Failure Mode Changes with Successive Component Improvements

verfasst von: D. H. Stone

Erschienen in: Journal of Failure Analysis and Prevention | Ausgabe 4/2016

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The relatively recent appearance of formerly rare vertical split rim wheel failures provides a good case study of how a shift in failure mode occurs when a material improvement is made to solve an existing problem. The mode of railroad wheel failures have changed three times over the past 40 years when the dominate failure mode has been identified and corrected. When the principal failure mode has been corrected the service life increases, but a new or previously minor failure mode assumes the role of principle failure cause. Because of the large population of railroad wheels in North American service, failure trends can be easily observed. This paper will discuss the evolution of failure mode with successive material and structural improvements.

Vorheriger Artikel Complexity of Understanding the Failure of Aerospace Composite Structures

Nächster Artikel Analysis of Frequent Failure of Oil Well Tubings Due to Formation of Longitudinal Slit

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

J.L. VanSwaaij, The mechanism of thermal cracking in railway wheels. Proceedings of the 3rd International Wheelset Congress, Sheffield, 1969, paper V.4

H.C. Iwand, D.H. Stone, G.J. Moyar, A theoretical and metallurgical model of martensite formation and tread spalling during wheel skid, Rail Transportation-1992, RTD, Vol. 5, (ASME, New York, 1992) pp. 105–116

D.H. Stone, Wheel failures due to brake heating—experience and solutions. Proceedings of the 8th International Wheelset Congress, Madrid, 1985 paper V.4

D.H. Stone, An interpretive review of wheel failure performance with respect to design and heat treatment. Proceedings of the 1988 ASME-IEEE Joint Railroad Conference, (ASME, New York, 1988) pp. 43–54

G.E. Novak, L.P. Greenfield, and D.H. Stone, Simulated operating stresses in 28-in. diameter wheels, ASME Paper 75-RT-10, April, 1975

Standard S-660, Wheel designs-locomotive and freight car-analytic evaluation, Manual of Standards and Recommended Practices, Section G, (Association of American Railroads, Washington, 2007)

S. Beretta, R. Roberti, A. Ghidini, G. Donzella, Deep shelling in railway wheels. Proceedings of the 12th International Wheelset Congress, Rome, September, 2001, Paper 23

Atlas of Wheel and Rail Defects, International Union of Railways (Paris, 2004) pp. 9–10

J.M. Galbraith, R.J. Fruehan, G.S. Casuccio, M.S. Potter, H. Matsuura, C.P. Lonsdale, Application of rapid inclusion identification and analysis to railway wheel steel microcleanliness. Proceedings of the 15th International Wheelset Congress, Prague, 2007

10.

A. Meddah, D.H. Stone, A neural network analysis of the causes of vertical split rim wheel failure. Proceedings of the 17th International Wheelset Congress, Kiev, 2013, Paper 1–1

11.

J. Kristan, D.H. Stone, J. Elkins, Effect of wheel loading on the occurrence of vertical split rim wheel failures. Proceedings of IMECHE 2004, (ASME, New York, 2004) Paper IMECE2004-59049

12.

C.P. Lonsdale, J. Oliver, Further research into wheel rim axial residual stress and vertical split rim failures, ASME Paper JRC2012-74010, April, 2012

13.

S.L. Dedmon, T. Fujimura, D.H. Stone, The effect of deformation on mechanical properties and shakedown of railroad wheels. ASME Paper JRC2014-3813, April, 2014

Titel: Failure Mode Changes with Successive Component Improvements
verfasst von: D. H. Stone
Publikationsdatum: 01.08.2016
Verlag: Springer US
Erschienen in: Journal of Failure Analysis and Prevention / Ausgabe 4/2016
Print ISSN: 1547-7029
Elektronische ISSN: 1864-1245
DOI: https://doi.org/10.1007/s11668-016-0126-x

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Springer Professional "Wirtschaft+Technik"

Weitere Artikel der Ausgabe 4/2016

Training

Finite Element Analysis of Laser Cut Edge Beam Section for High Stress Intensity Structural Assessment

Effect of Fatigue Damage Parameter on the Cumulative Life of a Turbine Rotor Under Multiaxial Loading

Prediction of Stress Intensity Factor on Precracked Composite Wing Rib Made up of Carbon-Epoxy IM7-8552

Events

A Degradation Feature Extraction Method for Hydraulic Pumps Based Upon MUWDF and MF-DFA

Premium Partner

Marktübersichten