Improvement of microwave dielectric characteristics in SrNdAlO4 ceramics by La-substitution

verfasst von: Xiaohua Zhou, Fan Yang, Xiaoyan Li, Chengli Sun, Shuren Zhang

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 11/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Single-phase Sr(Nd1−xLax)AlO4 (x = 0, 0.1, 0.3, 0.5, 0.7, 0.9, and 1) solid solutions with tetragonal K2NiF4-type structure were obtained by a standard solid-state reaction approach in the entire composition range. Their microwave dielectric characteristics were investigated together with microstructures, and were significantly modified by La-substitution. The X-ray diffraction results presented that the samples were SrNdAlO4 and SrLaAlO4. And the dielectric constant (ε r ) changed slightly, the temperature coefficient of resonant frequency (τ f ) varied from −9 to −34 ppm/°C. The significantly improved Q × f value was achieved in the present ceramics with x = 0.9 and reached the maximum of 65,900 GHz. The ionic radius difference of A-site affects the distortion in the rock-salt layer and the tolerance t affects the interlayer mismatch, both of them will predominantly affect the Q × f value. The best combination of microwave characteristics was achieved at x = 0.9: ε r  = 18.49, Q × f = 65,900 GHz, τ f  = −27 ppm/°C.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat C. Zhang, L. Yi, L. Li, X.M. Chen, Int. J. Appl. Ceram. Technol. 10, E70–E76 (2013)CrossRef C. Zhang, L. Yi, L. Li, X.M. Chen, Int. J. Appl. Ceram. Technol. 10, E70–E76 (2013)CrossRef
5.
Zurück zum Zitat M.M. Mao, L. Li, Y.W. Zeng, X.M. Chen, Ferroelectrics 470, 117–125 (2014)CrossRef M.M. Mao, L. Li, Y.W. Zeng, X.M. Chen, Ferroelectrics 470, 117–125 (2014)CrossRef
6.
Zurück zum Zitat X.M. Chen, Y. Xiao, X.Q. Liu, X. Hu, J. Electroceram. 10, 111–115 (2003)CrossRef X.M. Chen, Y. Xiao, X.Q. Liu, X. Hu, J. Electroceram. 10, 111–115 (2003)CrossRef
7.
Zurück zum Zitat X.Q. Liu, X.M. Chen, Y. Xiao, Mater. Sci. Eng. B. 103, 276–280 (2003)CrossRef X.Q. Liu, X.M. Chen, Y. Xiao, Mater. Sci. Eng. B. 103, 276–280 (2003)CrossRef
8.
9.
Zurück zum Zitat M.M. Mao, X.M. Chen, Int. J. Appl. Ceram. Tecnol. 8, 1023–1030 (2011)CrossRef M.M. Mao, X.M. Chen, Int. J. Appl. Ceram. Tecnol. 8, 1023–1030 (2011)CrossRef
10.
Zurück zum Zitat L.Q. Peng, M.M. Mao, X.M. Chen, J. Am. Ceram. Soc. 93, 4066–4070 (2010)CrossRef L.Q. Peng, M.M. Mao, X.M. Chen, J. Am. Ceram. Soc. 93, 4066–4070 (2010)CrossRef
11.
12.
13.
Zurück zum Zitat A. Benabbas, Acta Crystallogr. Sect. B Struct. Sci. 62, 9–15 (2006)CrossRef A. Benabbas, Acta Crystallogr. Sect. B Struct. Sci. 62, 9–15 (2006)CrossRef
14.
Zurück zum Zitat A. Magrez, M. Cochet, O. Joubert, G. Louarn, M. Ganne, O. Chauvet, Chem. Mater. 13, 3893–3898 (2001)CrossRef A. Magrez, M. Cochet, O. Joubert, G. Louarn, M. Ganne, O. Chauvet, Chem. Mater. 13, 3893–3898 (2001)CrossRef
17.
Zurück zum Zitat P. Wise, I. Reaney, W. Lee, T. Price, D. Iddles, D. Cannell, J. Eur. Ceram. Soc. 21, 1723–1726 (2001)CrossRef P. Wise, I. Reaney, W. Lee, T. Price, D. Iddles, D. Cannell, J. Eur. Ceram. Soc. 21, 1723–1726 (2001)CrossRef
18.
Zurück zum Zitat Z. Fang, B. Tang, Y. Li, F. Si, S. Zhang, J. Electron. Mater. 44, 4236–4242 (2015)CrossRef Z. Fang, B. Tang, Y. Li, F. Si, S. Zhang, J. Electron. Mater. 44, 4236–4242 (2015)CrossRef
19.
Zurück zum Zitat Z.-X. Fang, B. Tang, F. Si, S.-R. Zhang, J. Mater. Sci. Mater. Electron. 27, 1913–1919 (2015)CrossRef Z.-X. Fang, B. Tang, F. Si, S.-R. Zhang, J. Mater. Sci. Mater. Electron. 27, 1913–1919 (2015)CrossRef
20.
Zurück zum Zitat X. Zhou, Y. Zhang, X. Yang, C. Sun, H. Chen, S. Zhang, J. Mater. Sci. Mater. Electron. 26, 7683–7689 (2015)CrossRef X. Zhou, Y. Zhang, X. Yang, C. Sun, H. Chen, S. Zhang, J. Mater. Sci. Mater. Electron. 26, 7683–7689 (2015)CrossRef
22.
Zurück zum Zitat P. Liao, T. Qiu, J. Yang, X. Lu, Electron. Mater. Lett. 10, 121–125 (2014)CrossRef P. Liao, T. Qiu, J. Yang, X. Lu, Electron. Mater. Lett. 10, 121–125 (2014)CrossRef
Metadaten
Titel
Improvement of microwave dielectric characteristics in SrNdAlO4 ceramics by La-substitution
verfasst von
Xiaohua Zhou
Fan Yang
Xiaoyan Li
Chengli Sun
Shuren Zhang
Publikationsdatum
04.07.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 11/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-5296-5

Weitere Artikel der Ausgabe 11/2016

Journal of Materials Science: Materials in Electronics 11/2016 Zur Ausgabe

Neuer Inhalt