Fabrication of inhibitor anion-intercalated layered double hydroxide host films on aluminum alloy 2024 and their anticorrosion properties

verfasst von: You Zhang, Jianhua Liu, Yingdong Li, Mei Yu, SongMei Li, Bing Xue

Erschienen in: Journal of Coatings Technology and Research | Ausgabe 2/2015

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

ZnAl layered double hydroxide (LDH) host films have been synthesized on aluminum alloy 2024 substrate via a facile crystallization method, and then intercalated with different corrosion inhibitor anions (vanadate, molybdate, and 2-mercaptobenzothiazolate). The structures, compositions, and morphologies of the as-synthesized films before and after the anion-exchange reaction were characterized by means of glancing-angle X-ray diffraction, Fourier transform infrared, X-ray photoelectron spectroscopy, and scanning electron microscope techniques. The anticorrosion performance of films was evaluated by potentiodynamic polarization and salt spray test. The results show that all inhibitor anions are successfully intercalated in the layered galleries, providing enhanced corrosion protection for the substrate alloy. The anticorrosion abilities of films loaded with inhibitor anions are ordered as LDH–VO3 > LDH–MBT > LDH–MoO4 > LDH–NO3.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Guo, X, Xu, S, Zhao, L, Lu, W, Zhang, F, Evans, DG, Duan, X, “One-Step Hydrothermal Crystallization of a Layered Double Hydroxide/Alumina Bilayer Film on Aluminum and Its Corrosion Resistance Properties.” Langmuir, 25 (17) 9894–9897 (2009)CrossRef Guo, X, Xu, S, Zhao, L, Lu, W, Zhang, F, Evans, DG, Duan, X, “One-Step Hydrothermal Crystallization of a Layered Double Hydroxide/Alumina Bilayer Film on Aluminum and Its Corrosion Resistance Properties.” Langmuir, 25 (17) 9894–9897 (2009)CrossRef
2.
Zurück zum Zitat Ishizaki, T, Chiba, S, Watanabe, K, Suzuki, H, “Corrosion Resistance of Mg–Al Layered Double Hydroxide Container-Containing Magnesium Hydroxide Films Formed Directly on Magnesium Alloy by Chemical-Free Steam Coating.” J. Mater. Chem. A, 1 (31) 8968–8977 (2013)CrossRef Ishizaki, T, Chiba, S, Watanabe, K, Suzuki, H, “Corrosion Resistance of Mg–Al Layered Double Hydroxide Container-Containing Magnesium Hydroxide Films Formed Directly on Magnesium Alloy by Chemical-Free Steam Coating.” J. Mater. Chem. A, 1 (31) 8968–8977 (2013)CrossRef
3.
Zurück zum Zitat Zhang, F, Zhao, L, Chen, H, Xu, S, Evans, DG, Duan, X, “Corrosion Resistance of Superhydrophobic Layered Double Hydroxide Films on Aluminum.” Angew. Chem. Int. Ed., 47 (13) 2466–2469 (2008)CrossRef Zhang, F, Zhao, L, Chen, H, Xu, S, Evans, DG, Duan, X, “Corrosion Resistance of Superhydrophobic Layered Double Hydroxide Films on Aluminum.” Angew. Chem. Int. Ed., 47 (13) 2466–2469 (2008)CrossRef
4.
Zurück zum Zitat Dong, Y, Wang, F, Zhou, Q, “Protective Behaviors of 2-Mercaptobenzothiazole Intercalated Zn–Al-Layered Double Hydroxide Coating.” J. Coat. Technol. Res., 11 793–803 (2014)CrossRef Dong, Y, Wang, F, Zhou, Q, “Protective Behaviors of 2-Mercaptobenzothiazole Intercalated Zn–Al-Layered Double Hydroxide Coating.” J. Coat. Technol. Res., 11 793–803 (2014)CrossRef
5.
Zurück zum Zitat Poznyak, S, Tedim, J, Rodrigues, L, Salak, A, Zheludkevich, M, Dick, L, Ferreira, M, “Novel Inorganic Host Layered Double Hydroxides Intercalated with Guest Organic Inhibitors for Anticorrosion Applications.” ACS Appl. Mater. Interfaces, 1 (10) 2353–2362 (2009)CrossRef Poznyak, S, Tedim, J, Rodrigues, L, Salak, A, Zheludkevich, M, Dick, L, Ferreira, M, “Novel Inorganic Host Layered Double Hydroxides Intercalated with Guest Organic Inhibitors for Anticorrosion Applications.” ACS Appl. Mater. Interfaces, 1 (10) 2353–2362 (2009)CrossRef
6.
Zurück zum Zitat Zhang, F, Sun, M, Xu, S, Zhao, L, Zhang, B, “Fabrication of Oriented Layered Double Hydroxide Films by Spin Coating and Their Use in Corrosion Protection.” Chem. Eng. J., 141 (1) 362–367 (2008)CrossRef Zhang, F, Sun, M, Xu, S, Zhao, L, Zhang, B, “Fabrication of Oriented Layered Double Hydroxide Films by Spin Coating and Their Use in Corrosion Protection.” Chem. Eng. J., 141 (1) 362–367 (2008)CrossRef
7.
Zurück zum Zitat Aradi, T, Hornok, V, Dékány, I, “Layered Double Hydroxides for Ultrathin Hybrid Film Preparation Using Layer-By-Layer and Spin Coating Methods.” Colloids Surf. A, 319 (1) 116–121 (2008)CrossRef Aradi, T, Hornok, V, Dékány, I, “Layered Double Hydroxides for Ultrathin Hybrid Film Preparation Using Layer-By-Layer and Spin Coating Methods.” Colloids Surf. A, 319 (1) 116–121 (2008)CrossRef
8.
Zurück zum Zitat Chen, H, Zhang, F, Fu, S, Duan, X, “In Situ Microstructure Control of Oriented Layered Double Hydroxide Monolayer Films with Curved Hexagonal Crystals as Superhydrophobic Materials.” Adv. Mater., 18 (23) 3089–3093 (2006)CrossRef Chen, H, Zhang, F, Fu, S, Duan, X, “In Situ Microstructure Control of Oriented Layered Double Hydroxide Monolayer Films with Curved Hexagonal Crystals as Superhydrophobic Materials.” Adv. Mater., 18 (23) 3089–3093 (2006)CrossRef
9.
Zurück zum Zitat Tedim, J, Zheludkevich, M, Salak, A, Lisenkov, A, Ferreira, M, “Nanostructured LDH-Container Layer with Active Protection Functionality.” J. Mater. Chem., 21 (39) 15464–15470 (2011)CrossRef Tedim, J, Zheludkevich, M, Salak, A, Lisenkov, A, Ferreira, M, “Nanostructured LDH-Container Layer with Active Protection Functionality.” J. Mater. Chem., 21 (39) 15464–15470 (2011)CrossRef
10.
Zurück zum Zitat Chen, J, Song, Y, Shan, D, Han, E-H, “In Situ Growth of Mg–Al Hydrotalcite Conversion Film on AZ31 Magnesium Alloy.” Corros. Sci., 53 (10) 3281–3288 (2011)CrossRef Chen, J, Song, Y, Shan, D, Han, E-H, “In Situ Growth of Mg–Al Hydrotalcite Conversion Film on AZ31 Magnesium Alloy.” Corros. Sci., 53 (10) 3281–3288 (2011)CrossRef
11.
Zurück zum Zitat Chen, J, Song, Y, Shan, D, Han, E-H, “Study of the Corrosion Mechanism of the In Situ Grown Mg–Al–CO3 2− Hydrotalcite Film on AZ31 Alloy.” Corros. Sci., 65 268–277 (2012)CrossRef Chen, J, Song, Y, Shan, D, Han, E-H, “Study of the Corrosion Mechanism of the In Situ Grown Mg–Al–CO3 2− Hydrotalcite Film on AZ31 Alloy.” Corros. Sci., 65 268–277 (2012)CrossRef
12.
Zurück zum Zitat Chen, J, Song, Y, Shan, D, Han, E-H, “Study of the In Situ Growth Mechanism of Mg–Al Hydrotalcite Conversion Film on AZ31 Magnesium Alloy.” Corros. Sci., 63 148–158 (2012)CrossRef Chen, J, Song, Y, Shan, D, Han, E-H, “Study of the In Situ Growth Mechanism of Mg–Al Hydrotalcite Conversion Film on AZ31 Magnesium Alloy.” Corros. Sci., 63 148–158 (2012)CrossRef
13.
Zurück zum Zitat Dong, Y, Ma, L, Zhou, Q, “Effect of the Incorporation of Montmorillonite-Layered Double Hydroxide Nanoclays on the Corrosion Protection of Epoxy Coatings.” J. Coat. Technol. Res., 10 (6) 909–921 (2013)CrossRef Dong, Y, Ma, L, Zhou, Q, “Effect of the Incorporation of Montmorillonite-Layered Double Hydroxide Nanoclays on the Corrosion Protection of Epoxy Coatings.” J. Coat. Technol. Res., 10 (6) 909–921 (2013)CrossRef
14.
Zurück zum Zitat Tedim, J, Poznyak, S, Kuznetsova, A, Raps, D, Hack, T, Zheludkevich, M, Ferreira, M, “Enhancement of Active Corrosion Protection Via Combination of Inhibitor-Loaded Nanocontainers.” ACS Appl. Mater. Interfaces, 2 (5) 1528–1535 (2010)CrossRef Tedim, J, Poznyak, S, Kuznetsova, A, Raps, D, Hack, T, Zheludkevich, M, Ferreira, M, “Enhancement of Active Corrosion Protection Via Combination of Inhibitor-Loaded Nanocontainers.” ACS Appl. Mater. Interfaces, 2 (5) 1528–1535 (2010)CrossRef
15.
Zurück zum Zitat Hang, TTX, Truc, TA, Duong, NT, Vu, PG, Hoang, T, “Preparation and Characterization of Nanocontainers of Corrosion Inhibitor Based on Layered Double Hydroxides.” Appl. Clay Sci., 67 18–25 (2012)CrossRef Hang, TTX, Truc, TA, Duong, NT, Vu, PG, Hoang, T, “Preparation and Characterization of Nanocontainers of Corrosion Inhibitor Based on Layered Double Hydroxides.” Appl. Clay Sci., 67 18–25 (2012)CrossRef
16.
Zurück zum Zitat Wang, Y, Zhang, D, “Synthesis, Characterization, and Controlled Release Anticorrosion Behavior of Benzoate Intercalated Zn–Al Layered Double Hydroxides.” Mater. Res. Bull., 46 (11) 1963–1968 (2011)CrossRef Wang, Y, Zhang, D, “Synthesis, Characterization, and Controlled Release Anticorrosion Behavior of Benzoate Intercalated Zn–Al Layered Double Hydroxides.” Mater. Res. Bull., 46 (11) 1963–1968 (2011)CrossRef
17.
Zurück zum Zitat Granizo, N, Vega, J, De La Fuente, D, Chico, B, Morcillo, M, “Ion-Exchange Pigments in Primer Paints for Anticorrosive Protection of Steel in Atmospheric Service: Anion-Exchange Pigments.” Prog. Org. Coat., 76 (2) 411–424 (2013)CrossRef Granizo, N, Vega, J, De La Fuente, D, Chico, B, Morcillo, M, “Ion-Exchange Pigments in Primer Paints for Anticorrosive Protection of Steel in Atmospheric Service: Anion-Exchange Pigments.” Prog. Org. Coat., 76 (2) 411–424 (2013)CrossRef
18.
Zurück zum Zitat Hang, TTX, Truc, TA, Duong, NT, Pébère, N, Olivier, M-G, “Layered Double Hydroxides as Containers of Inhibitors in Organic Coatings for Corrosion Protection of Carbon Steel.” Prog. Org. Coat., 74 (2) 343–348 (2012)CrossRef Hang, TTX, Truc, TA, Duong, NT, Pébère, N, Olivier, M-G, “Layered Double Hydroxides as Containers of Inhibitors in Organic Coatings for Corrosion Protection of Carbon Steel.” Prog. Org. Coat., 74 (2) 343–348 (2012)CrossRef
19.
Zurück zum Zitat Tedim, J, Zheludkevich, M, Bastos, A, Salak, A, Lisenkov, A, Ferreira, M, “Influence of Preparation Conditions of Layered Double Hydroxide Conversion Films on Corrosion Protection.” Electrochim. Acta, 117 164–171 (2014)CrossRef Tedim, J, Zheludkevich, M, Bastos, A, Salak, A, Lisenkov, A, Ferreira, M, “Influence of Preparation Conditions of Layered Double Hydroxide Conversion Films on Corrosion Protection.” Electrochim. Acta, 117 164–171 (2014)CrossRef
20.
Zurück zum Zitat Wang, L, Zhang, K, He, H, Sun, W, Zong, Q, Liu, G, “Enhanced Corrosion Resistance of MgAl Hydrotalcite Conversion Coating on Aluminum by Chemical Conversion Treatment.” Surf. Coat. Technol., 235 484–488 (2013)CrossRef Wang, L, Zhang, K, He, H, Sun, W, Zong, Q, Liu, G, “Enhanced Corrosion Resistance of MgAl Hydrotalcite Conversion Coating on Aluminum by Chemical Conversion Treatment.” Surf. Coat. Technol., 235 484–488 (2013)CrossRef
21.
Zurück zum Zitat Yu, X, Wang, J, Zhang, M, Yang, L, Li, J, Yang, P, Cao, D, “Synthesis, Characterization and Anticorrosion Performance of Molybdate Pillared Hydrotalcite In Situ Created ZnO Composite as Pigment for Mg–Li Alloy Protection.” Surf. Coat. Technol., 203 (3) 250–255 (2008)CrossRef Yu, X, Wang, J, Zhang, M, Yang, L, Li, J, Yang, P, Cao, D, “Synthesis, Characterization and Anticorrosion Performance of Molybdate Pillared Hydrotalcite In Situ Created ZnO Composite as Pigment for Mg–Li Alloy Protection.” Surf. Coat. Technol., 203 (3) 250–255 (2008)CrossRef
22.
Zurück zum Zitat Moutarlier, V, Neveu, B, Gigandet, M, “Evolution of Corrosion Protection for Sol–Gel Coatings Doped with Inorganic Inhibitors.” Surf. Coat. Technol., 202 (10) 2052–2058 (2008)CrossRef Moutarlier, V, Neveu, B, Gigandet, M, “Evolution of Corrosion Protection for Sol–Gel Coatings Doped with Inorganic Inhibitors.” Surf. Coat. Technol., 202 (10) 2052–2058 (2008)CrossRef
23.
Zurück zum Zitat Hu, J, Gan, M, Ma, L, Li, Z, Yan, J, Zhang, J, “Synthesis and Anticorrosive Properties of Polymer–Clay Nanocomposites Via Chemical Grafting of Polyaniline onto Zn–Al Layered Double Hydroxides.” Surf. Coat. Technol., 240 55–62 (2014)CrossRef Hu, J, Gan, M, Ma, L, Li, Z, Yan, J, Zhang, J, “Synthesis and Anticorrosive Properties of Polymer–Clay Nanocomposites Via Chemical Grafting of Polyaniline onto Zn–Al Layered Double Hydroxides.” Surf. Coat. Technol., 240 55–62 (2014)CrossRef
24.
Zurück zum Zitat Xu, ZP, Braterman, PS, “High Affinity of Dodecylbenzene Sulfonate for Layered Double Hydroxide and Resulting Morphological Changes.” J. Mater. Chem., 13 (2) 268–273 (2003)CrossRef Xu, ZP, Braterman, PS, “High Affinity of Dodecylbenzene Sulfonate for Layered Double Hydroxide and Resulting Morphological Changes.” J. Mater. Chem., 13 (2) 268–273 (2003)CrossRef
25.
Zurück zum Zitat Kloprogge, JT, Hickey, L, Frost, RL, “The Effect of Varying Synthesis Conditions on Zinc Chromium Hydrotalcite: A Spectroscopic Study.” Mater. Chem. Phys., 89 (1) 99–109 (2005)CrossRef Kloprogge, JT, Hickey, L, Frost, RL, “The Effect of Varying Synthesis Conditions on Zinc Chromium Hydrotalcite: A Spectroscopic Study.” Mater. Chem. Phys., 89 (1) 99–109 (2005)CrossRef
26.
Zurück zum Zitat Pedregosa, J, Baran, E, Aymonino, P, “Kristallchemisches Verhalten und IR-Spektren einiger Divanadate des Thortveitit-Typs und verwandter Strukturen.” Zeitschrift für anorganische und allgemeine Chemie, 404 (3) 308–320 (1974)CrossRef Pedregosa, J, Baran, E, Aymonino, P, “Kristallchemisches Verhalten und IR-Spektren einiger Divanadate des Thortveitit-Typs und verwandter Strukturen.” Zeitschrift für anorganische und allgemeine Chemie, 404 (3) 308–320 (1974)CrossRef
27.
Zurück zum Zitat Markova-Velichkova, M, Iordanova, R, Dimitriev, Y, “Glass Formation in the V2O5–MoO3–ZnO System.” Phys. Status Solidi C, 8 (11–12) 3159–3162 (2011)CrossRef Markova-Velichkova, M, Iordanova, R, Dimitriev, Y, “Glass Formation in the V2O5–MoO3–ZnO System.” Phys. Status Solidi C, 8 (11–12) 3159–3162 (2011)CrossRef
28.
Zurück zum Zitat de Azevedo Marques, AP, de Melo, D, Paskocimas, CA, Pizani, PS, Joya, MR, Leite, ER, Longo, E, “Photoluminescent BaMoO4 Nanopowders Prepared by Complex Polymerization Method (CPM).” J. Solid State Chem., 179 (3) 671–678 (2006)CrossRef de Azevedo Marques, AP, de Melo, D, Paskocimas, CA, Pizani, PS, Joya, MR, Leite, ER, Longo, E, “Photoluminescent BaMoO4 Nanopowders Prepared by Complex Polymerization Method (CPM).” J. Solid State Chem., 179 (3) 671–678 (2006)CrossRef
29.
Zurück zum Zitat Thongtem, T, Phuruangrat, A, Thongtem, S, “Characterization of MMoO4 (M = Ba, Sr and Ca) with Different Morphologies Prepared Using a Cyclic Microwave Radiation.” Mater. Lett., 62 (3) 454–457 (2008)CrossRef Thongtem, T, Phuruangrat, A, Thongtem, S, “Characterization of MMoO4 (M = Ba, Sr and Ca) with Different Morphologies Prepared Using a Cyclic Microwave Radiation.” Mater. Lett., 62 (3) 454–457 (2008)CrossRef
30.
Zurück zum Zitat Zhang, K, Yarmolenko, M, Rogachev, A, Zhou, B, Jiang, X, Shen, R, Liu, X, “Formation of Complex Bis(β-mercaptobenzothiazole)–Zinc (II) Films by Pulsed Laser Deposition.” Appl. Surf. Sci., 273 836–840 (2013)CrossRef Zhang, K, Yarmolenko, M, Rogachev, A, Zhou, B, Jiang, X, Shen, R, Liu, X, “Formation of Complex Bis(β-mercaptobenzothiazole)–Zinc (II) Films by Pulsed Laser Deposition.” Appl. Surf. Sci., 273 836–840 (2013)CrossRef
31.
Zurück zum Zitat Gao, Y, Nagai, M, Masuda, Y, Sato, F, Seo, W, Koumoto, K, “Surface Precipitation of Highly Porous Hydrotalcite-Like Film on Al from a Zinc Aqueous Solution.” Langmuir, 22 (8) 3521–3527 (2006)CrossRef Gao, Y, Nagai, M, Masuda, Y, Sato, F, Seo, W, Koumoto, K, “Surface Precipitation of Highly Porous Hydrotalcite-Like Film on Al from a Zinc Aqueous Solution.” Langmuir, 22 (8) 3521–3527 (2006)CrossRef
32.
Zurück zum Zitat Grohmann, I, Peplinski, B, Unger, W, “New Entries in the XPS Fingerprint Database for the Characterization of Precipitated Cu Zn Al Oxide Catalysts.” Surf. Interface Anal., 19 (1–12) 591–594 (1992)CrossRef Grohmann, I, Peplinski, B, Unger, W, “New Entries in the XPS Fingerprint Database for the Characterization of Precipitated Cu Zn Al Oxide Catalysts.” Surf. Interface Anal., 19 (1–12) 591–594 (1992)CrossRef
33.
Zurück zum Zitat Fleutot, S, Dupin, J-C, Renaudin, G, Martinez, H, “Intercalation and Grafting of Benzene Derivatives into Zinc–Aluminum and Copper–Chromium Layered Double Hydroxide Hosts: An XPS Monitoring Study.” Phys. Chem. Chem. Phys., 13 (39) 17564–17578 (2011)CrossRef Fleutot, S, Dupin, J-C, Renaudin, G, Martinez, H, “Intercalation and Grafting of Benzene Derivatives into Zinc–Aluminum and Copper–Chromium Layered Double Hydroxide Hosts: An XPS Monitoring Study.” Phys. Chem. Chem. Phys., 13 (39) 17564–17578 (2011)CrossRef
34.
Zurück zum Zitat Wei, M, Xu, X, Wang, X, Li, F, Zhang, H, Lu, Y, Pu, M, Evans, DG, Duan, X, “Study on the Photochromism of Ni–Al Layered Double Hydroxides Containing Nitrate Anions.” Eur. J. Inorg. Chem., 2006 (14) 2831–2838 (2006)CrossRef Wei, M, Xu, X, Wang, X, Li, F, Zhang, H, Lu, Y, Pu, M, Evans, DG, Duan, X, “Study on the Photochromism of Ni–Al Layered Double Hydroxides Containing Nitrate Anions.” Eur. J. Inorg. Chem., 2006 (14) 2831–2838 (2006)CrossRef
35.
Zurück zum Zitat Choi, D, Blomgren, GE, Kumta, PN, “Fast and Reversible Surface Redox Reaction in Nanocrystalline Vanadium Nitride Supercapacitors.” Adv. Mater., 18 (9) 1178–1182 (2006)CrossRef Choi, D, Blomgren, GE, Kumta, PN, “Fast and Reversible Surface Redox Reaction in Nanocrystalline Vanadium Nitride Supercapacitors.” Adv. Mater., 18 (9) 1178–1182 (2006)CrossRef
36.
Zurück zum Zitat Buchheit, RG, Guan, H, Mahajanam, S, Wong, F, “Active Corrosion Protection and Corrosion Sensing in Chromate-Free Organic Coatings.” Prog. Org. Coat., 47 (3) 174–182 (2003)CrossRef Buchheit, RG, Guan, H, Mahajanam, S, Wong, F, “Active Corrosion Protection and Corrosion Sensing in Chromate-Free Organic Coatings.” Prog. Org. Coat., 47 (3) 174–182 (2003)CrossRef
37.
Zurück zum Zitat Iannuzzi, M, Frankel, GS, “Mechanisms of Corrosion Inhibition of AA2024-T3 by Vanadates.” Corros. Sci., 49 (5) 2371–2391 (2007)CrossRef Iannuzzi, M, Frankel, GS, “Mechanisms of Corrosion Inhibition of AA2024-T3 by Vanadates.” Corros. Sci., 49 (5) 2371–2391 (2007)CrossRef
38.
Zurück zum Zitat Kartsonakis, IA, Balaskas, AC, Kordas, GC, “Influence of Cerium Molybdate Containers on the Corrosion Performance of Epoxy Coated Aluminium Alloys 2024-T3.” Corros. Sci., 53 (11) 3771–3779 (2011)CrossRef Kartsonakis, IA, Balaskas, AC, Kordas, GC, “Influence of Cerium Molybdate Containers on the Corrosion Performance of Epoxy Coated Aluminium Alloys 2024-T3.” Corros. Sci., 53 (11) 3771–3779 (2011)CrossRef
Metadaten
Titel
Fabrication of inhibitor anion-intercalated layered double hydroxide host films on aluminum alloy 2024 and their anticorrosion properties
verfasst von
You Zhang
Jianhua Liu
Yingdong Li
Mei Yu
SongMei Li
Bing Xue
Publikationsdatum
01.03.2015
Verlag
Springer US
Erschienen in
Journal of Coatings Technology and Research / Ausgabe 2/2015
Print ISSN: 1547-0091
Elektronische ISSN: 1935-3804
DOI
https://doi.org/10.1007/s11998-014-9644-1

Weitere Artikel der Ausgabe 2/2015

Journal of Coatings Technology and Research 2/2015 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.