Abstract
The influence of different solvents on the morphology of cellulose during the dissolution process was studied. Spruce sulfite pulp, cotton linters and hydrolysed cotton linters were treated for a short time with lithium chloride: N,N-dimethylacetamide (LiCl:DMAc) and an alkaline solution of iron sodium tartrate (EWNN), respectively. The changes occurring at the fibre surfaces and within the cell walls were observed by scanning as well as by transmission electron microscopy. The cellulose fibres show significant differences in the dissolution behaviour when comparing the reaction of the two solvents. Using LiCl:DMAc, the cotton linters fibres become lamellar separated and within the spruce sulfite pulp fibres solvent channels appear in the first step with the fibrils becoming separated. In contrast, EWNN has a swelling effect on the surface of the cellulose fibres. Both solvent systems predominantly affect the ends of the fibres and places where the wall structure has been damaged.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Dolmetsch, H. (1961) Anzeichen für eine Kettenfaltung in der Feinstruktur der Cellulose.Kolloid Z. 176, 63–64.
Fink, H. P. (1990) Röntgenbeugungsuntersuchungen zur übermolekularen Struktur von Cellulose und deren Verä nderungen infolge Alkalisierung. Thesis B, Academy of Science of the GDR, Teltow-Seehof.
Fink, H.-P., Fanter, D. and Philipp, B. (1985) Röntgenweitwinkeluntersuchungen zur ü bermolekularen Struktur beim Cellulose-I-II-Phasenübergang.Acta Polymerica 36, 1–8.
Forcher, B., Sarto, V. and Prati, G. (1985) Celluloseaktivierung: Geeignete Behandlungen und Strukturveränderungen.Angew. Makromol. Chem. 135, 161–175.
Hampe, H. (1974) Beitrag zum Quell- und Löseverhalten von Cellulosematerialien in wäßrigen Lösungsmitteln unter spezieller Berücksichtigung der Charakterisierung hochgekräuselter Celluloseregeneratfasern. Thesis, Technische Universität Dresden.
Hearle, J. W. S. (1958) A fringed fibril theory of structure in crystalline polymers.J. Polym. Sci. 28, 432–435.
Herlinger, H. and Hengstberger, M. (1985) Verhalten von Cellulose in nicht-konventionellen Lösungsmitteln.Lenzinger Berichte 59, 96–103.
Jayme, G. and Balser, K. (1970) Beitrag zur Elektronenmikroskopie und zum Feinbau der Baumwollfaser.Melliand Textilber. 51, 3–11.
Jayme, G. and El-Kodsi, G. (1968) Über ein neues Verfahren zur Herstellung praktisch sauerstoffunempfindlicher Cellulose-EWNNmod-Lösungen für Viskositätsmessungen und damit erhaltene Ergebnisse.Das Papier 22, 120–124.
Jayme, G. and Harders-Steinhäuser, M. (1960) Vorgänge beim Quellen und Lösen faserfö rmiger Pflanzenzellen in neuen Lösungsmitteln.Das Papier 14, 228–234.
Kling, W., Mahl, H. and Heumann, W. (1963) Beobachtungen an Modifierfasern.Melliand Textilber. 44, 335–339.
Kočevar, F., Pogačnik, M. and Povoden, V. (1957) Eine Modifizierung der Schnellmethode zur Bestimmung des Durchschnittspolymerisationsgrades von Cellulose nach H. Doering.Das Papier 11, 301–303.
Krässig, H. (1977) Neue Strukturuntersuchungen an Cellulosefasern unter Verwendung von Methoden der Molekularcharakterisierung, der IR-Spektroskopie und der Röntgendiffraktion.Lenzinger Ber. 43, 141–151.
Krässig, H. (1984) Struktur und Reaktivität von Cellulosefasern.Das Papier 38, 571–582.
Krässig, H. (1993)Cellulose: structure, accessibility and reactivity. Yverdon: Gordon and Breach Science Publishers.
McCormick, C. L., Callais, P. A. and Hutchinson, B. H., Jr. (1985) Solution studies of cellulose in lithium chloride and N,N-dimethylacetamide.Macromolecules 18, 2394–2401.
Nagler, H. (1994) Veränderungern der Cellulosestruktur unter dem Einfluß von LiCl/N,N-Dimethylacetamid und alkalischer Eisennatriumtartratlösung. Thesis, Technische Universität Dresden.
Philipp, B., Fink, H.-P., Kunze, J. and Figge, K. (1985) NMR-spektroskopische und rö ntgendiffraktometrische Untersuchungen zur Wechselwirkung zwischen Cellulose und Natronlauge.Ann. Physik 42, 507–523.
Prati, G., Forcher, B. and Sarto, V. (1985) Celluloseaktivierung: Geeignete Behandlungen und Strukturveränderungen.Lenzinger Ber. 59, 118–124.
Purz, H. J. and Fink, H.-P. (1983) Zur Morphologie und Gitterumwandlung bei der Alkalisierung von Cellulose.Acta Polymerica 34, 546–558.
Schleicher, H. (1981) Durch Aktivierung der Cellulose verursachte Reaktivitätsveränderungen.Plaste und Kautschuk 28, 495–498.
Schleicher, H. and Philipp, B. (1980) Reaktivitätsbeeinflussung der Cellulose durch Aktivierung.Das Papier,34, 550–554.
Schurz, J. (1980) Die Struktur der Cellulose.Lenzinger Ber. 49, 15–24.
Spurr, A. R. (1969) A low-viscosity epoxy resin embedding medium for electron microscopy.J. Ultrastruct. Res. 26, 31–43.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Pionteck, H., Berger, W., Morgenstern, B. et al. Changes in cellulose structure during dissolution in LiCl:N,N-dimethylacetamide and in the alkaline iron tartrate system EWNN. Cellulose 3, 127–139 (1996). https://doi.org/10.1007/BF02228796
Issue Date:
DOI: https://doi.org/10.1007/BF02228796