Influence of Cr Content on the Microstructure and Electrochemical Corrosion in Plasma Cladding Ni-Cr Coatings

verfasst von: Wenya Zhang, Canming Wang, Qiang Song, Hongzhi Cui, Xiaoli Feng, Chunzhi Zhang

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 11/2019

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Ni-xCr (x = 20, 30 and 40 wt pct, respectively) alloy corrosion resistant coatings were manufactured on Q235 substrate by plasma cladding. The effects of the Cr content on the phase composition, microstructure, and corrosion resistance of the Ni-xCr coatings were investigated in detail. The results showed that the main phases of the Ni-xCr coatings were γ-[Ni, Fe] solid solutions with face-centered cubic (FCC) structure. Electrochemical corrosion tests of different polarization voltages showed that the inhomogeneous distribution of composition and the presence of the multiphase structure led to the occurrence of corrosion. The occurrence of the Cr-rich phase increased the sensitivity of the Cr-poor phase and further accelerated the corrosion process. The Ni-xCr coating with intermediate Cr content (Ni-30Cr) had the best corrosion resistance, which depends on the phase composition of the coating.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat H. Liu, Q. Xu, C. Wang and X. Zhang: J. Alloys Compd., 2015, vol. 621, pp. 357-363.CrossRef H. Liu, Q. Xu, C. Wang and X. Zhang: J. Alloys Compd., 2015, vol. 621, pp. 357-363.CrossRef
2.
Zurück zum Zitat S. P. Sidel’nikova, V. V. Parshutin, G. F. Volodina, N. V. Chernyshova and A. V. Koval’: Russ. J. Appl. Chem., 2017, vol. 89, pp. 1740-1746.CrossRef S. P. Sidel’nikova, V. V. Parshutin, G. F. Volodina, N. V. Chernyshova and A. V. Koval’: Russ. J. Appl. Chem., 2017, vol. 89, pp. 1740-1746.CrossRef
3.
Zurück zum Zitat P. SureshBabu, Y. Madhavi, L. RamaKrishna, D. SrinivasaRao and G. Padmanabham: Jom, 2018, vol. 70, pp. 2636-2649.CrossRef P. SureshBabu, Y. Madhavi, L. RamaKrishna, D. SrinivasaRao and G. Padmanabham: Jom, 2018, vol. 70, pp. 2636-2649.CrossRef
4.
Zurück zum Zitat G. Y. Koga, W. Wolf, R. Schulz, S. Savoie, C. Bolfarini, C. S. Kiminami and W. J. Botta: Surf. Coat. Technol., 2019, vol. 357, pp. 993-1003.CrossRef G. Y. Koga, W. Wolf, R. Schulz, S. Savoie, C. Bolfarini, C. S. Kiminami and W. J. Botta: Surf. Coat. Technol., 2019, vol. 357, pp. 993-1003.CrossRef
5.
Zurück zum Zitat 5. M. F. Pillis, G. A. Geribola, G. Scheidt, E. G. de Araújo, M. C. L. de Oliveira and R. A. Antunes: Corros. Sci., 2016, vol. 102, pp. 317-325.CrossRef 5. M. F. Pillis, G. A. Geribola, G. Scheidt, E. G. de Araújo, M. C. L. de Oliveira and R. A. Antunes: Corros. Sci., 2016, vol. 102, pp. 317-325.CrossRef
6.
Zurück zum Zitat 6. H. B. Lee and M. Y. Wu: Metall. Mater. Trans. A, 2017, vol. 48, pp. 4667-4680.CrossRef 6. H. B. Lee and M. Y. Wu: Metall. Mater. Trans. A, 2017, vol. 48, pp. 4667-4680.CrossRef
7.
Zurück zum Zitat R. Garg, N. Rajagopalan, M. Pyeon, Y. Gönüllü, T. Fischer, A. S. Khanna and S. Mathur: Surf. Coat. Technol., 2018, vol. 356, pp. 49-55.CrossRef R. Garg, N. Rajagopalan, M. Pyeon, Y. Gönüllü, T. Fischer, A. S. Khanna and S. Mathur: Surf. Coat. Technol., 2018, vol. 356, pp. 49-55.CrossRef
8.
Zurück zum Zitat Y. Q. Jiang, J. Li, Y. F. Juan, Z. J. Lu and W. L. Jia: J. Alloys Compd., 2019, vol. 775, pp. 1-14.CrossRef Y. Q. Jiang, J. Li, Y. F. Juan, Z. J. Lu and W. L. Jia: J. Alloys Compd., 2019, vol. 775, pp. 1-14.CrossRef
9.
Zurück zum Zitat 9. J. Liu, J. Li, X. Cheng and H. Wang: Metall. Mater. Trans. A, 2017, vol. 49, pp. 595-603. 9. J. Liu, J. Li, X. Cheng and H. Wang: Metall. Mater. Trans. A, 2017, vol. 49, pp. 595-603.
10.
Zurück zum Zitat 10. A. Kunyarong and K. Fakpan: Mater. Today: Proceedings, 2018, vol. 5, pp. 9244-9249. 10. A. Kunyarong and K. Fakpan: Mater. Today: Proceedings, 2018, vol. 5, pp. 9244-9249.
11.
Zurück zum Zitat 11. M. Q. Wan, J. Shi, L. Lei, Z. Y. Cui, H. L. Wang and X. Wang: J. Mater. Eng. Perform., 2018, vol. 27, pp. 2844-2854.CrossRef 11. M. Q. Wan, J. Shi, L. Lei, Z. Y. Cui, H. L. Wang and X. Wang: J. Mater. Eng. Perform., 2018, vol. 27, pp. 2844-2854.CrossRef
12.
Zurück zum Zitat 12. B. Liu, X. Wei, W. Wang, J. Lu and J. Ding: Sol. Energy Mater. Sol. Cells., 2017, vol. 170, pp. 77-86.CrossRef 12. B. Liu, X. Wei, W. Wang, J. Lu and J. Ding: Sol. Energy Mater. Sol. Cells., 2017, vol. 170, pp. 77-86.CrossRef
13.
Zurück zum Zitat 13. Z. Feng, M. Tang, Y. Liu, Z. Yan, G. Li and R. Zhang: Surf. Eng., 2017, vol. 34, pp. 309-315.CrossRef 13. Z. Feng, M. Tang, Y. Liu, Z. Yan, G. Li and R. Zhang: Surf. Eng., 2017, vol. 34, pp. 309-315.CrossRef
14.
Zurück zum Zitat 14. G. Jin, Y. Li, H. Cui, X. Cui and Z. Cai: J. Mater. Eng. Perform., 2016, vol. 25, pp. 2412-2419.CrossRef 14. G. Jin, Y. Li, H. Cui, X. Cui and Z. Cai: J. Mater. Eng. Perform., 2016, vol. 25, pp. 2412-2419.CrossRef
15.
Zurück zum Zitat 15. J. Wen, H. Cui, N. Wei, X. Song, G. Zhang, C. Wang and Q. Song: J. Alloys Compd., 2017, vol. 695, pp. 2424-2433.CrossRef 15. J. Wen, H. Cui, N. Wei, X. Song, G. Zhang, C. Wang and Q. Song: J. Alloys Compd., 2017, vol. 695, pp. 2424-2433.CrossRef
16.
Zurück zum Zitat 16. Q. Ye, K. Feng, Z. Li, F. Lu, R. Li, J. Huang and Y. Wu: Appl. Surf. Sci., 2017, vol. 396, pp. 1420-1426.CrossRef 16. Q. Ye, K. Feng, Z. Li, F. Lu, R. Li, J. Huang and Y. Wu: Appl. Surf. Sci., 2017, vol. 396, pp. 1420-1426.CrossRef
17.
Zurück zum Zitat 17. H. Sun, M. Guo, F. Meng and A. Liu: Trans. Indian Inst. Met., 2015, vol. 69, pp. 1369-1376.CrossRef 17. H. Sun, M. Guo, F. Meng and A. Liu: Trans. Indian Inst. Met., 2015, vol. 69, pp. 1369-1376.CrossRef
18.
Zurück zum Zitat 18. Y. Lu, G. Lu, F. Liu, Z. Chen and K. Tang: J. Alloys Compd., 2015, vol. 637, pp. 149-154.CrossRef 18. Y. Lu, G. Lu, F. Liu, Z. Chen and K. Tang: J. Alloys Compd., 2015, vol. 637, pp. 149-154.CrossRef
19.
Zurück zum Zitat 19. K. Liu, Y. Li and J. Wang: Mater. Des., 2016, vol. 105, pp. 171-178.CrossRef 19. K. Liu, Y. Li and J. Wang: Mater. Des., 2016, vol. 105, pp. 171-178.CrossRef
21.
Zurück zum Zitat 21. V. Raghavan: J. Phase Equilib. Diffus., 2008, vol. 30, pp. 94-95.CrossRef 21. V. Raghavan: J. Phase Equilib. Diffus., 2008, vol. 30, pp. 94-95.CrossRef
22.
23.
Zurück zum Zitat 23. M. S. Kabir, P. Munroe, Z. Zhou and Z. Xie: Ceram. Int., 2018, vol. 44, pp. 11364-11373.CrossRef 23. M. S. Kabir, P. Munroe, Z. Zhou and Z. Xie: Ceram. Int., 2018, vol. 44, pp. 11364-11373.CrossRef
24.
Zurück zum Zitat 24. T.-T. Shun, L.-Y. Chang and M.-H. Shiu: Mater. Charact., 2012, vol. 70, pp. 63-67.CrossRef 24. T.-T. Shun, L.-Y. Chang and M.-H. Shiu: Mater. Charact., 2012, vol. 70, pp. 63-67.CrossRef
25.
Zurück zum Zitat 25. M. Wang, Z. Zhou, L. Wu, Y. Ding, F. Xu and Z. Wang: J. Therm. Spray Technol., 2018, vol. 27, pp. 769-777.CrossRef 25. M. Wang, Z. Zhou, L. Wu, Y. Ding, F. Xu and Z. Wang: J. Therm. Spray Technol., 2018, vol. 27, pp. 769-777.CrossRef
26.
Zurück zum Zitat 26. M. Yan and W. Z. Zhu: Surf. Coat. Technol., 1997, vol. 92, pp. 157-163.CrossRef 26. M. Yan and W. Z. Zhu: Surf. Coat. Technol., 1997, vol. 92, pp. 157-163.CrossRef
27.
Zurück zum Zitat 27. J. Lei, C. Shi, S. Zhou, Z. Gu and L.-C. Zhang: Surf. Coat. Technol., 2018, vol. 334, pp. 274-285.CrossRef 27. J. Lei, C. Shi, S. Zhou, Z. Gu and L.-C. Zhang: Surf. Coat. Technol., 2018, vol. 334, pp. 274-285.CrossRef
28.
Zurück zum Zitat 28. L. Zhang, D. Sun, H. Yu and H. Li: Mater. Sci. Eng. A, 2007, vol. 457, pp. 319-324.CrossRef 28. L. Zhang, D. Sun, H. Yu and H. Li: Mater. Sci. Eng. A, 2007, vol. 457, pp. 319-324.CrossRef
29.
Zurück zum Zitat 29. Y. F. Juan, J. Li, Y. Q. Jiang, W. L. Jia and Z. J. Lu: Appl. Surf. Sci., 2019, vol. 465, pp. 700-714.CrossRef 29. Y. F. Juan, J. Li, Y. Q. Jiang, W. L. Jia and Z. J. Lu: Appl. Surf. Sci., 2019, vol. 465, pp. 700-714.CrossRef
30.
Zurück zum Zitat 30. B. Sefer and S. Virtanen: Corros. Sci., 2019, vol. 154, pp. 287-304.CrossRef 30. B. Sefer and S. Virtanen: Corros. Sci., 2019, vol. 154, pp. 287-304.CrossRef
31.
Zurück zum Zitat Ohmi T, Murota Y, Kirihara K, Kudoh M (2001) J. Jpn. Inst Met. 65:458-463.CrossRef Ohmi T, Murota Y, Kirihara K, Kudoh M (2001) J. Jpn. Inst Met. 65:458-463.CrossRef
32.
Zurück zum Zitat 32. J. J. Marattukalam, A. K. Singh, S. Datta, M. Das, V. K. Balla, S. Bontha and S. K. Kalpathy: Mater. Sci. Eng. C, 2015, vol. 57, pp. 309-13.CrossRef 32. J. J. Marattukalam, A. K. Singh, S. Datta, M. Das, V. K. Balla, S. Bontha and S. K. Kalpathy: Mater. Sci. Eng. C, 2015, vol. 57, pp. 309-13.CrossRef
33.
Zurück zum Zitat 33. H. Luo, Q. Yu, C. Dong, G. Sha, Z. Liu, J. Liang, L. Wang, G. Han and X. Li: Corros. Sci., 2018, vol. 139, pp. 185-196.CrossRef 33. H. Luo, Q. Yu, C. Dong, G. Sha, Z. Liu, J. Liang, L. Wang, G. Han and X. Li: Corros. Sci., 2018, vol. 139, pp. 185-196.CrossRef
34.
Zurück zum Zitat A. Conde, R. Colaco, R. Vilar and J. D. Damboreaen: Mater. Des., 2000, vol. 21, pp. 441-445.CrossRef A. Conde, R. Colaco, R. Vilar and J. D. Damboreaen: Mater. Des., 2000, vol. 21, pp. 441-445.CrossRef
35.
Zurück zum Zitat 35. X. Gong, Y. Li, Y. Nie, Z. Huang, F. Liu, L. Huang, L. Jiang and H. Mei: Corros. Sci., 2018, vol. 139, pp. 68-75.CrossRef 35. X. Gong, Y. Li, Y. Nie, Z. Huang, F. Liu, L. Huang, L. Jiang and H. Mei: Corros. Sci., 2018, vol. 139, pp. 68-75.CrossRef
36.
Zurück zum Zitat 36. V. M. C. A. Oliveira, C. Aguiar, A. M. Vazquez, A. Robin and M. J. R. Barboza: Corros. Sci., 2014, vol. 88, pp. 317-327.CrossRef 36. V. M. C. A. Oliveira, C. Aguiar, A. M. Vazquez, A. Robin and M. J. R. Barboza: Corros. Sci., 2014, vol. 88, pp. 317-327.CrossRef
37.
Zurück zum Zitat 37. M. L. Zheludkevich, R. Serra, M. F. Montemor, K. A. Yasakau, I. M. M. Salvado and M. G. S. Ferreira: Electrochim. Acta, 2005, vol. 51, pp. 208-217.CrossRef 37. M. L. Zheludkevich, R. Serra, M. F. Montemor, K. A. Yasakau, I. M. M. Salvado and M. G. S. Ferreira: Electrochim. Acta, 2005, vol. 51, pp. 208-217.CrossRef
38.
Zurück zum Zitat 38. J. B. Sun, G. A. Zhang, W. Liu and M. X. Lu: Corros. Sci., 2012, vol. 57, pp. 131-138.CrossRef 38. J. B. Sun, G. A. Zhang, W. Liu and M. X. Lu: Corros. Sci., 2012, vol. 57, pp. 131-138.CrossRef
39.
Zurück zum Zitat 39. H. Luo, Z. Li, A. M. Mingers and D. Raabe: Corros. Sci., 2018, vol. 134, pp. 131-139.CrossRef 39. H. Luo, Z. Li, A. M. Mingers and D. Raabe: Corros. Sci., 2018, vol. 134, pp. 131-139.CrossRef
40.
Zurück zum Zitat 40. C. P. Lee, C. C. Chang, Y. Y. Chen, J. W. Yeh and H. C. Shih: Corros. Sci., 2008, vol. 50, pp. 2053-2060.CrossRef 40. C. P. Lee, C. C. Chang, Y. Y. Chen, J. W. Yeh and H. C. Shih: Corros. Sci., 2008, vol. 50, pp. 2053-2060.CrossRef
41.
Zurück zum Zitat 41. B. Deng, Z. Wang, Y. Jiang, H. Wang, J. Gao and J. Li: Electrochim. Acta, 2009, vol. 54, pp. 2790-2794.CrossRef 41. B. Deng, Z. Wang, Y. Jiang, H. Wang, J. Gao and J. Li: Electrochim. Acta, 2009, vol. 54, pp. 2790-2794.CrossRef
42.
Zurück zum Zitat 42. T. Poornima, N. Jagannatha and A. N. Shetty: Port. Electrochim. Acta, 2010, vol. 28, pp. 173-188.CrossRef 42. T. Poornima, N. Jagannatha and A. N. Shetty: Port. Electrochim. Acta, 2010, vol. 28, pp. 173-188.CrossRef
43.
Zurück zum Zitat 43. M. P. Ryan, D. E. Williams, R. J. Chater, B. M. Hutton and D. S. McPhail: Nature, 2002, vol. 415, p 770.CrossRef 43. M. P. Ryan, D. E. Williams, R. J. Chater, B. M. Hutton and D. S. McPhail: Nature, 2002, vol. 415, p 770.CrossRef
44.
Zurück zum Zitat 44. S. K. Bonagani, V. Bathula and V. Kain: Corros. Sci., 2018, vol. 131, pp. 340-354.CrossRef 44. S. K. Bonagani, V. Bathula and V. Kain: Corros. Sci., 2018, vol. 131, pp. 340-354.CrossRef
45.
Zurück zum Zitat 45. J. Gong, Y. M. Jiang, B. Deng, J. L. Xu, J. P. Hu and J. Li: Electrochim. Acta, 2010, vol. 55, pp. 5077-5083.CrossRef 45. J. Gong, Y. M. Jiang, B. Deng, J. L. Xu, J. P. Hu and J. Li: Electrochim. Acta, 2010, vol. 55, pp. 5077-5083.CrossRef
Metadaten
Titel
Influence of Cr Content on the Microstructure and Electrochemical Corrosion in Plasma Cladding Ni-Cr Coatings
verfasst von
Wenya Zhang
Canming Wang
Qiang Song
Hongzhi Cui
Xiaoli Feng
Chunzhi Zhang
Publikationsdatum
13.09.2019
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 11/2019
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-019-05440-5

Weitere Artikel der Ausgabe 11/2019

Metallurgical and Materials Transactions A 11/2019 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.