Published in: Journal of Materials Science: Materials in Electronics 24/2017

08-09-2017

Temperature dependent properties of spray deposited Cu2CoSnS4 (CCTS) thin films

Authors: P. S. Maldar, A. A. Mane, S. S. Nikam, S. D. Giri, A. Sarkar, A. V. Moholkar

Published in: Journal of Materials Science: Materials in Electronics | Issue 24/2017

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

A modified spray pyrolysis technique was employed for the deposition of Cu2CoSnS4 (CCTS) thin films. X-ray diffraction study showed that the CCTS thin films exhibit stannite structure with preferred orientation along (112) plane. The phase purity of sprayed CCTS films was confirmed from Raman analysis, as the most intense peak is observed at 320 cm−1 corresponding to A1 mode. With increase in substrate temperature the grains over the surface of the CCTS films become more distinct. The EDAX spectrum revealed the presence of different constituent elements such as, Cu, Co, Sn and S for the films deposited at 325 °C. The optical absorption study showed that the energy band gap values of the CCTS films are decreasing from 1.70 to 1.46 eV with respect to increase in substrate temperature from 275 to 325 °C.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literature
1.
go back to reference F. López-Vergara, A. Galdámez, V. Manríquez, G. González, Solid State Sci. 49, 54–60 (2015)CrossRef F. López-Vergara, A. Galdámez, V. Manríquez, G. González, Solid State Sci. 49, 54–60 (2015)CrossRef
2.
go back to reference Y. Xie, C. Zhang, G. Yang, J. Yang, X. Zhou, J. Ma, J. Alloys Compd. 696, 938–946 (2017)CrossRef Y. Xie, C. Zhang, G. Yang, J. Yang, X. Zhou, J. Ma, J. Alloys Compd. 696, 938–946 (2017)CrossRef
3.
go back to reference W. Schfifer, R. Nitsche, 9, 645–654 (1974) W. Schfifer, R. Nitsche, 9, 645–654 (1974)
4.
go back to reference A. Khare, B. Himmetoglu, M. Johnson, D.J. Norris, M. Cococcioni, E.S. Aydil, J. Appl. Phys. 111, 083707 (2012)CrossRef A. Khare, B. Himmetoglu, M. Johnson, D.J. Norris, M. Cococcioni, E.S. Aydil, J. Appl. Phys. 111, 083707 (2012)CrossRef
5.
go back to reference C. An, K. Tang, G. Shen, C. Wang, L. Huang, Y. Qian, Mater. Res. Bull. 38, 823–830 (2003)CrossRef C. An, K. Tang, G. Shen, C. Wang, L. Huang, Y. Qian, Mater. Res. Bull. 38, 823–830 (2003)CrossRef
6.
7.
go back to reference K. Mokurala, S. Mallick, P. Bhargava, J. Power Sources 305, 134–143 (2016)CrossRef K. Mokurala, S. Mallick, P. Bhargava, J. Power Sources 305, 134–143 (2016)CrossRef
8.
go back to reference J.Y. Chane-Ching, a Gillorin, O. Zaberca, A. Balocchi, X. Marie, Chem. Commun 47, 5229–5231 (2011)CrossRef J.Y. Chane-Ching, a Gillorin, O. Zaberca, A. Balocchi, X. Marie, Chem. Commun 47, 5229–5231 (2011)CrossRef
9.
go back to reference B. Murali, M. Madhuri, S.B. Krupanidhi, Cryst. Growth Des 14, 3685–3691 (2014)CrossRef B. Murali, M. Madhuri, S.B. Krupanidhi, Cryst. Growth Des 14, 3685–3691 (2014)CrossRef
10.
go back to reference A. Gupta, K. Mokurala, A. Kamble, S. Shankar, S. Mallick, P. Bhargava, AIP Conf. Proc. 1665, 140022 (2015)CrossRef A. Gupta, K. Mokurala, A. Kamble, S. Shankar, S. Mallick, P. Bhargava, AIP Conf. Proc. 1665, 140022 (2015)CrossRef
11.
go back to reference F. López-Vergara, A. Galdámez, V. Manríquez, P. Barahona, O. Peña, J. Solid State Chem. 198, 386–391 (2013)CrossRef F. López-Vergara, A. Galdámez, V. Manríquez, P. Barahona, O. Peña, J. Solid State Chem. 198, 386–391 (2013)CrossRef
13.
go back to reference F. Ozel, A. Yar, E. Aslan, E. Arkan, A. Aljabour, M. Can, I.H. Patir, M. Kus, M. Ersoz, ChemNanoMat 1 477–481 (2015)CrossRef F. Ozel, A. Yar, E. Aslan, E. Arkan, A. Aljabour, M. Can, I.H. Patir, M. Kus, M. Ersoz, ChemNanoMat 1 477–481 (2015)CrossRef
14.
15.
go back to reference M. Benchikri, O. Zaberca, R. El Ouatib, B. Durand, F. Oftinger, A. Balocchi, J.Y. Chane-Ching, Mater. Lett. 68, 340–343 (2012)CrossRef M. Benchikri, O. Zaberca, R. El Ouatib, B. Durand, F. Oftinger, A. Balocchi, J.Y. Chane-Ching, Mater. Lett. 68, 340–343 (2012)CrossRef
16.
go back to reference O. Zaberca, A. Gillorin, B. Durand, J.Y. Chane-Ching, J. Mater. Chem. 21, 6483 (2011)CrossRef O. Zaberca, A. Gillorin, B. Durand, J.Y. Chane-Ching, J. Mater. Chem. 21, 6483 (2011)CrossRef
17.
go back to reference L.D. Gulay, O.P. Nazarchuk, I.D. Olekseyuk, J. Alloys Compd. 377, 306–311 (2004)CrossRef L.D. Gulay, O.P. Nazarchuk, I.D. Olekseyuk, J. Alloys Compd. 377, 306–311 (2004)CrossRef
18.
go back to reference M. Quintero, E. Moreno, S. Alvarez, J. Marquina, C. Rincón, E. Quintero, P. Grima, J. Heano, M.A. Macías, Rev. Lat. Met. Mater. 4, 28–38 (2014) M. Quintero, E. Moreno, S. Alvarez, J. Marquina, C. Rincón, E. Quintero, P. Grima, J. Heano, M.A. Macías, Rev. Lat. Met. Mater. 4, 28–38 (2014)
19.
go back to reference S.P. Desai, M.P. Suryawanshi, S.M. Bhosale, J.H. Kim, A.V. Moholkar, Ceram. Int. 41, 4867–4873 (2015)CrossRef S.P. Desai, M.P. Suryawanshi, S.M. Bhosale, J.H. Kim, A.V. Moholkar, Ceram. Int. 41, 4867–4873 (2015)CrossRef
20.
go back to reference G. Ghosh, A. Biswas, A. Thangavel, R., and Udayabhanu, RSC Adv 6, 96025–96034 (2016)CrossRef G. Ghosh, A. Biswas, A. Thangavel, R., and Udayabhanu, RSC Adv 6, 96025–96034 (2016)CrossRef
21.
go back to reference R.D. Angelo, C.L. Azanza Ricardo, A. Mittiga, P. Scardi, M. Leoni, J. Sol–Gel Sci. Technol 72, 490–495 (2014)CrossRef R.D. Angelo, C.L. Azanza Ricardo, A. Mittiga, P. Scardi, M. Leoni, J. Sol–Gel Sci. Technol 72, 490–495 (2014)CrossRef
22.
go back to reference T.K. Chaudhuri, D. Tiwari, Sol. Energy Mater. Sol. Cells 101, 46–50 (2012)CrossRef T.K. Chaudhuri, D. Tiwari, Sol. Energy Mater. Sol. Cells 101, 46–50 (2012)CrossRef
23.
go back to reference G. Rajesh, N. Muthukumarasamy, E.P. Subramaniam, S. Agilan, D. Velauthapillai, J. Sol–Gel Sci. Technol. 66, 288–292 (2013)CrossRef G. Rajesh, N. Muthukumarasamy, E.P. Subramaniam, S. Agilan, D. Velauthapillai, J. Sol–Gel Sci. Technol. 66, 288–292 (2013)CrossRef
24.
go back to reference S. Dias, B. Murali, S.B. Krupanidhi, Mater. Chem. Phys. 167, 309–314 (2015)CrossRef S. Dias, B. Murali, S.B. Krupanidhi, Mater. Chem. Phys. 167, 309–314 (2015)CrossRef
25.
go back to reference Z. Seboui, A. Gassoumi, N. Kamoun-turki, Mater. Sci. Semicond. Process. 26, 360–366 (2014)CrossRef Z. Seboui, A. Gassoumi, N. Kamoun-turki, Mater. Sci. Semicond. Process. 26, 360–366 (2014)CrossRef
26.
go back to reference S. Ikeda, M. Nonogaki, W. Septina, G. Gunawan, T. Harada, M. Matsumura, Catal. Sci. Technol. 3, 1849–1854 (2013)CrossRef S. Ikeda, M. Nonogaki, W. Septina, G. Gunawan, T. Harada, M. Matsumura, Catal. Sci. Technol. 3, 1849–1854 (2013)CrossRef
28.
go back to reference A.A. Mane, M.P. Suryawanshi, J.H. Kim, A.V. Moholkar, J. Colloid Interface Sci. 483, 220–231 (2016)CrossRef A.A. Mane, M.P. Suryawanshi, J.H. Kim, A.V. Moholkar, J. Colloid Interface Sci. 483, 220–231 (2016)CrossRef
29.
31.
go back to reference G. Nichols, S. Byard, M.J. Bloxham, J. Botterill, N.J. Dawson, A. Dennis, V. Diart, N.C. North, J.D. Sherwood, J. Pharm. Sci. 91, 2103–2109 (2002)CrossRef G. Nichols, S. Byard, M.J. Bloxham, J. Botterill, N.J. Dawson, A. Dennis, V. Diart, N.C. North, J.D. Sherwood, J. Pharm. Sci. 91, 2103–2109 (2002)CrossRef
33.
go back to reference P.E. Agbo, Adv. Appl. Sci. Res. 3, 599–604 (2012) P.E. Agbo, Adv. Appl. Sci. Res. 3, 599–604 (2012)
34.
35.
go back to reference A. Ghosh, D.K. Chaudhary, A. Biswas, T. Rajalingam, G. Udayabhanu, RSC Adv. 6 115204–115212 (2016)CrossRef A. Ghosh, D.K. Chaudhary, A. Biswas, T. Rajalingam, G. Udayabhanu, RSC Adv. 6 115204–115212 (2016)CrossRef
Metadata
Title
Temperature dependent properties of spray deposited Cu2CoSnS4 (CCTS) thin films
Authors
P. S. Maldar
A. A. Mane
S. S. Nikam
S. D. Giri
A. Sarkar
A. V. Moholkar
Publication date
08-09-2017
Publisher
Springer US
Published in
Journal of Materials Science: Materials in Electronics / Issue 24/2017
Print ISSN: 0957-4522
Electronic ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-017-7842-1

Other articles of this Issue 24/2017

Journal of Materials Science: Materials in Electronics 24/2017 Go to the issue