Formation of VKNA-4U powder alloy using the SPS technology with preliminary mechanical activation

verfasst von: Liliya I. Shevtsova, Maksim A. Esikov, Vladimir N. Malikov, Ruslan I. Kuz’min

Erschienen in: Metallurgist | Ausgabe 5/2024

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The results of structural studies and assessment of the bending strength of a VKNA-4U alloy based on nickel aluminide are presented. It is for the first time that this alloy was produced by spark plasma sintering of mechanically activated powders of the starting components. The mechanical activation of the powders lasted for 1.5, 3.5, and 5 min. X‑ray diffraction analysis was performed to determine the optimal duration (3 min 30 sec) of mechanical activation for this alloy. To obtain a dense low-defect workpiece, the VKNA-4U alloy was sintered at a heating temperature of 1100 °C, a pressure of 40 MPa, and a holding time of 5 min. This material has higher ultimate bending strength at room temperature (σbend = 1215 ± 65 MPa) than the strength of Ni3Al intermetallic compound produced in similar conditions and microhardness 690 ± 25 HV.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Nochovnaya NA, Bazyleva OA, Kablov DE, Panin PV (2018) Intermetallic Alloys Based on Titanium and Nickel. Izd. VIAM, Moscow Nochovnaya NA, Bazyleva OA, Kablov DE, Panin PV (2018) Intermetallic Alloys Based on Titanium and Nickel. Izd. VIAM, Moscow
2.
Zurück zum Zitat Taub AI, Fleischer RL (1989) Intermetallic compounds for high-temperature structural use. Science 243(4891):616–621CrossRefPubMed Taub AI, Fleischer RL (1989) Intermetallic compounds for high-temperature structural use. Science 243(4891):616–621CrossRefPubMed
6.
Zurück zum Zitat Grinberg BA, Ivanov MA (2002) Intermetallic Compounds Ni3Al and TiAl: Microstructure, Deformation Behavior. UrO RAN, Yekaterinburg Grinberg BA, Ivanov MA (2002) Intermetallic Compounds Ni3Al and TiAl: Microstructure, Deformation Behavior. UrO RAN, Yekaterinburg
7.
Zurück zum Zitat Kablov EN, Ospennikova OG, Bazyleva OA (2011) “Materials for highly thermally loaded parts of gas-turbine engines,” Vestn. MGTU im. N. E. Baumana, Ser. Mashinostr SP2:13–19 Kablov EN, Ospennikova OG, Bazyleva OA (2011) “Materials for highly thermally loaded parts of gas-turbine engines,” Vestn. MGTU im. N. E. Baumana, Ser. Mashinostr SP2:13–19
8.
Zurück zum Zitat Bazyleva OA, Arginbaeva EG, Yu. Turenko E (2013) High-temperature intermetallic alloys for GTE parts. Aviats Mater Tekhnol No 3:26–31 Bazyleva OA, Arginbaeva EG, Yu. Turenko E (2013) High-temperature intermetallic alloys for GTE parts. Aviats Mater Tekhnol No 3:26–31
10.
Zurück zum Zitat Ospennikova OG, Bazyleva OA, Arginbaeva EG et al (2017) “Creation of intermetallic nickel alloys and their composite materials,” Vestn. MGTU im. N. E. Baumana, Ser. Mashinostr 3:75–89 Ospennikova OG, Bazyleva OA, Arginbaeva EG et al (2017) “Creation of intermetallic nickel alloys and their composite materials,” Vestn. MGTU im. N. E. Baumana, Ser. Mashinostr 3:75–89
11.
Zurück zum Zitat Kotoban D, Nazarova A, Shishkovsky I (2017) Comparative study of selective laser melting and direct laser metal deposition of Ni3Al intermetallic alloy. Procedia IUTAM 23:138–146CrossRef Kotoban D, Nazarova A, Shishkovsky I (2017) Comparative study of selective laser melting and direct laser metal deposition of Ni3Al intermetallic alloy. Procedia IUTAM 23:138–146CrossRef
12.
Zurück zum Zitat Korchagin MA, Grigor’eva TF, Bokhonov BB et al (2002) Mechanical activation and self-propagating high-temperature synthesis in producing monophase fine-grained intermetallic compounds. Vopr Materialoved 1(29):418–423 Korchagin MA, Grigor’eva TF, Bokhonov BB et al (2002) Mechanical activation and self-propagating high-temperature synthesis in producing monophase fine-grained intermetallic compounds. Vopr Materialoved 1(29):418–423
15.
Zurück zum Zitat Makena IM, Shongwe MB, Ramakokovhu MM et al (2017) A review on sintered nickel-based alloys. In: Proc. World Congress on Engineering, vol 2: 922–927 Makena IM, Shongwe MB, Ramakokovhu MM et al (2017) A review on sintered nickel-based alloys. In: Proc. World Congress on Engineering, vol 2: 922–927
16.
Zurück zum Zitat Dudina DV (2020) Modern Powder Sintering Methods: Features of Structurization of Sintered Materials. NGTU, Novosibirsk Dudina DV (2020) Modern Powder Sintering Methods: Features of Structurization of Sintered Materials. NGTU, Novosibirsk
17.
Zurück zum Zitat Tokita M (1993) Trends in advanced SPS (spark plasma sintering) systems and technology. J Soc Powd Tech Japan 30(11):790–804CrossRef Tokita M (1993) Trends in advanced SPS (spark plasma sintering) systems and technology. J Soc Powd Tech Japan 30(11):790–804CrossRef
18.
Zurück zum Zitat Shevtsova LI (2014) Structure and mechanical properties of Ni3Al intermetallic compound produced by spark plasma sintering of mechanically activated Ni–Al powder mixture. Obrab Met (tekhnol Oborud Instr) No 3(64):21–27 Shevtsova LI (2014) Structure and mechanical properties of Ni3Al intermetallic compound produced by spark plasma sintering of mechanically activated Ni–Al powder mixture. Obrab Met (tekhnol Oborud Instr) No 3(64):21–27
26.
Zurück zum Zitat Sintered Hard Alloys Method of Determination of Density. Izd. Standartov, Moscow, pp 20018–20074 Sintered Hard Alloys Method of Determination of Density. Izd. Standartov, Moscow, pp 20018–20074
Metadaten
Titel
Formation of VKNA-4U powder alloy using the SPS technology with preliminary mechanical activation
verfasst von
Liliya I. Shevtsova
Maksim A. Esikov
Vladimir N. Malikov
Ruslan I. Kuz’min
Publikationsdatum
05.09.2024
Verlag
Springer US
Erschienen in
Metallurgist / Ausgabe 5/2024
Print ISSN: 0026-0894
Elektronische ISSN: 1573-8892
DOI
https://doi.org/10.1007/s11015-024-01781-8

Weitere Artikel der Ausgabe 5/2024

Metallurgist 5/2024 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.