Impact of calcination temperature on structural, optical, and magnetic properties of spinel CuFe2O4 for enhancing photocatalytic activity

verfasst von: V. Anto Feradrick Samson, S. Bharathi Bernadsha, M. Mahendiran, K. Leo Lawrence, J. Madhavan, M. Victor Antony Raj, S. Prathap

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 9/2020

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Variation in temperature during synthesis is a favorite aspect to get enhanced structural, optical, magnetic, and catalytic properties. Here, in this work, Spinel (CuFe2O4) ferrites were formulated with various calcination temperatures. The method used is a simple, economical, and eco-friendly microwave combustion method. Impact of annealing temperature on structural analysis is confirmed by XRD analysis. Under the following parameters, the structural changes are discussed: diametrical size, lattice parameter, strain, tetrahedral and octahedral hopping length, and bond length, respectively. HR-TEM results assure the spherical-shaped morphology. The average diametrical size calculated is in good agreement with the XRD results. The EDAX spectrum confirms the composition of sample and its purity. A FT-IR study exemplifies the ferrite characteristic peaks available as synthesized sample. The UV–Vis analysis and Tauc’s plot of the samples give us the optical bandgaps as 2.2, 2.1, and 2.08 eV, respectively. An increase in calcination temperature exhibits an enhancement in saturation magnetization (Ms), remnant magnetization (Mr), and coercivity (Hc) at room temperature. Degradation activity of methylene blue (MB) studied by catalyst CuF-MW, CuF-500, and CuF-600 expresses the degradation efficiency of the catalyst. CuF-MW exhibits an excellent result than other samples, due to large surface area and the small diametrical size.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat N.R. Dhineshbabu, R. Vettumperumal, A. Narendrakumar, M. Manimala, R.K. Rajesh, Adv. Sci. Eng. Med. 9(5), 377–383(7) (2017) N.R. Dhineshbabu, R. Vettumperumal, A. Narendrakumar, M. Manimala, R.K. Rajesh, Adv. Sci. Eng. Med. 9(5), 377–383(7) (2017)
2.
Zurück zum Zitat Q. Song, Z.J. Zhang, J. Am. Chem. Soc. 134(24), 10182–10190 (2012) Q. Song, Z.J. Zhang, J. Am. Chem. Soc. 134(24), 10182–10190 (2012)
3.
Zurück zum Zitat C. Liu, B. Zou, A.J. Rondinone, Z.J. Zhang, J. Phys. Chem. B 104(6), 1141–2114 (2000) C. Liu, B. Zou, A.J. Rondinone, Z.J. Zhang, J. Phys. Chem. B 104(6), 1141–2114 (2000)
4.
Zurück zum Zitat Q. Song, Z.J. Zhang, J. Am. Chem. Soc. 126(19), 6164–6168 (2004) Q. Song, Z.J. Zhang, J. Am. Chem. Soc. 126(19), 6164–6168 (2004)
5.
Zurück zum Zitat V.G. Harris, A. Geiler, Y. Chen, S.D. Yoon, M. Wu, A. Yang, Z. Chen, P. He, J. Magn. Magn. Mater. 321(14), 2035–2047 (2009) V.G. Harris, A. Geiler, Y. Chen, S.D. Yoon, M. Wu, A. Yang, Z. Chen, P. He, J. Magn. Magn. Mater. 321(14), 2035–2047 (2009)
6.
Zurück zum Zitat D. Carta, M.F. Casula, A. Falqui, D. Loche, G. Mountjoy, C. Sangregorio, A. Corrias, J. Phys. Chem. C 113(20), 8606–8615 (2009) D. Carta, M.F. Casula, A. Falqui, D. Loche, G. Mountjoy, C. Sangregorio, A. Corrias, J. Phys. Chem. C 113(20), 8606–8615 (2009)
7.
Zurück zum Zitat M.A. Willard, Y. Nakamura, D.E. Laughlin, M.E. McHenry, J. Am. Ceram. Soc. 82(12), 3342–3346 (1999) M.A. Willard, Y. Nakamura, D.E. Laughlin, M.E. McHenry, J. Am. Ceram. Soc. 82(12), 3342–3346 (1999)
8.
Zurück zum Zitat M.A. Laguna-Bercero, M.L. Sanjuán, R.I. Merino, J. Phys. 19, 18 (2007) M.A. Laguna-Bercero, M.L. Sanjuán, R.I. Merino, J. Phys. 19, 18 (2007)
9.
Zurück zum Zitat A. Sutka, G. Mezinskis, Front. Mater. Sci. 6(2), 128–141 (2012) A. Sutka, G. Mezinskis, Front. Mater. Sci. 6(2), 128–141 (2012)
10.
Zurück zum Zitat J.G.M.S. Machado, F.A. Brehm, C.A.M. Moraes, C.A. dosSantos, A.C.F. Vilela, J.B.M. daCunha, J. Hazard. Mater. 136(3), 953–960 (2006) J.G.M.S. Machado, F.A. Brehm, C.A.M. Moraes, C.A. dosSantos, A.C.F. Vilela, J.B.M. daCunha, J. Hazard. Mater. 136(3), 953–960 (2006)
11.
Zurück zum Zitat S. Mathur, M. Veith, M. Haas, H. Shen, N. Lecerf, V. Huch, S. Hüfner, R. Haberkorn, H.P. Beck, M. Jilavi, J. Am. Soc. 84(9), 1921–1928 (2001) S. Mathur, M. Veith, M. Haas, H. Shen, N. Lecerf, V. Huch, S. Hüfner, R. Haberkorn, H.P. Beck, M. Jilavi, J. Am. Soc. 84(9), 1921–1928 (2001)
12.
Zurück zum Zitat B.Z. Tang, Y. Geng, J.W.Y. Lam, B. Li, Chem. Mater. 11(6), 1581–1589 (1999) B.Z. Tang, Y. Geng, J.W.Y. Lam, B. Li, Chem. Mater. 11(6), 1581–1589 (1999)
13.
Zurück zum Zitat J.Z. Jiang, G.F. Goya, H.R. Rechenberg, J. Phys. 11, 20 (1999) J.Z. Jiang, G.F. Goya, H.R. Rechenberg, J. Phys. 11, 20 (1999)
14.
Zurück zum Zitat T. Zaki, D. Saed, D. Aman, S.A. Younis, Y.M. Moustafa, J. Sol-Gel Sci. Technol. 65(2), 269–276 (2013) T. Zaki, D. Saed, D. Aman, S.A. Younis, Y.M. Moustafa, J. Sol-Gel Sci. Technol. 65(2), 269–276 (2013)
15.
Zurück zum Zitat E. Solano, L. Perez-Mirabet, F. Martinez-Julian, R. Guzmán, J. Arbiol, T. Puig, X. Obradors, R. Yañez, A. Pomar, S. Ricart, J. Nanopart. Res. 14, 1034 (2012) E. Solano, L. Perez-Mirabet, F. Martinez-Julian, R. Guzmán, J. Arbiol, T. Puig, X. Obradors, R. Yañez, A. Pomar, S. Ricart, J. Nanopart. Res. 14, 1034 (2012)
16.
Zurück zum Zitat V.A.F. Samson, K.M. Racik, S. Prathap, Mater. Today Proc. 8(1), 386–392 (2019) V.A.F. Samson, K.M. Racik, S. Prathap, Mater. Today Proc. 8(1), 386–392 (2019)
17.
Zurück zum Zitat S. Vanetsev, V.K. Ivanov, Y.D. Doklady, Chemistry 387(4–6), 332–334 (2002) S. Vanetsev, V.K. Ivanov, Y.D. Doklady, Chemistry 387(4–6), 332–334 (2002)
18.
Zurück zum Zitat B.S.P.A. Kumar, K.H.V. Reddy, B. Madhav, K. Ramesh, Y.V.D. Nageswar, Tetrahedron Lett. 53(34), 4595–4599 (2012) B.S.P.A. Kumar, K.H.V. Reddy, B. Madhav, K. Ramesh, Y.V.D. Nageswar, Tetrahedron Lett. 53(34), 4595–4599 (2012)
19.
Zurück zum Zitat M. Akbar, Z. Mojgan, Lett. Org. Chem. 11(2), 152–157(6) (2014) M. Akbar, Z. Mojgan, Lett. Org. Chem. 11(2), 152–157(6) (2014)
20.
Zurück zum Zitat P. Laokul, V. Amornkitbamrung, S. Seraphin, S. Maensiri, Curr. Appl. Phys. 11(1), 101–108 (2011) P. Laokul, V. Amornkitbamrung, S. Seraphin, S. Maensiri, Curr. Appl. Phys. 11(1), 101–108 (2011)
22.
Zurück zum Zitat S.S. Selima, M. Khairy, M.A. Mousa, Ceram. Int. 45(5), 6535–6540 (2019) S.S. Selima, M. Khairy, M.A. Mousa, Ceram. Int. 45(5), 6535–6540 (2019)
23.
Zurück zum Zitat P. Amaliya, S. Anand, S. Pauline, J. Magn. Magn. Mater. 467, 14–28 (2018) P. Amaliya, S. Anand, S. Pauline, J. Magn. Magn. Mater. 467, 14–28 (2018)
24.
Zurück zum Zitat A. Kumar, A. Singh, M.S. Yadav, M. Arora, R.P. Pant, Thin Solid Films 519, 1056 (2010) A. Kumar, A. Singh, M.S. Yadav, M. Arora, R.P. Pant, Thin Solid Films 519, 1056 (2010)
25.
Zurück zum Zitat H.W. Wang, S.C. Kung, J. Magn. Magn. Mater. 270, 230 (2004) H.W. Wang, S.C. Kung, J. Magn. Magn. Mater. 270, 230 (2004)
26.
Zurück zum Zitat S. Zahi, M. Hashim, A.R. Daud, J. Magn. Magn. Mater. 308, 177 (2007) S. Zahi, M. Hashim, A.R. Daud, J. Magn. Magn. Mater. 308, 177 (2007)
27.
Zurück zum Zitat M.R. Uddin, M.R. Khan, M.W. Rahman, A. Yousuf, C.K. Cheng, React. Kinet. Mech. Catal. 116(2), 589–604 (2015) M.R. Uddin, M.R. Khan, M.W. Rahman, A. Yousuf, C.K. Cheng, React. Kinet. Mech. Catal. 116(2), 589–604 (2015)
28.
Zurück zum Zitat C. Karunakaran, S. SakthiRaadha, P. Gomathisankar, P. Vinayagamoorthy, RSC Adv. 3(37), 16728–16738 (2013) C. Karunakaran, S. SakthiRaadha, P. Gomathisankar, P. Vinayagamoorthy, RSC Adv. 3(37), 16728–16738 (2013)
29.
Zurück zum Zitat P.B. Pandya, H.H. Joshi, R.G. Kulkarni, J. Mater. Sci. Lett. 10(8), 474–476 (1991) P.B. Pandya, H.H. Joshi, R.G. Kulkarni, J. Mater. Sci. Lett. 10(8), 474–476 (1991)
30.
Zurück zum Zitat M. Estrella, L. Barrio, G. Zhou, X. Wang, Q. Wang, W. Wen, J.C. Hanson, A.I. Frenkel, J.A. Rodriguez, J. Phys. Chem. C 113(32), 14411–14417 (2009) M. Estrella, L. Barrio, G. Zhou, X. Wang, Q. Wang, W. Wen, J.C. Hanson, A.I. Frenkel, J.A. Rodriguez, J. Phys. Chem. C 113(32), 14411–14417 (2009)
31.
Zurück zum Zitat G.F. Goya, H.R. Rechenberg, Nanostructured Mater. 10(6), 1001–1011 (1998) G.F. Goya, H.R. Rechenberg, Nanostructured Mater. 10(6), 1001–1011 (1998)
32.
Zurück zum Zitat M. Sertkol, Y. Koseoglu, A. Baykal, H. Kavas, M.S. Toprak, J. Magn. Magn. Mater. 322, 866 (2010) M. Sertkol, Y. Koseoglu, A. Baykal, H. Kavas, M.S. Toprak, J. Magn. Magn. Mater. 322, 866 (2010)
33.
Zurück zum Zitat M.M. Kothawale, R.B. Tangsali, G.K. Naik, J.S. Budkuley, J. Supercond. Nov. Magn. 25, 1907 (2012) M.M. Kothawale, R.B. Tangsali, G.K. Naik, J.S. Budkuley, J. Supercond. Nov. Magn. 25, 1907 (2012)
34.
Zurück zum Zitat Md Amir, M. Geleri, S. Guner, A. Baykal, H. Sozeri, J. Inorg. Organomet. Polym. 25, 1111 (2015) Md Amir, M. Geleri, S. Guner, A. Baykal, H. Sozeri, J. Inorg. Organomet. Polym. 25, 1111 (2015)
35.
Zurück zum Zitat Md Amir, A. Baykal, S. Guner, M. Sertkol, H. Sozeri, M. Toprak, J. Inorg. Organomet. Polym. 25, 747 (2015) Md Amir, A. Baykal, S. Guner, M. Sertkol, H. Sozeri, M. Toprak, J. Inorg. Organomet. Polym. 25, 747 (2015)
36.
Zurück zum Zitat A. Baykal, H. Deligoz, H. Sozeri, Z. Durmus, M.S. Toprak, J. Supercond. Nov. Magn. 25, 1879 (2012) A. Baykal, H. Deligoz, H. Sozeri, Z. Durmus, M.S. Toprak, J. Supercond. Nov. Magn. 25, 1879 (2012)
37.
Zurück zum Zitat Md Amir, M. Sertkol, A. Baykal, H. Sozeri, J. Supercond. Nov. Magn. 28, 2447 (2015) Md Amir, M. Sertkol, A. Baykal, H. Sozeri, J. Supercond. Nov. Magn. 28, 2447 (2015)
38.
Zurück zum Zitat Md Amir, A. Baykal, M. Sertkol, H. Sözeri, J. Inorg. Organomet. Polym. Mater. 25(4), 619–626 (2015) Md Amir, A. Baykal, M. Sertkol, H. Sözeri, J. Inorg. Organomet. Polym. Mater. 25(4), 619–626 (2015)
39.
Zurück zum Zitat S. Rana, R.S. Srivastava, M.M. Sorensson, R.D.K. Misra, Mater. Sci. Eng. B 119(2), 144–151 (2005) S. Rana, R.S. Srivastava, M.M. Sorensson, R.D.K. Misra, Mater. Sci. Eng. B 119(2), 144–151 (2005)
40.
Zurück zum Zitat Y. Fu, H. Chen, X. Sun, X. Wang 111–112, 280–287 (2012) Y. Fu, H. Chen, X. Sun, X. Wang 111–112, 280–287 (2012)
41.
Zurück zum Zitat S. Rana, J. Rawat, R.D.K. Misra, Acta Biomater. 1(6), 691–703 (2005) S. Rana, J. Rawat, R.D.K. Misra, Acta Biomater. 1(6), 691–703 (2005)
42.
Zurück zum Zitat B. Baruwati, D. Guin, S.V. Manorama, Org. Lett. 9(26), 5377–5380 (2007) B. Baruwati, D. Guin, S.V. Manorama, Org. Lett. 9(26), 5377–5380 (2007)
43.
Zurück zum Zitat Y. Fu, Q. Chen, M. He, Y. Wan, X. Sun, H. Xia, X. Wang, Ind. Eng. Chem. Res. 51(36), 11700–11709 (2012) Y. Fu, Q. Chen, M. He, Y. Wan, X. Sun, H. Xia, X. Wang, Ind. Eng. Chem. Res. 51(36), 11700–11709 (2012)
44.
Zurück zum Zitat T. Peng, X. Zhang, H. Lv, L. Zan, Catal. Commun. 28, 116–119 (2012) T. Peng, X. Zhang, H. Lv, L. Zan, Catal. Commun. 28, 116–119 (2012)
45.
Zurück zum Zitat P. Xiong, J. Zhu, X. Wang, Ind. Eng. Chem. Res. 52(48), 17126–17133 (2013) P. Xiong, J. Zhu, X. Wang, Ind. Eng. Chem. Res. 52(48), 17126–17133 (2013)
46.
Zurück zum Zitat C. Wei, N. Zhan, J. Tao, S. Pang, L. Zhang, C. Cheng, D. Zhang, Appl. Surf. Sci. 453, 288–296 (2018) C. Wei, N. Zhan, J. Tao, S. Pang, L. Zhang, C. Cheng, D. Zhang, Appl. Surf. Sci. 453, 288–296 (2018)
47.
Zurück zum Zitat C. Wei, Q. Ru, X. Kang, H. Hou, C. Cheng, D. Zhang, Appl. Surf. Sci. 435, 993–1001 (2018) C. Wei, Q. Ru, X. Kang, H. Hou, C. Cheng, D. Zhang, Appl. Surf. Sci. 435, 993–1001 (2018)
48.
Zurück zum Zitat P. Jing, J. Li, L. Pan, J. Wang, J. Hazard. Mater. 284, 163–170 (2015) P. Jing, J. Li, L. Pan, J. Wang, J. Hazard. Mater. 284, 163–170 (2015)
49.
Zurück zum Zitat C. Wei, R. Zhang, X. Zheng, Q. Chen, C. Cui, G. Li, D. Zhang, Inorg. Chem. Front. 5, 3126–3134 (2018) C. Wei, R. Zhang, X. Zheng, Q. Chen, C. Cui, G. Li, D. Zhang, Inorg. Chem. Front. 5, 3126–3134 (2018)
50.
Zurück zum Zitat C. Wei, Q. Chen, C. Cheng, R. Liu, Q. Zhang, L. Zhang, Inorg. Chem. Front. 6, 1851–1860 (2019) C. Wei, Q. Chen, C. Cheng, R. Liu, Q. Zhang, L. Zhang, Inorg. Chem. Front. 6, 1851–1860 (2019)
51.
Zurück zum Zitat B. Issa, I.M. Obaidat, B.A. Albiss, Y. Haik, Int. J. Mol. Sci. 14(11), 21266–21305 (2013) B. Issa, I.M. Obaidat, B.A. Albiss, Y. Haik, Int. J. Mol. Sci. 14(11), 21266–21305 (2013)
53.
Zurück zum Zitat M.N. Akhtar, A. Bakar Sulong, M.A. Khan, M. Ahmad, G. Murtaza, M.R. Raza, R. Raza, M. Saleem, M. Kashif, J. Magn. Magn. Mater. 401, 425–431 (2016) M.N. Akhtar, A. Bakar Sulong, M.A. Khan, M. Ahmad, G. Murtaza, M.R. Raza, R. Raza, M. Saleem, M. Kashif, J. Magn. Magn. Mater. 401, 425–431 (2016)
Metadaten
Titel
Impact of calcination temperature on structural, optical, and magnetic properties of spinel CuFe2O4 for enhancing photocatalytic activity
verfasst von
V. Anto Feradrick Samson
S. Bharathi Bernadsha
M. Mahendiran
K. Leo Lawrence
J. Madhavan
M. Victor Antony Raj
S. Prathap
Publikationsdatum
18.03.2020
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 9/2020
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-020-03213-0

Weitere Artikel der Ausgabe 9/2020

Journal of Materials Science: Materials in Electronics 9/2020 Zur Ausgabe

Neuer Inhalt