Facile synthesis of α-MnO2 nanowires/spherical activated carbon composite for supercapacitor application in aqueous neutral electrolyte

verfasst von: Zesheng Li, Zhenghui Liu, Dehao Li, Bolin Li, Qingyu Li, Youguo Huang, Hongqiang Wang

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 1/2015

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

One-dimensional (1-D) α-MnO2 nanowires/spherical activated carbon composite, namely the α-MnO2 nanowires growth onto the surface of activated mesocarbon microbeads (a-MCMB), has been prepared by using a simple hydrothermal synthesis method. The α-MnO2 nanowires are found to be less than 50 nm in diameter and have a characteristic length up to 2 μm. The novel α-MnO2 nanowires/a-MCMB composite when used for supercapacitor electrode material exhibits a specific capacitance (C s) of 357 F g−1 in 1 M Na2SO4 aqueous neutral solution. The C s based on the α-MnO2 nanowires is estimated to be as high as 890 F g−1. A good cycling stability of this composite material is also demonstrated for supercapacitor application.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat F. Wang, S. Xiao, Y. Hou, C. Hu, L. Liu, Y. Wu, RSC Adv. 3, 13059–13084 (2013)CrossRef F. Wang, S. Xiao, Y. Hou, C. Hu, L. Liu, Y. Wu, RSC Adv. 3, 13059–13084 (2013)CrossRef
2.
Zurück zum Zitat K. Jia, X. Zhuang, B. Cheng, S. Shi, Z. Shi, B. Zhang, J. Mater. Sci.: Mater. Electron. 24, 4769–4773 (2013) K. Jia, X. Zhuang, B. Cheng, S. Shi, Z. Shi, B. Zhang, J. Mater. Sci.: Mater. Electron. 24, 4769–4773 (2013)
3.
Zurück zum Zitat L. Yang, M. Li, Y. Zhang, K. Yi, J. Ma, Y. Liu, J. Mater. Sci.: Mater. Electron. 25, 1047–1052 (2014) L. Yang, M. Li, Y. Zhang, K. Yi, J. Ma, Y. Liu, J. Mater. Sci.: Mater. Electron. 25, 1047–1052 (2014)
4.
Zurück zum Zitat C. Lei, N. Amini, F. Markoulidis, P. Wilson, S. Tennisonb, C. Lekakou, J. Mater. Chem. A 1, 6037–6042 (2013)CrossRef C. Lei, N. Amini, F. Markoulidis, P. Wilson, S. Tennisonb, C. Lekakou, J. Mater. Chem. A 1, 6037–6042 (2013)CrossRef
5.
Zurück zum Zitat M. Jeong, K. Zhuo, S. Cherevko, W. Kim, C. Chung, J. Power Sources 244, 806–811 (2013)CrossRef M. Jeong, K. Zhuo, S. Cherevko, W. Kim, C. Chung, J. Power Sources 244, 806–811 (2013)CrossRef
6.
7.
Zurück zum Zitat X. Zhang, D. Zhao, Y. Zhao, P. Tang, Y. Shen, C. Xu, H. Lia, Y. Xiao, J. Mater. Chem. A 1, 3706–3712 (2013)CrossRef X. Zhang, D. Zhao, Y. Zhao, P. Tang, Y. Shen, C. Xu, H. Lia, Y. Xiao, J. Mater. Chem. A 1, 3706–3712 (2013)CrossRef
8.
Zurück zum Zitat Q. Li, Z. Wang, G. Li, R. Guo, L. Ding, Y. Tong, Nano Lett. 12, 3803–3807 (2012)CrossRef Q. Li, Z. Wang, G. Li, R. Guo, L. Ding, Y. Tong, Nano Lett. 12, 3803–3807 (2012)CrossRef
9.
Zurück zum Zitat X. Lu, M. Yu, G. Wang, T. Zhai, S. Xie, Y. Ling, Y. Tong, Y. Li, Adv. Mater. 25, 267–272 (2013)CrossRef X. Lu, M. Yu, G. Wang, T. Zhai, S. Xie, Y. Ling, Y. Tong, Y. Li, Adv. Mater. 25, 267–272 (2013)CrossRef
10.
Zurück zum Zitat Z. Yu, B. Duong, D. Abbitt, J. Thomas, Adv. Mater. 25, 3302–3306 (2013)CrossRef Z. Yu, B. Duong, D. Abbitt, J. Thomas, Adv. Mater. 25, 3302–3306 (2013)CrossRef
11.
Zurück zum Zitat L. Chen, J. Kang, Y. Hou, P. Liu, T. Fujita, A. Hirataa, M. Chen, J. Mater. Chem. A 1, 9202–9207 (2013)CrossRef L. Chen, J. Kang, Y. Hou, P. Liu, T. Fujita, A. Hirataa, M. Chen, J. Mater. Chem. A 1, 9202–9207 (2013)CrossRef
12.
Zurück zum Zitat X. Lang, A. Hirata, T. Fujita, M. Chen, Nat. Nanotechnol. 6, 232–236 (2011)CrossRef X. Lang, A. Hirata, T. Fujita, M. Chen, Nat. Nanotechnol. 6, 232–236 (2011)CrossRef
13.
Zurück zum Zitat Y. Huang, Y. Li, Z. Hu, G. Wei, J. Guo, J. Liu, J. Mater. Chem. A 1, 9809–9813 (2013)CrossRef Y. Huang, Y. Li, Z. Hu, G. Wei, J. Guo, J. Liu, J. Mater. Chem. A 1, 9809–9813 (2013)CrossRef
14.
Zurück zum Zitat F. Xiao, Y. Xu, J. Mater. Sci.: Mater. Electron. 24, 1913–1920 (2013) F. Xiao, Y. Xu, J. Mater. Sci.: Mater. Electron. 24, 1913–1920 (2013)
15.
16.
Zurück zum Zitat H. Wang, Z. Li, J. Yang, Q. Li, X. Zhong, J. Power Sources 194, 1218–1221 (2009)CrossRef H. Wang, Z. Li, J. Yang, Q. Li, X. Zhong, J. Power Sources 194, 1218–1221 (2009)CrossRef
17.
Zurück zum Zitat F. Li, W. Chi, Z. Shen, Y. Wu, Y. Liu, H. Liu, Fuel Process. Technol. 91, 17–24 (2010)CrossRef F. Li, W. Chi, Z. Shen, Y. Wu, Y. Liu, H. Liu, Fuel Process. Technol. 91, 17–24 (2010)CrossRef
18.
19.
Zurück zum Zitat T. Brousse, M. Toupin, R. Dugas, L. Athouël, O. Crosnier, D. Bélanger, J. Electrochem. Soc. 153, A2171–A2180 (2006)CrossRef T. Brousse, M. Toupin, R. Dugas, L. Athouël, O. Crosnier, D. Bélanger, J. Electrochem. Soc. 153, A2171–A2180 (2006)CrossRef
20.
Zurück zum Zitat S. Devaraj, N. Munichandraiah, J. Phys. Chem. C 112, 4406–4417 (2008)CrossRef S. Devaraj, N. Munichandraiah, J. Phys. Chem. C 112, 4406–4417 (2008)CrossRef
21.
22.
Zurück zum Zitat H. Wang, F. Xiao, L. Yu, B. Liu, X.W. Lou, Small 10, 3181–3186 (2014)CrossRef H. Wang, F. Xiao, L. Yu, B. Liu, X.W. Lou, Small 10, 3181–3186 (2014)CrossRef
23.
Zurück zum Zitat S. Pang, M. Anderson, T. Chapm, J. Electrochem. Soc. 147, 444–450 (2000)CrossRef S. Pang, M. Anderson, T. Chapm, J. Electrochem. Soc. 147, 444–450 (2000)CrossRef
24.
Zurück zum Zitat X. Yang, Y. Wang, H. Xiong, Y. Xia, Electrochim. Acta 53, 752–757 (2007)CrossRef X. Yang, Y. Wang, H. Xiong, Y. Xia, Electrochim. Acta 53, 752–757 (2007)CrossRef
25.
Zurück zum Zitat M. Huang, S. Mao, H. Feick, H. Yan, Y. Wu, H. Kind, E. Weber, R. Russo, P. Yang, Science 292, 1897–1899 (2001)CrossRef M. Huang, S. Mao, H. Feick, H. Yan, Y. Wu, H. Kind, E. Weber, R. Russo, P. Yang, Science 292, 1897–1899 (2001)CrossRef
Metadaten
Titel
Facile synthesis of α-MnO2 nanowires/spherical activated carbon composite for supercapacitor application in aqueous neutral electrolyte
verfasst von
Zesheng Li
Zhenghui Liu
Dehao Li
Bolin Li
Qingyu Li
Youguo Huang
Hongqiang Wang
Publikationsdatum
01.01.2015
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 1/2015
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-014-2407-z

Weitere Artikel der Ausgabe 1/2015

Journal of Materials Science: Materials in Electronics 1/2015 Zur Ausgabe

Neuer Inhalt