Failure Analysis of an 18% Cr Ferritic Stainless Steel in a Simulated Exhaust Condensate Containing Urea
Erschienen in: Journal of Failure Analysis and Prevention | Ausgabe 1/2018
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Exposure in the laboratory simulating a selective catalytic exhaust system component using urea injection for NO
x
reduction and an artificial exhaust condensate in a diesel application has been performed. The hot, cyclic corrosion test was designed to simulate the conditions seen during use in a commercial vehicle application. The sample was subjected to a cyclic thermal gradient from ambient to a high of 500 °C and a 5% solution of urea containing sulfates, chlorides, and nitrates. During material evaluation for a selective catalytic exhaust component, a perforation was observed in a 439 ferritic stainless steel component. Examination of the sample found multiple modes of failure and multiple types of deposits from the urea test solution.