01.02.2017 | Case History---Peer-Reviewed | Ausgabe 1/2017 Open Access

Journal of Failure Analysis and Prevention 1/2017

Fatigue Failure of a 2500-Ton Forge Press

Zeitschrift:
Journal of Failure Analysis and Prevention > Ausgabe 1/2017
Autoren:
Nicoli Ames, Joseph Lemberg, Robert Caligiuri

Abstract

Large industrial equipment can fail spectacularly, and analyzing the failure can prove difficult, as catastrophic failures can provide red herrings that confound the failure analysis. One such case involved the fatigue failure of a 2500-ton forge press. During operation, two tie rods failed, leading to catastrophic failure of the press. During post-mortem analysis, several fatigue cracks were found in the upper platen of the forge press and misalignment of some of the tie rod nuts was observed. Finite element modeling revealed that the presence of the platen fatigue cracks and the misaligned nuts had little effect on the fatigue behavior of the press. Instead, the high strength of the two failed tie rods led to higher-than-intended service stresses in these tie rods and resulted in a reduced fatigue life.

Unsere Produktempfehlungen

Premium-Abo der Gesellschaft für Informatik

Sie erhalten uneingeschränkten Vollzugriff auf alle acht Fachgebiete von Springer Professional und damit auf über 45.000 Fachbücher und ca. 300 Fachzeitschriften.

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 1/2017

Journal of Failure Analysis and Prevention 1/2017 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise