Abstract
Some magnetic properties of the spinel structure compound, Li0.5+0.5xTixFe2.5-1.5xO4, wherex=0−0.5, have been studied by different methods. The initial permeability, μi, was measured as a function of temperature at a constant frequency of 10 kHz. A maximum value was observed for each composition indicating the Curie temperature,Tc, which decreases with increasing titanium concentration. The magnetization,M, and theB-H loop were measured atRT in the range of magnetizing field from 0–1200 Am−1 and at constant fieldH=205 Am−1, respectively. The relative permeability, μr, depends on the magnetizing field and composition. It was found from theB-H loop that the remanence induction,Br, and the apparent loss energy,Ps, depend on the composition but the coercive force,Hc, is independent of composition.
Similar content being viewed by others
References
T. G. W. STIJNTIES, J. KLERK and A. BROESE VAN GROENOU,Philips Res. Rep. 25 (1970) 95.
R. HOHNE, K. MELZER, H. HOCHSCHILD, G. LIBOR and R. KRAUSE,Phys. Status solids (a) 27 (1975) K 711.
A. H. WAFIK, S. A. MAZEN and S. F. MANSOUR,J. Phys. D Appl. Phys. 26 (1993) 2010.
J. K. GALT, I. J. MATTHIAS and J. P. REMEIKA,Phys. Rev. 79 (1950) 391.
J. K. GALT,ibid. 85 (1952) 664.
J. L. DORMANN, M. EL HARFAOUI, M. NOGUES and J. JOVE,J. Phys. C Solid State Phys. 20 (1987) L 161.
A. A. YOUSIF, M. E. ELZAIN, S. A. MAZEN, H. H. SUTHERLAND, M. H. ABDALLA and S. F. MANSOUR,J. Phys. C Condensed Matter 6 (1994) 5717.
S. A. POLTINNIKOV and E. I. TURKEVICH,Sov. Phys. Solid State 8 (1966) 1144.
R. BOLL, “Weichmagnetische Werkstoffe”, Vol 3, ‘Völlig überarbeitete und erweiterte Auflage”, (Vacuumschmelze GMBH, 1977).
G. O. WHITE and C. E. PATTON,J. Magn Magn Mater. 9 (1978) 299.
Y. YAFET and C. KITTEL,Phys. Rev. 87 (1952) 290.
K. STANDLY, “Oxide Magnetic Materials” (Clarendon, Oxford, 1972).
H. H. JOSHI and R. G. KULKARNI,J. Mater. Sci. 21 (1986) 2138.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Mazen, S.A., Wafik, A.H. & Mansour, S.F. The effect of Ti4+ ions on some magnetic properties of lithium ferrite. J Mater Sci 31, 2661–2665 (1996). https://doi.org/10.1007/BF00687297
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/BF00687297