Abstract
Phase equilibria in the Al corner of the Al-Fe-Mn-Si system at 550 °C have been explored. Twenty-six quaternary alloys were prepared and analyzed by microprobe analysis. Elemental powders were mixed under air and molten at 1000 °C under argon flux. These specimens received a heat treatment at 550 °C during 4 to 12 weeks and finally were water quenched. A four-phase region, where Al, Si,α-Al(Fe,Mn)Si, andβ-Al(Fe,Mn)Si are in equilibrium with each other, was found. The presence of a single-phaseα-Al(Fe,Mn)Si region, starting in the Al-Mn-Si subsystem and extending toward the Al-Fe-Si subsystem, could be confirmed. Some problems concerning the fit of the quaternary system with its ternary Al-Fe-Mn subsystem remain to be solved.
Similar content being viewed by others
References
V. Stefaniay, A. Griger, and T. Turmezey:J. Mater. Sci. 1987, vol. 22 (2), pp. 539–46.
G. Ghosh: inTernary Alloys: A Comprehensive Compendium of Evaluated Constitutional Data and Phase Diagrams Volume 5, 1st ed., G. Petzow and G. Effenberg, eds., VCH Verlagsgesellschaft, Weinheim, 1992, pp. 394–438.
A. Prince: inTernary Alloys: A Comprehensive Compendium of Evaluated Constitutional Data and Phase Diagrams Volume 7, 1st ed. G. Petzow and G. Effenberg, eds., VCH Verlagsgesellschaft, Weinheim, 1993, pp. 110–28.
P. Rogl and F. Weitzer: University of Vienna, Vienna, unpublished research, 1994.
H.W.L. Phillips and P.C. Varley:JIM, 1943, vol. 69, pp. 317–50.
G. Phragmén:JIM, 1950, vol. 77, pp. 489–552.
J.G. Barlock and L.F. Mondolfo:Z. Metallk., 1975, vol. 66, pp. 605–11.
L.F. Mondolfo:Aluminum Alloys, Structures and Properties, 1st ed., Butterworth and Co., London, 1976, pp. 661–63.
A.M. Zakharov, I.T. Gul’din, A.A. Amol’d, and Yu. A. Matsenko:Izv. Akad. Nauk SSSR, Metall., 1989, vol. 4, pp. 214–18 (English translation).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Davignon, G., Verlinden, B., Delaey, L. et al. An isothermal section at 550 °C in the Al-Rich corner of the Al-Fe-Mn-Si system. Metall Mater Trans A 27, 3357–3361 (1996). https://doi.org/10.1007/BF02595428
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF02595428