Facile fabrication of hierarchically porous NiO microspheres as anode materials for lithium ion batteries

verfasst von: Fangcai Zheng, Shihao Xu, Yuanguang Zhang

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 4/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In this work, we report a novel and facile route for the large-scale fabrication of hierarchically porous NiO microspheres, which involves the thermal decomposition of β-Ni(OH)2 precursor at 450 °C in air for 2 h. The superstructures exhibit high specific surface area, large porous volume, and broad pore size distribution. The electrochemical properties of the hierarchically porous NiO microspheres were examined by cyclic voltammetry and galvanostatic charge/discharge studies. The results demonstrate that the hierarchically porous NiO microspheres are promising anode materials with enhanced lithium storage capacity and excellent cycling stability. The hierarchically porous NiO microspheres can retain a reversible capacity of 612 mA h g−1 after 50 cycles at a current density of 100 mA g−1. The improved electrochemical performance is attributed to their hierarchical structure and large amounts of mesopores within the nanosheets, which can effectively improve structural stability, reduce the diffusion length for lithium ions and electrons, and buffer volume expansion during the charge/discharge processes.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat A.R. Armstrong, C. Lyness, P.M. Panchmatia, M.S. Islam, P.G. Bruce, Nat. Mater. 10, 223–229 (2011)CrossRef A.R. Armstrong, C. Lyness, P.M. Panchmatia, M.S. Islam, P.G. Bruce, Nat. Mater. 10, 223–229 (2011)CrossRef
2.
Zurück zum Zitat M.V. Reddy, G.V.S.B. Rao, V.R. Chowdari, Chem. Rev. 113, 5364–5457 (2013)CrossRef M.V. Reddy, G.V.S.B. Rao, V.R. Chowdari, Chem. Rev. 113, 5364–5457 (2013)CrossRef
4.
Zurück zum Zitat M.V. Reddy, G. Prithvi, K.P. Loh, B.V.R. Chowdari, ACS Appl. Mater. Interfaces 6, 680–690 (2014)CrossRef M.V. Reddy, G. Prithvi, K.P. Loh, B.V.R. Chowdari, ACS Appl. Mater. Interfaces 6, 680–690 (2014)CrossRef
5.
Zurück zum Zitat Y.J. Zhang, Y. Yan, X.Y. Wang, G. Li, D.R. Deng, L. Jiang, C.Y. Shu, C.R. Wang, Chem. Eur. J. 20, 6126–6130 (2014)CrossRef Y.J. Zhang, Y. Yan, X.Y. Wang, G. Li, D.R. Deng, L. Jiang, C.Y. Shu, C.R. Wang, Chem. Eur. J. 20, 6126–6130 (2014)CrossRef
6.
Zurück zum Zitat S.M. Xu, C.M. Hessel, H. Ren, R.B. Yu, Q. Jin, M. Yang, H.J. Zhao, D. Wang, Energy Environ. Sci. 7, 632–637 (2014)CrossRef S.M. Xu, C.M. Hessel, H. Ren, R.B. Yu, Q. Jin, M. Yang, H.J. Zhao, D. Wang, Energy Environ. Sci. 7, 632–637 (2014)CrossRef
7.
Zurück zum Zitat X.W. Li, S.L. Xiong, J.F. Li, X. Liang, J.Z. Wang, J. Bai, Y.T. Qian, Chem. Eur. J. 19, 11310–11319 (2013)CrossRef X.W. Li, S.L. Xiong, J.F. Li, X. Liang, J.Z. Wang, J. Bai, Y.T. Qian, Chem. Eur. J. 19, 11310–11319 (2013)CrossRef
8.
Zurück zum Zitat F.C. Zheng, D.Q. Zhu, Q.W. Chen, ACS Appl. Mater. Interfaces 6, 9256–9264 (2014)CrossRef F.C. Zheng, D.Q. Zhu, Q.W. Chen, ACS Appl. Mater. Interfaces 6, 9256–9264 (2014)CrossRef
9.
Zurück zum Zitat D. Xie, W.W. Yuan, Z.M. Dong, Q.M. Su, J. Zhang, G.H. Du, Electrochim. Acta 92, 87–92 (2013)CrossRef D. Xie, W.W. Yuan, Z.M. Dong, Q.M. Su, J. Zhang, G.H. Du, Electrochim. Acta 92, 87–92 (2013)CrossRef
10.
Zurück zum Zitat G.P. Kim, S. Park, I. Nam, J. Park, J. Yi, J. Power Sources 237, 172–177 (2013)CrossRef G.P. Kim, S. Park, I. Nam, J. Park, J. Yi, J. Power Sources 237, 172–177 (2013)CrossRef
11.
Zurück zum Zitat D. Xie, Q.M. Su, Z.M. Dong, J. Zhang, G.H. Du, CrystEngComm 15, 8314–8319 (2013)CrossRef D. Xie, Q.M. Su, Z.M. Dong, J. Zhang, G.H. Du, CrystEngComm 15, 8314–8319 (2013)CrossRef
12.
Zurück zum Zitat J.H. Pan, Q.Z. Huang, Z.Y. Koh, D. Neo, X.Z. Wang, Q. Wang, ACS Appl. Mater. Interfaces 5, 6292–6299 (2013)CrossRef J.H. Pan, Q.Z. Huang, Z.Y. Koh, D. Neo, X.Z. Wang, Q. Wang, ACS Appl. Mater. Interfaces 5, 6292–6299 (2013)CrossRef
13.
Zurück zum Zitat H. Liu, G.X. Wang, J. Liu, S.Z. Qiao, H.J. Ahn, J. Mater. Chem. 21, 3046–3052 (2011)CrossRef H. Liu, G.X. Wang, J. Liu, S.Z. Qiao, H.J. Ahn, J. Mater. Chem. 21, 3046–3052 (2011)CrossRef
14.
Zurück zum Zitat X.H. Wang, X.W. Li, X.L. Sun, F. Li, Q.M. Liu, Q. Wang, D.Y. He, J. Mater. Chem. 21, 3571–3573 (2011)CrossRef X.H. Wang, X.W. Li, X.L. Sun, F. Li, Q.M. Liu, Q. Wang, D.Y. He, J. Mater. Chem. 21, 3571–3573 (2011)CrossRef
15.
Zurück zum Zitat Z.C. Bai, Z.C. Ju, C.L. Guo, Y.T. Qian, B. Tang, S.L. Xiong, Nanoscale 6, 3268–3273 (2014)CrossRef Z.C. Bai, Z.C. Ju, C.L. Guo, Y.T. Qian, B. Tang, S.L. Xiong, Nanoscale 6, 3268–3273 (2014)CrossRef
16.
Zurück zum Zitat M. Sasidharan, N. Gunawardhana, C. Senthil, M. Yoshio, J. Mater. Chem. A 2, 7337–7344 (2014)CrossRef M. Sasidharan, N. Gunawardhana, C. Senthil, M. Yoshio, J. Mater. Chem. A 2, 7337–7344 (2014)CrossRef
17.
Zurück zum Zitat N.N. Wang, L. Chen, X.J. Ma, J. Yue, F.E. Niu, H.Y. Xu, J. Yang, Y.T. Qian, J. Mater. Chem. A 2, 16847–16850 (2014)CrossRef N.N. Wang, L. Chen, X.J. Ma, J. Yue, F.E. Niu, H.Y. Xu, J. Yang, Y.T. Qian, J. Mater. Chem. A 2, 16847–16850 (2014)CrossRef
18.
Zurück zum Zitat H. Huang, J.P. Tu, C.Q. Zhang, F. Zhou, Electrochim. Acta 55, 8981–8985 (2010)CrossRef H. Huang, J.P. Tu, C.Q. Zhang, F. Zhou, Electrochim. Acta 55, 8981–8985 (2010)CrossRef
19.
Zurück zum Zitat L. Hu, Y.K. Sun, F.P. Zhang, Q.W. Chen, J. Alloys Compd. 576, 86–92 (2013)CrossRef L. Hu, Y.K. Sun, F.P. Zhang, Q.W. Chen, J. Alloys Compd. 576, 86–92 (2013)CrossRef
20.
Zurück zum Zitat J.B. Zhu, L.F. Bai, Y.F. Sun, X.D. Zhang, Q.Y. Li, B.X. Cao, W.S. Yan, Y. Xie, Nanoscale 5, 5241–5246 (2013)CrossRef J.B. Zhu, L.F. Bai, Y.F. Sun, X.D. Zhang, Q.Y. Li, B.X. Cao, W.S. Yan, Y. Xie, Nanoscale 5, 5241–5246 (2013)CrossRef
21.
Zurück zum Zitat X. Zhang, Y.T. Qian, Y.C. Zhu, K.B. Tang, Nanoscale 6, 1725–1731 (2014)CrossRef X. Zhang, Y.T. Qian, Y.C. Zhu, K.B. Tang, Nanoscale 6, 1725–1731 (2014)CrossRef
22.
Zurück zum Zitat F.C. Zheng, D.Q. Zhu, X.H. Shi, Q.W. Chen, J. Mater. Chem. A 3, 2815–2824 (2015)CrossRef F.C. Zheng, D.Q. Zhu, X.H. Shi, Q.W. Chen, J. Mater. Chem. A 3, 2815–2824 (2015)CrossRef
23.
24.
Zurück zum Zitat X.H. Zhang, Z.B. Yang, X.L. Sun, X.W. Li, D.S. Wang, P. Wang, D.Y. He, J. Chem. Chem. 21, 9988–9990 (2011) X.H. Zhang, Z.B. Yang, X.L. Sun, X.W. Li, D.S. Wang, P. Wang, D.Y. He, J. Chem. Chem. 21, 9988–9990 (2011)
25.
Zurück zum Zitat B. Wang, J.L. Cheng, Y.P. Wu, D. Wang, D.N. He, Electrochem. Commun. 23, 5–8 (2012)CrossRef B. Wang, J.L. Cheng, Y.P. Wu, D. Wang, D.N. He, Electrochem. Commun. 23, 5–8 (2012)CrossRef
26.
Zurück zum Zitat X.H. Sun, X.W. Li, X.L. Sun, F. Li, Q.M. Liu, Q. Wang, D.Y. He, J. Mater. Chem. 21, 3571–3573 (2011)CrossRef X.H. Sun, X.W. Li, X.L. Sun, F. Li, Q.M. Liu, Q. Wang, D.Y. He, J. Mater. Chem. 21, 3571–3573 (2011)CrossRef
27.
Zurück zum Zitat X.H. Wang, L. Qiao, X.L. Sun, D.K. Hu, Q. Zhang, D.Y. He, J. Mater. Chem. A 1, 4173–4176 (2013)CrossRef X.H. Wang, L. Qiao, X.L. Sun, D.K. Hu, Q. Zhang, D.Y. He, J. Mater. Chem. A 1, 4173–4176 (2013)CrossRef
28.
Zurück zum Zitat X.N. Li, Y.C. Zhu, X. Zhang, J.W. Liang, Y.T. Qian, RSC Adv. 3, 10001–10006 (2013)CrossRef X.N. Li, Y.C. Zhu, X. Zhang, J.W. Liang, Y.T. Qian, RSC Adv. 3, 10001–10006 (2013)CrossRef
29.
Zurück zum Zitat C.X. Yang, Q.M. Gao, W.Q. Tian, Y.L. Tan, T. Zhang, K. Yang, L.H. Zhu, J. Mater. Chem. A 2, 19975–19982 (2014)CrossRef C.X. Yang, Q.M. Gao, W.Q. Tian, Y.L. Tan, T. Zhang, K. Yang, L.H. Zhu, J. Mater. Chem. A 2, 19975–19982 (2014)CrossRef
30.
Zurück zum Zitat Y.J. Mai, S.G. Shi, D. Zhang, Y. Lu, C.D. Gu, J.P. Tu, J. Power Sources 204, 155 (2012)CrossRef Y.J. Mai, S.G. Shi, D. Zhang, Y. Lu, C.D. Gu, J.P. Tu, J. Power Sources 204, 155 (2012)CrossRef
31.
Zurück zum Zitat F.C. Zheng, M.N. He, Y. Yang, Q.W. Chen, Nanoscale 7, 3410–3417 (2015)CrossRef F.C. Zheng, M.N. He, Y. Yang, Q.W. Chen, Nanoscale 7, 3410–3417 (2015)CrossRef
32.
Zurück zum Zitat G.H. Zhang, Y.J. Chen, B.H. Qu, L.L. Hu, L. Mei, D.N. Lei, Q. Li, L.B. Chen, Q.H. Li, T.H. Wang, Electrochim. Acta 80, 140–147 (2012)CrossRef G.H. Zhang, Y.J. Chen, B.H. Qu, L.L. Hu, L. Mei, D.N. Lei, Q. Li, L.B. Chen, Q.H. Li, T.H. Wang, Electrochim. Acta 80, 140–147 (2012)CrossRef
33.
Zurück zum Zitat S.M. Abbas, S.T. Hussain, S. Ali, K.S. Munawar, N. Ahmad, N. Ali, Mater. Lett. 107, 158–161 (2013)CrossRef S.M. Abbas, S.T. Hussain, S. Ali, K.S. Munawar, N. Ahmad, N. Ali, Mater. Lett. 107, 158–161 (2013)CrossRef
Metadaten
Titel
Facile fabrication of hierarchically porous NiO microspheres as anode materials for lithium ion batteries
verfasst von
Fangcai Zheng
Shihao Xu
Yuanguang Zhang
Publikationsdatum
02.01.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 4/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-015-4194-6

Weitere Artikel der Ausgabe 4/2016

Journal of Materials Science: Materials in Electronics 4/2016 Zur Ausgabe

Neuer Inhalt