Evaluation of Structural Performance of Concrete with Ambient-Cured Alkali-Activated Binders

verfasst von : Kruthi Kiran Ramagiri, Darshan Chauhan, Shashank Gupta, Arkamitra Kar, Dibyendu Adak

Erschienen in: Proceedings of SECON'19

Verlag: Springer International Publishing

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Enormous global CO2 emissions associated with cement production necessitates the use of sustainable cementitious alternatives. Alkali-activated binder (AAB) which utilizes industrial wastes as precursors is a promising substitute for cement. To promote the practical use of AAB concrete, this paper presents an investigation on the mechanical and microstructural properties of ambient-cured AAB concrete. Fly ash/slag ratio is varied and the optimum mix is proposed based on compressive strength test results. Pull-out test is performed to evaluate the bond strength of ambient-cured reinforced AAB concrete. The specimen-level tests are supplemented with results from X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy and scanning electron microscopy (SEM) along with energy-dispersive spectroscopic (EDS) analysis of the AAB paste samples. This is done to corroborate the microstructural characteristics with the mechanical properties at specimen-level. Fly ash: slag ratio of 70:30 is recommended as the optimum proportion considering both strength and economical aspects. Incorporation of slag results in the formation of the additional reaction products, refining the pore structure and enhancing strength. The AAB mix with fly ash: slag ratio of 50:50 exhibits the highest compressive strength and bond strength.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Stafford FN, Raupp-Pereira F, Labrincha JA, Hotza D (2016) Life cycle assessment of the production of cement: a Brazilian case study. J Cleaner Prod 137:1293–1299 Stafford FN, Raupp-Pereira F, Labrincha JA, Hotza D (2016) Life cycle assessment of the production of cement: a Brazilian case study. J Cleaner Prod 137:1293–1299
2.
Zurück zum Zitat Turner LK, Collins FG (2013) Carbon dioxide equivalent (CO2-e) emissions: a comparison between geopolymer and OPC cement concrete. Constr Build Mater 43:125–130 Turner LK, Collins FG (2013) Carbon dioxide equivalent (CO2-e) emissions: a comparison between geopolymer and OPC cement concrete. Constr Build Mater 43:125–130
3.
Zurück zum Zitat Ke X, Bernal SA, Provis JL (2017) Uptake of chloride and carbonate by Mg-Al and Ca-Al layered double hydroxides in simulated pore solutions of alkali-activated slag cement. Cem Concr Res 100:1–3 Ke X, Bernal SA, Provis JL (2017) Uptake of chloride and carbonate by Mg-Al and Ca-Al layered double hydroxides in simulated pore solutions of alkali-activated slag cement. Cem Concr Res 100:1–3
4.
Zurück zum Zitat Gebregziabiher BS, Thomas R, Peethamparan S (2015) Very early-age reaction kinetics and microstructural development in alkali-activated slag. Cem Concr Compo 55:91–102 Gebregziabiher BS, Thomas R, Peethamparan S (2015) Very early-age reaction kinetics and microstructural development in alkali-activated slag. Cem Concr Compo 55:91–102
5.
Zurück zum Zitat Fernández-Jiménez A, García-Lodeiro I, Palomo A (2007) Durability of alkali-activated fly ash cementitious materials. J Mater Sci 42(9):3055–3065 Fernández-Jiménez A, García-Lodeiro I, Palomo A (2007) Durability of alkali-activated fly ash cementitious materials. J Mater Sci 42(9):3055–3065
6.
Zurück zum Zitat García-Lodeiro I, Palomo A, Fernández-Jiménez A (2007) Alkali-aggregate reaction in activated fly ash systems. Cem Concr Res 37(2):175–183 García-Lodeiro I, Palomo A, Fernández-Jiménez A (2007) Alkali-aggregate reaction in activated fly ash systems. Cem Concr Res 37(2):175–183
7.
Zurück zum Zitat Fernandez-Jimenez AM, Palomo A, Lopez-Hombrados C (2006) Engineering properties of alkali-activated fly ash concrete. ACI Mater J 103(2):106–112 Fernandez-Jimenez AM, Palomo A, Lopez-Hombrados C (2006) Engineering properties of alkali-activated fly ash concrete. ACI Mater J 103(2):106–112
8.
Zurück zum Zitat Sarker PK (2011) Bond strength of reinforcing steel embedded in fly ash-based geopolymer concrete. Mater Struct 44(5):1021–1030 Sarker PK (2011) Bond strength of reinforcing steel embedded in fly ash-based geopolymer concrete. Mater Struct 44(5):1021–1030
9.
Zurück zum Zitat Yang KH, Song JK (2012) Empirical equations for mechanical properties of Ca(OH)2-based alkali-activated slag concrete. ACI Mater J 109(4):431–440 Yang KH, Song JK (2012) Empirical equations for mechanical properties of Ca(OH)2-based alkali-activated slag concrete. ACI Mater J 109(4):431–440
10.
Zurück zum Zitat Castel A, Foster SJ (2015) Bond strength between blended slag and Class F fly ash geopolymer concrete with steel reinforcement. Cem Concr Res 72:48–53 Castel A, Foster SJ (2015) Bond strength between blended slag and Class F fly ash geopolymer concrete with steel reinforcement. Cem Concr Res 72:48–53
11.
Zurück zum Zitat Adak D, Sarkar M, Mandal S (2017) Structural performance of nano-silica modified fly-ash based geopolymer concrete. Constr Build Mater 135:430–439 Adak D, Sarkar M, Mandal S (2017) Structural performance of nano-silica modified fly-ash based geopolymer concrete. Constr Build Mater 135:430–439
12.
Zurück zum Zitat ASTM (2011) Standard test method for compressive strength of cylindrical concrete specimens. ASTM C39/C39M11, West Conshohocken, PA ASTM (2011) Standard test method for compressive strength of cylindrical concrete specimens. ASTM C39/C39M11, West Conshohocken, PA
13.
Zurück zum Zitat Indian Standards (1967) Methods of testing bond in reinforced concrete, Part 1: Pull-out test. IS 2770-1, Bureau of Indian Standards, New Delhi, India Indian Standards (1967) Methods of testing bond in reinforced concrete, Part 1: Pull-out test. IS 2770-1, Bureau of Indian Standards, New Delhi, India
14.
Zurück zum Zitat Criado M, Aperador W, Sobrados I (2016) Microstructural and mechanical properties of alkali activated Colombian raw materials. Materials 9(3):158(Multidisciplinary Digital Publishing Institute (MDPI)) Criado M, Aperador W, Sobrados I (2016) Microstructural and mechanical properties of alkali activated Colombian raw materials. Materials 9(3):158(Multidisciplinary Digital Publishing Institute (MDPI))
15.
Zurück zum Zitat Ma Y (2013) Microstructure and engineering properties of alkali activated fly ash-as an environment friendly alternative to Portland cement. Ph.D. dissertation, TU Delft, Netherlands Ma Y (2013) Microstructure and engineering properties of alkali activated fly ash-as an environment friendly alternative to Portland cement. Ph.D. dissertation, TU Delft, Netherlands
16.
Zurück zum Zitat Walkley B, Rees GJ, San Nicolas R, van Deventer JS, Hanna JV, Provis JL (2018) New structural model of hydrous sodium aluminosilicate gels and the role of charge-balancing extra-framework Al. J Phys Chem C 122(10):5673–5685 Walkley B, Rees GJ, San Nicolas R, van Deventer JS, Hanna JV, Provis JL (2018) New structural model of hydrous sodium aluminosilicate gels and the role of charge-balancing extra-framework Al. J Phys Chem C 122(10):5673–5685
17.
Zurück zum Zitat Bakharev T (2005) Geopolymeric materials prepared using Class F fly ash and elevated temperature curing. Cem Concr Res 35(6):1224–1232 Bakharev T (2005) Geopolymeric materials prepared using Class F fly ash and elevated temperature curing. Cem Concr Res 35(6):1224–1232
Metadaten
Titel
Evaluation of Structural Performance of Concrete with Ambient-Cured Alkali-Activated Binders
verfasst von
Kruthi Kiran Ramagiri
Darshan Chauhan
Shashank Gupta
Arkamitra Kar
Dibyendu Adak
Copyright-Jahr
2020
DOI
https://doi.org/10.1007/978-3-030-26365-2_1