Impact of thermal annealing inducing oxidation process on the crystalline powder of In2S3

verfasst von: A. Timoumi, W. Zayoud, A. Sharma, M. Kraini, N. Bouguila, A. Hakamy, N. Revaprasadu, S. Alaya

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 16/2020

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Inorganic two-dimensional semiconductor indium sulfide (In2S3) has recently attracted considerable attention as a buffer material in the field of thin-film photovoltaics, photo electrochemical cells and other energy-related applications. Compared with this growing interest, however, detailed characterizations of the commercial material are not done. The present investigation deals with the systematic investigation of the physical properties of powdered β-indium sulfide (In2S3). The crystalline structure, the composition, and the morphological properties of the samples were characterized using a range of techniques such as X-ray powder diffraction (XRD), Fourier transform infrared (FTIR), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). X-ray diffraction patterns revealed mixed peaks of In2S3 and In2O3 for the sample annealed at 400 °C. The In2O3 peaks were crystalline with a cubic phase with a (222) preferential orientation. These results were supported by the FTIR, and XPS studies. Thus, a significant correlation was established between the annealing temperature and the TEM images. The main conclusion of the paper opens the possibility of using In2S3 layers for solar cells.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat H. Wang, L. Zhang, Z. Chen, J. Hu, S. Li, Z. Wang, J. Liu, X. Wang, Chem. Soc. Rev. 43, 5234 (2014) H. Wang, L. Zhang, Z. Chen, J. Hu, S. Li, Z. Wang, J. Liu, X. Wang, Chem. Soc. Rev. 43, 5234 (2014)
2.
Zurück zum Zitat L.Y. Ding, H. Chen, Q.Q. Wang, T.F. Zhou, Q. Jiang, Y.H. Yuan, J.L. Li, J.C. Hu, Chem. Commun. 52, 994 (2016) L.Y. Ding, H. Chen, Q.Q. Wang, T.F. Zhou, Q. Jiang, Y.H. Yuan, J.L. Li, J.C. Hu, Chem. Commun. 52, 994 (2016)
3.
Zurück zum Zitat M.H. Cao, P.F. Wang, Y.H. Ao, C. Wang, J. Hou, J. Qian, Chem. Eng. J. 264, 113 (2015) M.H. Cao, P.F. Wang, Y.H. Ao, C. Wang, J. Hou, J. Qian, Chem. Eng. J. 264, 113 (2015)
4.
Zurück zum Zitat N. Revathi, P. Prathap, R.W. Miles, R.K.T. Ramakrishna, Sol. Energy Mater. Sol. Cells 94, 1487 (2010) N. Revathi, P. Prathap, R.W. Miles, R.K.T. Ramakrishna, Sol. Energy Mater. Sol. Cells 94, 1487 (2010)
5.
Zurück zum Zitat N. Barreau, Sol. Energy 83, 363 (2009) N. Barreau, Sol. Energy 83, 363 (2009)
6.
Zurück zum Zitat S.H. Yu, L. Shu, Y.S. Wu, J. Yang, Y. Xie, Y.T. Qian, J. Am. Ceram. Soc. 82, 457 (1999) S.H. Yu, L. Shu, Y.S. Wu, J. Yang, Y. Xie, Y.T. Qian, J. Am. Ceram. Soc. 82, 457 (1999)
7.
Zurück zum Zitat S. Gorai, D. Ganguli, S. Chaudhuri, Mater. Chem. Phys. 82, 974 (2003) S. Gorai, D. Ganguli, S. Chaudhuri, Mater. Chem. Phys. 82, 974 (2003)
8.
Zurück zum Zitat T. Asikainen, M. Ritala, M. Leskela, Appl. Surf. Sci. 82–83, 122 (1994) T. Asikainen, M. Ritala, M. Leskela, Appl. Surf. Sci. 82–83, 122 (1994)
9.
Zurück zum Zitat M. Kraini, J. El Ghoul, R. Souissi, A. Sharma, F. Aldbea, H. Abassi, N. Bouguila, C. Vázquez-Vázquez, Mater. Res. Express 6(10), 106431 (2019) M. Kraini, J. El Ghoul, R. Souissi, A. Sharma, F. Aldbea, H. Abassi, N. Bouguila, C. Vázquez-Vázquez, Mater. Res. Express 6(10), 106431 (2019)
10.
Zurück zum Zitat W. Gao, W. Liu, Y. Leng, X. Wang, X. Wang, B. Hu, D. Yu, Y. Sang, H. Liu, Appl. Catal. B 176, 83 (2015) W. Gao, W. Liu, Y. Leng, X. Wang, X. Wang, B. Hu, D. Yu, Y. Sang, H. Liu, Appl. Catal. B 176, 83 (2015)
11.
Zurück zum Zitat J. Xu, Ch Liu, J. Niu, M. Chen, Sep. Purif. Technol. 230, 2 (2020) J. Xu, Ch Liu, J. Niu, M. Chen, Sep. Purif. Technol. 230, 2 (2020)
12.
Zurück zum Zitat P.K. Kumta, P.P. Phule, S.H. Risbud, Mater. Lett. 5, 401 (1987) P.K. Kumta, P.P. Phule, S.H. Risbud, Mater. Lett. 5, 401 (1987)
13.
Zurück zum Zitat E. Dalas, S. Sakkopoulos, E. Vitoratos, G. Maroulis, L. Kobotiatis, J. Mater. Sci. 28, 5456 (1993) E. Dalas, S. Sakkopoulos, E. Vitoratos, G. Maroulis, L. Kobotiatis, J. Mater. Sci. 28, 5456 (1993)
14.
Zurück zum Zitat A. Strohm, L. Eisenmann, R.K. Gebhardt, A. Harding, T. Schlotzer, D. Abou-Ras, H.W. Schock, Thin Solid Films 480–481, 162 (2005) A. Strohm, L. Eisenmann, R.K. Gebhardt, A. Harding, T. Schlotzer, D. Abou-Ras, H.W. Schock, Thin Solid Films 480–481, 162 (2005)
15.
Zurück zum Zitat S.P. Nehra, S. Chander, A. Sharma, M.S. Dhaka, Mater. Sci. Semicond. Process. 40, 25 (2015) S.P. Nehra, S. Chander, A. Sharma, M.S. Dhaka, Mater. Sci. Semicond. Process. 40, 25 (2015)
16.
Zurück zum Zitat K.R. Nagabhushana, Nucl. Instr. Meth. Phys. Res. B 266, 1040 (2008) K.R. Nagabhushana, Nucl. Instr. Meth. Phys. Res. B 266, 1040 (2008)
17.
Zurück zum Zitat M.K. Woka, L. Ottaviano, J. Szuber, Thin Solid Films 515, 8328 (2007) M.K. Woka, L. Ottaviano, J. Szuber, Thin Solid Films 515, 8328 (2007)
18.
Zurück zum Zitat A. Timoumi, H. Bouzouita, M. Kanzari, B. Rezig, Thin Solid Films 480, 124 (2005) A. Timoumi, H. Bouzouita, M. Kanzari, B. Rezig, Thin Solid Films 480, 124 (2005)
19.
Zurück zum Zitat A. Timoumi, H. Bouzouita, R. Brini, M. Kanzari, B. Rezig, Appl. Surf. Sci. 253(1), 306 (2006) A. Timoumi, H. Bouzouita, R. Brini, M. Kanzari, B. Rezig, Appl. Surf. Sci. 253(1), 306 (2006)
20.
Zurück zum Zitat A. Timoumi, H. Bouzouita, B. Rezig, Thin Solid Films 519(21), 7615 (2011) A. Timoumi, H. Bouzouita, B. Rezig, Thin Solid Films 519(21), 7615 (2011)
21.
Zurück zum Zitat N. Bouguila, A. Timoumi, H. Bouzouita, E. Lacaze, H. Bouchriha, B. Rezig, Eur. Phys. J. Appl. Phys. 63(2), 20301 (2013) N. Bouguila, A. Timoumi, H. Bouzouita, E. Lacaze, H. Bouchriha, B. Rezig, Eur. Phys. J. Appl. Phys. 63(2), 20301 (2013)
22.
Zurück zum Zitat N. Bouguila, A. Timoumi, H. Bouzouita, Eur. Phys. J. Appl. Phys. 65(2), 20304 (2014) N. Bouguila, A. Timoumi, H. Bouzouita, Eur. Phys. J. Appl. Phys. 65(2), 20304 (2014)
23.
Zurück zum Zitat N. Bouguila, D. Bchiri, M. Kraini, A. Timoumi, I. Halidou, K. Khirouni, S. Alaya, J. Mater. Sci.: Mater. Electron. 26(12), 9845 (2015) N. Bouguila, D. Bchiri, M. Kraini, A. Timoumi, I. Halidou, K. Khirouni, S. Alaya, J. Mater. Sci.: Mater. Electron. 26(12), 9845 (2015)
24.
Zurück zum Zitat A. Timoumi, N. Bouguila, M. Chaari, M. Kraini, A. Matoussi, H. Bouzouita, J. Alloys Compd. 679, 59 (2016) A. Timoumi, N. Bouguila, M. Chaari, M. Kraini, A. Matoussi, H. Bouzouita, J. Alloys Compd. 679, 59 (2016)
25.
Zurück zum Zitat H. Abassi, N. Bouguila, A. Timoumi, J. Electron. Mater. 47(5), 2519 (2018) H. Abassi, N. Bouguila, A. Timoumi, J. Electron. Mater. 47(5), 2519 (2018)
26.
Zurück zum Zitat M. Hamici, Kh Guessoum, L. Vaillant, Y. Gagou, P. Saint-Grégoire, J. Electron. Mater. 48(7), 4715 (2019) M. Hamici, Kh Guessoum, L. Vaillant, Y. Gagou, P. Saint-Grégoire, J. Electron. Mater. 48(7), 4715 (2019)
27.
Zurück zum Zitat S.C. Masikane, N. Revaprasadu, Mater. Sci. Semicond. Process. 76(15), 73 (2018) S.C. Masikane, N. Revaprasadu, Mater. Sci. Semicond. Process. 76(15), 73 (2018)
28.
Zurück zum Zitat S.C. Masikane, P.D. McNaughter, D.J. Lewis, I.V. Yrezabal, B.P. Doyle, E. Carleschi, P. O’Brien, N. Revaprasadu, Eur. J. Inorg. Chem. 10, 1421 (2019) S.C. Masikane, P.D. McNaughter, D.J. Lewis, I.V. Yrezabal, B.P. Doyle, E. Carleschi, P. O’Brien, N. Revaprasadu, Eur. J. Inorg. Chem. 10, 1421 (2019)
29.
Zurück zum Zitat N. Revaprasadu, M. Azad Malik, J. Carstens, P. O’Brien, J. Mater. Chem. 9, 2885 (1999) N. Revaprasadu, M. Azad Malik, J. Carstens, P. O’Brien, J. Mater. Chem. 9, 2885 (1999)
30.
Zurück zum Zitat M. Kraini, N. Bouguila, I. Halidou, A. Timoumi, S. Alaya, Mater. Sci. Semicond. Process. 16, 1388 (2013) M. Kraini, N. Bouguila, I. Halidou, A. Timoumi, S. Alaya, Mater. Sci. Semicond. Process. 16, 1388 (2013)
31.
Zurück zum Zitat V. Pyragas, V. Lisauskas, K. Sliuziene, B. Vengalis, Lith. J. Phys. 51, 47 (2011) V. Pyragas, V. Lisauskas, K. Sliuziene, B. Vengalis, Lith. J. Phys. 51, 47 (2011)
32.
Zurück zum Zitat A. Manohar, C. Krishnamoorthi, J. Cryst. Growth 473, 66 (2017) A. Manohar, C. Krishnamoorthi, J. Cryst. Growth 473, 66 (2017)
33.
Zurück zum Zitat K. Ravichandran, P. Philominathan, Sol. Energy 82, 1062 (2008) K. Ravichandran, P. Philominathan, Sol. Energy 82, 1062 (2008)
34.
Zurück zum Zitat W.D. Zhou, D. Dastan, J. Li, X.T. Yin, Q. Wang, Nanomater. 10, 785 (2020) W.D. Zhou, D. Dastan, J. Li, X.T. Yin, Q. Wang, Nanomater. 10, 785 (2020)
35.
Zurück zum Zitat A. Jafari, M.H. Alam, D. Dastan, S. Ziakhodadadian, Z. Shi, H. Garmestani, A.S. Weidenbach, Ş. Ţălu, J. Mater. Sci: Mater. Electron. 30, 21185 (2019) A. Jafari, M.H. Alam, D. Dastan, S. Ziakhodadadian, Z. Shi, H. Garmestani, A.S. Weidenbach, Ş. Ţălu, J. Mater. Sci: Mater. Electron. 30, 21185 (2019)
36.
Zurück zum Zitat X.T. Yin, W.D. Zhou, J. Li, P. Lv, Q. Wang, D. Wang, F. Wu, D. Dastan, H. Garmestani, Z. Shi, Ş. Ţălu, J. Mater. Sci: Mater. Electron. 30, 14687 (2019) X.T. Yin, W.D. Zhou, J. Li, P. Lv, Q. Wang, D. Wang, F. Wu, D. Dastan, H. Garmestani, Z. Shi, Ş. Ţălu, J. Mater. Sci: Mater. Electron. 30, 14687 (2019)
37.
Zurück zum Zitat A. Jafaria, K. Tahanib, D. Dastanc, S. Asgaryd, Z. Shie, X.T. Yinf, W.D. Zhoug, H. Garmestanic, Ş. Ţălu, Surf. Interfaces 18, 100463 (2020) A. Jafaria, K. Tahanib, D. Dastanc, S. Asgaryd, Z. Shie, X.T. Yinf, W.D. Zhoug, H. Garmestanic, Ş. Ţălu, Surf. Interfaces 18, 100463 (2020)
38.
Zurück zum Zitat A.U. Moreh, B. Hamza, S. Abdullahi, A. Bala, Z. Abdullahi, M.S. Shehu, Int. J. Innov. Appl. Stud. 9, 913 (2014) A.U. Moreh, B. Hamza, S. Abdullahi, A. Bala, Z. Abdullahi, M.S. Shehu, Int. J. Innov. Appl. Stud. 9, 913 (2014)
39.
Zurück zum Zitat B. Yahmadi, N. Kamoun, C. Guasch, R. Bennaceur, Mater. Chem. Phys. 127, 239 (2011) B. Yahmadi, N. Kamoun, C. Guasch, R. Bennaceur, Mater. Chem. Phys. 127, 239 (2011)
40.
Zurück zum Zitat D. Dastan, Appl. Phys. A 123(699), 1 (2017) D. Dastan, Appl. Phys. A 123(699), 1 (2017)
41.
Zurück zum Zitat M. Kraini, N. Bouguila, J. El Ghoul, I. Halidou, S.A. Gomez-Lopera, C. Vazquez-Vazquez, M.A. Lopez-Quintela, S. Alaya, J. Mater Sci: Mater Electron. 26, 5774 (2015) M. Kraini, N. Bouguila, J. El Ghoul, I. Halidou, S.A. Gomez-Lopera, C. Vazquez-Vazquez, M.A. Lopez-Quintela, S. Alaya, J. Mater Sci: Mater Electron. 26, 5774 (2015)
42.
Zurück zum Zitat X.T. Yin, P. Lv, J. Li, A. Jafari, F.Y. Wu, Q. Wang, D. Dastan, Z. Shi, S. Yu, H. Garmestani, J Alloys Compd. 825, 154105 (2020) X.T. Yin, P. Lv, J. Li, A. Jafari, F.Y. Wu, Q. Wang, D. Dastan, Z. Shi, S. Yu, H. Garmestani, J Alloys Compd. 825, 154105 (2020)
43.
Zurück zum Zitat D. Dastan, P.U. Londhe, N.B. Chaure, J. Mater. Sci: Mater. Electron. 25, 3473 (2014) D. Dastan, P.U. Londhe, N.B. Chaure, J. Mater. Sci: Mater. Electron. 25, 3473 (2014)
44.
Zurück zum Zitat D. Dastan, S.L. Panahi, N.B. Chaure, J. Mater. Sci: Mater. Electron. 27, 12291 (2016) D. Dastan, S.L. Panahi, N.B. Chaure, J. Mater. Sci: Mater. Electron. 27, 12291 (2016)
45.
Zurück zum Zitat S.L. Panahi, D. Dastan, N.B. Chaure, Adv. Sci. Lett. 22(4), 941 (2016) S.L. Panahi, D. Dastan, N.B. Chaure, Adv. Sci. Lett. 22(4), 941 (2016)
46.
Zurück zum Zitat Z. Gao, B. Xu, M. Ma, A. Feng, Y. Zhang, X. Liu, Z. Jia, G. Wu, Compos. Part B Eng. 179, 107417 (2019) Z. Gao, B. Xu, M. Ma, A. Feng, Y. Zhang, X. Liu, Z. Jia, G. Wu, Compos. Part B Eng. 179, 107417 (2019)
47.
Zurück zum Zitat Z. Gao, Z. Jia, J. Zhang, A. Feng, Z. Huang, G. Wu, J. Mater. Sci.: Mater. Electron. 30(14), 13474 (2019) Z. Gao, Z. Jia, J. Zhang, A. Feng, Z. Huang, G. Wu, J. Mater. Sci.: Mater. Electron. 30(14), 13474 (2019)
Metadaten
Titel
Impact of thermal annealing inducing oxidation process on the crystalline powder of In2S3
verfasst von
A. Timoumi
W. Zayoud
A. Sharma
M. Kraini
N. Bouguila
A. Hakamy
N. Revaprasadu
S. Alaya
Publikationsdatum
09.07.2020
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 16/2020
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-020-03921-7

Weitere Artikel der Ausgabe 16/2020

Journal of Materials Science: Materials in Electronics 16/2020 Zur Ausgabe

Neuer Inhalt