Influence of Nanoclay/Phenol Formaldehyde Resin on Wood Polymer Nanocomposites

verfasst von : M. R. Rahman

Erschienen in: Wood Polymer Nanocomposites

Verlag: Springer International Publishing

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In this study, the introduction of nanofiller into phenol formaldehyde matrix formed wood polymer nanocomposites (WPNCs). FT-IR results showed that the addition of nanoclay into phenol formaldehyde (PF) formed H-bonding interaction with hydroxyl groups by reducing the wave number of the peak. The Thermogravimetric Analysis (TGA) results showed that WPNCs were thermally stable compared to the raw ones. The MOE and MOR of WPNCs were significantly improved for Eugenia spp., Xylopia spp., Artocarpus Rigidus, and Artocarpus Elasticus respectively. The Young’s modulus of WPNCs on Eugenia spp. was significantly higher compared to raw wood. From X-ray diffraction results, WPNCs showed improved crystallinity at the amorphous region due to the polymer loading. SEM micrograph of WPNCs showed that void space was filled with the polymer, and the waxy substance was removed. All the nanofiller/phenol formaldehyde was significantly effective on Eugenia spp. followed by Xylopia spp., Artocarpus Rigidus, and Artocarpus Elasticus wood species, respectively.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
Zurück zum Zitat Adebhar T, Roscher C, Adam J (2001) Reinforcing nanoparticles in reactive resins. Eur Coat J 4:144 Adebhar T, Roscher C, Adam J (2001) Reinforcing nanoparticles in reactive resins. Eur Coat J 4:144
Zurück zum Zitat Cai XB, Riedl SY, Zhang Wan H (2007) Formation and properties of nanocomposites made up from solid aspen wood, melamine-urea-formaldehyde, and clay. Holz 61:148–154 Cai XB, Riedl SY, Zhang Wan H (2007) Formation and properties of nanocomposites made up from solid aspen wood, melamine-urea-formaldehyde, and clay. Holz 61:148–154
Zurück zum Zitat Cai X, Riedl B, Zhang SY, Wan H (2008) The impact of the nature of nanofillers on the performance of wood polymer nanocomposites. Compos Part A 39:727–737CrossRef Cai X, Riedl B, Zhang SY, Wan H (2008) The impact of the nature of nanofillers on the performance of wood polymer nanocomposites. Compos Part A 39:727–737CrossRef
Zurück zum Zitat Choi YK, Sugimoto KI, Song SM, Gotoh Y, Ohkoshi Y, Endo M (2005) Mechanical and physical properties of epoxy composites reinforced by vapor grown carbon nanofibers. Carbon 43:208–2199CrossRef Choi YK, Sugimoto KI, Song SM, Gotoh Y, Ohkoshi Y, Endo M (2005) Mechanical and physical properties of epoxy composites reinforced by vapor grown carbon nanofibers. Carbon 43:208–2199CrossRef
Zurück zum Zitat Haggenmueller R, Du F, Fischer JE, Winey KI (2006) Interfacial in situ polymerization of single wall carbon nanotube/nylon 66 nanocomposites. Polym 47:2381–2388CrossRef Haggenmueller R, Du F, Fischer JE, Winey KI (2006) Interfacial in situ polymerization of single wall carbon nanotube/nylon 66 nanocomposites. Polym 47:2381–2388CrossRef
Zurück zum Zitat Hamdan S, Talib ZA, Rahman MR, Ahmed AS, Islam MS (2010) Dynamic Young’s modulus measurement of treated and post-treated tropical wood polymer composites (WPC). BioRes 5(1):324–342 Hamdan S, Talib ZA, Rahman MR, Ahmed AS, Islam MS (2010) Dynamic Young’s modulus measurement of treated and post-treated tropical wood polymer composites (WPC). BioRes 5(1):324–342
Zurück zum Zitat Kinloch AJ, Lee JH, Taylor AC, Sprenger S, Eger C, Egan D (2003) Toughening structural adhesives via nano- and micro-phase inclusions. J Adhes 79:73–867CrossRef Kinloch AJ, Lee JH, Taylor AC, Sprenger S, Eger C, Egan D (2003) Toughening structural adhesives via nano- and micro-phase inclusions. J Adhes 79:73–867CrossRef
Zurück zum Zitat Mulinari DR, Voorwald HJC, Cioffi MOH, Rocha GJ, Pinto Da Silva MLC (2010) Surface modification of sugarcane bagasse cellulose and its effect on mechanical and water absorption properties of sugarcane bagasse cellulose/HDPE composites. BioRes 5(2):661–671 Mulinari DR, Voorwald HJC, Cioffi MOH, Rocha GJ, Pinto Da Silva MLC (2010) Surface modification of sugarcane bagasse cellulose and its effect on mechanical and water absorption properties of sugarcane bagasse cellulose/HDPE composites. BioRes 5(2):661–671
Zurück zum Zitat Owen NL, Thomas DW (1989) Infrared studies of hard and soft woods. Appl Spec 43:451–455CrossRef Owen NL, Thomas DW (1989) Infrared studies of hard and soft woods. Appl Spec 43:451–455CrossRef
Zurück zum Zitat Rahman MR, Hamdan S, Saleh AA, Islam MS (2010) Mechanical and biological performance of sodium mataperiodate impregnated plasticized wood (PW). BioRes 5(2):1022–1035 Rahman MR, Hamdan S, Saleh AA, Islam MS (2010) Mechanical and biological performance of sodium mataperiodate impregnated plasticized wood (PW). BioRes 5(2):1022–1035
Zurück zum Zitat Rodgers RM, Mahfuz H, Rangari VK, Chisholm N, Jeelani S (2005) Infusion of SiC nanoparticles into SC-15 epoxy: an investigation of thermal and mechanical response. Macromol Mater Eng 290:423–429CrossRef Rodgers RM, Mahfuz H, Rangari VK, Chisholm N, Jeelani S (2005) Infusion of SiC nanoparticles into SC-15 epoxy: an investigation of thermal and mechanical response. Macromol Mater Eng 290:423–429CrossRef
Zurück zum Zitat Shah RK, Paul DR (2004) Nylon 6 nanocomposites prepared by a melt mixing masterbatch process. Polym 45:2991–3000CrossRef Shah RK, Paul DR (2004) Nylon 6 nanocomposites prepared by a melt mixing masterbatch process. Polym 45:2991–3000CrossRef
Zurück zum Zitat Uddin M, Sun CT (2008) Strength of unidirectional glass/epoxy composite with silica nanoparticle-enhanced matrix. Compos Sci Technol 68:1637–1643CrossRef Uddin M, Sun CT (2008) Strength of unidirectional glass/epoxy composite with silica nanoparticle-enhanced matrix. Compos Sci Technol 68:1637–1643CrossRef
Zurück zum Zitat Varhegyi G, Antal MJJ, Jakab E (1997) Kinetics modeling of biomass pyrolysis. J Anal Appl Pyrol 42:73–87CrossRef Varhegyi G, Antal MJJ, Jakab E (1997) Kinetics modeling of biomass pyrolysis. J Anal Appl Pyrol 42:73–87CrossRef
Zurück zum Zitat Wu CL, Li XP, Qing SL (2004) Cellulose solvent: current research status and its application prospect. Trans China Pulp Paper 19(2):171–175 Wu CL, Li XP, Qing SL (2004) Cellulose solvent: current research status and its application prospect. Trans China Pulp Paper 19(2):171–175
Zurück zum Zitat Yasmin A, Abot JL, Daniel IM (2003) Processing of clay/epoxy nanocomposites by shear mixing. Scripta Mater 49:6–81CrossRef Yasmin A, Abot JL, Daniel IM (2003) Processing of clay/epoxy nanocomposites by shear mixing. Scripta Mater 49:6–81CrossRef
Zurück zum Zitat Zheng H, Ning R, Zheng Y (2005) Study of SiO2 nanoparticles on the improved performance of epoxy and fiber composites. J Reinf Plastic Compos 24:223–233CrossRef Zheng H, Ning R, Zheng Y (2005) Study of SiO2 nanoparticles on the improved performance of epoxy and fiber composites. J Reinf Plastic Compos 24:223–233CrossRef
Zurück zum Zitat Zilg C, Mulhaupt R, Finter J (1999) Morphology and toughness/stiffness balance of nanocomposites based upon anhydride-cured epoxy resins and layered silicates. Macromol Chem Phys 200:661CrossRef Zilg C, Mulhaupt R, Finter J (1999) Morphology and toughness/stiffness balance of nanocomposites based upon anhydride-cured epoxy resins and layered silicates. Macromol Chem Phys 200:661CrossRef
Zurück zum Zitat Zilg C, Thomman T, Finter J, Mulhaupt R (2000) The influence of silicate modification and compatibilizers on mechanical properties and morphology of anhydridecured epoxy nanocomposites. Macromol Mater Eng 280:41CrossRef Zilg C, Thomman T, Finter J, Mulhaupt R (2000) The influence of silicate modification and compatibilizers on mechanical properties and morphology of anhydridecured epoxy nanocomposites. Macromol Mater Eng 280:41CrossRef
Metadaten
Titel
Influence of Nanoclay/Phenol Formaldehyde Resin on Wood Polymer Nanocomposites
verfasst von
M. R. Rahman
Copyright-Jahr
2018
DOI
https://doi.org/10.1007/978-3-319-65735-6_8

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.