Fabrication of X8R-type Ba0.991Bi0.006TiO3@Nb2O5–Co3O4–La2O3@ZnO–B2O3–SiO2 ceramics with a fine-grained microstructure and low sintering temperature
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 8/2018
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
BaTiO3-based ceramics with a fine-crystalline microstructure, high temperature stability, and low sintering temperature have potential applications in multilayer capacitors (MLCCs). Here, a novel core–shell structured Ba0.991Bi0.006TiO3@Nb2O5–Co3O4–La2O3@ZnO–B2O3–SiO2 (BBT@NCL@ZBSO) ceramics were prepared by a double-coating method. The NCL was to improve the temperature stability of the ceramics and produce fine-grained ceramics. The ZBSO coating layer was advantageous to reducing the sintering temperature. As a result, the sintering temperature of the samples decreased from more than 1300 to 1100 °C. Moreover the ceramics loaded with 4.0 wt% ZBSO coating content by low temperature sintering at 1100 °C show the optimum dielectric constant of 2841, the dielectric loss is 0.0044, and the average grain size of the ceramic is 300 nm, which is similar to the BBT@NCL powder particle size (285 nm). The results indicated that the low-temperature-sintered BBT@NCL@ZBSO ceramics could be a promising dielectric material for X8R-type MLCCs.