Abstract
Experimental investigations have been carried out to study the phase separation process in the TeO2-B2O3 system. It was found that the phase diagram is of a eutectic-like type (monotectic invariant reaction), with a wide region of stable and metastable phase separation. During the cooling of the melts two phases are obtained. One has a high TeO2 content and is a transparent glass. The other, richer in B2O3, is opaque and in structure constitutes a complicated microheterogeneous system.
Access this article
We’re sorry, something doesn't seem to be working properly.
Please try refreshing the page. If that doesn't work, please contact support so we can address the problem.
Similar content being viewed by others
References
N. Toropov, V. Barzakovskii, V. Lapin and N. Kurtseva, “Diagrammi sostoyaniya silikatnih sistem” (Nauka, Leningrad, 1969).
R. J. Charles, j. Amer. Ceram. Soc. 49 (1966) 55.
R. R. Shaw and D. R. Uhlmann, ibid 51 (1968) 377.
S. Malutin, Ph.D. Thesis, MHTI “D. Mendeleev” (Moskow, 1970).
A. Yahkind and N. Martyshchenko, Comm. Acad. Scis. USSR, Inorganic Materials 6 (1970) 1459.
V. I. Mazepova, K. K. Samplavskaya, M. H. Karapetyants and V. I. Grachev, Trudi MHTI “D. Mendeleev” 67 (1970) 45.
Y. Dimitriev, M. Marinov, Y. Ivanova and L. Lakov, Compt. Rend. Acad. Bulg. Sci. 25 (1972) 1533.
W. Vogel, W. Schmidt and L. Horn, Silikattechnik 23 (1974) 112.
F. Galahov, “Strukturnie prevrashcheniya v steklah pri povishenih temperaturah” (Nauka, Moscow, Leningrad, 1965).
R. Roy, j. Amer. Ceram. Soc. 43 (1960) 670.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Dimitriev, Y., Kashchieva, E. Immiscibility in the TeO2-B2O3 system. J Mater Sci 10, 1419–1424 (1975). https://doi.org/10.1007/BF00540832
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF00540832