Enhanced ferroelectric relaxor behavior of Ho2O3-modified barium zirconate titanate ceramics

verfasst von: Chen Zhang, Fangxu Chen, Xin Zhong, Zhixin Ling, Zhuming Tang, Gang Jian

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 19/2018

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Ho2O3 doped Ba(Zr0.1Ti0.9)O3 ceramics were prepared by conventional solid state reaction route and their microstructure, dielectric properties and ferroelectric properties were investigated with the variation of Ho2O3 content using X-ray diffraction, scanning electron microscope, LCR measuring system and ferroelectric tester. It is found that the Ho3+ ions initially substitute the B-site host ions maintaining the perovskite structure in Ba(Zr0.1Ti0.9)O3 ceramics and then contribute to the formation of secondary phase with the continuous increase of Ho2O3 content. The average grain size decreases significantly as the Ho2O3 concentration increases. The ferroelectric-paraelectric phase transition temperature Tm of Ba(Zr0.1Ti0.9)O3 ceramics decreases with increasing Ho2O3 content. Based on the increase of critical exponent γ from the modified Curie–Weiss equation as well as the increase of deviation from Curie–Weiss law, the diffuse phase transition behavior is enhanced with increasing Ho2O3 content, indicating a composition-induced diffuse transition. A normal ferroelectric behavior with diffuse phase transition is obtained for the undoped Ba(Zr0.1Ti0.9)O3 ceramics. However, the relaxor-like ferroelectric behavior with a strong frequency dispersion of relative permittivity maximum εrmax at T < Tm and a strong diffuse phase transition is found for Ba(Zr0.1Ti0.9)O3 ceramics with high Ho2O3 content. The high Ho2O3 content ceramics obey the empirical Vogel–Fulcher relation, which confirms the relaxor behavior of Ba(Zr0.1Ti0.9)O3 ceramics with high Ho2O3 content. The remnant polarization increases and then decreases with the increasing Ho2O3 content while the coercive field decreases with the increase of Ho2O3 content in Ba(Zr0.1Ti0.9)O3 ceramics.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat G.N. Bhargavi, A. Khare, T. Badapanda, P.K. Ray, N. Brahme, Ceram. Int. 44, 1817 (2018)CrossRef G.N. Bhargavi, A. Khare, T. Badapanda, P.K. Ray, N. Brahme, Ceram. Int. 44, 1817 (2018)CrossRef
2.
Zurück zum Zitat C. Zhang, F. Chen, Z. Ling, G. Jian, Y. Li, Mater. Sci. Pol. 35, 806 (2018)CrossRef C. Zhang, F. Chen, Z. Ling, G. Jian, Y. Li, Mater. Sci. Pol. 35, 806 (2018)CrossRef
3.
Zurück zum Zitat X. Chou, J. Zhai, H. Jiang, X. Yao, J. Appl. Phys. 102, 084106 (2007)CrossRef X. Chou, J. Zhai, H. Jiang, X. Yao, J. Appl. Phys. 102, 084106 (2007)CrossRef
4.
Zurück zum Zitat S.J. Kuang, X.G. Tang, L.Y. Li, Y.P. Jiang, Q.X. Liu, Scr. Mater. 61, 68 (2009)CrossRef S.J. Kuang, X.G. Tang, L.Y. Li, Y.P. Jiang, Q.X. Liu, Scr. Mater. 61, 68 (2009)CrossRef
5.
Zurück zum Zitat U. Weber, G. Greuel, U. Boettger, S. Weber, D. Hennings, R. Waser, J. Am. Ceram. Soc. 84, 759 (2001)CrossRef U. Weber, G. Greuel, U. Boettger, S. Weber, D. Hennings, R. Waser, J. Am. Ceram. Soc. 84, 759 (2001)CrossRef
6.
7.
11.
Zurück zum Zitat T. Badapanda, S.K. Rout, L.S. Cavalcante, J.C. Sczancoski, S. Panigrahi, T.P. Sinha, E. Longo, Mater. Chem. Phys. 121, 147 (2010)CrossRef T. Badapanda, S.K. Rout, L.S. Cavalcante, J.C. Sczancoski, S. Panigrahi, T.P. Sinha, E. Longo, Mater. Chem. Phys. 121, 147 (2010)CrossRef
12.
Zurück zum Zitat X. Diez-Betriu, J.E. Garcia, C. Ostos, A.U. Boya, D.A. Ochoa, L. Mestres, R. Perez, Mater. Chem. Phys. 125, 493 (2011)CrossRef X. Diez-Betriu, J.E. Garcia, C. Ostos, A.U. Boya, D.A. Ochoa, L. Mestres, R. Perez, Mater. Chem. Phys. 125, 493 (2011)CrossRef
13.
Zurück zum Zitat K.J. Park, C.H. Kim, Y.J. Yoon, S.M. Song, Y.T. Kim, K.H. Hur, J. Eur. Ceram. Soc. 29, 1735 (2009)CrossRef K.J. Park, C.H. Kim, Y.J. Yoon, S.M. Song, Y.T. Kim, K.H. Hur, J. Eur. Ceram. Soc. 29, 1735 (2009)CrossRef
14.
15.
Zurück zum Zitat C. Ciomaga, M. Viviani, M.T. Buscaglia, V. Buscaglia, L. Mitoseriu, A. Stancu, P. Nanni, J. Eur. Ceram. Soc. 27, 4061 (2007)CrossRef C. Ciomaga, M. Viviani, M.T. Buscaglia, V. Buscaglia, L. Mitoseriu, A. Stancu, P. Nanni, J. Eur. Ceram. Soc. 27, 4061 (2007)CrossRef
16.
Zurück zum Zitat C. Zhang, Z. Ling, F. Chen, G. Jian, Y. Li, J. Mater. Sci.: Mater. Electron. 29, 331 (2018) C. Zhang, Z. Ling, F. Chen, G. Jian, Y. Li, J. Mater. Sci.: Mater. Electron. 29, 331 (2018)
17.
18.
Zurück zum Zitat C. Zhang, F. Chen, Z. Ling, X. Zhong, G. Jian, Y. Li, J. Mater. Sci.: Mater. Electron. 29, 9397 (2018) C. Zhang, F. Chen, Z. Ling, X. Zhong, G. Jian, Y. Li, J. Mater. Sci.: Mater. Electron. 29, 9397 (2018)
19.
Zurück zum Zitat X.P. Jiang, M. Zeng, H.L.W. Chan, C.L. Choy, Mater. Sci. Eng. A 438–440, 198 (2006)CrossRef X.P. Jiang, M. Zeng, H.L.W. Chan, C.L. Choy, Mater. Sci. Eng. A 438–440, 198 (2006)CrossRef
20.
Zurück zum Zitat K.M. Sangwan, N. Ahlawat, R.S. Kundu, S. Rani, S. Rani, N. Ahlawat, S. Murugavel, J. Phys. Chem. Solids 117, 158 (2018)CrossRef K.M. Sangwan, N. Ahlawat, R.S. Kundu, S. Rani, S. Rani, N. Ahlawat, S. Murugavel, J. Phys. Chem. Solids 117, 158 (2018)CrossRef
21.
22.
Zurück zum Zitat J. Chen, C. Fu, W. Cai, G. Chen, S. Ran, J. Alloys Compd. 544, 82 (2012)CrossRef J. Chen, C. Fu, W. Cai, G. Chen, S. Ran, J. Alloys Compd. 544, 82 (2012)CrossRef
23.
Zurück zum Zitat H. Sun, Y. Zhang, X. Liu, Y. Liu, W. Chen, Ceram. Int. 41, 555 (2015)CrossRef H. Sun, Y. Zhang, X. Liu, Y. Liu, W. Chen, Ceram. Int. 41, 555 (2015)CrossRef
24.
Zurück zum Zitat J.W. Zhai, X. Yao, J. Shen, L.Y. Zhang, H. Chen, J. Phys. D 37, 748 (2004)CrossRef J.W. Zhai, X. Yao, J. Shen, L.Y. Zhang, H. Chen, J. Phys. D 37, 748 (2004)CrossRef
25.
Zurück zum Zitat C. Zhang, Z. Ling, G. Jian, J. Mater. Sci.: Mater. Electron. 27, 11770 (2016) C. Zhang, Z. Ling, G. Jian, J. Mater. Sci.: Mater. Electron. 27, 11770 (2016)
Metadaten
Titel
Enhanced ferroelectric relaxor behavior of Ho2O3-modified barium zirconate titanate ceramics
verfasst von
Chen Zhang
Fangxu Chen
Xin Zhong
Zhixin Ling
Zhuming Tang
Gang Jian
Publikationsdatum
30.07.2018
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 19/2018
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-018-9766-9

Weitere Artikel der Ausgabe 19/2018

Journal of Materials Science: Materials in Electronics 19/2018 Zur Ausgabe

Neuer Inhalt