High filling alumina/epoxy nanocomposite as coating layer for Fe-based amorphous powder cores with enhanced magnetic performance

verfasst von: Yiqun Zhang, Yaqiang Dong, Lei Liu, Liang Chang, Bang Zhou, Qiang Chi, Xinmin Wang

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 16/2019

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

A high-filling alumina/epoxy nanocomposite with improved thermal stability and insulation performance has been successfully designed as an organic–inorganic coating layer for the toroid-shaped FeSiBPNbCr amorphous magnetic powder cores (AMPCs). Unlike the organic coating, the organic–inorganic hybrid coating cores exhibited superior magnetic properties without compromising on saturation magnetization and permeability. The core loss declined by 40%, and the quality factor was 13% higher as half alumina was introduced into the epoxy resin matrix. A thin and uniform-coating layer of alumina/epoxy nanocomposite led to better high-frequency characteristics than those obtained with direct coating of the cores with alumina. Besides the outstanding magnetic properties, the Fe-based AMPCs with a convenient insulation-coating process cost lesser than Fe–Ni magnetic powder cores, thereby rendering the Fe-based AMPCs a potential candidate for a variety of industrial applications.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat H. Shokrollahi, K. Janghorban, J. Mater. Process. Technol. 189, 1–12 (2007)CrossRef H. Shokrollahi, K. Janghorban, J. Mater. Process. Technol. 189, 1–12 (2007)CrossRef
3.
4.
Zurück zum Zitat E.A. Périgo, B. Weidenfeller, P. Kollár, J. Füzer, Appl. Phys. Rev. 5, 031301 (2018)CrossRef E.A. Périgo, B. Weidenfeller, P. Kollár, J. Füzer, Appl. Phys. Rev. 5, 031301 (2018)CrossRef
5.
6.
Zurück zum Zitat J.M. Silveyra, E. Ferrara, D.L. Huber, T.C. Monson, Science 362, 418 (2018)CrossRef J.M. Silveyra, E. Ferrara, D.L. Huber, T.C. Monson, Science 362, 418 (2018)CrossRef
7.
Zurück zum Zitat H. Chen, B.S. Dong, S.X. Zhou, X.X. Li, J.Y. Qin, Sci. Rep. 8, 5680 (2018)CrossRef H. Chen, B.S. Dong, S.X. Zhou, X.X. Li, J.Y. Qin, Sci. Rep. 8, 5680 (2018)CrossRef
8.
Zurück zum Zitat M. Yagi, I. Endo, I. Otsuka, H. Yamamoto, R. Okuno, H. Koshimoto, A. Shintani, J. Magn. Magn. Mater. 215, 284–287 (2000)CrossRef M. Yagi, I. Endo, I. Otsuka, H. Yamamoto, R. Okuno, H. Koshimoto, A. Shintani, J. Magn. Magn. Mater. 215, 284–287 (2000)CrossRef
9.
Zurück zum Zitat H.P. Xu, R.W. Wang, D. Wei, C. Zeng, J. Magn. Magn. Mater. 385, 326–330 (2015)CrossRef H.P. Xu, R.W. Wang, D. Wei, C. Zeng, J. Magn. Magn. Mater. 385, 326–330 (2015)CrossRef
10.
Zurück zum Zitat I. Otsuka, T. Kadomura, K. Ishiyama, M. Yagi, IEEE Trans. Magn. 45, 4294–4297 (2009)CrossRef I. Otsuka, T. Kadomura, K. Ishiyama, M. Yagi, IEEE Trans. Magn. 45, 4294–4297 (2009)CrossRef
11.
Zurück zum Zitat X.Y. Wang, C.W. Lu, F. Guo, Z.C. Lu, D.R. Li, S.X. Zhou, J. Magn. Magn. Mater. 324, 2727–2730 (2012)CrossRef X.Y. Wang, C.W. Lu, F. Guo, Z.C. Lu, D.R. Li, S.X. Zhou, J. Magn. Magn. Mater. 324, 2727–2730 (2012)CrossRef
12.
Zurück zum Zitat X.X. Zhong, J.C. Chen, L. Wang, B.J. Li, L.Z. Li, J. Alloys Compd. 735, 1603–1610 (2018)CrossRef X.X. Zhong, J.C. Chen, L. Wang, B.J. Li, L.Z. Li, J. Alloys Compd. 735, 1603–1610 (2018)CrossRef
13.
14.
Zurück zum Zitat H.J. Kim, K.S. Kim, J.J. Song, S.C. Yoon, S.I. Kim, K.Y. Sohn, NSTI Nano. 1, 581–583 (2011) H.J. Kim, K.S. Kim, J.J. Song, S.C. Yoon, S.I. Kim, K.Y. Sohn, NSTI Nano. 1, 581–583 (2011)
15.
Zurück zum Zitat A.H. Taghvaei, H. Shokrollahi, A. Ebrahimi, K. Janghorban, Mater. Chem. Phys. 116, 247–253 (2009)CrossRef A.H. Taghvaei, H. Shokrollahi, A. Ebrahimi, K. Janghorban, Mater. Chem. Phys. 116, 247–253 (2009)CrossRef
16.
Zurück zum Zitat M.M. Dias, H.J. Mozetic, J.S. Barboza, R.M. Martins, L. Pelegrini, L. Schaeffer, Pow. Tech. 237, 213–220 (2013)CrossRef M.M. Dias, H.J. Mozetic, J.S. Barboza, R.M. Martins, L. Pelegrini, L. Schaeffer, Pow. Tech. 237, 213–220 (2013)CrossRef
17.
Zurück zum Zitat Y.Y. Zheng, Y.G. Wang, G.T. Xia, J. Magn. Magn. Mater. 396, 97–101 (2015)CrossRef Y.Y. Zheng, Y.G. Wang, G.T. Xia, J. Magn. Magn. Mater. 396, 97–101 (2015)CrossRef
18.
Zurück zum Zitat L.W. Qian, J.G. Peng, Z. Xiang, Y.F. Pan, W. Lu, J. Alloys Compd. 778, 712–720 (2019)CrossRef L.W. Qian, J.G. Peng, Z. Xiang, Y.F. Pan, W. Lu, J. Alloys Compd. 778, 712–720 (2019)CrossRef
19.
Zurück zum Zitat L. Huan, X.L. Tang, H. Su, H.W. Zhang, Y.L. Jing, J. Mater. Sci. 26, 3275–3281 (2015) L. Huan, X.L. Tang, H. Su, H.W. Zhang, Y.L. Jing, J. Mater. Sci. 26, 3275–3281 (2015)
20.
21.
Zurück zum Zitat X.L. Li, Y.Q. Dong, M. Liu, C.T. Chang, X.M. Wang, J. Alloys Compd. 696, 1323–1328 (2017)CrossRef X.L. Li, Y.Q. Dong, M. Liu, C.T. Chang, X.M. Wang, J. Alloys Compd. 696, 1323–1328 (2017)CrossRef
22.
Zurück zum Zitat S. Nakahara, E.A. Périgo, Y. Pittini, Y. Hazan, T. Graule, Acta Mater. 58, 5695–5703 (2010)CrossRef S. Nakahara, E.A. Périgo, Y. Pittini, Y. Hazan, T. Graule, Acta Mater. 58, 5695–5703 (2010)CrossRef
23.
Zurück zum Zitat J.X. Li, J. Yu, W.C. Li, S.L. Che, J.W. Zheng, Q. Liang, Y. Yao, J. Magn. Magn. Mater. 454, 103–109 (2018)CrossRef J.X. Li, J. Yu, W.C. Li, S.L. Che, J.W. Zheng, Q. Liang, Y. Yao, J. Magn. Magn. Mater. 454, 103–109 (2018)CrossRef
24.
Zurück zum Zitat W.C. Li, W. Wang, J.J. Lv, Y. Ying, J. Yu, J.W. Zheng, Q. Liang, S.L. Che, J. Magn. Magn. Mater. 456, 333–340 (2018)CrossRef W.C. Li, W. Wang, J.J. Lv, Y. Ying, J. Yu, J.W. Zheng, Q. Liang, S.L. Che, J. Magn. Magn. Mater. 456, 333–340 (2018)CrossRef
25.
Zurück zum Zitat J. Lei, J.W. Zheng, H.D. Zheng, L. Qiao, Y. Ying, W. Cai, J. Magn. Magn. Mater. 472, 7–13 (2019)CrossRef J. Lei, J.W. Zheng, H.D. Zheng, L. Qiao, Y. Ying, W. Cai, J. Magn. Magn. Mater. 472, 7–13 (2019)CrossRef
26.
Zurück zum Zitat M. Strečková, Ľ. Medvecký, J. Füzer, P. Kollár, R. Bureš, M. Fáberová, Mater. Lett. 101, 37–40 (2013)CrossRef M. Strečková, Ľ. Medvecký, J. Füzer, P. Kollár, R. Bureš, M. Fáberová, Mater. Lett. 101, 37–40 (2013)CrossRef
27.
Zurück zum Zitat M. Strečková, T. Sopcáka, L. Medvecký, R. Bureš, M. Fáberováa, I. Batko, J. Briancin, Chem. Eng. J. 180, 343–353 (2012)CrossRef M. Strečková, T. Sopcáka, L. Medvecký, R. Bureš, M. Fáberováa, I. Batko, J. Briancin, Chem. Eng. J. 180, 343–353 (2012)CrossRef
28.
Zurück zum Zitat C. Wu, M.Q. Huang, D.H. Luo, Y.Z. Jiang, M. Yan, J. Alloys Compd. 741, 35–43 (2018)CrossRef C. Wu, M.Q. Huang, D.H. Luo, Y.Z. Jiang, M. Yan, J. Alloys Compd. 741, 35–43 (2018)CrossRef
29.
30.
Zurück zum Zitat Y.D. Peng, J.W. Nie, W.J. Zhang, J. Ma, C.X. Bao, Y. Cao, J. Magn. Magn. Mater. 399, 88–93 (2016)CrossRef Y.D. Peng, J.W. Nie, W.J. Zhang, J. Ma, C.X. Bao, Y. Cao, J. Magn. Magn. Mater. 399, 88–93 (2016)CrossRef
31.
Zurück zum Zitat K.J. Sunday, K.A. Darling, F.G. Hanejko, B. Anasori, Y.C. Liu, M.L. Taheri, J. Alloys Compd. 653, 61–68 (2015)CrossRef K.J. Sunday, K.A. Darling, F.G. Hanejko, B. Anasori, Y.C. Liu, M.L. Taheri, J. Alloys Compd. 653, 61–68 (2015)CrossRef
32.
Zurück zum Zitat C. Wu, X.W. Gao, G.L. Zhao, Y.Z. Jiang, M. Yan, J. Magn. Magn. Mater. 452, 114–119 (2018)CrossRef C. Wu, X.W. Gao, G.L. Zhao, Y.Z. Jiang, M. Yan, J. Magn. Magn. Mater. 452, 114–119 (2018)CrossRef
33.
Zurück zum Zitat M.S. Goyat, S. Ray, P.K. Ghosh, Compos. Part A 42, 1421–1431 (2011)CrossRef M.S. Goyat, S. Ray, P.K. Ghosh, Compos. Part A 42, 1421–1431 (2011)CrossRef
34.
Zurück zum Zitat K. Szendrei, W. Gomulya, M. Yarema, W. Heiss, M.A. Loi, Appl. Phys. Lett. 97, 115–119 (2010)CrossRef K. Szendrei, W. Gomulya, M. Yarema, W. Heiss, M.A. Loi, Appl. Phys. Lett. 97, 115–119 (2010)CrossRef
35.
Zurück zum Zitat M. G. Jonzalez, J. C. Cabanelas, Infra. Spec. (2011) M. G. Jonzalez, J. C. Cabanelas, Infra. Spec. (2011)
36.
Zurück zum Zitat Y. Pittini, E.A. Périgo, Y. Hazan, S. Nakahara, Acta Mater. 59, 4291–4302 (2011)CrossRef Y. Pittini, E.A. Périgo, Y. Hazan, S. Nakahara, Acta Mater. 59, 4291–4302 (2011)CrossRef
37.
Zurück zum Zitat T. Suzuki, P. Sharma, L. Jiang, Y. Zhang, A. Makino, IEEE Trans. Magn. 11, 1–5 (2018)CrossRef T. Suzuki, P. Sharma, L. Jiang, Y. Zhang, A. Makino, IEEE Trans. Magn. 11, 1–5 (2018)CrossRef
38.
Zurück zum Zitat W.C. Li, H.W. Cai, Y. Kang, Y. Ying, JYuJW Zheng, Q. Liang, Y. Jiang, S.L. Che, Acta Mater. 167, 267–274 (2019)CrossRef W.C. Li, H.W. Cai, Y. Kang, Y. Ying, JYuJW Zheng, Q. Liang, Y. Jiang, S.L. Che, Acta Mater. 167, 267–274 (2019)CrossRef
39.
41.
Zurück zum Zitat L. Huan, X.L. Tang, H. Su, H.W. Zhang, Y.L. Jing, B.Y. Liu, IEEE Trans. Magn. 50, 1–4 (2014)CrossRef L. Huan, X.L. Tang, H. Su, H.W. Zhang, Y.L. Jing, B.Y. Liu, IEEE Trans. Magn. 50, 1–4 (2014)CrossRef
Metadaten
Titel
High filling alumina/epoxy nanocomposite as coating layer for Fe-based amorphous powder cores with enhanced magnetic performance
verfasst von
Yiqun Zhang
Yaqiang Dong
Lei Liu
Liang Chang
Bang Zhou
Qiang Chi
Xinmin Wang
Publikationsdatum
15.07.2019
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 16/2019
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-019-01858-0

Weitere Artikel der Ausgabe 16/2019

Journal of Materials Science: Materials in Electronics 16/2019 Zur Ausgabe

Neuer Inhalt