Eutectic Formation During Solidification of Ni-Based Single-Crystal Superalloys with Additional Carbon

verfasst von: Fu Wang, Dexin Ma, Andreas Bührig-Polaczek

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 11/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

γ/γ′ eutectics’ nucleation behavior during the solidification of a single-crystal superalloy with additional carbon was investigated by using directional solidification quenching method. The results show that the nucleation of the γ/γ′ eutectics can directly occur on the existing γ dendrites, directly in the remaining liquid, or on the primary MC-type carbides. The γ/γ′ eutectics formed through the latter two mechanisms have different crystal orientations than that of the γ matrix. This suggests that the conventional Ni-based single-crystal superalloy castings with additional carbon only guarantee the monocrystallinity of the γ matrix and some γ/γ′ eutectics and, in addition to the carbides, there are other misoriented polycrystalline microstructures existing in macroscopically considered “single-crystal” superalloy castings.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat L. Liu, T. Jin, N. Zhao, X. Sun, H. Guan, and Z. Hu: Mater. Sci. Eng. A, 2003, vol. 361, pp. 191-7.CrossRef L. Liu, T. Jin, N. Zhao, X. Sun, H. Guan, and Z. Hu: Mater. Sci. Eng. A, 2003, vol. 361, pp. 191-7.CrossRef
2.
Zurück zum Zitat Y. Xu, Q. Jin, X. Xiao, X. Cao, G. Jia, Y. Zhu, and H. Yin: Mater. Sci. Eng. A, 2011, vol. 528, pp. 4600-7.CrossRef Y. Xu, Q. Jin, X. Xiao, X. Cao, G. Jia, Y. Zhu, and H. Yin: Mater. Sci. Eng. A, 2011, vol. 528, pp. 4600-7.CrossRef
3.
Zurück zum Zitat D. Duhl: Superalloys, supercomposites and superceramics, p. 164, Academic Press, New York, 1989. D. Duhl: Superalloys, supercomposites and superceramics, p. 164, Academic Press, New York, 1989.
4.
Zurück zum Zitat M Gell, D Duhl, and A Giamei: in Superalloys 1980, J Tien, S Wlodek, H Morrow, M Gell, and G Mauer, eds., AMS, Metals Park, OH, 1980, pp. 205-214. M Gell, D Duhl, and A Giamei: in Superalloys 1980, J Tien, S Wlodek, H Morrow, M Gell, and G Mauer, eds., AMS, Metals Park, OH, 1980, pp. 205-214.
5.
Zurück zum Zitat S. Tin and T. Pollock: Mater. Sci. Eng. A, 2003, vol. 348, pp. 111-21.CrossRef S. Tin and T. Pollock: Mater. Sci. Eng. A, 2003, vol. 348, pp. 111-21.CrossRef
6.
Zurück zum Zitat S Tin, T Pollock, and W King: in Superalloys 2000, T Pollock, R Kissinger, R Bowman, K Green, M McLean, S Olson, and J Scbirra, eds., TMS, Warrendale, PA, 2000, pp. 201-210. S Tin, T Pollock, and W King: in Superalloys 2000, T Pollock, R Kissinger, R Bowman, K Green, M McLean, S Olson, and J Scbirra, eds., TMS, Warrendale, PA, 2000, pp. 201-210.
7.
Zurück zum Zitat S. Tin, T. Pollock, and W. Murphy: Metall. Mater. Trans. A, 2001, vol. 32, pp. 1743-53.CrossRef S. Tin, T. Pollock, and W. Murphy: Metall. Mater. Trans. A, 2001, vol. 32, pp. 1743-53.CrossRef
8.
Zurück zum Zitat J. Minalisin, J. Corrigan, G. Gratti, and R. Vogt: U.S. Patent 20020007877 A1, 2002. J. Minalisin, J. Corrigan, G. Gratti, and R. Vogt: U.S. Patent 20020007877 A1, 2002.
9.
Zurück zum Zitat F Ross and K O’hara: in Superalloys 1996, R Kissinger, D Bye, D Anton, A Cetel, M Nathal, T Pollock, and D Woodford, eds., TMS, Warrendale, PA, 1996, pp. 19-25. F Ross and K O’hara: in Superalloys 1996, R Kissinger, D Bye, D Anton, A Cetel, M Nathal, T Pollock, and D Woodford, eds., TMS, Warrendale, PA, 1996, pp. 19-25.
10.
Zurück zum Zitat L. Zheng, C. Gu, and Y. Zheng: Scripta Mater., 2004, vol. 50, pp. 435-9.CrossRef L. Zheng, C. Gu, and Y. Zheng: Scripta Mater., 2004, vol. 50, pp. 435-9.CrossRef
11.
Zurück zum Zitat Y. Liang, J. Li, A. Li, X. Pang, and H. Wang: Scripta Mater., 2017, vol. 127, pp. 58-62.CrossRef Y. Liang, J. Li, A. Li, X. Pang, and H. Wang: Scripta Mater., 2017, vol. 127, pp. 58-62.CrossRef
12.
Zurück zum Zitat N. D’Souza, H. Dong, M. Ardanani, and B. Shollock: Scripta Mater., 2005, vol. 53, pp. 729-33.CrossRef N. D’Souza, H. Dong, M. Ardanani, and B. Shollock: Scripta Mater., 2005, vol. 53, pp. 729-33.CrossRef
13.
Zurück zum Zitat F. Wang, D. Ma, J. Zhang, L. Liu, J. Hong, S. Bogner, and A. Bührig-Polaczek: J. Cryst. Growth, 2014, vol. 389, pp. 47-54.CrossRef F. Wang, D. Ma, J. Zhang, L. Liu, J. Hong, S. Bogner, and A. Bührig-Polaczek: J. Cryst. Growth, 2014, vol. 389, pp. 47-54.CrossRef
14.
Zurück zum Zitat F. Wang, D. Ma, J. Zhang, L. Liu, S. Bogner, and A. Bührig-Polaczek: J. Alloy. Compd., 2014, vol. 616, pp. 102-9.CrossRef F. Wang, D. Ma, J. Zhang, L. Liu, S. Bogner, and A. Bührig-Polaczek: J. Alloy. Compd., 2014, vol. 616, pp. 102-9.CrossRef
15.
16.
Zurück zum Zitat Y Zhu, S Zhang, L Xu, J Bi, Z Hu, and C Shi: in Superalloys 1988, S Reichman, D Duhl, G Maurer, S Antolovich, and C Lund, eds., TMS, Warrendale, PA, 1988, pp. 703-712. Y Zhu, S Zhang, L Xu, J Bi, Z Hu, and C Shi: in Superalloys 1988, S Reichman, D Duhl, G Maurer, S Antolovich, and C Lund, eds., TMS, Warrendale, PA, 1988, pp. 703-712.
17.
Zurück zum Zitat N. D’Souza, M. Lekstrom, H. Dai, B. Shollock, and H. Dong: Mater. Sci. Technol., 2007, vol. 23, pp. 1085-92.CrossRef N. D’Souza, M. Lekstrom, H. Dai, B. Shollock, and H. Dong: Mater. Sci. Technol., 2007, vol. 23, pp. 1085-92.CrossRef
18.
Zurück zum Zitat F. Wang, D. Ma, J. Zhang, S. Bogner, and A. Bührig-Polaczek: Mater. Character., 2015, vol. 101, pp. 20-5.CrossRef F. Wang, D. Ma, J. Zhang, S. Bogner, and A. Bührig-Polaczek: Mater. Character., 2015, vol. 101, pp. 20-5.CrossRef
19.
Zurück zum Zitat N D’Souza and H Dong: in Superalloys 2008, R Reed, K Green, P Caron, T Gabb, M Fahrmann, E Huron, and S Woodard, eds., TMS, Warrendale, PA, 2008, pp. 261-269. N D’Souza and H Dong: in Superalloys 2008, R Reed, K Green, P Caron, T Gabb, M Fahrmann, E Huron, and S Woodard, eds., TMS, Warrendale, PA, 2008, pp. 261-269.
20.
Zurück zum Zitat N. Warnken, D. Ma, M. Mathes, and I. Steinbach: Mater. Sci. Eng. A, 2005, vol. 413-414, pp. 267-71.CrossRef N. Warnken, D. Ma, M. Mathes, and I. Steinbach: Mater. Sci. Eng. A, 2005, vol. 413-414, pp. 267-71.CrossRef
21.
Zurück zum Zitat F. Wang, D. Ma, and A. Bührig-Polaczek: Mater. Character., 2017, vol. 127, pp. 311-6.CrossRef F. Wang, D. Ma, and A. Bührig-Polaczek: Mater. Character., 2017, vol. 127, pp. 311-6.CrossRef
22.
23.
Zurück zum Zitat A. Heckl, R. Rettig, S. Cenanovic, M. Göken, and R. Singer: J. Cryst. Growth, 2007, vol. 312, pp. 2137–44.CrossRef A. Heckl, R. Rettig, S. Cenanovic, M. Göken, and R. Singer: J. Cryst. Growth, 2007, vol. 312, pp. 2137–44.CrossRef
24.
Zurück zum Zitat F. Wang, D. Ma, S. Bogner, and A. Bührig-Polaczek: Metall. Mater. Trans. A, 2016, vol. 47, pp. 2376-86.CrossRef F. Wang, D. Ma, S. Bogner, and A. Bührig-Polaczek: Metall. Mater. Trans. A, 2016, vol. 47, pp. 2376-86.CrossRef
Metadaten
Titel
Eutectic Formation During Solidification of Ni-Based Single-Crystal Superalloys with Additional Carbon
verfasst von
Fu Wang
Dexin Ma
Andreas Bührig-Polaczek
Publikationsdatum
07.09.2017
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 11/2017
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-017-4317-1

Weitere Artikel der Ausgabe 11/2017

Metallurgical and Materials Transactions A 11/2017 Zur Ausgabe

Topical Collection: Carl Koch Symposium: Mechanical Behavior of Nanomaterials

Bulk Nanostructured Materials

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.