Investigating the Significance of Bicarbonate with the Corrosion of High-Strength Steel in CO2-Saturated Solutions

verfasst von: Faysal Fayez Eliyan, Akram Alfantazi

Erschienen in: Journal of Materials Engineering and Performance | Ausgabe 11/2014

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

This paper presents an electrochemical study on the corrosion behavior of API-X100 steel, heat-treated to have microstructures similar to those of the heat-affected zones (HAZs) of pipeline welding, in bicarbonate-CO2 saturated solutions. The corrosion reactions, onto the surface and through the passive films, are simulated by cyclic voltammetry. The interrelation between bicarbonate concentration and CO2 hydration is analyzed during the filming process at the open-circuit potentials. In dilute bicarbonate solutions, H2CO3 drives more dominantly the cathodic reduction and the passive films form slowly. In the concentrated solutions, bicarbonate catalyzes both the anodic and cathodic reactions, only initially, after which it drives a fast-forming thick passivation that inhibits the underlying dissolution and impedes the cathodic reduction. The significance of the substrate is as critical as that of passivation in controlling the course of the corrosion reactions in the dilute solutions. For fast-cooled (heat treatment) HAZs, its metallurgical significance becomes more comparable to that of slower-cooled HAZs as the bicarbonate concentration is higher.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat G. Bolzon, T. Boukharouba, G. Gabetta, M. Elboujdaini, and M. Mellas, Integrity of Pipelines Transporting Hydrocarbons: Corrosion, Mechanisms, Control, and Management, 1st ed., Springer, Dordrecht, 2011CrossRef G. Bolzon, T. Boukharouba, G. Gabetta, M. Elboujdaini, and M. Mellas, Integrity of Pipelines Transporting Hydrocarbons: Corrosion, Mechanisms, Control, and Management, 1st ed., Springer, Dordrecht, 2011CrossRef
2.
Zurück zum Zitat A. Otazo, PDVSA’S Possible Sale of CITGO and the Subsequent Ramifications on US Foreign and Energy Policy, Energy Policy, 2012, 42, p 89–94CrossRef A. Otazo, PDVSA’S Possible Sale of CITGO and the Subsequent Ramifications on US Foreign and Energy Policy, Energy Policy, 2012, 42, p 89–94CrossRef
3.
Zurück zum Zitat A. Kemp, An Assessment of UK North Sea Oil and Gas Policies Twenty-Five Years, Energy Policy, 1990, 18, p 599–623CrossRef A. Kemp, An Assessment of UK North Sea Oil and Gas Policies Twenty-Five Years, Energy Policy, 1990, 18, p 599–623CrossRef
4.
Zurück zum Zitat M. Ozturk, Y. Yuksel, and N. Ozek, A Bridge Between East and West: Turkey’s Natural Gas Policy, Renew. Sustain. Energy Rev., 2011, 15, p 4286–4294CrossRef M. Ozturk, Y. Yuksel, and N. Ozek, A Bridge Between East and West: Turkey’s Natural Gas Policy, Renew. Sustain. Energy Rev., 2011, 15, p 4286–4294CrossRef
5.
Zurück zum Zitat F. Eliyan and A. Alfantazi, Corrosion of the Heat-Affected Zones (HAZs) of API-X100 Pipeline Steel in Dilute Bicarbonate Solutions at 90 °C: An Electrochemical Evaluation, Corros. Sci., 2013, 74, p 297–307CrossRef F. Eliyan and A. Alfantazi, Corrosion of the Heat-Affected Zones (HAZs) of API-X100 Pipeline Steel in Dilute Bicarbonate Solutions at 90 °C: An Electrochemical Evaluation, Corros. Sci., 2013, 74, p 297–307CrossRef
6.
Zurück zum Zitat F. Mohammadi, F. Eliyan, and A. Alfantazi, Corrosion of Simulated Weld HAZ of API, X-80 Pipeline Steel, Corros. Sci., 2012, 63, p 323–333CrossRef F. Mohammadi, F. Eliyan, and A. Alfantazi, Corrosion of Simulated Weld HAZ of API, X-80 Pipeline Steel, Corros. Sci., 2012, 63, p 323–333CrossRef
7.
Zurück zum Zitat F. Eliyan, F. Icre, A. Alfantazi, Passivation of HAZs of API-X100 Pipeline Steel in Bicarbonate-Carbonate Solutions at 298 K, Mater. Corros., 2013. doi:10.1002/maco.201206985 F. Eliyan, F. Icre, A. Alfantazi, Passivation of HAZs of API-X100 Pipeline Steel in Bicarbonate-Carbonate Solutions at 298 K, Mater. Corros., 2013. doi:10.​1002/​maco.​201206985
8.
Zurück zum Zitat R. Parkins and S. Zhou, The Stress Corrosion Cracking of C-Mn Steel in CO2-HCO3 −-CO3 2− Solutions. II. Electrochemical and Other Data, Corros. Sci., 1997, 39, p 175–191CrossRef R. Parkins and S. Zhou, The Stress Corrosion Cracking of C-Mn Steel in CO2-HCO3 -CO3 2− Solutions. II. Electrochemical and Other Data, Corros. Sci., 1997, 39, p 175–191CrossRef
9.
Zurück zum Zitat F. Eliyan and A. Alfantazi, Influence of Temperature on the Corrosion of API-X100 Pipeline Steel in 1-Bar CO2-HCO3 − Solutions: An Electrochemical Study, Mater. Chem. Phys., 2013, 140, p 508–515CrossRef F. Eliyan and A. Alfantazi, Influence of Temperature on the Corrosion of API-X100 Pipeline Steel in 1-Bar CO2-HCO3 Solutions: An Electrochemical Study, Mater. Chem. Phys., 2013, 140, p 508–515CrossRef
10.
Zurück zum Zitat G. Burstein and D. Davies, The Electrochemical Behavior of Scratched Iron Surfaces in Aqueous Solutions, J. Electrochem. Soc., 1981, 128, p 33–39CrossRef G. Burstein and D. Davies, The Electrochemical Behavior of Scratched Iron Surfaces in Aqueous Solutions, J. Electrochem. Soc., 1981, 128, p 33–39CrossRef
11.
Zurück zum Zitat E. Castro, C. Valentini, C. Moina, J. Vilche, and A. Arvia, The Influence of Ionic Composition on the Electrodissolution and Passivation of Iron Electrodes in Potassium Carbonate-Bicarbonate Solutions in the 8.4-10.5 pH Range at 25 °C, Corros. Sci., 1986, 26, p 791–793CrossRef E. Castro, C. Valentini, C. Moina, J. Vilche, and A. Arvia, The Influence of Ionic Composition on the Electrodissolution and Passivation of Iron Electrodes in Potassium Carbonate-Bicarbonate Solutions in the 8.4-10.5 pH Range at 25 °C, Corros. Sci., 1986, 26, p 791–793CrossRef
12.
Zurück zum Zitat C. Valentini and C. Moina, The Electrochemical Behavior of Iron in Stagnant and Stirred Potassium Carbonate-Bicarbonate Solutions in the 0-75 °C Temperature Range, Corros. Sci., 1985, 25, p 985–997CrossRef C. Valentini and C. Moina, The Electrochemical Behavior of Iron in Stagnant and Stirred Potassium Carbonate-Bicarbonate Solutions in the 0-75 °C Temperature Range, Corros. Sci., 1985, 25, p 985–997CrossRef
13.
Zurück zum Zitat C. de Waard, D.E. Milliams, Prediction of Carbonic Acid Corrosion in Natural Gas Pipelines, First International Conference on the Internal and External Corrosion of Pipes, Paper F1, University of Durham, Durham, 1975 C. de Waard, D.E. Milliams, Prediction of Carbonic Acid Corrosion in Natural Gas Pipelines, First International Conference on the Internal and External Corrosion of Pipes, Paper F1, University of Durham, Durham, 1975
14.
Zurück zum Zitat S. Simard, M. Drogowska, and H. Menard, Electrochemical Behavior of 1024, Mild Steel in Slightly Alkaline Bicarbonate Solutions, J. Appl. Electrochem., 1997, 27, p 317–324CrossRef S. Simard, M. Drogowska, and H. Menard, Electrochemical Behavior of 1024, Mild Steel in Slightly Alkaline Bicarbonate Solutions, J. Appl. Electrochem., 1997, 27, p 317–324CrossRef
15.
Zurück zum Zitat D. Davies and G. Burstein, The Effects of Bicarbonate on the Corrosion and Passivation of Iron, Corrosion, 1980, 36, p 416–422CrossRef D. Davies and G. Burstein, The Effects of Bicarbonate on the Corrosion and Passivation of Iron, Corrosion, 1980, 36, p 416–422CrossRef
16.
Zurück zum Zitat E. Castro, J. Vilche, and A. Arvia, Iron Dissolution and Passivation in K2CO3-KHCO3 Solutions. Rotating Ring Disc Electrode and XPS Studies, Corros. Sci., 1991, 32, p 37–50CrossRef E. Castro, J. Vilche, and A. Arvia, Iron Dissolution and Passivation in K2CO3-KHCO3 Solutions. Rotating Ring Disc Electrode and XPS Studies, Corros. Sci., 1991, 32, p 37–50CrossRef
17.
Zurück zum Zitat Z. Lu, C. Huang, D. Huang, and W. Yang, Effects of a Magnetic Field on the Anodic Dissolution, Passivation and Transpassivation Behaviour of Iron in Weakly Alkaline Solutions with or Without Halides, Corros. Sci., 2006, 48, p 3049–3077CrossRef Z. Lu, C. Huang, D. Huang, and W. Yang, Effects of a Magnetic Field on the Anodic Dissolution, Passivation and Transpassivation Behaviour of Iron in Weakly Alkaline Solutions with or Without Halides, Corros. Sci., 2006, 48, p 3049–3077CrossRef
18.
Zurück zum Zitat F. Eliyan, A. Alfantazi, Mechanisms of Corrosion and Electrochemical Significance of Metallurgy and Environment with Corrosion of Iron and Steel in Bicarbonate and Carbonate Solutions: A Review, Corrosion. doi:10.5006/1213, in press F. Eliyan, A. Alfantazi, Mechanisms of Corrosion and Electrochemical Significance of Metallurgy and Environment with Corrosion of Iron and Steel in Bicarbonate and Carbonate Solutions: A Review, Corrosion. doi:10.​5006/​1213, in press
19.
Zurück zum Zitat F. Eliyan, A. Alfantazi, Corrosion Cyclic Voltammetry of Two Types of Heat-Affected Zones (HAZs) of API-X100 Steel in Bicarbonate Solutions, Metall. Mater. Trans. B, under review F. Eliyan, A. Alfantazi, Corrosion Cyclic Voltammetry of Two Types of Heat-Affected Zones (HAZs) of API-X100 Steel in Bicarbonate Solutions, Metall. Mater. Trans. B, under review
20.
Zurück zum Zitat G. Burstein and D. Davies, The Effects of Anions on the Behaviour of Scratched Iron Electrodes in Aqueous Solutions, Corros. Sci., 1980, 20, p 1143–1155CrossRef G. Burstein and D. Davies, The Effects of Anions on the Behaviour of Scratched Iron Electrodes in Aqueous Solutions, Corros. Sci., 1980, 20, p 1143–1155CrossRef
21.
Zurück zum Zitat E. Castro and J. Vilche, Electrooxidation/Electroreduction Processes at Composite Iron Hydroxide Layers in Carbonate-Bicarbonate Buffers, J. Appl. Electrochem., 1991, 21, p 543–551CrossRef E. Castro and J. Vilche, Electrooxidation/Electroreduction Processes at Composite Iron Hydroxide Layers in Carbonate-Bicarbonate Buffers, J. Appl. Electrochem., 1991, 21, p 543–551CrossRef
22.
Zurück zum Zitat C. Rangel, I. Fonseca, and R. Leitão, Some Aspects of the Electrochemical Behavior of Mild Steel in Carbonate/Bicarbonate Solutions, Electrochim. Acta, 1986, 31, p 1659–1662CrossRef C. Rangel, I. Fonseca, and R. Leitão, Some Aspects of the Electrochemical Behavior of Mild Steel in Carbonate/Bicarbonate Solutions, Electrochim. Acta, 1986, 31, p 1659–1662CrossRef
23.
Zurück zum Zitat L. Niu and Y. Cheng, Corrosion Behaviour of X-70 Pipe Steel in Near-Neutral pH Solution, Appl. Surf. Sci., 2007, 253, p 8626–8631CrossRef L. Niu and Y. Cheng, Corrosion Behaviour of X-70 Pipe Steel in Near-Neutral pH Solution, Appl. Surf. Sci., 2007, 253, p 8626–8631CrossRef
24.
Zurück zum Zitat B. Sherar, P. Keech, Z. Qin, F. King, D. Shoesmith, Nominally Aerobic Corrosion of Carbon Steel in Near-Neutral pH Saline Environments, Corrosion, 2010, 66, p 45001-1–45001-11 B. Sherar, P. Keech, Z. Qin, F. King, D. Shoesmith, Nominally Aerobic Corrosion of Carbon Steel in Near-Neutral pH Saline Environments, Corrosion, 2010, 66, p 45001-1–45001-11
25.
Zurück zum Zitat G. Zhang and Y. Cheng, Micro-electrochemical Characterization and Mott-Schottky Analysis of Corrosion of Welded X70 Pipeline Steel in Carbonate/Bicarbonate Solution, Electrochim. Acta, 2009, 55, p 316–324CrossRef G. Zhang and Y. Cheng, Micro-electrochemical Characterization and Mott-Schottky Analysis of Corrosion of Welded X70 Pipeline Steel in Carbonate/Bicarbonate Solution, Electrochim. Acta, 2009, 55, p 316–324CrossRef
26.
Zurück zum Zitat A. Fu and Y. Cheng, Electrochemical Polarization Behavior of X70 Steel in Thin Carbonate/Bicarbonate Solution Layers Trapped Under a Disbonded Coating and its Implication on Pipeline SCC, Corros. Sci., 2010, 52, p 2511–2518CrossRef A. Fu and Y. Cheng, Electrochemical Polarization Behavior of X70 Steel in Thin Carbonate/Bicarbonate Solution Layers Trapped Under a Disbonded Coating and its Implication on Pipeline SCC, Corros. Sci., 2010, 52, p 2511–2518CrossRef
27.
Zurück zum Zitat F. Eliyan, E. Mahdi, and A. Alfantazi, Electrochemical Evaluation of the Corrosion Behaviour of API-X100 Pipeline Steel in Aerated Bicarbonate Solutions, Corros. Sci., 2012, 58, p 181–191CrossRef F. Eliyan, E. Mahdi, and A. Alfantazi, Electrochemical Evaluation of the Corrosion Behaviour of API-X100 Pipeline Steel in Aerated Bicarbonate Solutions, Corros. Sci., 2012, 58, p 181–191CrossRef
28.
Zurück zum Zitat F. Eliyan, E. Mahdi, Z. Farhat, and A. Alfantazi, Interpreting the Passivation of HSLA Steel from Electrochemical Corrosion Investigations in Bicarbonate-Oil Aqueous Emulsions, Int. J. Electrochem. Sci., 2013, 8, p 3026–3038 F. Eliyan, E. Mahdi, Z. Farhat, and A. Alfantazi, Interpreting the Passivation of HSLA Steel from Electrochemical Corrosion Investigations in Bicarbonate-Oil Aqueous Emulsions, Int. J. Electrochem. Sci., 2013, 8, p 3026–3038
29.
Zurück zum Zitat B. Linter and G. Burstein, Reactions of Pipeline Steels in Carbon Dioxide Solutions, Corros. Sci., 1999, 41, p 117–139CrossRef B. Linter and G. Burstein, Reactions of Pipeline Steels in Carbon Dioxide Solutions, Corros. Sci., 1999, 41, p 117–139CrossRef
30.
Zurück zum Zitat D. Brasher, Stability of the Oxide Film on Metals in Relation to Inhibition of Corrosion. II. Dual Role of the Anion in the Mild Inhibition of the Corrosion of Mild Steel, Br. Corros. J., 1968, 4, p 122–128CrossRef D. Brasher, Stability of the Oxide Film on Metals in Relation to Inhibition of Corrosion. II. Dual Role of the Anion in the Mild Inhibition of the Corrosion of Mild Steel, Br. Corros. J., 1968, 4, p 122–128CrossRef
31.
Zurück zum Zitat J. Thomas, T. Nurse, and R. Walker, Anodic Passivation of Iron in Carbonate Solutions, Br. Corros. J., 1970, 5, p 87–92CrossRef J. Thomas, T. Nurse, and R. Walker, Anodic Passivation of Iron in Carbonate Solutions, Br. Corros. J., 1970, 5, p 87–92CrossRef
32.
Zurück zum Zitat M. Nagayama and M. Cohen, The Anodic Oxidation of Iron in a Neutral Solution II. Effect of Ferrous Ion and pH on the Behavior of Passive Iron, J. Electrochem. Soc., 1963, 110, p 670–680CrossRef M. Nagayama and M. Cohen, The Anodic Oxidation of Iron in a Neutral Solution II. Effect of Ferrous Ion and pH on the Behavior of Passive Iron, J. Electrochem. Soc., 1963, 110, p 670–680CrossRef
33.
Zurück zum Zitat L. Moiseeva, Carbon Dioxide Corrosion of Oil and Gas Field Equipment, Prot. Met, 2005, 41, p 76–83CrossRef L. Moiseeva, Carbon Dioxide Corrosion of Oil and Gas Field Equipment, Prot. Met, 2005, 41, p 76–83CrossRef
34.
Zurück zum Zitat K. Videm and A. Koren, Corrosion, Passivity, and Pitting of Carbon Steel in Aqueous Solutions of HCO3 −, CO2, and Cl−, Corrosion, 1993, 49, p 746–754CrossRef K. Videm and A. Koren, Corrosion, Passivity, and Pitting of Carbon Steel in Aqueous Solutions of HCO3 , CO2, and Cl, Corrosion, 1993, 49, p 746–754CrossRef
Metadaten
Titel
Investigating the Significance of Bicarbonate with the Corrosion of High-Strength Steel in CO2-Saturated Solutions
verfasst von
Faysal Fayez Eliyan
Akram Alfantazi
Publikationsdatum
01.11.2014
Verlag
Springer US
Erschienen in
Journal of Materials Engineering and Performance / Ausgabe 11/2014
Print ISSN: 1059-9495
Elektronische ISSN: 1544-1024
DOI
https://doi.org/10.1007/s11665-014-1200-8

Weitere Artikel der Ausgabe 11/2014

Journal of Materials Engineering and Performance 11/2014 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.