Influence of Mechanical and Durability Properties of Concrete with Limestone Powder

verfasst von : Nishat Naila Meghna, Ismat Abida, Nayeem Mohammad Mashfiq, Tasnia Ahmed, Mohammad Rezaul Karim, Md. Jahidul Islam

Erschienen in: Proceedings of the Canadian Society for Civil Engineering Annual Conference 2023, Volume 6

Verlag: Springer Nature Switzerland

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Concrete is the most commonly used material in the world for construction, and to produce this large amount of concrete requires the production of large quantities of cement, which results in the degradation of the environment by releasing harmful gases. One approach for making eco-friendly concrete is to use less cement in concrete; for that aim, other cementitious materials can be utilized as a partial replacement for cement. This study focuses on the mechanical and durability properties of concrete having limestone powder (LSP) as a partial replacement for cement. Five different combinations are considered for this study; the LSP replacement level is 5, 10, 15, and 20% (by weight). The result indicates that the slump value increases with increasing LSP content. At 28 days, compressive strength and flexural strength are the highest for replacing 10% cement with LSP. The concrete cylinders are subjected to elevated temperatures (200 and 400 °C) for one hour and then cooled down to room temperature (25 °C). Reduction in compressive strength with increased temperature is up to 6% at 200 °C temperature and up to 11% at 400 °C temperature. Therefore, incorporating 10% LSP in concrete as a replacement for Portland cement will increase concrete's mechanical and durability properties.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Mehta PK, Monteiro PJM (2014) Concrete: microstructure, properties, and materials, 4th edn. McGraw-Hill Education, New YorkMATH Mehta PK, Monteiro PJM (2014) Concrete: microstructure, properties, and materials, 4th edn. McGraw-Hill Education, New YorkMATH
2.
Zurück zum Zitat Mehta K (2001) Reducing the environmental impact of concrete. Concr Int 23:61–66MATH Mehta K (2001) Reducing the environmental impact of concrete. Concr Int 23:61–66MATH
3.
Zurück zum Zitat Meddah MS, Lmbachiya MC, Dhir RKJC, Materials B (2014) Potential use of binary and composite limestone cements in concrete production. Constr Build Mater 58:193–205CrossRefMATH Meddah MS, Lmbachiya MC, Dhir RKJC, Materials B (2014) Potential use of binary and composite limestone cements in concrete production. Constr Build Mater 58:193–205CrossRefMATH
4.
Zurück zum Zitat BS EN 197–1:2011 (2011) Cement-part 1: composition, specifications and conformity criteria for common cements. British Standards Institution BS EN 197–1:2011 (2011) Cement-part 1: composition, specifications and conformity criteria for common cements. British Standards Institution
5.
Zurück zum Zitat Malhotra VM, Mehta PK (2008) High performance, high-volume fly ash concrete for building sustainable and durable structure. 3rd edn. Canada Malhotra VM, Mehta PK (2008) High performance, high-volume fly ash concrete for building sustainable and durable structure. 3rd edn. Canada
6.
Zurück zum Zitat Islam MJ, Borsha NT, Meghna NN, Enam RBT (2023) Mechanical and durability properties of fly ash blended concrete with Gi Fiber. In: Proceedings of the Canadian society of civil engineering annual conference 2021 Singapore. Springer Nature Singapore, pp 135–145 Islam MJ, Borsha NT, Meghna NN, Enam RBT (2023) Mechanical and durability properties of fly ash blended concrete with Gi Fiber. In: Proceedings of the Canadian society of civil engineering annual conference 2021 Singapore. Springer Nature Singapore, pp 135–145
7.
Zurück zum Zitat Mehta P (2010) Sustainable cements and concrete for the climate change era–a review. In: 2nd international conference on sustainable construction materials and technologies Mehta P (2010) Sustainable cements and concrete for the climate change era–a review. In: 2nd international conference on sustainable construction materials and technologies
8.
Zurück zum Zitat Celik K et al (2014) High-volume natural volcanic pozzolan and limestone powder as partial replacements for Portland cement in self-compacting and sustainable concrete. Cement Concr Compos 45:136–147CrossRefMATH Celik K et al (2014) High-volume natural volcanic pozzolan and limestone powder as partial replacements for Portland cement in self-compacting and sustainable concrete. Cement Concr Compos 45:136–147CrossRefMATH
9.
Zurück zum Zitat Pipilikaki P, Katsioti M (2009) Study of the hydration process of quaternary blended cements and durability of the produced mortars and concretes. Constr Build Mater 23:2246–2250 Pipilikaki P, Katsioti M (2009) Study of the hydration process of quaternary blended cements and durability of the produced mortars and concretes. Constr Build Mater 23:2246–2250
10.
Zurück zum Zitat Vance K, Kumar A, Sant G, Neithalath N (2013) The rheological properties of ternary binders containing portland cement, limestone, and Metakaolin or Fly Ash. Cem Concr Res 52:196–207 Vance K, Kumar A, Sant G, Neithalath N (2013) The rheological properties of ternary binders containing portland cement, limestone, and Metakaolin or Fly Ash. Cem Concr Res 52:196–207
11.
Zurück zum Zitat Lothenbach B, Le Saout G, Gallucci E, Scrivener K (2008) Influence of limestone on the hydration of Portland cements. Cem Concr Res 38(6):848–860 Lothenbach B, Le Saout G, Gallucci E, Scrivener K (2008) Influence of limestone on the hydration of Portland cements. Cem Concr Res 38(6):848–860
12.
Zurück zum Zitat Celik K, Hay R, Hargis CW, Moon J (2019) Effect of volcanic ash pozzolan or limestone replacement on hydration of Portland cement. Constr Build Mater 197:803–812CrossRef Celik K, Hay R, Hargis CW, Moon J (2019) Effect of volcanic ash pozzolan or limestone replacement on hydration of Portland cement. Constr Build Mater 197:803–812CrossRef
13.
Zurück zum Zitat Pliya P, Cree D (2015) Limestone derived eggshell powder as a replacement in Portland cement mortar. Constr Build Mater 95:1–9 Pliya P, Cree D (2015) Limestone derived eggshell powder as a replacement in Portland cement mortar. Constr Build Mater 95:1–9
14.
Zurück zum Zitat ASTM C188–17 (2017) Standard test method for density of hydraulic cement. ASTM International ASTM C188–17 (2017) Standard test method for density of hydraulic cement. ASTM International
15.
Zurück zum Zitat ASTM C33–18 (2018) Standard specification for concrete aggregates. ASTM International, West Conshohocken, PA ASTM C33–18 (2018) Standard specification for concrete aggregates. ASTM International, West Conshohocken, PA
16.
Zurück zum Zitat ASTM C143–15 (2015) Standard test method for slump of hydraulic-cement concrete. ASTM International, West Conshohocken, PA ASTM C143–15 (2015) Standard test method for slump of hydraulic-cement concrete. ASTM International, West Conshohocken, PA
17.
Zurück zum Zitat ASTM C39–20 (2020) Standard test method for compressive strength of cylindrical concrete specimens. ASTM International, West Conshohocken, PA ASTM C39–20 (2020) Standard test method for compressive strength of cylindrical concrete specimens. ASTM International, West Conshohocken, PA
18.
Zurück zum Zitat ASTM C78–16 (2016) Standard test method for flexural strength of concrete (using simple beam with third-point loading). ASTM International, West Conshohocken, PA ASTM C78–16 (2016) Standard test method for flexural strength of concrete (using simple beam with third-point loading). ASTM International, West Conshohocken, PA
19.
Zurück zum Zitat Wang D, Shi C, Farzadnia N, Shi Z, Jia H (2018) A review on effects of limestone powder on the properties of concrete. Constr Build Mater 192:153–166 Wang D, Shi C, Farzadnia N, Shi Z, Jia H (2018) A review on effects of limestone powder on the properties of concrete. Constr Build Mater 192:153–166
20.
Zurück zum Zitat Sellevold EJ, Bager DH, Klitgaard Jensen E, Knudsen T (1982) Silica fume cement paste—hydration and pore structure. In: Silica fume cement paste—hydration and pore structure, presented at the condensed silica fume in concrete. Norwegian Institute of Technology, University of Trondheim, Norway Sellevold EJ, Bager DH, Klitgaard Jensen E, Knudsen T (1982) Silica fume cement paste—hydration and pore structure. In: Silica fume cement paste—hydration and pore structure, presented at the condensed silica fume in concrete. Norwegian Institute of Technology, University of Trondheim, Norway
21.
Zurück zum Zitat Li W, Huang Z, Cao F, Sun Z, Shah SP (2015) Effects of nano-silica and nano-limestone on flowability and mechanical properties of ultra-high-performance concrete matrix. Constr Build Mater 95:366–374 Li W, Huang Z, Cao F, Sun Z, Shah SP (2015) Effects of nano-silica and nano-limestone on flowability and mechanical properties of ultra-high-performance concrete matrix. Constr Build Mater 95:366–374
22.
Zurück zum Zitat Wang D, Shi C, Farzadnia N, Shi Z, Jia H, Ou Z (2018) A review on use of limestone powder in cement-based materials: mechanism, hydration and microstructures. Constr Build Mater 181:659–672 Wang D, Shi C, Farzadnia N, Shi Z, Jia H, Ou Z (2018) A review on use of limestone powder in cement-based materials: mechanism, hydration and microstructures. Constr Build Mater 181:659–672
23.
Zurück zum Zitat Janotka I, Nürnbergerová T (2005) Effect of temperature on structural quality of the cement paste and high-strength concrete with silica fume. Nucl Eng Des 235(17):2019–2032 Janotka I, Nürnbergerová T (2005) Effect of temperature on structural quality of the cement paste and high-strength concrete with silica fume. Nucl Eng Des 235(17):2019–2032
24.
Zurück zum Zitat Le QX, Dao VTN, Torero JL, Maluk C, Bisby L (2017) Effects of temperature and temperature gradient on concrete performance at elevated temperatures. Adv Struct Eng 21(8):1223–1233 Le QX, Dao VTN, Torero JL, Maluk C, Bisby L (2017) Effects of temperature and temperature gradient on concrete performance at elevated temperatures. Adv Struct Eng 21(8):1223–1233
25.
Zurück zum Zitat Shen J, Xu Q (2019) Effect of elevated temperatures on compressive strength of concrete. Constr Build Mater 229:116846 Shen J, Xu Q (2019) Effect of elevated temperatures on compressive strength of concrete. Constr Build Mater 229:116846
26.
Zurück zum Zitat Chang YF, Chen YH, Sheu MS, Yao GC (2006) Residual stress–strain relationship for concrete after exposure to high temperatures. Cem Concr Res 36(10):1999–2005 Chang YF, Chen YH, Sheu MS, Yao GC (2006) Residual stress–strain relationship for concrete after exposure to high temperatures. Cem Concr Res 36(10):1999–2005
27.
Zurück zum Zitat Mohammadhosseini H, Tahir MM, Alyousef R, Alabduljabbar H, Samadi M (2019) Effect of elevated temperatures on properties of sustainable concrete composites incorporating waste metalized plastic fibres. SN Appl Sci 1(11):1520 Mohammadhosseini H, Tahir MM, Alyousef R, Alabduljabbar H, Samadi M (2019) Effect of elevated temperatures on properties of sustainable concrete composites incorporating waste metalized plastic fibres. SN Appl Sci 1(11):1520
28.
Zurück zum Zitat Fletcher I, Welch S, Torero J, Carvel R, Usmani A (2007) Behaviour of concrete structures in fire. Therm Sci-THERM SCI 11:37–52 Fletcher I, Welch S, Torero J, Carvel R, Usmani A (2007) Behaviour of concrete structures in fire. Therm Sci-THERM SCI 11:37–52
29.
Zurück zum Zitat Shen Z, Zhou H, Brooks A, Hanna D (2021) Evolution of elastic and thermal properties of cementitious composites containing micro-size lightweight fillers after exposure to elevated temperature. Cem Concr Compos 118:103931 Shen Z, Zhou H, Brooks A, Hanna D (2021) Evolution of elastic and thermal properties of cementitious composites containing micro-size lightweight fillers after exposure to elevated temperature. Cem Concr Compos 118:103931
Metadaten
Titel
Influence of Mechanical and Durability Properties of Concrete with Limestone Powder
verfasst von
Nishat Naila Meghna
Ismat Abida
Nayeem Mohammad Mashfiq
Tasnia Ahmed
Mohammad Rezaul Karim
Md. Jahidul Islam
Copyright-Jahr
2025
DOI
https://doi.org/10.1007/978-3-031-61507-8_9