Synthesis and characterization of novel blue emitting Na₂CaSiO₄:Ce³⁺ phosphor

The blue phosphors Na_(2−x)Ca_(1−x)SiO₄:xCe³⁺ were synthesized by the sol–gel method and their luminescence characteristics were investigated for the first time. Structural information about prepared samples is obtained by analyzing the XRD patterns and SEM micrographs. The photoluminescence (PL) excitation spectra indicate that the Na_(2−x)Ca_(1−x)SiO₄:xCe³⁺ phosphors can be effectively excited by ultraviolet (360 nm) light. The PL emission spectra exhibit tunable blue broadband emission with the dominant wavelength of 427–447 nm under excitation of 360 nm by controlling the doping concentration of Ce³⁺. The concentration quenching effect for Ce³⁺ was found at the optimum doping concentration of 4 mol%. The Commission Internationale de l’Eclairage 1931 chromaticity coordinates of Na_1.96Ca_0.96SiO₄:0.04Ce³⁺ are (0.1447, 0.0787), which are better color purity compared to the commercial Eu²⁺-doped BaMgAl₁₀O₁₇ phosphor. Na_1.96Ca_0.96SiO₄:0.04Ce³⁺ composition shows intense blue emission (peak wavelength, 439 nm) with relative intensity versus commercial BaMgAl₁₀O₁₇:Eu²⁺ blue phosphor (Nichia) 65 and 158 % under 254 and 365 nm excitation, respectively. All the results indicate that Na_(2−x)Ca_(1−x)SiO₄:xCe³⁺ phosphors are potential candidate as a blue emitting phosphor for UV-converting white light-emitting diodes.