Investigation of Microstructural Evolution and Mechanical Properties of IN617 Superalloy During Long-Term Operating at High Temperature

verfasst von: Mohsen Mehdizadeh, Hassan Farhangi

Erschienen in: Metals and Materials International | Ausgabe 11/2022

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In the present paper, microstructural evolutions and its effect on the mechanical properties of IN617 were investigated in as-received and worked conditions. Worked samples had been operated at 800 °C, under average working stress for operating times of 65,000 and 98,000 h. The different phases were extracted by phase extraction methods. The OM, SEM, TEM, XRD, hardness, impact, stress rupture and tensile tests are used to investigate the microstructure and mechanical properties of operated alloys. The main phases in the specimens are M23C6 and M6C carbides and Ti(C,N) compounds. In addition to these three compounds, γ' phase was also observed in both samples, despite the long operating time; although its volume fraction in the second sample (98,000 h) was less than the first sample (65,000 h). A very small amount of δ phase, topologically closed packed phase, was also detected in the samples. With increasing operating time, the area fraction of carbides increased from 0.5% in the as-received plate to 5.5% in the 98,000 h specimen. Unlike M23C6 carbide, which has an increasing trend with operating time, M6C carbide decreased from 25.7% in the 65,000 h sample to 18.7% in the 98,000 h sample. This decrease is attributed to the M6C + M′ → M23C6 + M′′ reaction. The observed phases are in the form of plate shape, quasi-spherical and irregular and their dimensions increase with increasing operating time. The hardness and strength values are higher in the 65,000 h sample than both the 98,000 h sample and the as-received plate. However these values in the 98,000 h are higher than as-received plate.

Graphical abstract

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat S. Chomette, J.M. Gentzbittel, B. Viguier, J. Nucl. Mater. 399, 266 (2010)CrossRef S. Chomette, J.M. Gentzbittel, B. Viguier, J. Nucl. Mater. 399, 266 (2010)CrossRef
2.
Zurück zum Zitat T.S. Jo, S.-H. Kim, D.-G. Kim, J.Y. Park, Y.D. Kim, Met. Mater. Int. 14, 739 (2008)CrossRef T.S. Jo, S.-H. Kim, D.-G. Kim, J.Y. Park, Y.D. Kim, Met. Mater. Int. 14, 739 (2008)CrossRef
3.
Zurück zum Zitat S.F. Di Martino, R.G. Faulkner, S.C. Hogg, S. Vujic, O. Tassa, Mater. Sci. Eng. A 619, 77 (2014)CrossRef S.F. Di Martino, R.G. Faulkner, S.C. Hogg, S. Vujic, O. Tassa, Mater. Sci. Eng. A 619, 77 (2014)CrossRef
4.
5.
Zurück zum Zitat Y. Yuan, Z.H. Zhong, Z.S. Yu, H.F. Yin, Y.Y. Dang, X.B. Zhao, Z. Yang, J.T. Lu, J.B. Yan, Y. Gu, Met. Mater. Int. 21, 659 (2015)CrossRef Y. Yuan, Z.H. Zhong, Z.S. Yu, H.F. Yin, Y.Y. Dang, X.B. Zhao, Z. Yang, J.T. Lu, J.B. Yan, Y. Gu, Met. Mater. Int. 21, 659 (2015)CrossRef
6.
Zurück zum Zitat D. Tytko, P.-P. Choi, J. Klower, A. Kostka, G. Inden, D. Raabe, Acta Mater. 60, 1731 (2012)CrossRef D. Tytko, P.-P. Choi, J. Klower, A. Kostka, G. Inden, D. Raabe, Acta Mater. 60, 1731 (2012)CrossRef
7.
Zurück zum Zitat Y. Zhao, H. Yao, X. Song, J. Jia, Z. Xiang, Met. Mater. Int. 24, 51 (2018)CrossRef Y. Zhao, H. Yao, X. Song, J. Jia, Z. Xiang, Met. Mater. Int. 24, 51 (2018)CrossRef
8.
Zurück zum Zitat M. Speicher, F. Kauffmann, J.-H. Shim, M. Chandran, Mater. Sci. Eng. A 711, 165 (2018)CrossRef M. Speicher, F. Kauffmann, J.-H. Shim, M. Chandran, Mater. Sci. Eng. A 711, 165 (2018)CrossRef
10.
11.
Zurück zum Zitat W.L. Mankins, J.C. Hosier, T.H. Bassford, Metall. Mater. Trans. B 5, 2579 (1974)CrossRef W.L. Mankins, J.C. Hosier, T.H. Bassford, Metall. Mater. Trans. B 5, 2579 (1974)CrossRef
12.
Zurück zum Zitat R. Krishna, S.V. Hainsworth, S.P.A. Gill, A. Strang, H.V. Atkinson, Metall. Mater. Trans. A 44, 1419 (2013)CrossRef R. Krishna, S.V. Hainsworth, S.P.A. Gill, A. Strang, H.V. Atkinson, Metall. Mater. Trans. A 44, 1419 (2013)CrossRef
13.
Zurück zum Zitat Q. Wu, H. Song, R.W. Swindeman, J.P. Shingledecker, V.K. Vasudevan, Metall. Mater. Trans. A 39, 2569 (2008)CrossRef Q. Wu, H. Song, R.W. Swindeman, J.P. Shingledecker, V.K. Vasudevan, Metall. Mater. Trans. A 39, 2569 (2008)CrossRef
14.
Zurück zum Zitat M. Cabibbo, E. Gariboldi, S. Spigarelli, D. Ripamonti, J. Mater. Sci. 43, 2912 (2008)CrossRef M. Cabibbo, E. Gariboldi, S. Spigarelli, D. Ripamonti, J. Mater. Sci. 43, 2912 (2008)CrossRef
15.
Zurück zum Zitat S. Kihara, J.B. Newkirk, A. Ohtomo, Y. Saiga, Metall. Trans. A 11, 1019 (1980)CrossRef S. Kihara, J.B. Newkirk, A. Ohtomo, Y. Saiga, Metall. Trans. A 11, 1019 (1980)CrossRef
16.
Zurück zum Zitat H.W. Jeong, S.M. Seo, B.G. Choi, Y.S. Yoo, Y.K. Ahn, J.H. Lee, Met. Mater. Int. 19, 917 (2013)CrossRef H.W. Jeong, S.M. Seo, B.G. Choi, Y.S. Yoo, Y.K. Ahn, J.H. Lee, Met. Mater. Int. 19, 917 (2013)CrossRef
17.
Zurück zum Zitat R. Krishna, S.V. Hainsworth, H.V. Atkinson, A. Strang, Mater. Sci. Technol. 26, 797 (2010)CrossRef R. Krishna, S.V. Hainsworth, H.V. Atkinson, A. Strang, Mater. Sci. Technol. 26, 797 (2010)CrossRef
20.
Zurück zum Zitat P.J. Ennis, A. Strang, S.P. Gill, G.M. McColvin, H.V. Atkinson, Energy Mater. 4, 184 (2009)CrossRef P.J. Ennis, A. Strang, S.P. Gill, G.M. McColvin, H.V. Atkinson, Energy Mater. 4, 184 (2009)CrossRef
22.
Zurück zum Zitat R. Krishna, H.V. Atkison, S.V. Hainsworth, S.P. Gill, Metall. Mater. Trans. A 47, 178 (2016)CrossRef R. Krishna, H.V. Atkison, S.V. Hainsworth, S.P. Gill, Metall. Mater. Trans. A 47, 178 (2016)CrossRef
23.
Zurück zum Zitat W.-G. Kim, I.M.W. Ekaputra, J.-Y. Park, M.-H. Kim, Y.-W. Kim, Nucl. Eng. Des. 306, 177 (2016)CrossRef W.-G. Kim, I.M.W. Ekaputra, J.-Y. Park, M.-H. Kim, Y.-W. Kim, Nucl. Eng. Des. 306, 177 (2016)CrossRef
Metadaten
Titel
Investigation of Microstructural Evolution and Mechanical Properties of IN617 Superalloy During Long-Term Operating at High Temperature
verfasst von
Mohsen Mehdizadeh
Hassan Farhangi
Publikationsdatum
03.06.2022
Verlag
The Korean Institute of Metals and Materials
Erschienen in
Metals and Materials International / Ausgabe 11/2022
Print ISSN: 1598-9623
Elektronische ISSN: 2005-4149
DOI
https://doi.org/10.1007/s12540-022-01174-z

Weitere Artikel der Ausgabe 11/2022

Metals and Materials International 11/2022 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.