Influence of Ni Content on the Microstructure and Dry Sliding Wear Properties of Cr₁₃Ni₅Si₂/γ Intermetallic Alloys

The effect of Ni content on microstructure, hardness, and wear resistance was studied for the Cr₁₃Ni₅Si₂-base intermetallic alloys toughened by Ni-base solid solution (γ). Volume fraction and microhardness of the Cr₁₃Ni₅Si₂ primary dendrite as well as the average hardness of the Cr₁₃Ni₅Si₂/γ alloy decrease with the increasing Ni content. The Cr₁₃Ni₅Si₂/γ alloys have excellent wear resistance under dry sliding wear test conditions, which increases under high contact load wear conditions and decreases under low contact load wear test conditions with the increasing Ni content. The high wear resistance is due to the combination of high toughness of γ and high hardness of Cr₁₃Ni₅Si₂ and formation of a transferred cover layer on the worn surface during wear process. The wear rate of the Cr₁₃Ni₅Si₂/γ alloy is governed by the slow process of microspalling or pullout of the cracked Cr₁₃Ni₅Si₂ primary dendrites. The Cr₁₃Ni₅Si₂/γ alloys have extremely low load sensitivity of wear and the load-sensitivity coefficient of wear decreases drastically as the Ni content increases.