Influence of La2O3 and Ce2O3 additions on structure and properties of aluminoborosilicate glasses

verfasst von: Yadong Lu, Hongting Liu, Ya Qu, Hao Lu, Sanxi Huang, Yunlong Yue

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 3/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Aluminoborosilicate glasses with different amounts of La2O3 and Ce2O3 were prepared respectively by the conventional melting-quenching method. The structure, thermal property parameters and dielectric property parameters were investigated by Fourier-Transform Infrared Spectroscopy (FTIR), Differential Scanning Calorimetry and the impedance analyzer. Results from FTIR displayed that the degree of polymerization increased first and then fell down with the addition of La2O3, and reached the maximum value when the amount was 0.5 mol%. Meanwhile, the degree of polymerization of glasses doped with Ce2O3 arrived at the largest as the content of Ce2O3 reached 2.0 mol%. The thermal stability of glasses doped with La2O3 got enhanced first and then deteriorated, and reached the maximum when the content was 0.5 mol%; Meanwhile, the glasses doped with Ce2O3 also fluctuated a little. The dielectric constant (ε) and dielectric loss (tan α) of the samples fell down as the frequency increased. The ε and tan α of the samples doped with La2O3 reached the minimum value when the amount got to 0.5 mol%; The ε of the glasses doped with Ce2O3 turned minimum when the amount was zero, but the tan α was the smallest when the amount reached 1.0 mol%.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
2.
Zurück zum Zitat S. Kerisit, J.V. Ryan, E.M. Pierce, J. Non-Cryst. Solids 378, 273 (2013)CrossRef S. Kerisit, J.V. Ryan, E.M. Pierce, J. Non-Cryst. Solids 378, 273 (2013)CrossRef
3.
Zurück zum Zitat P. Lin, G. Zhao, Y. Hao, J. Wang, W. Weng, G. Han, J. Chin. Ceram. Soc. 35, 856 (2007) P. Lin, G. Zhao, Y. Hao, J. Wang, W. Weng, G. Han, J. Chin. Ceram. Soc. 35, 856 (2007)
4.
Zurück zum Zitat N. Ollier, T. Charpentier, B. Boizot, G. Wallez, D. Ghaleb, J. Non-Cryst. Solids 341, 26 (2004)CrossRef N. Ollier, T. Charpentier, B. Boizot, G. Wallez, D. Ghaleb, J. Non-Cryst. Solids 341, 26 (2004)CrossRef
6.
Zurück zum Zitat X. Zhang, Y. Yue, H. Wu, J. Mater. Sci. Mater. Electron. 24, 2755 (2013)CrossRef X. Zhang, Y. Yue, H. Wu, J. Mater. Sci. Mater. Electron. 24, 2755 (2013)CrossRef
7.
Zurück zum Zitat M. Bengisu, R.K. Brow, E. Yilmaz, S.T. Reis, J. Non-Cryst. Solids 352, 3668 (2006)CrossRef M. Bengisu, R.K. Brow, E. Yilmaz, S.T. Reis, J. Non-Cryst. Solids 352, 3668 (2006)CrossRef
8.
Zurück zum Zitat J.G. Wood, S. Prabakar, K.T. Mueller, C.G. Pantano, J. Non-Cryst. Solids 349, 276 (2004)CrossRef J.G. Wood, S. Prabakar, K.T. Mueller, C.G. Pantano, J. Non-Cryst. Solids 349, 276 (2004)CrossRef
9.
Zurück zum Zitat M. Piotrowicz, D. Cianciara XXIst International Congress on Glass (ICG 2007), vol 49 (2011, p. 192) M. Piotrowicz, D. Cianciara XXIst International Congress on Glass (ICG 2007), vol 49 (2011, p. 192)
10.
Zurück zum Zitat A. Quintas, O. Majérus, D. Caurant, J.L. Dussossoy, P. Vermaut, J. Am. Ceram. Soc. 90, 712 (2007)CrossRef A. Quintas, O. Majérus, D. Caurant, J.L. Dussossoy, P. Vermaut, J. Am. Ceram. Soc. 90, 712 (2007)CrossRef
11.
Zurück zum Zitat J. Marchi, D.S. Morais, J. Schneider, J.C. Bressiani, A.H.A. Bressiani, J. Non-Cryst. Solids 87, 863 (2005)CrossRef J. Marchi, D.S. Morais, J. Schneider, J.C. Bressiani, A.H.A. Bressiani, J. Non-Cryst. Solids 87, 863 (2005)CrossRef
12.
Zurück zum Zitat D. Caurant, A. Quintas, O. Majérus, T. Charpentier, I. Bardez, Adv. Mater. Res. 39–40, 19 (2008)CrossRef D. Caurant, A. Quintas, O. Majérus, T. Charpentier, I. Bardez, Adv. Mater. Res. 39–40, 19 (2008)CrossRef
13.
Zurück zum Zitat S.V. Smiljanić, S.R. Grujić, M.B. Tošić et al., Ceram. Int. 40, 297 (2014)CrossRef S.V. Smiljanić, S.R. Grujić, M.B. Tošić et al., Ceram. Int. 40, 297 (2014)CrossRef
14.
15.
Zurück zum Zitat N.S. Rao, L.S. Rao, Y. Gandhi, N. Veeraiah, V. Ravikumar, Phys. B 405, 4092 (2010)CrossRef N.S. Rao, L.S. Rao, Y. Gandhi, N. Veeraiah, V. Ravikumar, Phys. B 405, 4092 (2010)CrossRef
16.
Zurück zum Zitat S.M. Lu, X.M. Yuan, X.H. Zhang, Y.J. Cui, H.T. Wu, Y.L. Yue, Adv. Mater. Res. 710, 127 (2013)CrossRef S.M. Lu, X.M. Yuan, X.H. Zhang, Y.J. Cui, H.T. Wu, Y.L. Yue, Adv. Mater. Res. 710, 127 (2013)CrossRef
17.
18.
Zurück zum Zitat Y. Ni, C. Lu, Y. Zhang, Q. Zhang, Z. Xu, J. Rare Earths 25, 94 (2007)CrossRef Y. Ni, C. Lu, Y. Zhang, Q. Zhang, Z. Xu, J. Rare Earths 25, 94 (2007)CrossRef
19.
20.
Zurück zum Zitat W. Mozgawa, M. Król, J. Dyczek, J. Deja, Spectrochim. Acta A 132, 889 (2014)CrossRef W. Mozgawa, M. Król, J. Dyczek, J. Deja, Spectrochim. Acta A 132, 889 (2014)CrossRef
21.
Zurück zum Zitat Q. Zheng, M. Potuzak, J.C. Mauro, M.M. Smedskjaer, R.E. Youngman, Y. Yue, J. Non-Cryst. Solids 358, 993 (2012)CrossRef Q. Zheng, M. Potuzak, J.C. Mauro, M.M. Smedskjaer, R.E. Youngman, Y. Yue, J. Non-Cryst. Solids 358, 993 (2012)CrossRef
22.
Zurück zum Zitat N.I. Ya-Ru, L.U. Chun-Hua, Y. Zhang, Q.T. Zhang, X.U. Zhong-Zi, J. Mater. Sci. Eng. 24, 858 (2006) N.I. Ya-Ru, L.U. Chun-Hua, Y. Zhang, Q.T. Zhang, X.U. Zhong-Zi, J. Mater. Sci. Eng. 24, 858 (2006)
23.
Zurück zum Zitat A. Quintas, O. Majérus, M. Lenoir, D. Caurant, K. Klementiev, A. Webb, J. Non-Cryst. Solids 354, 98 (2008)CrossRef A. Quintas, O. Majérus, M. Lenoir, D. Caurant, K. Klementiev, A. Webb, J. Non-Cryst. Solids 354, 98 (2008)CrossRef
24.
Zurück zum Zitat E. Malchukova, B. Boizot, G. Petite, D. Ghaleb, J. Non-Cryst. Solids 354, 3592 (2008)CrossRef E. Malchukova, B. Boizot, G. Petite, D. Ghaleb, J. Non-Cryst. Solids 354, 3592 (2008)CrossRef
25.
Zurück zum Zitat Q. Zheng, M. Potuzak, J.C. Mauro, M.M. Smedskjaer, R.E. Youngman, Y. Yue, J. Non-Cryst. Solids 358, 993 (2012)CrossRef Q. Zheng, M. Potuzak, J.C. Mauro, M.M. Smedskjaer, R.E. Youngman, Y. Yue, J. Non-Cryst. Solids 358, 993 (2012)CrossRef
26.
Zurück zum Zitat A.A. Alemi, H. Sedghi, A.R. Mirmohseni, V. Golsanamlu, Bull. Mater. Sci. 29, 55 (2006)CrossRef A.A. Alemi, H. Sedghi, A.R. Mirmohseni, V. Golsanamlu, Bull. Mater. Sci. 29, 55 (2006)CrossRef
27.
Zurück zum Zitat W. Soppe, C.V.D. Marel, W.F.V. Gunsteren, H.W.D. Hartog, J. Non-Cryst. Solids 103, 201 (1988)CrossRef W. Soppe, C.V.D. Marel, W.F.V. Gunsteren, H.W.D. Hartog, J. Non-Cryst. Solids 103, 201 (1988)CrossRef
28.
29.
Zurück zum Zitat I. Dyamant, E. Korin, J. Hormadaly, J. Non-Cryst. Solids 354, 3135 (2008)CrossRef I. Dyamant, E. Korin, J. Hormadaly, J. Non-Cryst. Solids 354, 3135 (2008)CrossRef
30.
31.
Zurück zum Zitat P.A. Bingham, R.J. Hand, S.D. Forder, Mater. Res. Bull. 41, 1622 (2006)CrossRef P.A. Bingham, R.J. Hand, S.D. Forder, Mater. Res. Bull. 41, 1622 (2006)CrossRef
32.
33.
Zurück zum Zitat A. Arora, K. Singh, O.P. Pandey, Int. J. Hydrogen Energy 36, 14948 (2011)CrossRef A. Arora, K. Singh, O.P. Pandey, Int. J. Hydrogen Energy 36, 14948 (2011)CrossRef
34.
Zurück zum Zitat A. Arora, A. Goel, E.R. Shaaban, K. Singh, O.P. Pandey, J.M.F. Ferreira, Phys. B 403, 1738 (2008)CrossRef A. Arora, A. Goel, E.R. Shaaban, K. Singh, O.P. Pandey, J.M.F. Ferreira, Phys. B 403, 1738 (2008)CrossRef
35.
Zurück zum Zitat N.O. Dantas, W.E.F. Ayta, A.C.A. Silva, N.F. Cano, S.W. Silva, P.C. Morais, Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 81, 140 (2011)CrossRef N.O. Dantas, W.E.F. Ayta, A.C.A. Silva, N.F. Cano, S.W. Silva, P.C. Morais, Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 81, 140 (2011)CrossRef
36.
37.
38.
Metadaten
Titel
Influence of La2O3 and Ce2O3 additions on structure and properties of aluminoborosilicate glasses
verfasst von
Yadong Lu
Hongting Liu
Ya Qu
Hao Lu
Sanxi Huang
Yunlong Yue
Publikationsdatum
14.10.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 3/2017
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-5850-1

Weitere Artikel der Ausgabe 3/2017

Journal of Materials Science: Materials in Electronics 3/2017 Zur Ausgabe

Neuer Inhalt