Erosive Wear of Alumina Coated Polyimide Composite

verfasst von : V. I. Bedina, A. A. Skiba, M. V. Limarenko

Erschienen in: Innovations and Technologies in Construction

Verlag: Springer International Publishing

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

A layer of aluminum oxide on the surface of a highly filled polymer composite based on polyimide and tungsten oxide was obtained by the method of detonation spraying. The thickness of the resulting coating is from 80 to 120 μm. The X-ray diffraction pattern of the coating showed the presence of only one modification of aluminum oxide—α-Al₂O₃. The erosion resistance of coated and uncoated polymer composite specimens at 25 °C was studied in accordance with ASTM G76-02. The test time for all samples was 1 h, the abrasive material consumption was 2.2 g/min, and corundum powder (Al₂O₃) with an average fraction of 50 μm was used as the abrasive material. The air pressure was 0.35 bar. The impact of the abrasive material jet was carried out at angles of 30, 60, and 90°. It has been established that the erosion wear of specimens with a ceramic coating of α-Al₂O₃ is almost an order of magnitude lower than that of specimens without a coating.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 340 Zeitschriften

aus folgenden Fachgebieten:

Bauwesen + Immobilien
Business IT + Informatik
Finance + Banking
Management + Führung
Marketing + Vertrieb
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Heat-Shielding Properties of Concrete Structures Reinforced with Composite Reinforcement

Nächstes Kapitel Biological and Climatic Resistance of Cement Composites Based on Biocidal Binders

Vilkov, F.E., Lozovan, A.A., Bazhanov, A.V., Kasitsyn, A.N., Schekoturova, O.E., Solovev, M.K.: Investigation of the radiation-protective properties of a highly filled liquid glass material. J. Surf. Investig. 11, 912–916 (2017). https://doi.org/10.1134/S1027451017050160CrossRef

Cherkashina, N.I., Pavlenko, V.I., Ivanitskiy, D.A.: Investigation of the mechanisms of synthesis and modification of nanocrystalline fillers of polymeric matrices. Bull. BSTU named after V. G. Shukhov 1, 185–190 (2016). https://doi.org/10.12737/22101

Keating, A., Goncalves, P., Pimenta, M., Brogueira, P., Zadeh, A., Daly, E.: Modeling the effects of low-LET cosmic rays on electronic components. Radiat. Environ. Biophys. 51, 245–254 (2012). https://doi.org/10.1007/S00411-012-0412-2CrossRef

Cherkashina, N.I., Pavlenko, V.I., Noskov, A.V.: Radiation shielding properties of polyimide composite materials. Radiat. Phys. Chem. 159, 111–117 (2019). https://doi.org/10.1016/J.RADPHYSCHEM.2019.02.041CrossRef

Ortner, H.M., Stadermann, F.J.: Degradation of space exposed surfaces by hypervelocity dust bombardment, and refractory materials for space. Int. J. Refract. Met. Hard Mater. 27, 949–956 (2009). https://doi.org/10.1016/J.IJRMHM.2009.05.009CrossRef

Pavlenko, V.I., Cherkashina, N.I., Noskov, A.V.: Calculation of proton passage through a highly filled polyimide composite. J. Surf. Investig. 15, 147–151 (2021). https://doi.org/10.1134/S1027451020060129CrossRef

Fang, X., Yang, Z., Zhang, S., Gao, L., Ding, M.: Synthesis and properties of polyimides derived from cis- and trans-1,2,3,4-cyclohexanetetracarboxylic dianhydrides. Polymer (Guildf) 45, 2539–2549 (2004). https://doi.org/10.1016/J.POLYMER.2004.02.008CrossRef

Cherkashina, N.I., Pavlenko, V.I., Noskov, A.V., Sirota, V.V., Zaitsev, S.V., Prokhorenkov, D.S., Sidelnikov, R.V.: Gamma radiation attenuation characteristics of polyimide composite with WO2. Prog. Nucl. Energy 137, 103795 (2021). https://doi.org/10.1016/J.PNUCENE.2021.103795CrossRef

Cherkashina, N.I., Pavlenko, V.I., Noskov, A.V.: Synthesis and property evaluations of highly filled polyimide composites under thermal cycling conditions from −190 °C to +200 °C. Cryogenics (Guildf) 104, 102995 (2019). https://doi.org/10.1016/J.CRYOGENICS.2019.102995

10.

Sirota, V.V., Zaitsev, S.V., Prokhorenkov, D.S., Limarenko, M.V., Skiba, A.A., Kovaleva, M.G.: Detonation spraying of composite targets based on Ni, Cr and B4C for magnetron multi-functional coating (2022). https://doi.org/10.4028/p-74w31h

11.

Kolisnichenko, O.V., Tyurin, Y.N., Tovbin, R.: Efficiency of process of coating spraying using multichamber detonation unit. Autom. Weld. 2017, 28–34 (2017). https://doi.org/10.15407/AS2017.10.03

12.

Kovaleva, M., Goncharov, I., Novikov, V., Yapryntsev, M., Vagina, O., Pavlenko, I., Sirota, V., Tyurin, Y., Kolisnichenko, O.: Effect of heat treatment on the microstructure and phase composition of ZrB2-MoSi2 coating. Coatings 9 (2019). https://doi.org/10.3390/COATINGS9120779

Titel: Erosive Wear of Alumina Coated Polyimide Composite
verfasst von: V. I. Bedina
A. A. Skiba
M. V. Limarenko
Verlag: Springer International Publishing
Buch: Innovations and Technologies in Construction
Print ISBN: 978-3-031-20458-6

Electronic ISBN: 978-3-031-20459-3

Copyright-Jahr: 2023
DOI: https://doi.org/10.1007/978-3-031-20459-3_21

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Springer Professional "Wirtschaft"