Abstract
TiB2 and ZrB2 have been synthesized by a mechano-chemical treatment of a mixture of titania or zirconia powder and amorphous boron followed by a relatively low temperature annealing (1100°C). Both the temperature and the kinetics of the borothermic transformations are affected by the mechano-chemical treatment when the size of the particles obtained after thermal annealing of the sample milled for a short time remains in the sub-micron range. The reaction paths are different for TiB2 and ZrB2 with the formation of TiBO3 and Ti2O3 as intermediate compounds in the case of the borothermic reduction of titania, while in the zirconia/boron system a direct borothermic reduction of zirconium oxide is observed.
Similar content being viewed by others
References
Annual Mineral Review,Am. Ceram. Soc. Bull. 73 (1994) 73.
K. Su andL. G. Sneddon,Chem. Mater. 3 (1991) 10.
Z. Jiang, W. E. Rhine,ibid. 4 (1992) 497.
Idem, J. Eur. Ceram. Soc. 12 (1993) 403.
K. Tkacova, in “Mechanical activation of minerals” Developments in Mineral Processing, Vol. 11, edited by D.W. Fuerstenau (Elsevier, Amsterdam, 1989).
A. P. Radlinski andA. Calka,Mater. Sci. Engng A134 (1991) 1376.
D. D. Radev andD. Klisurski,J. Alloys Comp. 206 (1994) 39.
Manufacturer: ANUtech Pty. Ltd., The Australian National University, Canberra, ACT 0200, Australia.
E. Gaffet, N. Malhouroux-Gaffet, M. Abdellaoui andA. Malchere,Rev. Metal.-CIT/SGM, no. 5 (1994) 757.
D. Michel, F. Faudot, E. Gaffet andL. Mazerolles,J. Amer. Ceram. Soc. 76 (1993) 2884.
Y. L. Chen, M. Qi, J. S. Wu, D. H. Wang andD. Z. Yang,Appl. Phys. Lett. 65 (1994) 303.
P. Millet andT. Hwang,J. Mater. Res. submitted.
P. Millet, private communication.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Millet, P., Hwang, T. Preparation of TiB2 and ZrB2. influence of a mechano-chemical treatment on the borothermic reduction of titania and zirconia. J Mater Sci 31, 351–355 (1996). https://doi.org/10.1007/BF01139151
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01139151