The paper presents a study on the effect of adding a small amount of particles to a technically pure aluminum alloy on its structure and mechanical properties. For this purpose laboratory castings of Al 1100 alloy with the addition of 0.5 and 1.0 wt% Al2O3 were produced. The introduction of master alloys containing particles into the melt was accompanied by ultrasonic treatment. Images of the structure of the alloys obtained showed that ultrasonic treatment contributes to producing a material with zero porosity; this fact is also confirmed by the measurement of density which values are close to the theoretical ones. Analysis of mechanical properties revealed that the conditional yield strength, tensile strength and hardness of the nanocomposite with a metal matrix Al 1100/wt. nano Al2O3 were prone to increase with increasing the percentage of aluminum oxide in the matrix alloy while reducing the plasticity. This behavior of studied alloys reinforced with nanoparticles is a consequence of refining the grain structure of the material during crystallization due to the presence of particles acting as inoculants.
Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten
Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:
Maruyama B, Hunt WP (1999) Discontinuously reinforced aluminum: current status and future direction. JOM 11: 59–61.
Yang Y, Li X (2007) Ultrasonic Cavitation Based Nanomanufacturing of Bulk Aluminum Matrix Nanocomposites. J. Manufact. Sci. Eng. 129: 497–501.
Hulya K, Necip U, Goller G, Ovecoglu L, Henein H (2011) Comparative processing-structure property studies of Al-Cu matrix composites reinforcewith TiC particulates. Compos. A 42: 812–824.
Yongbiao Y. Zhimin Z. Xing Z (2012) Processing map of Al 2O 3 particulate reinforced Al alloy matrix composites. Mat. Sci. Eng. A 558: 112–118.
Umasankar V, Anthony Xavior M, Karthikeyan S (2014) Experimental evaluation of the influence of processing parameters on the mechanical properties of SiC particle reinforced AA6061 aluminium alloy matrix composite by powder processing. J. Alloys Comp. 582: 380–386.
Cunzhu N, Jiajun G, Junliang L, Di Z (2008) Investigation on microstructures and interface character of B 4C particles reinforced 2024Al matrix composites fabricated by mechanical alloying. J. Alloys Comp. 454: 118–122.
Ramesh CS, Keshavamurthy R, Madhusudhan J (2014) Fatigue behavior of Ni-P coated Si3N4 reinforced Al6061 composites. Pro. Mater. Sci. 6: 1444–1454.
Sreekumar VM, Babu NH, Eskin DG (2017) Prospects of In-Situ α-Al 2O 3 as an Inoculant in Aluminum: A Feasibility Study. J. Mater. Eng. Perf. 26 (9): 4166–4176.
Dieringa H (2011) Properties of magnesium alloys reinforced with nanoparticles and carbon nanotubes: a review. J. Mater. Sci. 46 (2): 289–306.
Puga H, Costa S, Barbosa J, Ribeiro S, Prokic M (2011) Influence of ultrasonic melttreatment on microstructure and mechanical properties of AlSi9Cu3 alloy. J. Mater. Process. Technol. 211: 1729–1735.
Kudryashova OB, Eskin DG, Khrustalev AP, Vorozhtsov SA (2017) Ultrasonic effect on thepenetration of the metallic melt into submicron particles and their agglomerates. Russ. J. Non-Ferrous Metals 58: 427–433.
Akbari MK, Baharvandi HR, Shirvanimoghaddam K (2015) Tensile and fracture behavior of nano/micro TiB 2 particle reinforced casting A356 aluminum alloy composites. Mater. Des. 66: 150–161.
Hong Y, Qiu H (2016) Fabrication of carbon nanotube reinforced A356 nanocomposites. J. Mater. Res. 31 (15): 2277–2283.
Vorozhtsov S, Zhukov I, Vorozhtsov A, Zhukov A, Eskin D, Kvetinskaya A. (2015). Synthesis of micro-and nanoparticles of metal oxides and their application for reinforcement of Al-based alloys. Adv. Mater. Sci. Eng. 2015: 1–5.
- Impact of Dispersion Hardening by Alumina Nano Particles on Mechanical Properties of Al 1100
in-adhesives, MKVS, Zühlke/© Zühlke, Nordson/© Nordson, ViscoTec/© ViscoTec, Hellmich GmbH/© Hellmich GmbH