High-boiling-point solvent synthesis of mesoporous NiCo2S4 with high specific surface area as supercapacitor electrode material
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 2/2017
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
A facile synthesis approach was successfully developed to synthesize mesoporous NiCo2S4 in ethylene glycol. X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, and N2 adsorption–desorption experiment were conducted to examine the morphology and microstructure of the as-prepared NiCo2S4. Furthermore, electrochemical measurements, including cyclic voltammetry, galvanostatic charge–discharge tests, and electrochemical impedance spectroscopy, were carried out in a three-electrode system to evaluate the electrochemical properties of the mesoporous NiCo2S4. The as-prepared NiCo2S4 possessed a high specific surface area of 223.6 m2 g−1 with a high specific capacity of 406 C g−1 at 0.5 A g−1. In addition, only a 6.3 % loss of specific capacity was observed at 5 A g−1 after 20,000 GCD cycles, suggesting a long life cycle.