Influence of Mg2+/Ga3+ doping on luminescence of Y3Al5O12:Ce3+ phosphors
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 20/2018
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Mg2+/Ga3+ doped Y3Al5O12:Ce3+ phosphors were synthesized through a solid state reaction. The phase and luminescent of the synthesized phosphors were investigated. For Ga3+ codoped Y2.96Ce0.04Al(5−x)GaxO12 phosphors, the emission intensity increases with the increase of Ga3+ concentration up to Y2.96Ce0.04Al4.80Ga0.20O12 and then decreases with a further increase of Ga3+ concentration, but the emission peak shifts to shorter wavelength continuously in the Ga3+ doping concentration range of 0.05–0.25. For Mg2+/Ga3+ codoped Y2.96Ce0.04Al(4.8−y)Ga0.20MgyO12 phosphors, the emission intensity decreases and the emission peak shifts to longer wavelength continuously in the Mg2+ doping concentration range of 0.02–0.12. The emission spectra of Y2.96Ce0.04Al(4.8−y)Ga0.20MgyO12 phosphors demonstrate that the codoped Mg2+/Ga3+ ions not only induce the enhancement of Y2.96Ce0.04Al5O12 emission intensity but also lead to the red shift of Y2.96Ce0.04Al5O12 emission peak. The decay lifetimes decrease in Mg2+/Ga3+ codoped Y2.96Ce0.04Al5O12 phosphors due to defects formed by substitutions of Y3+ by Mg2+/Ga3+.