Vacuum Hot Rolling Preparation of a Stainless Steel Clad Plate and Its Numerical Simulation

Authors: H. R. Jin, R. Wei, Y. H. Wang, Y. L. Yi, C. Z. Jia, D. X. Zhao

Published in: Strength of Materials | Issue 1/2022

Login to get access
share
SHARE

Abstract

Vacuum hot rolling was used to prepare stainless steel clad plate samples. As a key process parameter, force analysis of the compound deformation process was conducted for the stainless steel clad plate samples. The hot rolling deformation area was subdivided into intervals I, II and III, and the force equilibrium equations of each interval were established with the slab method. A mathematical model for the calculation of rolling force was derived. 2205/NI/EH40 clad plate samples were prepared according to the technical parameter of vacuum hot rolling, which was calculated with the modeling system. Based on the mathematical model, the effects of rolling speed, friction coefficient, composite ratio, base thickness, and other rolling parameters on rolling force were simulated. The results show that: as the rolling speed, external friction and the thickness of the cladding increased, rolling force increased. However, the rolling force decreases with the increase of base thickness. By comparing and analyzing the results of the rolling experiment and rolling simulation, it could be found that the errors between the two was within 5.5%, which verified the validity of the finite element model.
Literature
1.
go back to reference H. Li, L. Y. Zhang, B. Y. Zhang, et al., “Microstructure characterization and mechanical properties of stainless steel clad plate,” Materials, 12, No.3, 509-516(2019). CrossRef H. Li, L. Y. Zhang, B. Y. Zhang, et al., “Microstructure characterization and mechanical properties of stainless steel clad plate,” Materials, 12, No.3, 509-516(2019). CrossRef
2.
go back to reference J. Jiang, H. Ding, Z. A. Luo, G. M. Xie, “Interfacial microstructure and mechanical properties of stainless steel clad plate prepared by vacuum hot rolling,” J. Iron Steel Res. Int., 25, No.7, 732–738(2018). CrossRef J. Jiang, H. Ding, Z. A. Luo, G. M. Xie, “Interfacial microstructure and mechanical properties of stainless steel clad plate prepared by vacuum hot rolling,” J. Iron Steel Res. Int., 25, No.7, 732–738(2018). CrossRef
3.
go back to reference L. Li, F. X. Yin, K. Nagai, “Progress of laminated materials and clad steels production.” Mater. Sci. Forum. No.1206, 675-677(2011). L. Li, F. X. Yin, K. Nagai, “Progress of laminated materials and clad steels production.” Mater. Sci. Forum. No.1206, 675-677(2011).
4.
go back to reference J. F. Shu, Y. Tomiko, Y.Y. Hara, “Influence of a Ni foil interlayer on interface properties of Mg-clad Al materials by vacuum roll bonding.” Mater. Trans., 61, No.5, 1020-1025(2020). CrossRef J. F. Shu, Y. Tomiko, Y.Y. Hara, “Influence of a Ni foil interlayer on interface properties of Mg-clad Al materials by vacuum roll bonding.” Mater. Trans., 61, No.5, 1020-1025(2020). CrossRef
5.
go back to reference G.M. Xie, Z.G. Luo, G.L. Wang, et al., “Interface characteristic and properties of stainless steel/HSLA steel clad plate by vacuum rolling cladding.” Mater. Trans., 52, No.8, 1709-1712(2011). CrossRef G.M. Xie, Z.G. Luo, G.L. Wang, et al., “Interface characteristic and properties of stainless steel/HSLA steel clad plate by vacuum rolling cladding.” Mater. Trans., 52, No.8, 1709-1712(2011). CrossRef
6.
go back to reference S. Ehsan, D. Kamran, “Effects of deformation conditions on the rolling force during variable gauge rolling.” J. Mater. Process. Manu., 2, No.3, 48-59(2018). S. Ehsan, D. Kamran, “Effects of deformation conditions on the rolling force during variable gauge rolling.” J. Mater. Process. Manu., 2, No.3, 48-59(2018).
7.
go back to reference W.T. Jia, L.F. Ma, Y. Tang, et al., “Prediction for magnesium alloy rolling force based on quantitative study of contact friction.” Rare Metal. Mat. Eng., 46, No.10, 2763-2769(2017). CrossRef W.T. Jia, L.F. Ma, Y. Tang, et al., “Prediction for magnesium alloy rolling force based on quantitative study of contact friction.” Rare Metal. Mat. Eng., 46, No.10, 2763-2769(2017). CrossRef
8.
go back to reference A. Parvizi, F. Afrouz, “Slab analysis of asymmetrical clad sheet bonded before rolling process.” Int. J. Adv. Manuf. Tech. 87, 137-150(2016). CrossRef A. Parvizi, F. Afrouz, “Slab analysis of asymmetrical clad sheet bonded before rolling process.” Int. J. Adv. Manuf. Tech. 87, 137-150(2016). CrossRef
9.
go back to reference H. Y. Wang, X. Li, Sun, J. et al. “Analysis of sandwich rolling with two different thicknesses outer layers based on slab method,” Int. J. Mech. Sci., 106, 194-208(2016). CrossRef H. Y. Wang, X. Li, Sun, J. et al. “Analysis of sandwich rolling with two different thicknesses outer layers based on slab method,” Int. J. Mech. Sci., 106, 194-208(2016). CrossRef
10.
go back to reference M. Qwamizadeh, M. Kadkhodaei, M. Salimi, “Asymmetrical rolling analysis of bonded two-layer sheets and evaluation of outgoing curvature,” Int. J. Adv. Manuf. Tech., 73, 521–533(2014). CrossRef M. Qwamizadeh, M. Kadkhodaei, M. Salimi, “Asymmetrical rolling analysis of bonded two-layer sheets and evaluation of outgoing curvature,” Int. J. Adv. Manuf. Tech., 73, 521–533(2014). CrossRef
11.
go back to reference C.H. Jeon, S.W. Han, B.D. Joo, et al., “Deformation analysis for cold rolling of Al-Cu double layered sheet by physical modeling and finite element method,” Met. Mater. Int., 19, 1069-1076(2013). CrossRef C.H. Jeon, S.W. Han, B.D. Joo, et al., “Deformation analysis for cold rolling of Al-Cu double layered sheet by physical modeling and finite element method,” Met. Mater. Int., 19, 1069-1076(2013). CrossRef
12.
go back to reference C.H. Moon, Y. Lee, “The effects of rolling method changes on productivity in thick plate rolling process,” J. Mater. Process. Tech., 210, 1844-1851(2010). CrossRef C.H. Moon, Y. Lee, “The effects of rolling method changes on productivity in thick plate rolling process,” J. Mater. Process. Tech., 210, 1844-1851(2010). CrossRef
13.
go back to reference B. Zeng, J. Wu, H. H. Zhang, “Numerical simulation of multi-pass rolling force and temperature field of plate steel during hot rolling,” Journal of Shanghai Jiaotong University (Science), 16, No.2, 141-144(2011). B. Zeng, J. Wu, H. H. Zhang, “Numerical simulation of multi-pass rolling force and temperature field of plate steel during hot rolling,” Journal of Shanghai Jiaotong University (Science), 16, No.2, 141-144(2011).
14.
go back to reference N. A. Razani, B. Mollaei Dariani, M. Soltanpour, “Analytical approach of asymmetrical thermomechanical rolling by slab method.” Int. J. Adv. Manuf. Technol., 21, 64-78(2017). N. A. Razani, B. Mollaei Dariani, M. Soltanpour, “Analytical approach of asymmetrical thermomechanical rolling by slab method.” Int. J. Adv. Manuf. Technol., 21, 64-78(2017).
15.
go back to reference A. Macwan, X.Q. Jiang, C. Li, et al. “Effect of annealing on interface microstructures and tensile properties of rolled Al/Mg/Al tri-layer clad sheets,” Mater. Sci. Eng. A, 587, 344-352(2013). CrossRef A. Macwan, X.Q. Jiang, C. Li, et al. “Effect of annealing on interface microstructures and tensile properties of rolled Al/Mg/Al tri-layer clad sheets,” Mater. Sci. Eng. A, 587, 344-352(2013). CrossRef
Metadata
Title
Vacuum Hot Rolling Preparation of a Stainless Steel Clad Plate and Its Numerical Simulation
Authors
H. R. Jin
R. Wei
Y. H. Wang
Y. L. Yi
C. Z. Jia
D. X. Zhao
Publication date
07-05-2022
Publisher
Springer US
Published in
Strength of Materials / Issue 1/2022
Print ISSN: 0039-2316
Electronic ISSN: 1573-9325
DOI
https://doi.org/10.1007/s11223-022-00388-1

Other articles of this Issue 1/2022

Strength of Materials 1/2022 Go to the issue

Premium Partners