Experimental Investigation on Strength and Durability of Fly Ash and GGBS Based Geopolymer Concrete

verfasst von : G. Asha, Jiji Antony

Erschienen in: Proceedings of SECON'19

Verlag: Springer International Publishing

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Geopolymer is an aluminosilicate binding material synthesized by thermal activation of solid aluminosilicate base material such as GGBS and fly ash. Geopolymer concrete is produced due to alkalization of materials rich in aluminum and silicon with alkali solution, an aqueous solution of sodium hydroxide and sodium silicate. Alkali solution was varied in different molar concentration with sodium hydroxide to sodium silicate ratio of 2.5. The effect of age on geopolymer binder cured at ambient temperature and microstructure of binder were studied. The material used in this study consists of fly ash, ground granulated blast furnace slag, alkaline liquid, fine aggregate and coarse aggregate and sisal fibre. The mechanical properties of geopolymer concrete and binder with or without the sisal fibre were determined. The durability tests such as acid attack test and chloride attack for various mix samples were also conducted.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Nath P, Sarker PK (2014) Effect of GGBFS on setting, workability and early strength properties of fly ash geopolymer concrete cured in ambient condition. Constr Build Mater 66:163–171CrossRef Nath P, Sarker PK (2014) Effect of GGBFS on setting, workability and early strength properties of fly ash geopolymer concrete cured in ambient condition. Constr Build Mater 66:163–171CrossRef
2.
Zurück zum Zitat Duan P, Yan C (2016) Fresh properties, mechanical strength and microstructure of fly ash geopolymer paste reinforced with sawdust. Constr Build Mater 111:600–610CrossRef Duan P, Yan C (2016) Fresh properties, mechanical strength and microstructure of fly ash geopolymer paste reinforced with sawdust. Constr Build Mater 111:600–610CrossRef
3.
Zurück zum Zitat Mane S, Jadhav HS (2012) Investigation of geopolymer mortar and concrete under high temperature. Int J Civ Eng Technol 2:384–390 Mane S, Jadhav HS (2012) Investigation of geopolymer mortar and concrete under high temperature. Int J Civ Eng Technol 2:384–390
4.
Zurück zum Zitat Cheah CB, Samsudin MH (2018) The use of high calcium wood ash in the preparation of ground granulated blast furnace slag and pulverized fly ash geopolymers a complete microstructural and mechanical characterization. Constr Build Mater 17:1–30 Cheah CB, Samsudin MH (2018) The use of high calcium wood ash in the preparation of ground granulated blast furnace slag and pulverized fly ash geopolymers a complete microstructural and mechanical characterization. Constr Build Mater 17:1–30
Metadaten
Titel
Experimental Investigation on Strength and Durability of Fly Ash and GGBS Based Geopolymer Concrete
verfasst von
G. Asha
Jiji Antony
Copyright-Jahr
2020
DOI
https://doi.org/10.1007/978-3-030-26365-2_5