Structural and electrical properties of Bi_1/2Na_1/2TiO₃–BaTiO₃–Sr₃CuNb₂O₉ lead-free piezoelectric ceramics

The structure, microstructure, field-induced strain, ferroelectric, piezoelectric and dielectric properties of (1 − x) (Bi_0.5Na_0.5)_0.935Ba_0.065TiO₃–xSr₃CuNb₂O₉ (BNT-BT6.5–xSCN, with x = 0, 0.003, 0.006, 0.009) ceramics were investigated. X-ray diffraction patterns show that all samples are pure perovskite structure and Sr₃CuNb₂O₉ (SCN) effectively diffused into the 0.935Bi_0.5Na_0.5TiO₃–0.065BaTiO₃ (BNT–BT6.5) solid solution which also reflected in the Raman spectra and the energy disperse spectroscopy (EDS) analysis. With the increases of SCN content, the coercive field (E _c  = 18.41 kV/cm) decreases greatly, whereas the remnant polarization (P _r  = 29.11 μC/cm²) increases a little at x = 0.003 which is showed in the polarization hysteresis (P–E) loops, the result indicate that the ferroelectric order would be disrupted. Around critical composition (x = 0.003) at a driving field of 60 kV/cm, a large unipolar strain of 0.29 % with a normalized strain (d ₃₃ ^*  = 483 pm/V) is obtained at room temperature. The results indicate that BNT-BT6.5-xSCN ceramics with excellent properties are promising to replace lead-based piezoelectric ceramics and can be used in practical applications.