Interfacial Kinetics of High-Al-Containing Ultra-Lightweight Steels with Calcium Silicate-Based Molten Oxides at High Temperature

verfasst von: Gi Hyun Kim, Il Sohn

Erschienen in: Metallurgical and Materials Transactions B | Ausgabe 3/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The kinetics of the high-temperature reaction between high-Al- and -Mn-containing steels and synthesized molten calcium silicate-based fluxes from 1623 K to 1643 K (1350 °C to 1370 °C) was studied. Cylindrical steel rods were rotated in the molten fluxes for 300 to 1200 seconds at various temperatures below the melting point of the steels. The rods were connected to a rheometer, and the initial reaction rates were estimated from the torque variations. The dissolution of the steel into the molten slag was correlated to the variation in torque. The kinetics of the reaction between the rods and the slag estimated from the torque and subsequently from the viscosity were confirmed from the mass balance and from the variation in the chemical compositions of the rods and the molten slags, respectively. The liquid-phase mass transfer coefficient of Al2O3 was calculated to be 1.14 × 10−2 cm/s at 1623 K (1350 °C) and 1.52 × 10−2 cm/s at 1633 K (1360 °C). The kinetics calculated assuming liquid-phase mass transfer control was observed to be similar to the aforementioned kinetics determined from the dynamic viscosity variations. On the basis of dimensionless analysis of the Sherwood number (Sh = 0.05·Re0.65Sc0.31), liquid-phase mass transfer from the metal/flux interface was observed to be the rate-controlling step.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat M.S. Kim, S.W. Lee, J.W. Cho, M.S. Park, H.G. Lee, and Y.B. Kang: Metall. Mater. Trans. B, 2013, vol. 44 (2), pp. 299-308.CrossRef M.S. Kim, S.W. Lee, J.W. Cho, M.S. Park, H.G. Lee, and Y.B. Kang: Metall. Mater. Trans. B, 2013, vol. 44 (2), pp. 299-308.CrossRef
2.
Zurück zum Zitat Y.B. Kang, M.S. Kim, S.W. Lee, J.W. Cho, M.S. Park, and H.G. Lee: Metall. Mater. Trans. B, 2013, vol. 44 (2), pp. 309-316.CrossRef Y.B. Kang, M.S. Kim, S.W. Lee, J.W. Cho, M.S. Park, and H.G. Lee: Metall. Mater. Trans. B, 2013, vol. 44 (2), pp. 309-316.CrossRef
3.
Zurück zum Zitat D.J. Kim and J.H. Park: Metall. Mater. Trans. B, 2012, vol. 43 (4), pp. 875-886.CrossRef D.J. Kim and J.H. Park: Metall. Mater. Trans. B, 2012, vol. 43 (4), pp. 875-886.CrossRef
4.
Zurück zum Zitat Q. Wang, S. Qiu, and P. Zhao: Metall. Mater. Trans. B, 2012, vol. 43 (2), pp. 424-430.CrossRef Q. Wang, S. Qiu, and P. Zhao: Metall. Mater. Trans. B, 2012, vol. 43 (2), pp. 424-430.CrossRef
5.
Zurück zum Zitat M. Wang, Y. Kobayashi, R. Endo, and M. Susa: ISIJ Int., 2013, vol. 53 (1), pp. 56-61.CrossRef M. Wang, Y. Kobayashi, R. Endo, and M. Susa: ISIJ Int., 2013, vol. 53 (1), pp. 56-61.CrossRef
7.
Zurück zum Zitat H.S. Park, H. Kim, and I. Sohn: Metall. Mater. Trans. B, 2011, vol. 42 (2), pp. 324-330.CrossRef H.S. Park, H. Kim, and I. Sohn: Metall. Mater. Trans. B, 2011, vol. 42 (2), pp. 324-330.CrossRef
8.
Zurück zum Zitat G.H. Kim and I. Sohn: J. Non-Cryst. Solids, 2012, vol. 358 (12-13), pp. 1530-1537.CrossRef G.H. Kim and I. Sohn: J. Non-Cryst. Solids, 2012, vol. 358 (12-13), pp. 1530-1537.CrossRef
9.
Zurück zum Zitat Y.U. Kim and R.D. Pehlke: Metall. Trans., 1974, vol. 5, pp. 2527-2532.CrossRef Y.U. Kim and R.D. Pehlke: Metall. Trans., 1974, vol. 5, pp. 2527-2532.CrossRef
10.
Zurück zum Zitat X. Yu, R.J. Pomfret, and K.S. Coley: Metall. Mater. Trans. B, 1997, vol. 288 (2), pp. 275-279.CrossRef X. Yu, R.J. Pomfret, and K.S. Coley: Metall. Mater. Trans. B, 1997, vol. 288 (2), pp. 275-279.CrossRef
11.
Zurück zum Zitat J.Y. Choi, H.G. Lee, and J.S. Kim: ISIJ Int., 2002, vol. 42 (8), pp. 852-860.CrossRef J.Y. Choi, H.G. Lee, and J.S. Kim: ISIJ Int., 2002, vol. 42 (8), pp. 852-860.CrossRef
12.
Zurück zum Zitat E.T. Turkdogan, Physical Chemistry of High Temperature Technology, Academic Press, New York, 1980. E.T. Turkdogan, Physical Chemistry of High Temperature Technology, Academic Press, New York, 1980.
13.
Zurück zum Zitat A.H. Bui, H.M. Ha, I.S. Chung, and H.G. Lee: ISIJ Int., 2005, vol. 45 (12), pp. 1856-1863.CrossRef A.H. Bui, H.M. Ha, I.S. Chung, and H.G. Lee: ISIJ Int., 2005, vol. 45 (12), pp. 1856-1863.CrossRef
14.
Zurück zum Zitat J.W. Robison and R.D. Pehlke: Metall. Trans., 1974, vol. 5 (5), pp. 1041-1051.CrossRef J.W. Robison and R.D. Pehlke: Metall. Trans., 1974, vol. 5 (5), pp. 1041-1051.CrossRef
15.
Zurück zum Zitat H.G. Katayama, T. Momono, M. Doe, and H. Saitoh: ISIJ int., 1994, vol. 34 (2), pp. 171-176.CrossRef H.G. Katayama, T. Momono, M. Doe, and H. Saitoh: ISIJ int., 1994, vol. 34 (2), pp. 171-176.CrossRef
16.
Zurück zum Zitat J. Park, S. Sridhar, and R. Fruehan: Metall. Mater. Trans. B, 2015, vol. 46 (1), pp. 109-118.CrossRef J. Park, S. Sridhar, and R. Fruehan: Metall. Mater. Trans. B, 2015, vol. 46 (1), pp. 109-118.CrossRef
17.
Zurück zum Zitat B. Pesic and T. Seal: Metall. Trans. B, 1990, vol. 21 (3), pp. 419-427.CrossRef B. Pesic and T. Seal: Metall. Trans. B, 1990, vol. 21 (3), pp. 419-427.CrossRef
18.
Zurück zum Zitat M. Lee, S. Sun, S. Wright, and S. Jahanshahi: Metall. Mater. Trans. B, 2001, vol. 32 (1), pp. 25-29.CrossRef M. Lee, S. Sun, S. Wright, and S. Jahanshahi: Metall. Mater. Trans. B, 2001, vol. 32 (1), pp. 25-29.CrossRef
19.
Zurück zum Zitat Z. Asaki, M. Shiki, H. Kusuno, H. Kato, H. Doi, and Y. Kondo: Metall. Trans. B, 1986, vol. 17 (4), pp. 639-645.CrossRef Z. Asaki, M. Shiki, H. Kusuno, H. Kato, H. Doi, and Y. Kondo: Metall. Trans. B, 1986, vol. 17 (4), pp. 639-645.CrossRef
Metadaten
Titel
Interfacial Kinetics of High-Al-Containing Ultra-Lightweight Steels with Calcium Silicate-Based Molten Oxides at High Temperature
verfasst von
Gi Hyun Kim
Il Sohn
Publikationsdatum
14.03.2016
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions B / Ausgabe 3/2016
Print ISSN: 1073-5615
Elektronische ISSN: 1543-1916
DOI
https://doi.org/10.1007/s11663-016-0650-9

Weitere Artikel der Ausgabe 3/2016

Metallurgical and Materials Transactions B 3/2016 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.