 (6) 473 (2014) CrossRef
20.
go back to reference Huang, K, Liu, Y, Wu, D, “Synthesis and Characterization of Polyacrylate Modified by Polysiloxane Latexes and Films.” Prog. Org. Coat., 77 (11) 1774–1779 (2014) CrossRef Huang, K, Liu, Y, Wu, D, “Synthesis and Characterization of Polyacrylate Modified by Polysiloxane Latexes and Films.” Prog. Org. Coat., 77 (11) 1774–1779 (2014) CrossRef
21.
go back to reference Kozakiewicz, J, Ofat, I, Trzaskowska, J, “Silicone-Containing Aqueous Polymer Dispersions with Hybrid Particle Structure.” Adv. Colloid Interface Sci., 223 1–39 (2015) CrossRef Kozakiewicz, J, Ofat, I, Trzaskowska, J, “Silicone-Containing Aqueous Polymer Dispersions with Hybrid Particle Structure.” Adv. Colloid Interface Sci., 223 1–39 (2015) CrossRef
22.
go back to reference Liu, BL, et al., “Preparation of the Stable Core–Shell Latex Particles Containing Organic-Siloxane in the Shell.” Prog. Org. Coat., 61 (1) 21–27 (2008) CrossRef Liu, BL, et al., “Preparation of the Stable Core–Shell Latex Particles Containing Organic-Siloxane in the Shell.” Prog. Org. Coat., 61 (1) 21–27 (2008) CrossRef
23.
go back to reference Kozakiewicz, J, et al., “Silicone-Acrylic Hybrid Aqueous Dispersions of Core–Shell Particle Structure and Corresponding Silicone-Acrylic Nanopowders Designed for Modification of Powder Coatings and Plastics. Part I—Effect of Silicone Resin Composition on Properties of Dispersions and Corresponding Nanopowders.” Prog. Org. Coat., 77 (3) 568–578 (2014) CrossRef Kozakiewicz, J, et al., “Silicone-Acrylic Hybrid Aqueous Dispersions of Core–Shell Particle Structure and Corresponding Silicone-Acrylic Nanopowders Designed for Modification of Powder Coatings and Plastics. Part I—Effect of Silicone Resin Composition on Properties of Dispersions and Corresponding Nanopowders.” Prog. Org. Coat., 77 (3) 568–578 (2014) CrossRef
24.
go back to reference Kozakiewicz, J., et al., “Studies on Synthesis and Characterization of Aqueous Hybrid Silicone-Acrylic and Acrylic-Silicone Dispersions and Coatings. Part I.” Coatings, 9 (1) 25 (2019) Kozakiewicz, J., et al., “Studies on Synthesis and Characterization of Aqueous Hybrid Silicone-Acrylic and Acrylic-Silicone Dispersions and Coatings. Part I.” Coatings, 9 (1) 25 (2019)
25.
go back to reference Rios, L, et al., “Polystyrene (1)/Poly(butyl acrylate-methacrylic acid)(2) Core-Shell Emulsion Polymers. Part I. Synthesis and Colloidal Characterization.” Colloid Polym. Sci., 269 (8) 812–824 (1991) CrossRef Rios, L, et al., “Polystyrene (1)/Poly(butyl acrylate-methacrylic acid)(2) Core-Shell Emulsion Polymers. Part I. Synthesis and Colloidal Characterization.” Colloid Polym. Sci., 269 (8) 812–824 (1991) CrossRef
26.
go back to reference Ito, F, et al., “Study on Preparation of Irregular Shaped Particle in Seeded Emulsion Polymerization Accompanied with Regulated Electrostatic Coagulation by Counter-Ion Species.” Colloids Surf. A Physicochem. Eng. Asp., 216 (1–3) 109–122 (2003) CrossRef Ito, F, et al., “Study on Preparation of Irregular Shaped Particle in Seeded Emulsion Polymerization Accompanied with Regulated Electrostatic Coagulation by Counter-Ion Species.” Colloids Surf. A Physicochem. Eng. Asp., 216 (1–3) 109–122 (2003) CrossRef
27.
go back to reference Ambrosone, L, et al., “Size Polydispersity Determination in Emulsion Systems by Free Diffusion Measurements via PFG-NMR.” J. Phys. Chem. B, 108 (48) 18472–18478 (2004) CrossRef Ambrosone, L, et al., “Size Polydispersity Determination in Emulsion Systems by Free Diffusion Measurements via PFG-NMR.” J. Phys. Chem. B, 108 (48) 18472–18478 (2004) CrossRef
28.
go back to reference Lakshmi, RV, Bharathidasan, T, Basu, BJ, “Superhydrophobic Sol–Gel Nanocomposite Coatings with Enhanced Hardness.” Appl. Surf. Sci., 257 (24) 10421–10426 (2012) CrossRef Lakshmi, RV, Bharathidasan, T, Basu, BJ, “Superhydrophobic Sol–Gel Nanocomposite Coatings with Enhanced Hardness.” Appl. Surf. Sci., 257 (24) 10421–10426 (2012) CrossRef
29.
go back to reference Li, K, et al., “Fabrication and Characterization of Stable Superhydrophobic Fluorinated-Polyacrylate/Silica Hybrid Coating.” Appl. Surf. Sci., 298 214–220 (2014) CrossRef Li, K, et al., “Fabrication and Characterization of Stable Superhydrophobic Fluorinated-Polyacrylate/Silica Hybrid Coating.” Appl. Surf. Sci., 298 214–220 (2014) CrossRef
30.
go back to reference Han, YH, et al., “UV Curing of Organic–Inorganic Hybrid Coating Materials.” J. Sol Gel Sci. Technol., 43 (1) 111–123 (2007) CrossRef Han, YH, et al., “UV Curing of Organic–Inorganic Hybrid Coating Materials.” J. Sol Gel Sci. Technol., 43 (1) 111–123 (2007) CrossRef
31.
go back to reference Obey, TM, Vincent, B, “Novel Monodisperse “Silicone Oil”/Water Emulsions.” J. Colloid Interface Sci., 163 (2) 454–463 (1994) CrossRef Obey, TM, Vincent, B, “Novel Monodisperse “Silicone Oil”/Water Emulsions.” J. Colloid Interface Sci., 163 (2) 454–463 (1994) CrossRef
32.
go back to reference Nocun, M, Cholewa-Kowalska, K, Łączka, M, “Structure of Hybrids Based on TEOS-Cyclic Forms of Siloxane System.” J. Mol. Struct., 938 (1–3) 24–28 (2009) CrossRef Nocun, M, Cholewa-Kowalska, K, Łączka, M, “Structure of Hybrids Based on TEOS-Cyclic Forms of Siloxane System.” J. Mol. Struct., 938 (1–3) 24–28 (2009) CrossRef
33.
go back to reference Effati, E, Pourabbas, B, “One-Pot Synthesis of Sub-50 nm Vinyl-and Acrylate-Modified Silica Nanoparticles.” Powder Technol., 219 276–283 (2012) CrossRef Effati, E, Pourabbas, B, “One-Pot Synthesis of Sub-50 nm Vinyl-and Acrylate-Modified Silica Nanoparticles.” Powder Technol., 219 276–283 (2012) CrossRef
34.
go back to reference Huang, WH, Lin, CS, “Robust Superhydrophobic Transparent Coatings Fabricated by a Low-Temperature Sol–Gel Process.” Appl. Surf. Sci., 305 702–709 (2014) CrossRef Huang, WH, Lin, CS, “Robust Superhydrophobic Transparent Coatings Fabricated by a Low-Temperature Sol–Gel Process.” Appl. Surf. Sci., 305 702–709 (2014) CrossRef
Metadata
Title
Physical properties and morphology of siloxane–polyacrylate dispersion and coating films
Authors
W. Pramualkijja
N. Jiratumnukul
Publication date
03-06-2020
Publisher
Springer US
Published in
Journal of Coatings Technology and Research / Issue 5/2020
Print ISSN: 1547-0091
Electronic ISSN: 1935-3804
DOI
https://doi.org/10.1007/s11998-020-00346-z

Other articles of this Issue 5/2020

Journal of Coatings Technology and Research 5/2020 Go to the issue

Premium Partners