Evaluation of In Vitro Fatigue Properties of Biodegradable Mg–0.3at.%Ca Alloy

verfasst von : Naoko Ikeo, Akihito Taguma, Taichi Uemura, Toshiji Mukai

Erschienen in: Magnesium Technology 2017

Verlag: Springer International Publishing

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Recently, biodegradable bone fixation devices have been demanded when considering the patient’s quality of life (QOL). During the fracture healing, the devices must support the repeated load due to daily performance. At the same time, surface of the magnesium devices was affected by body fluid. Thus in this research, in vitro fatigue properties of biodegradable Mg–0.3at.%Ca alloy was evaluated by using simulated body fluid. Though there was fatigue limit when the test was conducted under the ambient condition, it cannot be confirmed during the test in the simulated body fluid. Inspection of fracture surface revealed that crack propagated along the grain boundary after both the fatigue tests.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Effect of Ca on the Microstructure, Texture and Mechanical Properties in Mg–Zn–Mn Based Alloy

Nächstes Kapitel Mechanical Properties and Fatigue Strength of Extruded Cobalt-Containing Magnetic Magnesium Alloys

F. Witte, The history of biodegradable magnesium implants: a review. Acta Biomater. 6, 1680–1692 (2010)CrossRef

D. Persaud-Sharma, A. McGoron, J. Biomim. Biomater. Tissue Eng. 12, 25–39 (2012)CrossRef

E. Zhang, L. Yang, Microstructure, mechanical properties and bio-corrosion properties of MgZn–MnCa alloy for biomedical application. Mater. Sci. Eng. A 497, 111–118 (2008)CrossRef

Z. Li, X. Gu, S. Lou, Y. Zheng, The development of binary Mg–Ca alloys for use as biodegradable materials within bone. Biomaterials 29, 1329–1344 (2008)CrossRef

H.R.B. Rad, M. Hasbullah Idris, M.R.A. Kadir, S. Farahany, Microstructure analysis and corrosion behavior of biodegradable Mg–Ca implant alloys. Mater. Des. 33, 88–97 (2012)

A. Yamamoto, S. Hiromoto, Effect of inorganic salts, amino acids and proteins on the degradation of pure magnesium in vitro. Mater. Sci. Eng. C 29, 1559–1568 (2009)CrossRef

D. Bian, W. Zhou, Y. Liu, N. Li, Y. Zheng, Z. Sun, Fatigue behaviors of HP–Mg, Mg–Ca and Mg–Zn–Ca biodegradable metals in air and simulated body fluid. Acta Biomater. 41, 351–360 (2016)CrossRef

T. Hase, T. Ohtagaki, M. Yamaguchi, N. Ikeo, T. Mukai, Effect of aluminum or zinc solute addition on enhancing impact fracture toughness in Mg–Ca alloys. Acta Mater. 104, 283–294 (2016)CrossRef

H. Somekawa, T. Inoue, K. Tsuzaki, Effect of solute atoms on fracture toughness in dilute magnesium alloys. Phil. Mag. 93, 4582–4592 (2013)CrossRef

Titel: Evaluation of In Vitro Fatigue Properties of Biodegradable Mg–0.3at.%Ca Alloy
verfasst von: Naoko Ikeo
Akihito Taguma
Taichi Uemura
Toshiji Mukai
Verlag: Springer International Publishing
Buch: Magnesium Technology 2017
Print ISBN: 978-3-319-52391-0

Electronic ISBN: 978-3-319-52392-7

Copyright-Jahr: 2017
DOI: https://doi.org/10.1007/978-3-319-52392-7_73

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht